CN107227061A - A kind of Formaldehyde-free art paint and preparation method thereof - Google Patents
A kind of Formaldehyde-free art paint and preparation method thereof Download PDFInfo
- Publication number
- CN107227061A CN107227061A CN201710604013.3A CN201710604013A CN107227061A CN 107227061 A CN107227061 A CN 107227061A CN 201710604013 A CN201710604013 A CN 201710604013A CN 107227061 A CN107227061 A CN 107227061A
- Authority
- CN
- China
- Prior art keywords
- parts
- raw material
- preparation
- formaldehyde
- powder raw
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of Formaldehyde-free art paint and preparation method thereof, include the raw material of following parts by weight:48 parts of mould inhibitor O, 75 86 parts of pigment powder, 22 30 parts of sodium sorbate, 58 parts of sodium alginate, 15 30 parts of glycerine, 12 22 parts of organosilicon, 15 25 parts of polyurethane, 34 50 parts of adhesive, 8 13 parts of polyvinyl alcohol 12 35 part, gram bacterium spirit;The adhesive includes synthetic glue powder raw material, natural gum powder raw material, NMF, crack resistence agent and distilled water.Formaldehyde is free of in the art painting pigment of the present invention, toxic gas will not be produced during the production and use of the art painting pigment, and there is good effect of drawing up to the growth of bacterium, it is safer.
Description
Technical field
The present invention relates to pigment preparing technical field, specifically a kind of Formaldehyde-free art paint and preparation method thereof.
Background technology
Pigment is exactly the material that object can be made to catch color.Pigment has solubility and insolubility, there is inorganic sum
Organically difference.Inorganic pigment is usually mineral material, and the mankind are known that very early uses inorganic pigment, using coloured soil and
Ore, draws a picture and smears body on palisades.Organic pigment is typically derived from plant and marine animal, such as alizarin blue, gamboge and Gu Luo
The purple that horse is refined from shellfish.
Art painting pigment by pigment powder, natural plant gum and added include be used for corrosion-resistant formaldehyde and NMF, levelling
The functional aids such as agent, antifreezing agent and crack resistence agent are constituted.Its preparation technology is, first dissolves natural plant gum progress immersion, mistake
Filter, bleaching and precipitation;Then formaldehyde and other auxiliary agents are added in the natural plant gum after precipitation;Finally pigment powder is added above-mentioned
Grinding can prepare drawing pigment in colloid.The following defect of drawing pigment prepared with the presence of above-mentioned technique:First, the face
Material has used formaldehyde to cook preservative, because formaldehyde is a kind of volatile noxious material, not only can be to workman in preparation engineering
Body composition injury, and the picture drawn is in a humid environment, and formaldehyde easily discharges volatilization so that the picture appearance preserved
Easy moldy metamorphism;Second, although formaldehyde is a kind of good preservative, the growth to bacterium is drawn up with good effect,
To on the dry film of the Aspergillus in contained in fruit tree glue and residual fungi, phycomycete and wet environment, Penicillium notatum and picture
Algal fungi the effect do not drawn up of bacterium, therefore not only used the pigment of formaldehyde not only shelf lives be shorter(18 months),
And the bright and new degree preservation and effect for the picture drawn using the pigment containing formol also will not be preferable.Therefore, the present invention is carried
For a kind of new Formaldehyde-free art paint and preparation method thereof.
The content of the invention
It is an object of the invention to provide a kind of Formaldehyde-free art paint and preparation method thereof, to solve above-mentioned background
The problem of being proposed in technology.
To achieve the above object, the present invention provides following technical scheme:
A kind of Formaldehyde-free art paint, includes the raw material of following parts by weight:4-8 parts of mould inhibitor O, pigment powder 75-86
Part, 22-30 parts of sodium sorbate, 5-8 parts of sodium alginate, 15-30 parts of glycerine, 12-22 parts of organosilicon, 15-25 parts of polyurethane, gluing
34-50 parts of agent, 12-35 parts of polyvinyl alcohol, gram 8-13 parts of bacterium spirit;It is former that the adhesive includes synthetic glue powder raw material, natural rubber powder
Material, NMF, crack resistence agent and distilled water.
It is used as further scheme of the invention:The synthetic glue powder raw material includes methylcellulose.
It is used as further scheme of the invention:The natural gum powder raw material includes peach gum and gum arabic.
