CN107226655B - Water-proofing anticracking crystallite and villa basement leakage method for repairing and mending - Google Patents
Water-proofing anticracking crystallite and villa basement leakage method for repairing and mending Download PDFInfo
- Publication number
- CN107226655B CN107226655B CN201710467944.3A CN201710467944A CN107226655B CN 107226655 B CN107226655 B CN 107226655B CN 201710467944 A CN201710467944 A CN 201710467944A CN 107226655 B CN107226655 B CN 107226655B
- Authority
- CN
- China
- Prior art keywords
- mass fraction
- water
- crystallite
- proofing anticracking
- carbon black
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention provides a kind of water-proofing anticracking crystallite and villa basement leakage method for repairing and mending, one layer of water-proofing anticracking crystallite coating is coated in villa basement back side, water-proofing anticracking crystallite includes following components: the graded sand that mass fraction is 44%~53.9%, 52.5 ordinary portland cement of label that mass fraction is 20%~29%, the 2000 mesh super finely ground slags that mass fraction is 5%~10%, the acrylic resin rubber powder that mass fraction is 20%~25%, the white carbon black that mass fraction is 1%~1.1%, SiO in white carbon black2Content is greater than 95%, the water-reducing agent that mass fraction is 0.05%~0.2%, water-proofing anticracking microcrystalline coating has the advantages that not crack, not hollowing, impermeability is good, caking property is good, durable and environmentally friendly, solve the problems, such as villa basement leakage humidity.
Description
Technical field
The invention belongs to water-proofing anticracking technical fields, and in particular to a kind of water-proofing anticracking crystallite and villa basement leakage are repaired
Compensating method.
Background technique
Villa basement leakage humidity is a common problem at present, since these villas have been delivered for use, in villa
Lower room upstream face does not have execution conditions, it is necessary to carry out leak stopping in villa basement back side.Basement waterproofing at present
Material is according to material shape point: water-repellent paint, waterproof roll, impervious agent, waterproofing agent.According to material properties point: flexible waterproof
Material and rigidity water-proofing material.But it is suitble to the material classification of negative side waterproofing seldom, and negative side waterproofing material is main at present
Or all there is cracking in rigid waterproofing mortar and rigid flexible waterproof coating, these materials, problem of aging all cannot permanently solve to seep
Leakage problem, needs periodic maintenance.
Summary of the invention
The present invention be to solve the above-mentioned problems and carry out, and it is an object of the present invention to provide it is a kind of do not crack, not hollowing, impermeability
The water-proofing anticracking crystallite and villa basement leakage method for repairing and mending good, caking property is good, durable and environmentally friendly.
The present invention provides a kind of water-proofing anticracking crystallites, which is characterized in that including following components: graded sand, mass fraction
It is 44%~53.9%;
52.5 ordinary portland cement of label, mass fraction are 20%~29%;
2000 mesh super finely ground slags, mass fraction are 5%~10%;
Acrylic resin rubber powder, mass fraction are 20%~25%;
SiO2Content is greater than 95% white carbon black, and mass fraction is 1%~1.1%;
Water-reducing agent, mass fraction are 0.05%~0.2%.
Further, it in water-proofing anticracking crystallite provided by the invention, can also have the following features: wherein, graded sand
Mass fraction be 53.9%, the mass fraction of 52.5 ordinary portland cement of label is 20%, the matter of 2000 mesh super finely ground slags
Measuring score is 5%, and the mass fraction of acrylic resin rubber powder is 20%, and the mass fraction of white carbon black is 1%, the quality of water-reducing agent
Score is 0.1%.
Further, it in water-proofing anticracking crystallite provided by the invention, can also have the following features: wherein, water-reducing agent
For melamine.
The present invention also provides a kind of villa basement leakage method for repairing and mending, it is characterised in that: in villa basement backwater
Coat one layer of water-proofing anticracking crystallite coating as described in any one of claims 1 to 3 claim in face.
