CN107201024A - A kind of flooring material being used in garden landscape and preparation method thereof - Google Patents
A kind of flooring material being used in garden landscape and preparation method thereof Download PDFInfo
- Publication number
- CN107201024A CN107201024A CN201710592605.8A CN201710592605A CN107201024A CN 107201024 A CN107201024 A CN 107201024A CN 201710592605 A CN201710592605 A CN 201710592605A CN 107201024 A CN107201024 A CN 107201024A
- Authority
- CN
- China
- Prior art keywords
- parts
- garden landscape
- flooring material
- weight
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention provides a kind of flooring material being used in garden landscape and preparation method thereof, is related to building material field, the raw material of following parts by weight is included for the flooring material in garden landscape：Nano titanium oxide, pitch, bauxite, tricalcium silicate, acrylic resin, quartz, calcium acetate, waste polyurethane foamed plastics, phenolic resin, polyamide, kaolin, aeroge, antioxidant, heat stabilizer, fire retardant and water；Preparation method comprises the following steps：(1) raw material, (2) quartz milling, the heating of (3) pitch, (4) crushing, (5) stirring, (6) extrusion forming, (7) drying are weighed.The present invention solves the flooring material being currently used in garden landscape and there is the problem of poor flame retardant properties, environmental-protecting performance are general, ageing resistance is general, pressure-proof and snap-resistent performance is high not enough.
Description
Technical field
The invention belongs to building material field, and in particular to a kind of flooring material being used in garden landscape and its preparation side
Method.
Background technology
Flooring material much uses wood materials in the process of construction of garden landscape, but wood floors material is existed
The problem of poor fire and anti-folding and anti-pressing poor performance.
Nanometer construction material of a kind of anti-folding and anti-pressing of Chinese patent literature of on 2 3rd, 2016 bulletins and preparation method thereof
(Authorization Notice No. CN104261758B), the nanometer construction material of described anti-folding and anti-pressing includes the raw material of following parts by weight：Receive
Rice titanium dioxide is 5-8 part, heat after pitch be 7-15 parts, bauxite be 11-19 parts, tricalcium silicate be 8-13 parts, poly- third
Olefine resin is 4-9 parts, the quartz powder of 400 mesh is 6-10 parts, calcium acetate is 5-9 parts, water is 15-23 parts.Preparation method includes
Heating, mixing, shaping, drying.
But the invention is present, and poor flame retardant properties, environmental-protecting performance are general, ageing resistance is general, pressure-proof and snap-resistent performance is high not enough
The problem of, it is impossible to meet the high standards of the combination property in landscape architecture to flooring material.
The content of the invention
In order to solve to be currently used for the flooring material in garden landscape, to there is poor flame retardant properties, environmental-protecting performance general, anti-ageing
The problem of property changed is general, pressure-proof and snap-resistent performance is high not enough, it is an object of the invention to provide a kind of ground being used in garden landscape
Plate material and preparation method thereof, it is obtained be used for garden landscape in flooring material have bending and compressive strength height, good flame resistance,
The advantage that the feature of environmental protection is good and ageing resistance is good.
The invention provides following technical scheme：
A kind of flooring material being used in garden landscape, includes the raw material of following parts by weight：5-8 parts of nano titanium oxide,
7-15 parts of pitch, 11-19 parts of bauxite, 8-13 parts of tricalcium silicate, 4-9 parts of acrylic resin, 6-10 parts of quartz, calcium acetate 5-
9 parts, 15-21 parts of waste polyurethane foamed plastics, 4-10 parts of phenolic resin, 6-14 parts of polyamide, 17-29 parts of kaolin,
15-21 parts of 11-21 parts of aeroge, 0.1-0.5 parts of antioxidant, 0.3-0.7 parts of heat stabilizer, 0.5-0.9 parts of fire retardant and water.
Waste polyurethane foamed plastics are with the addition of in raw material, the purpose of energy-conserving and environment-protective has been reached.
Preferably, the raw material of following parts by weight is included：6.5 parts of nano titanium oxide, 11 parts of pitch, 15 parts of bauxite, silicon
Sour 10.5 parts of DFP, 6.5 parts of acrylic resin, 8 parts of quartz, 7 parts of calcium acetate, 18 parts of waste polyurethane foamed plastics, phenolic aldehyde
7 parts of resin, 10 parts of polyamide, 23 parts of kaolin, 16 parts of aeroge, 0.3 part of antioxidant, 0.5 part of heat stabilizer, fire retardant
0.7 part and 18 parts of water.