It is used as further scheme of the invention:The synthetic glue powder raw material, natural gum powder raw material, NMF, crack resistence agent
Mass ratio with distilled water is 1:0.5:0.1:0.15:20.
It is used as further scheme of the invention:Include the raw material of following parts by weight:5.5 parts of mould inhibitor O, pigment powder 82
Part, 25 parts of sodium sorbate, 7 parts of sodium alginate, 21 parts of glycerine, 14 parts of organosilicon, 18 parts of polyurethane, 46 parts of adhesive, polyethylene
11 parts of alcohol 21 part, gram bacterium spirit.
A kind of preparation method of Formaldehyde-free art paint and preparation method thereof, comprises the following steps:
(1)It is prepared by adhesive:Synthetic glue powder raw material, natural gum powder raw material, NMF, crack resistence agent and distilled water are mixed,
15-35min is stirred at a temperature of 58-69 DEG C;
(2)By formula weigh pigment powder, mould inhibitor O, sodium sorbate, sodium alginate, glycerine, organosilicon, polyurethane, adhesive,
Polyvinyl alcohol, gram bacterium spirit, it is standby;
(3)Pigment powder, sodium alginate, organosilicon, adhesive are mixed after 20-35min, is ground, obtains mixture
A;
(4)Glycerine, sodium sorbate, polyurethane, polyvinyl alcohol are added in mixture A, 22- is mixed at 45-60 DEG C
40min, obtains mixture B;
(5)Gram bacterium spirit, mould inhibitor O are added in mixture B, mediation is carried out and is prepared into drawing pigment.
It is used as further scheme of the invention:Step(1)It is prepared by adhesive:By synthetic glue powder raw material, natural gum powder raw material,
NMF, crack resistence agent and distilled water mixing, 20min is stirred at a temperature of 62 DEG C.
It is used as further scheme of the invention:Step(4)Glycerine, sodium sorbate, polyurethane, polyvinyl alcohol are added into mixing
In thing A, 30min is mixed at 49 DEG C, mixture B is obtained.
Compared with prior art, the beneficial effects of the invention are as follows:
Formaldehyde is free of in the art painting pigment of the present invention, will not be produced during the production and use of the art painting pigment
Toxic gas, and growth of the art painting pigment to bacterium has good effect of drawing up, also to institute in fruit tree glue
Contain and the fungi that remains, phycomycete have good effect of drawing up, it is safer, and the shelf-life of the drawing pigment reach 50
More than month;The art painting pigment preparation technology of the present invention is simple, is adapted to industrialized production, with preferable economic value.
Embodiment
The technical scheme of this patent is described in more detail with reference to embodiment.
Embodiment 1
A kind of Formaldehyde-free art paint, includes the raw material of following parts by weight:4-8 parts of mould inhibitor O, 75 parts of pigment powder, mountain
22 parts of sodium of pears acid, 5 parts of sodium alginate, 15 parts of glycerine, 12 parts of organosilicon, 15 parts of polyurethane, 34 parts of adhesive, polyvinyl alcohol 12
8 parts of part, gram bacterium spirit;The adhesive includes synthetic glue powder raw material, natural gum powder raw material, NMF, crack resistence agent and distilled water.
The synthetic glue powder raw material includes methylcellulose.The natural gum powder raw material includes peach gum and gum arabic.The synthesis
Rubber powder raw material, natural gum powder raw material, NMF, the mass ratio of crack resistence agent and distilled water are 1:0.5:0.1:0.15:20.
A kind of preparation method of Formaldehyde-free art paint and preparation method thereof, comprises the following steps:
(1)It is prepared by adhesive:Synthetic glue powder raw material, natural gum powder raw material, NMF, crack resistence agent and distilled water are mixed,
15min is stirred at a temperature of 58 DEG C;(2)Weigh pigment powder by formula, it is mould inhibitor O, sodium sorbate, sodium alginate, glycerine, organic
Silicon, polyurethane, adhesive, polyvinyl alcohol, gram bacterium spirit, it is standby;(3)Pigment powder, sodium alginate, organosilicon, adhesive are mixed
Stir after 20min, be ground, obtain mixture A;(4)Glycerine, sodium sorbate, polyurethane, polyvinyl alcohol are added into mixture
In A, 22min is mixed at 45 DEG C, mixture B is obtained;(5)Gram bacterium spirit, mould inhibitor O are added in mixture B, adjusted
Be prepared into drawing pigment.