The present invention has the advantage that
Related water-proofing anticracking crystallite according to the present invention, due to using 52.5 ordinary portland cement of label and graded sand
For primary raw material, improves the intensity of water-proofing anticracking crystallite and moist construction environment can be suitble to, mix super finely ground slag and height
Purity white carbon black is the density and durability for improving water-proofing anticracking crystallite, significantly improves the impermeability of water-proofing anticracking crystallite
Can, permanently solve the problems, such as villa basement leakage from back side, what incorporation high proportion acrylic resin rubber powder to apply on wall
Water-proofing anticracking microcrystalline coating has 5% elongation percentage, does not crack, while good with the caking ability of base, not hollowing;Mix diminishing
Agent diminishing construction water amount, further increases the density of water-proofing anticracking crystallite;Each component is nontoxic, and it is nonirritant it is big,
The big substance of volatility, therefore, water-proofing anticracking crystallite of the invention have do not crack, not hollowing, impermeability is good, caking property is good,
Durable and environmentally friendly advantage.
Villa basement leakage method for repairing and mending of the invention is coated in villa underground using water-proofing anticracking crystallite as coating
The back side of room, it is dry and hard after dope layer do not crack, not hollowing, impermeability is good, caking property is good, durable, environmentally friendly and apply
Work is convenient, solves the problems, such as that villa basement internal cause leakage is moist.
Specific embodiment
In order to be easy to understand the technical means, the creative features, the aims and the efficiencies achieved by the present invention, tie below
Embodiment is closed to be specifically addressed water-proofing anticracking crystallite of the invention and villa basement leakage method for repairing and mending.
<embodiment one>
In the present embodiment, water-proofing anticracking crystallite includes following components: the graded sand that mass fraction is 53.9%;Quality point
52.5 ordinary portland cement of label that number is 20%;The 2000 mesh super finely ground slags that mass fraction is 5%, mass fraction 20%
Acrylic resin rubber powder, mass fraction be 1% white carbon black, and white carbon black be SiO2Content is greater than 95% white carbon black;Matter
Measure the water-reducing agent that score is 0.1%, wherein water-reducing agent is melamine.
According to aforementioned proportion when production, Agravicmixer will be entered by transmission device after above-mentioned various component weighings,
After being stirred, product is transferred to finished product material library, then is transferred to packing machine and carries out subpackage, finally seals.
A kind of villa basement leakage method for repairing and mending, this method are to coat one layer of above-mentioned waterproof in villa basement back side
Cracking resistance crystallite coating.
<embodiment two>
In the present embodiment, water-proofing anticracking crystallite includes following components: the graded sand that mass fraction is 44%;Mass fraction
For 29% 52.5 ordinary portland cement of label;The 2000 mesh super finely ground slags that mass fraction is 5%, mass fraction 20%
Acrylic resin rubber powder, mass fraction be 1% white carbon black, and white carbon black be SiO2Content is greater than 95% white carbon black;Matter
Measure the water-reducing agent that score is 0.05%.
According to aforementioned proportion when production, Agravicmixer will be entered by transmission device after above-mentioned various component weighings,
After being stirred, product is transferred to finished product material library, then is transferred to packing machine and carries out subpackage, finally seals.
A kind of villa basement leakage method for repairing and mending, this method are to coat one layer of above-mentioned waterproof in villa basement back side
Cracking resistance crystallite coating.
<embodiment three>
In the present embodiment, water-proofing anticracking crystallite includes following components: the graded sand that mass fraction is 48%;Mass fraction
For 20% 52.5 ordinary portland cement of label;The 2000 mesh super finely ground slags that mass fraction is 10%, mass fraction 20%
Acrylic resin rubber powder, mass fraction be 1% white carbon black, and white carbon black be SiO2Content is greater than 95% white carbon black;Matter
Measure the water-reducing agent that score is 0.2%, wherein water-reducing agent is melamine.
According to aforementioned proportion when production, Agravicmixer will be entered by transmission device after above-mentioned various component weighings,
After being stirred, product is transferred to finished product material library, then is transferred to packing machine and carries out subpackage, finally seals.
A kind of villa basement leakage method for repairing and mending, this method are to coat one layer of above-mentioned waterproof in villa basement back side
Cracking resistance crystallite coating.
<example IV>
In the present embodiment, water-proofing anticracking crystallite includes following components: the graded sand that mass fraction is 46%;Mass fraction
For 20% 52.5 ordinary portland cement of label;The 2000 mesh super finely ground slags that mass fraction is 7%, mass fraction 25%
Acrylic resin rubber powder, mass fraction be 1.05% white carbon black, and white carbon black be SiO2Content is greater than 95% white carbon black;
The water-reducing agent that mass fraction is 0.1%.
