CN107192661A - 一种适用于c环试样的挂架结构 - Google Patents

一种适用于c环试样的挂架结构 Download PDF

Info

Publication number
CN107192661A
CN107192661A CN201710557829.5A CN201710557829A CN107192661A CN 107192661 A CN107192661 A CN 107192661A CN 201710557829 A CN201710557829 A CN 201710557829A CN 107192661 A CN107192661 A CN 107192661A
Authority
CN
China
Prior art keywords
hanging rack
rack structure
sample
samples
ring samples
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201710557829.5A
Other languages
English (en)
Other versions
CN107192661B (zh
Inventor
王庆东
张小康
杨中燕
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Kell Dreyfus Stress Corrosion Test Equipment Co Ltd
Original Assignee
Shanghai Kell Dreyfus Stress Corrosion Test Equipment Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai Kell Dreyfus Stress Corrosion Test Equipment Co Ltd filed Critical Shanghai Kell Dreyfus Stress Corrosion Test Equipment Co Ltd
Priority to CN201710557829.5A priority Critical patent/CN107192661B/zh
Publication of CN107192661A publication Critical patent/CN107192661A/zh
Application granted granted Critical
Publication of CN107192661B publication Critical patent/CN107192661B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种适用于C环试样的挂架结构，包括多个试样安放单元，每个试样安放单元均水平设一凸块，所述凸块两侧均竖直设一通槽，所述通槽的底部一侧设挡板，两个所述通槽的形状与C环试样的开口形状相适配。本发明结构简单，易于加工，且与试样绝缘，避免了接触腐蚀和缝隙腐蚀。试样安装方便快捷，极大地降低了劳动强度和作业时间。C环试样的竖直安装，有利于试样表面水分的沥干，更加接近试验模拟的环境工况。