Embodiment 2
A kind of Formaldehyde-free art paint, includes the raw material of following parts by weight:4-8 parts of mould inhibitor O, 86 parts of pigment powder, mountain
30 parts of sodium of pears acid, 8 parts of sodium alginate, 30 parts of glycerine, 22 parts of organosilicon, 25 parts of polyurethane, 50 parts of adhesive, polyvinyl alcohol 35
13 parts of part, gram bacterium spirit;The adhesive includes synthetic glue powder raw material, natural gum powder raw material, NMF, crack resistence agent and distillation
Water.The synthetic glue powder raw material includes methylcellulose.The natural gum powder raw material includes peach gum and gum arabic.It is described to close
Plastic powder raw material, natural gum powder raw material, NMF, the mass ratio of crack resistence agent and distilled water are 1:0.5:0.1:0.15:20.
A kind of preparation method of Formaldehyde-free art paint and preparation method thereof, comprises the following steps:
(1)It is prepared by adhesive:Synthetic glue powder raw material, natural gum powder raw material, NMF, crack resistence agent and distilled water are mixed,
35min is stirred at a temperature of 58-69 DEG C;(2)Pigment powder, mould inhibitor O are weighed by formula, sodium sorbate, sodium alginate, glycerine, had
Machine silicon, polyurethane, adhesive, polyvinyl alcohol, gram bacterium spirit, it is standby;(3)Pigment powder, sodium alginate, organosilicon, adhesive are mixed
Close after stirring 35min, be ground, obtain mixture A;(4)Glycerine, sodium sorbate, polyurethane, polyvinyl alcohol are added into mixing
In thing A, 40min is mixed at 60 DEG C, mixture B is obtained;(5)Gram bacterium spirit, mould inhibitor O are added in mixture B, carried out
Mediation is prepared into drawing pigment.
Embodiment 3
A kind of Formaldehyde-free art paint, includes the raw material of following parts by weight:5.5 parts of mould inhibitor O, 82 parts of pigment powder, mountain
25 parts of sodium of pears acid, 7 parts of sodium alginate, 21 parts of glycerine, 14 parts of organosilicon, 18 parts of polyurethane, 46 parts of adhesive, polyvinyl alcohol 21
11 parts of part, gram bacterium spirit.The synthetic glue powder raw material includes methylcellulose.The natural gum powder raw material includes peach gum and Arab
Natural gum.The synthetic glue powder raw material, natural gum powder raw material, NMF, the mass ratio of crack resistence agent and distilled water are 1:0.5:
0.1:0.15:20。
A kind of preparation method of Formaldehyde-free art paint and preparation method thereof, comprises the following steps:
(1)It is prepared by adhesive:Synthetic glue powder raw material, natural gum powder raw material, NMF, crack resistence agent and distilled water are mixed,
20min is stirred at a temperature of 62 DEG C;(2)Weigh pigment powder by formula, it is mould inhibitor O, sodium sorbate, sodium alginate, glycerine, organic
Silicon, polyurethane, adhesive, polyvinyl alcohol, gram bacterium spirit, it is standby;(3)Pigment powder, sodium alginate, organosilicon, adhesive are mixed
Stir after 28min, be ground, obtain mixture A;(4)Glycerine, sodium sorbate, polyurethane, polyvinyl alcohol are added into mixture
In A, 30min is mixed at 49 DEG C, mixture B is obtained;(5)Gram bacterium spirit, mould inhibitor O are added in mixture B, adjusted
Be prepared into drawing pigment.
Embodiment 4
A kind of Formaldehyde-free art paint, includes the raw material of following parts by weight:4-8 parts of mould inhibitor O, 80 parts of pigment powder, mountain
25 parts of sodium of pears acid, 6 parts of sodium alginate, 17 parts of glycerine, 14 parts of organosilicon, 17 parts of polyurethane, 38 parts of adhesive, polyvinyl alcohol 18
9 parts of part, gram bacterium spirit;The adhesive includes synthetic glue powder raw material, natural gum powder raw material, NMF, crack resistence agent and distilled water.
The synthetic glue powder raw material includes methylcellulose.The natural gum powder raw material includes peach gum and gum arabic.The synthesis
Rubber powder raw material, natural gum powder raw material, NMF, the mass ratio of crack resistence agent and distilled water are 1:0.5:0.1:0.15:20.