According to aforementioned proportion when production, Agravicmixer will be entered by transmission device after above-mentioned various component weighings,
After being stirred, product is transferred to finished product material library, then is transferred to packing machine and carries out subpackage, finally seals.
A kind of villa basement leakage method for repairing and mending, this method are to coat one layer of above-mentioned waterproof in villa basement back side
Cracking resistance crystallite coating.
<embodiment five>
In the present embodiment, water-proofing anticracking crystallite includes following components: the graded sand that mass fraction is 47%;Mass fraction
For 24% 52.5 ordinary portland cement of label;The 2000 mesh super finely ground slags that mass fraction is 5%, mass fraction are 22%
Acrylic resin rubber powder, the white carbon black that mass fraction is 1.1%, and white carbon black are SiO2Content is greater than 95% white carbon black;Matter
Measure the water-reducing agent that score is 0.1%.
According to aforementioned proportion when production, Agravicmixer will be entered by transmission device after above-mentioned various component weighings,
After being stirred, product is transferred to finished product material library, then is transferred to packing machine and carries out subpackage, finally seals.
A kind of villa basement leakage method for repairing and mending, this method are to coat one layer of above-mentioned waterproof in villa basement back side
Cracking resistance crystallite coating.
Water-proofing anticracking crystallite of the invention aims at villa basement back side seepage repairment and researches and develops, and product is with strong points,
Thoroughly solve the problems, such as that back side leaks using hard and soft technical principle.Villa basement is once leak, and construction environment is very
Humidity, water-proofing anticracking crystallite of the invention can be firmly bonded with base in a humidity environment, not hollowing, never drop-off, and
Water-proofing anticracking crystallite has 5% elongation percentage, it is not easy to crack.Also, water-proofing anticracking crystallite intensity is high, and anti-permeability performance is good, changes
It is low the previous back side seepage repairment strength of materials is become, anti-permeability performance is poor and base's bonding is insecure, and durability difference etc. is multiple to be lacked
Point.Moreover, water-proofing anticracking crystallite can with permanent closure New-old concrete junction crack, concrete and brick wall junction crack,
Basement concrete wall plank split is very suitable to from digging villa basement back side seepage repairment.
The present invention is respectively tested water-proofing anticracking crystallite and general polymer cement mortar, and and JC/T984-
2011G polymer waterproof cement mortar national sector standard is compared.It is anti-that waterproof in embodiment one is only enumerated in following table 1
Split the data of crystallite test result, general polymer cement mortar test result and national sector standard.
1. contrast test result of table
From table 1 it follows that water-proofing anticracking crystallite is compared to general polymer cement mortar in impervious, resistance to compression, anti-folding
Aspect is significantly improved, and adhesive strength also increases, shrinking percentage and water absorption rate decrease, it was demonstrated that water-proofing anticracking crystallite
Crack resistence effect is good and impervious good.
Water-proofing anticracking crystallite and villa basement leakage method for repairing and mending according to the present invention is not limited to specific embodiment
Range.The above content is only basic explanation of the invention, and any equivalent transformation made by technical solution according to the present invention,
It is within the scope of protection of the invention.
Claims (4)
1. a kind of water-proofing anticracking crystallite, which is characterized in that including following components:
Graded sand, mass fraction are 44%~53.9%;
52.5 ordinary portland cement of label, mass fraction are 20%~29%;
2000 mesh super finely ground slags, mass fraction are 5%~10%;
Acrylic resin rubber powder, mass fraction are 20%~25%;
SiO2Content is greater than 95% white carbon black, and mass fraction is 1%~1.1%;
Water-reducing agent, mass fraction are 0.05%~0.2%.
2. water-proofing anticracking crystallite according to claim 1, it is characterised in that:
Wherein, the mass fraction of the graded sand is 53.9%, and the mass fraction of 52.5 ordinary portland cement of label is
20%, the mass fraction of the 2000 mesh super finely ground slag is 5%, and the mass fraction of the acrylic resin rubber powder is 20%, institute
The mass fraction for stating white carbon black is 1%, and the mass fraction of the water-reducing agent is 0.1%.
3. water-proofing anticracking crystallite according to claim 1, it is characterised in that:
Wherein, the water-reducing agent is melamine.
4. a kind of villa basement leakage method for repairing and mending, it is characterised in that:
One layer of water-proofing anticracking as described in any one of claims 1 to 3 claim is coated in villa basement back side
Crystallite coating.