Description

一种适用于C环试样的挂架结构
技术领域
本发明涉及应力腐蚀试验，尤其涉及一种适用于C环试样的挂架结构。
背景技术
C环试样应力腐蚀试验属于气候条件模拟试验，它可模拟潮水涨落引起的潮差带腐蚀剂波浪冲击、大气中经常遇到间断降雨、结露和干湿交替出现的状态以及化工设备中液面升降引起的腐蚀。试验前，C环试样通过螺钉施加预应力，并逐一吊挂在挂架上。吊挂试样时，为了防止接触腐蚀和缝隙腐蚀，应确保试样不与其他金属材质接触，各个试样之间也应保持足够的距离，防止试样相互接触或碰撞。试验时，C环试样和挂架一起浸泡在溶液中10min，接着曝露在空气中50min，如此循环往复进行试验。
目前，C环试样应力腐蚀试验设备多采用常规吊挂方式，即试样在加载预应力之后，用塑料绳逐个系在周期交替的挂架上。在C环试样应力腐蚀试验中，试样的数量一般比较多，一次试验往往要上百个试样。若单个试样的吊挂比较麻烦，整体上就会给实验员带来较为繁琐的工作，并耽误大量的时间。
发明内容
为了解决上述存在的技术问题，本发明提出一种适用于C环试样的挂架结构，其简单方便、节省时间，同时又不影响试验要求。
一种适用于C环试样的挂架结构，包括多个试样安放单元，每个试样安放单元均水平设一凸块，所述凸块两侧均竖直设一通槽，所述通槽的底部一侧设挡板，两个所述通槽的形状与C环试样的开口形状相适配。
作为本发明的一种适用于C环试样的挂架结构的改进，所述凸块、通槽和挡板均由有机玻璃材质制成。
作为本发明的一种适用于C环试样的挂架结构的改进，所述凸块和通槽为一体成型结构。
作为本发明的一种适用于C环试样的挂架结构的改进，所述C环试样穿设有螺钉，所述螺钉用以向所述C环试样提供预应力。
作为本发明的一种适用于C环试样的挂架结构的改进，所述凸块为向外的倒锥形结构或两侧形成一定弧度的燕尾结构。
作为本发明的一种适用于C环试样的挂架结构的改进，两个所述通槽为弧形结构。
作为本发明的一种适用于C环试样的挂架结构的改进，该挂架结构为线型结构，多个试样安放单元均匀布置在所述挂架结构的一侧或两侧。
与现有技术相比，本发明采取的技术方案的有益技术效果是：
挂架上设有倒锥形结构或燕尾结构，方便C环试样放入；
通槽的底部一侧设挡板，用以放置C环试样；
凸块、通槽和挡板的材质均为有机玻璃，有效避免了C环试样和挂架的接触腐蚀和缝隙腐蚀；
C环试样的安装方式为竖直安装，有利于试样从溶液中升起后表面水分的沥干，更加接近试验模拟的环境工况。
当然，实施本发明的任一产品并不一定需要同时达到以上所述的所有优点。
附图说明
图1为本发明的一种适用于C环试样的挂架结构的示意图。
图中，1-凸块；2-通槽；3-挡板；4-C环试样；5-螺钉。
具体实施方式
为使本发明的目的、技术方案和优点更加清楚，下面将结合附图对本发明的各实施方式进行详细的阐述。
如图1所示，一种适用于C环试样4的挂架结构，包括多个试样安放单元，多个试样安放单元均匀布置在挂架结构的一侧或两侧，挂架结构可以是线型结构，也可以是环形结构或者其他结构。
C环试样4上穿设有螺钉5，通过旋拧螺钉5向C环试样4施加预应力，将C环试样4挂接在挂架结构上，并将挂架结构放置于模拟场景中，从而进行C环试样4应力腐蚀试验。
每个试样安放单元均水平设一凸块1，凸块1两侧均竖直设一通槽2，通槽2的底部一侧设挡板3，两个通槽2的形状与C环试样4的开口形状相适配。本实施例中，“水平”和“竖直”是相对而言的，不影响本挂架结构的其他使用方式。C环试样4的开口两端从上而下分别插入两个通槽2至挡板3侧。当放松C环试样4时，由于两个通槽2的形状与C环试样4的开口形状相适配， C环试样4的开口与两个通槽2前后相抵接，C环试样4可能会略微向一侧倾斜，但是能够侧挂于挂架结构上。采用这种侧挂方式，可以避免“当C环试样4开口朝上时，挂架结构从溶液中升起后，C环试样4上容易积存水分，不利于表面快速沥干”的情况。
作为本发明的一个实施例，两个通槽2为弧形结构，有利于C环试样4 的开口两端从上而下分别插入弧形结构至挡板3侧，通过C环试样4的开口与两个通槽2前后相抵接，使C环试样4侧挂于挂架结构上，而由于挡板3 的阻碍和C环试样4自身的重力作用，C环试样4不会从上而下穿过通槽2 而导致脱出挂架结构。
作为本发明的一个实施例，凸块1为向外的倒锥形结构或两侧形成一定弧度的燕尾结构。该设计有利于C环试样4的开口套接在倒锥形结构或燕尾结构上，从而卡接在两个底部设有挡板3的通槽2上。C环试样4由于受螺钉5 的加载力度不同，其开口大小也不相同，倒锥形结构或燕尾结构根据C环试样4的最小开口而定，可以满足不同预应力的C环试样4放入。
C环试样4可能会发生旋转，在旋转的过程中，穿设在C环试样4的螺钉5会碰到挂架结构，阻止了C环试样4的旋转，从而避免了C环试样4因为旋转而脱出凸块1的可能性。本挂架结构的设计可以使用多种型号的C环试样4。
作为本发明的一个实施例，凸块1、通槽2和挡板3均由有机玻璃材质制成。该设计避免了C环试样4和挂架结构的接触腐蚀和缝隙腐蚀。
作为本发明的一个实施例，凸块1、通槽2和挡板3可以为一体成型结构，使挂架结构更加牢固耐用。
本发明结构简单，材质使用有机玻璃，易于加工，且与C环试样4绝缘，避免了产生接触腐蚀和缝隙腐蚀的可能性。C环试样4安装方便快捷，极大地降低了劳动强度和作业时间。C环试样4竖直安装，还有利于C环表面的水分沥干，更接近试验模拟的环境工况。
以上所述，仅为本发明较佳的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明揭露的技术范围内，可轻易想到的变化或替换，都应涵盖在本发明的保护范围之内。因此，本发明的保护范围应该以权利要求的保护范围为准。

Claims (7)

1.一种适用于C环试样的挂架结构，其特征在于：包括多个试样安放单元，每个试样安放单元均水平设一凸块，所述凸块两侧均竖直设一通槽，所述通槽的底部一侧设挡板，两个所述通槽的形状与C环试样的开口形状相适配。
2.如权利要求1所述的一种适用于C环试样的挂架结构，其特征在于：所述凸块、通槽和挡板均由有机玻璃材质制成。
3.如权利要求2所述的一种适用于C环试样的挂架结构，其特征在于：所述凸块和通槽为一体成型结构。
4.如权利要求1所述的一种适用于C环试样的挂架结构，其特征在于：所述C环试样穿设有螺钉，所述螺钉用以向所述C环试样提供预应力。
5.如权利要求1所述的一种适用于C环试样的挂架结构，其特征在于：所述凸块为向外的倒锥形结构或两侧形成一定弧度的燕尾结构。
6.如权利要求1所述的一种适用于C环试样的挂架结构，其特征在于：两个所述通槽为弧形结构。
7.如权利要求1所述的一种适用于C环试样的挂架结构，其特征在于：该挂架结构为线型结构，多个试样安放单元均匀布置在所述挂架结构的一侧或两侧。
CN201710557829.5A 2017-07-10 2017-07-10 一种适用于c环试样的挂架结构 Active CN107192661B (zh)