Preferably, the antioxidant be diphenylamines, diphenylamines can delay or suppress prepare be used for garden landscape in
Flooring material oxidation course, improve preparation be used for garden landscape in flooring material life-span.
Preferably, the heat stabilizer is aluminum stearate, is favorably improved the flooring board being used in garden landscape of preparation
The heat endurance of material.
Preferably, the fire retardant is flame retardant of magnesium hydroxide, flame retardant of magnesium hydroxide by improving the thermal capacitance of polymer,
It is set to absorb more heats before heat decomposition temperature is reached, so as to improve its fire resistance.
Preferably, the flooring material being used in garden landscape also includes the talcum powder that parts by weight are 11-17 parts, sliding
Stone flour has the advantages that lubricity is good, fire resistance is good, corrosion resistance is good, chemical property is stable and good insulating.
Preferably, the flooring material being used in garden landscape also includes the aluminum oxide that parts by weight are 3-11 parts, oxygen
Changing aluminium has the advantages that good corrosion resistance and fire resistance are good.
Preferably, the flooring material being used in garden landscape also includes the glass fibre that parts by weight are 6-12 parts,
Glass fibre has the advantages that good insulating, fire resistance be good, heat-resist and high mechanical strength.
A kind of preparation method for the flooring material being used in garden landscape, comprises the following steps：
(1) raw material is weighed according to the parts by weight for the flooring material raw material in garden landscape；
(2) by quartz grinds, the mesh number of powder is 400 mesh；
(3) pitch is heated to 90 DEG C, pitch is in heating process along with stirring；
(4) waste polyurethane foamed plastics are added in pulverizer and crushed, produce crushed material；
(5) by the crushed material in 400 mesh silica flours in step (2), the heated asphalt in step (3), step (4) and its
His surplus stock is added in mixer and stirred, and mixing time is 30-40min, produces compound；
(6) by the compound injection moulding mould in step (5), extrusion forming produces molding mass；
(7) molding mass in step (6) is dried, drying temperature is 75-85 DEG C, and drying time is 5-6h, is produced
For the flooring material in garden landscape.
The beneficial effects of the invention are as follows：
1st, the present invention solves the flooring material being currently used in garden landscape and there is poor flame retardant properties, environmental-protecting performance one
As, the problem of ageing resistance is general, pressure-proof and snap-resistent performance is high not enough.
2nd, waste polyurethane foamed plastics are with the addition of in raw material of the invention, has reached the purpose of energy-conserving and environment-protective.
3rd, heretofore described antioxidant be diphenylamines, diphenylamines can delay or suppress prepare be used for garden landscape
In flooring material oxidation course, improve preparation be used for garden landscape in flooring material life-span.
4th, heretofore described heat stabilizer is aluminum stearate, is favorably improved the floor being used in garden landscape of preparation
The heat endurance of material.
5th, heretofore described fire retardant is flame retardant of magnesium hydroxide, and flame retardant of magnesium hydroxide is by improving the heat of polymer
Hold, it is absorbed more heats before heat decomposition temperature is reached, so as to improve its fire resistance.
6th, the heretofore described flooring material being used in garden landscape also includes the talcum that parts by weight are 11-17 parts
Powder, talcum powder has the advantages that lubricity is good, fire resistance is good, corrosion resistance is good, chemical property is stable and good insulating.
7th, the heretofore described flooring material being used in garden landscape also includes the aluminum oxide that parts by weight are 3-11 parts,
Aluminum oxide has the advantages that good corrosion resistance and fire resistance are good.
8th, the heretofore described flooring material being used in garden landscape also includes the glass fibers that parts by weight are 6-12 parts
Dimension, glass fibre has the advantages that good insulating, fire resistance be good, heat-resist and high mechanical strength.
Embodiment
Embodiment 1
A kind of flooring material being used in garden landscape, includes the raw material of following parts by weight：6.5 parts of nano titanium oxide,
It is 11 parts of pitch, 15 parts of bauxite, 10.5 parts of tricalcium silicate, 6.5 parts of acrylic resin, 8 parts of quartz, 7 parts of calcium acetate, discarded poly-
18 parts of urethane foamed plastics, 7 parts of phenolic resin, 10 parts of polyamide, 23 parts of kaolin, 16 parts of aeroge, antioxidant 0.3
Part, 0.5 part of heat stabilizer, 0.7 part of fire retardant and 18 parts of water.
Waste polyurethane foamed plastics are with the addition of in raw material, the purpose of energy-conserving and environment-protective has been reached.
Antioxidant is diphenylamines, and diphenylamines can delay or suppress the flooring material being used in garden landscape prepared
Oxidation course, improves the life-span of the flooring material being used in garden landscape of preparation.