A kind of preparation method of Formaldehyde-free art paint and preparation method thereof, comprises the following steps:
(1)It is prepared by adhesive:Synthetic glue powder raw material, natural gum powder raw material, NMF, crack resistence agent and distilled water are mixed,
17min is stirred at a temperature of 60 DEG C;(2)Weigh pigment powder by formula, it is mould inhibitor O, sodium sorbate, sodium alginate, glycerine, organic
Silicon, polyurethane, adhesive, polyvinyl alcohol, gram bacterium spirit, it is standby;(3)Pigment powder, sodium alginate, organosilicon, adhesive are mixed
Stir after 22min, be ground, obtain mixture A;(4)Glycerine, sodium sorbate, polyurethane, polyvinyl alcohol are added into mixture
In A, 25min is mixed at 49 DEG C, mixture B is obtained;(5)Gram bacterium spirit, mould inhibitor O are added in mixture B, adjusted
Be prepared into drawing pigment.
Embodiment 5
A kind of Formaldehyde-free art paint, includes the raw material of following parts by weight:4-8 parts of mould inhibitor O, 84 parts of pigment powder, mountain
28 parts of sodium of pears acid, 7 parts of sodium alginate, 27 parts of glycerine, 20 parts of organosilicon, 22 parts of polyurethane, 43 parts of adhesive, polyvinyl alcohol 32
11 parts of part, gram bacterium spirit;The adhesive includes synthetic glue powder raw material, natural gum powder raw material, NMF, crack resistence agent and distillation
Water.The synthetic glue powder raw material includes methylcellulose.The natural gum powder raw material includes peach gum and gum arabic.It is described to close
Plastic powder raw material, natural gum powder raw material, NMF, the mass ratio of crack resistence agent and distilled water are 1:0.5:0.1:0.15:20.
A kind of preparation method of Formaldehyde-free art paint and preparation method thereof, comprises the following steps:
(1)It is prepared by adhesive:Synthetic glue powder raw material, natural gum powder raw material, NMF, crack resistence agent and distilled water are mixed,
31min is stirred at a temperature of 65 DEG C;(2)Weigh pigment powder by formula, it is mould inhibitor O, sodium sorbate, sodium alginate, glycerine, organic
Silicon, polyurethane, adhesive, polyvinyl alcohol, gram bacterium spirit, it is standby;(3)Pigment powder, sodium alginate, organosilicon, adhesive are mixed
Stir after 32min, be ground, obtain mixture A;(4)Glycerine, sodium sorbate, polyurethane, polyvinyl alcohol are added into mixture
In A, 37min is mixed at 58 DEG C, mixture B is obtained;(5)Gram bacterium spirit, mould inhibitor O are added in mixture B, adjusted
Be prepared into drawing pigment.
Embodiment 6
A kind of Formaldehyde-free art paint, includes the raw material of following parts by weight:4-8 parts of mould inhibitor O, 76 parts of pigment powder, mountain
28 parts of sodium of pears acid, 6 parts of sodium alginate, 28 parts of glycerine, 13 parts of organosilicon, 24 parts of polyurethane, 35 parts of adhesive, polyvinyl alcohol 33
9 parts of part, gram bacterium spirit;The adhesive includes synthetic glue powder raw material, natural gum powder raw material, NMF, crack resistence agent and distilled water.
The synthetic glue powder raw material includes methylcellulose.The natural gum powder raw material includes peach gum and gum arabic.The synthesis
Rubber powder raw material, natural gum powder raw material, NMF, the mass ratio of crack resistence agent and distilled water are 1:0.5:0.1:0.15:20.
A kind of preparation method of Formaldehyde-free art paint and preparation method thereof, comprises the following steps:
(1)It is prepared by adhesive:Synthetic glue powder raw material, natural gum powder raw material, NMF, crack resistence agent and distilled water are mixed,
16min is stirred at a temperature of 68 DEG C;(2)Weigh pigment powder by formula, it is mould inhibitor O, sodium sorbate, sodium alginate, glycerine, organic
Silicon, polyurethane, adhesive, polyvinyl alcohol, gram bacterium spirit, it is standby;(3)Pigment powder, sodium alginate, organosilicon, adhesive are mixed
Stir after 34min, be ground, obtain mixture A;(4)Glycerine, sodium sorbate, polyurethane, polyvinyl alcohol are added into mixture
In A, 39min is mixed at 46 DEG C, mixture B is obtained;(5)Gram bacterium spirit, mould inhibitor O are added in mixture B, adjusted
Be prepared into drawing pigment.