Heat stabilizer is aluminum stearate, be favorably improved preparation be used for garden landscape in flooring material it is thermally-stabilised
Property.
Fire retardant is flame retardant of magnesium hydroxide, and flame retardant of magnesium hydroxide is reaching it by improving the thermal capacitance of polymer
More heats are absorbed before heat decomposition temperature, so as to improve its fire resistance.
Also include the talcum powder that parts by weight are 14 parts for the flooring material in garden landscape, talcum powder has lubricity
Well, fire resistance is good, corrosion resistance is good, stable and good insulating the advantage of chemical property.
Also include the aluminum oxide that parts by weight are 7 parts for the flooring material in garden landscape, aluminum oxide has corrosion-resistant
Property the good and good advantage of fire resistance.
Also include the glass fibre that parts by weight are 9 parts for the flooring material in garden landscape, glass fibre has exhausted
Edge is good, good, heat-resist and high mechanical strength the advantage of fire resistance.
A kind of preparation method for the flooring material being used in garden landscape, comprises the following steps：
(1) raw material is weighed according to the parts by weight for the flooring material raw material in garden landscape；
(2) by quartz grinds, the mesh number of powder is 400 mesh；
(3) pitch is heated to 90 DEG C, pitch is in heating process along with stirring；
(4) waste polyurethane foamed plastics are added in pulverizer and crushed, produce crushed material；
(5) by the crushed material in 400 mesh silica flours in step (2), the heated asphalt in step (3), step (4) and its
His surplus stock is added in mixer and stirred, and mixing time is 30-40min, produces compound；
(6) by the compound injection moulding mould in step (5), extrusion forming produces molding mass；
(7) molding mass in step (6) is dried, drying temperature is 75-85 DEG C, and drying time is 5-6h, is produced
For the flooring material in garden landscape.
Embodiment 2
A kind of flooring material being used in garden landscape, includes the raw material of following parts by weight：5 parts of nano titanium oxide, drip
Blue or green 7 parts, 11 parts of bauxite, 8 parts of tricalcium silicate, 4 parts of acrylic resin, 6 parts of quartz, 5 parts of calcium acetate, waste polyurethane foam
15 parts of plastics, 4 parts of phenolic resin, 6 parts of polyamide, 17 parts of kaolin, 11 parts of aeroge, 0.1 part of antioxidant, heat stabilizer
15 parts of 0.3 part, 0.5 part of fire retardant and water.
Waste polyurethane foamed plastics are with the addition of in raw material, the purpose of energy-conserving and environment-protective has been reached.
Antioxidant is diphenylamines, and diphenylamines can delay or suppress the flooring material being used in garden landscape prepared
Oxidation course, improves the life-span of the flooring material being used in garden landscape of preparation.
Heat stabilizer is aluminum stearate, be favorably improved preparation be used for garden landscape in flooring material it is thermally-stabilised
Property.
Fire retardant is flame retardant of magnesium hydroxide, and flame retardant of magnesium hydroxide is reaching it by improving the thermal capacitance of polymer
More heats are absorbed before heat decomposition temperature, so as to improve its fire resistance.
Also include the talcum powder that parts by weight are 11 parts for the flooring material in garden landscape, talcum powder has lubricity
Well, fire resistance is good, corrosion resistance is good, stable and good insulating the advantage of chemical property.
Also include the aluminum oxide that parts by weight are 3 parts for the flooring material in garden landscape, aluminum oxide has corrosion-resistant
Property the good and good advantage of fire resistance.
Also include the glass fibre that parts by weight are 6 parts for the flooring material in garden landscape, glass fibre has exhausted
Edge is good, good, heat-resist and high mechanical strength the advantage of fire resistance.
A kind of preparation method for the flooring material being used in garden landscape, comprises the following steps：
(1) raw material is weighed according to the parts by weight for the flooring material raw material in garden landscape；
(2) by quartz grinds, the mesh number of powder is 400 mesh；
(3) pitch is heated to 90 DEG C, pitch is in heating process along with stirring；
(4) waste polyurethane foamed plastics are added in pulverizer and crushed, produce crushed material；
(5) by the crushed material in 400 mesh silica flours in step (2), the heated asphalt in step (3), step (4) and its
His surplus stock is added in mixer and stirred, and mixing time is 30-40min, produces compound；
(6) by the compound injection moulding mould in step (5), extrusion forming produces molding mass；
(7) molding mass in step (6) is dried, drying temperature is 75-85 DEG C, and drying time is 5-6h, is produced
For the flooring material in garden landscape.
Embodiment 3
A kind of flooring material being used in garden landscape, includes the raw material of following parts by weight：8 parts of nano titanium oxide, drip
Blue or green 15 parts, 19 parts of bauxite, 13 parts of tricalcium silicate, 9 parts of acrylic resin, 10 parts of quartz, 9 parts of calcium acetate, waste polyurethane
21 parts of foamed plastics, 10 parts of phenolic resin, 14 parts of polyamide, 29 parts of kaolin, 21 parts of aeroge, 0.5 part of antioxidant, heat
21 parts of 0.7 part of stabilizer, 0.9 part of fire retardant and water.
Waste polyurethane foamed plastics are with the addition of in raw material, the purpose of energy-conserving and environment-protective has been reached.
Antioxidant is diphenylamines, and diphenylamines can delay or suppress the flooring material being used in garden landscape prepared
Oxidation course, improves the life-span of the flooring material being used in garden landscape of preparation.
Heat stabilizer is aluminum stearate, be favorably improved preparation be used for garden landscape in flooring material it is thermally-stabilised
Property.
Fire retardant is flame retardant of magnesium hydroxide, and flame retardant of magnesium hydroxide is reaching it by improving the thermal capacitance of polymer
More heats are absorbed before heat decomposition temperature, so as to improve its fire resistance.
Also include the talcum powder that parts by weight are 17 parts for the flooring material in garden landscape, talcum powder has lubricity
Well, fire resistance is good, corrosion resistance is good, stable and good insulating the advantage of chemical property.
Also include the aluminum oxide that parts by weight are 11 parts for the flooring material in garden landscape, aluminum oxide has corrosion-resistant
Property the good and good advantage of fire resistance.
Also include the glass fibre that parts by weight are 12 parts for the flooring material in garden landscape, glass fibre has exhausted
Edge is good, good, heat-resist and high mechanical strength the advantage of fire resistance.
A kind of preparation method for the flooring material being used in garden landscape, comprises the following steps：
(1) raw material is weighed according to the parts by weight for the flooring material raw material in garden landscape；
(2) by quartz grinds, the mesh number of powder is 400 mesh；
(3) pitch is heated to 90 DEG C, pitch is in heating process along with stirring；
(4) waste polyurethane foamed plastics are added in pulverizer and crushed, produce crushed material；
(5) by the crushed material in 400 mesh silica flours in step (2), the heated asphalt in step (3), step (4) and its
His surplus stock is added in mixer and stirred, and mixing time is 30-40min, produces compound；
(6) by the compound injection moulding mould in step (5), extrusion forming produces molding mass；
(7) molding mass in step (6) is dried, drying temperature is 75-85 DEG C, and drying time is 5-6h, is produced
For the flooring material in garden landscape.
Comparative example 1
A kind of nanometer construction material of anti-folding and anti-pressing, includes the raw material of following parts by weight：6.5 parts of nano titanium oxide, drip
20 parts of blue or green 11 parts, 15 parts of bauxite, 10.5 parts of tricalcium silicate, 6.5 parts of acrylic resin, 8 parts of quartz, 7 parts of calcium acetate and water.
A kind of preparation method of the nanometer construction material of anti-folding and anti-pressing, comprises the following steps：
(1) raw material is weighed according to the parts by weight of the nanometer raw material of building materials of anti-folding and anti-pressing；
(2) by quartz grinds, the mesh number of powder is 400 mesh；
(3) pitch is heated to 90 DEG C, pitch is in heating process along with stirring；
(4) by 400 mesh silica flours in step (2), the heated asphalt in step (3), nano titanium oxide, bauxite,
Tricalcium silicate, acrylic resin, calcium acetate and water are added in mixer and stirred, and mixing time is 30-40min, produces mixing
Material；
(5) by the compound injection moulding mould in step (4), extrusion forming produces molding mass；
(6) molding mass in step (5) is dried, drying temperature is 80-90 DEG C, and drying time is 4-5h, is produced
For the flooring material in garden landscape.
It will be made in the obtained flooring material and comparative example 1 in garden landscape of embodiment 1, embodiment 2 and embodiment 3
The nanometer construction material for obtaining anti-folding and anti-pressing carries out performance test, and test result is as shown in table 1：
From the data of table 1 compare as can be seen that it is an advantage of the invention that：
1st, a kind of flooring material being used in garden landscape and preparation method thereof, can from the rupture strength value measured
Go out, embodiment 1-3 rupture strength value is above comparative example 1, illustrate the anti-of the flooring material that the present invention is used in garden landscape
Roll over intensity high.