Formaldehyde is free of in the art painting pigment of the present invention, will not during the production and use of the art painting pigment
Toxic gas is produced, and growth of the art painting pigment to bacterium has good effect of drawing up, also to fruit tree glue
In contained and residual fungi, phycomycete there is good effect of drawing up, it is safer, and the shelf-life of the drawing pigment reach
More than 50 months;The art painting pigment preparation technology of the present invention is simple, is adapted to industrialized production, with preferable economic valency
Value.
, it is necessary to illustrate, unless otherwise clear and definite in the description of this Formaldehyde-free art paint and preparation method thereof
Regulation and restriction, term " setting ", " connected " and " connection " should be interpreted broadly, for example, it may be fixedly connected, can also
It is to be detachably connected, or is integrally connected;Can be joined directly together, can also be indirectly connected to by intermediary, can be two
The connection of individual element internal.For the ordinary skill in the art, with concrete condition above-mentioned term can be understood in this hair
Concrete meaning in bright.
The better embodiment to this patent is explained in detail above, but this patent is not limited to above-mentioned embodiment party
, can also be on the premise of this patent objective not be departed from formula, the knowledge that one skilled in the relevant art possesses
Make a variety of changes.
Claims (8)
1. a kind of Formaldehyde-free art paint and preparation method thereof, it is characterised in that include the raw material of following parts by weight:It is anti-
Mould dose of 4-8 parts of O, 75-86 parts of pigment powder, 22-30 parts of sodium sorbate, 5-8 parts of sodium alginate, 15-30 parts of glycerine, organosilicon 12-
22 parts, 15-25 parts of polyurethane, 34-50 parts of adhesive, 12-35 parts of polyvinyl alcohol, gram 8-13 parts of bacterium spirit;The adhesive includes
Synthetic glue powder raw material, natural gum powder raw material, NMF, crack resistence agent and distilled water.
2. Formaldehyde-free art paint according to claim 1 and preparation method thereof, it is characterised in that the rubber polymer
Powder raw material includes methylcellulose.
3. Formaldehyde-free art paint according to claim 1 and preparation method thereof, it is characterised in that the natural gum
Powder raw material includes peach gum and gum arabic.
4. Formaldehyde-free art paint according to claim 1 and preparation method thereof, it is characterised in that the rubber polymer
Powder raw material, natural gum powder raw material, NMF, the mass ratio of crack resistence agent and distilled water are 1:0.5:0.1:0.15:20.
5. Formaldehyde-free art paint according to claim 1 and preparation method thereof, it is characterised in that including following heavy
Measure the raw material of number:It is 5.5 parts of mould inhibitor O, 82 parts of pigment powder, 25 parts of sodium sorbate, 7 parts of sodium alginate, 21 parts of glycerine, organic
14 parts of silicon, 18 parts of polyurethane, 46 parts of adhesive, 11 parts of polyvinyl alcohol 21 part, gram bacterium spirit.
6. a kind of preparation method of Formaldehyde-free art paint as described in claim 1-5 is any and preparation method thereof, its
It is characterised by, comprises the following steps:
(1)It is prepared by adhesive:Synthetic glue powder raw material, natural gum powder raw material, NMF, crack resistence agent and distilled water are mixed,
15-35min is stirred at a temperature of 58-69 DEG C;
(2)By formula weigh pigment powder, mould inhibitor O, sodium sorbate, sodium alginate, glycerine, organosilicon, polyurethane, adhesive,
Polyvinyl alcohol, gram bacterium spirit, it is standby;
(3)Pigment powder, sodium alginate, organosilicon, adhesive are mixed after 20-35min, is ground, obtains mixture
A;
(4)Glycerine, sodium sorbate, polyurethane, polyvinyl alcohol are added in mixture A, 22- is mixed at 45-60 DEG C
40min, obtains mixture B;
(5)Gram bacterium spirit, mould inhibitor O are added in mixture B, mediation is carried out and is prepared into drawing pigment.
7. the preparation method of Formaldehyde-free art paint according to claim 6 and preparation method thereof, it is characterised in that
Step(1)It is prepared by adhesive:Synthetic glue powder raw material, natural gum powder raw material, NMF, crack resistence agent and distilled water are mixed,
20min is stirred at a temperature of 62 DEG C.
8. the preparation method of Formaldehyde-free art paint according to claim 6 and preparation method thereof, it is characterised in that
Step(4)Glycerine, sodium sorbate, polyurethane, polyvinyl alcohol are added in mixture A, 30min is mixed at 49 DEG C, obtains
Mixture B.