2nd, a kind of flooring material being used in garden landscape and preparation method thereof, can from the compression strength value measured
Go out, embodiment 1-3 compression strength value is above comparative example 1, illustrate the anti-of the flooring material that the present invention is used in garden landscape
Compressive Strength is high.
3rd, a kind of flooring material being used in garden landscape and preparation method thereof, according to national standard《Construction material and system
Product classification system for fire performance》GB862, the flame retardant rating measured as can be seen that embodiment 1-3 flame retardant rating is superior to comparative example 1,
Illustrate the good flame resistance of the flooring material being used in garden landscape.
4th, a kind of flooring material and preparation method thereof being used in garden landscape, can be with from the data of each index measured
Find out, embodiment 1 is superior to embodiment 2, embodiment 3 and comparative example 1, illustrate the flooring material that the present invention is used in garden landscape
Composition of raw materials and preparation method reasonability.
The preferred embodiments of the present invention are the foregoing is only, are not intended to limit the invention, although with reference to foregoing reality
Apply example the present invention is described in detail, for those skilled in the art, it still can be to foregoing each implementation
Technical scheme described in example is modified, or equivalent substitution, all essences in the present invention are carried out to which part technical characteristic
God is with principle, and any modification, equivalent substitution and improvements made etc. should be included in the scope of the protection.
Claims (9)
1. a kind of flooring material being used in garden landscape, it is characterised in that include the raw material of following parts by weight：Nanometer titanium dioxide
5-8 parts of titanium, 7-15 parts of pitch, 11-19 parts of bauxite, 8-13 parts of tricalcium silicate, 4-9 parts of acrylic resin, 6-10 parts of quartz,
5-9 parts of calcium acetate, 15-21 parts of waste polyurethane foamed plastics, 4-10 parts of phenolic resin, 6-14 parts of polyamide, kaolin
17-29 parts, 11-21 parts of aeroge, 0.1-0.5 parts of antioxidant, 0.3-0.7 parts of heat stabilizer, 0.5-0.9 parts of fire retardant and water
15-21 parts.
2. the flooring material according to claim 1 being used in garden landscape, it is characterised in that including following parts by weight
Raw material：6.5 parts of nano titanium oxide, 11 parts of pitch, 15 parts of bauxite, 10.5 parts of tricalcium silicate, 6.5 parts of acrylic resin, stone
8 parts of diamond stone, 7 parts of calcium acetate, 18 parts of waste polyurethane foamed plastics, 7 parts of phenolic resin, 10 parts of polyamide, kaolin 23
Part, 16 parts of aeroge, 0.3 part of antioxidant, 0.5 part of heat stabilizer, 0.7 part of fire retardant and 18 parts of water.
3. the flooring material according to claim 1 being used in garden landscape, it is characterised in that：The antioxidant is hexichol
Amine.
4. the flooring material according to claim 1 being used in garden landscape, it is characterised in that：The heat stabilizer is hard
Resin acid aluminium.
5. the flooring material according to claim 1 being used in garden landscape, it is characterised in that：The fire retardant is hydrogen-oxygen
Change magnesium fire retardant.
6. the flooring material according to claim 1 being used in garden landscape, it is characterised in that：It is described to be used for garden landscape
In flooring material also to include parts by weight be 11-17 parts of talcum powder.
7. the flooring material according to claim 1 being used in garden landscape, it is characterised in that：It is described to be used for garden landscape
In flooring material also to include parts by weight be 3-11 parts of aluminum oxide.
8. the flooring material according to claim 1 being used in garden landscape, it is characterised in that：It is described to be used for garden landscape
In flooring material also to include parts by weight be 6-12 parts of glass fibre.
9. a kind of preparation method of flooring material being used in garden landscape as described in claim 1-8 any one, it is special
Levy and be, comprise the following steps：
(1) raw material is weighed according to the parts by weight for the flooring material raw material in garden landscape；
(2) by quartz grinds, the mesh number of powder is 400 mesh；
(3) pitch is heated to 90 DEG C, pitch is in heating process along with stirring；
(4) waste polyurethane foamed plastics are added in pulverizer and crushed, produce crushed material；
(5) crushed material in 400 mesh silica flours in step (2), the heated asphalt in step (3), step (4) is remained with other
Remaining raw material is added in mixer and stirred, and mixing time is 30-40min, produces compound；
(6) by the compound injection moulding mould in step (5), extrusion forming produces molding mass；
(7) molding mass in step (6) is dried, drying temperature is 75-85 DEG C, and drying time is 5-6h, and producing is used for
Flooring material in garden landscape.