CN107180962A - A kind of porous graphite doping and the preparation method of carbon coating graphite cathode material - Google Patents
A kind of porous graphite doping and the preparation method of carbon coating graphite cathode material Download PDFInfo
- Publication number
- CN107180962A CN107180962A CN201710461072.XA CN201710461072A CN107180962A CN 107180962 A CN107180962 A CN 107180962A CN 201710461072 A CN201710461072 A CN 201710461072A CN 107180962 A CN107180962 A CN 107180962A
- Authority
- CN
- China
- Prior art keywords
- graphite
- porous
- doping
- carbon
- carbon coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of doping of porous graphite and the preparation method of carbon coating graphite cathode material, the modification of porous carbon doping and carbon coating to graphite can solve graphite high rate capability it is poor the problem of, because the porous carbon of doping serves the effect of electric transmission cushion in graphite material, therefore the introducing of the cycle performance and the other carbon material of high magnification charge and discharge point performance that improve graphite material can effectively suppress common embedding effect of the electrolyte to graphite, the anti-organic solvent erosiveness of graphite is improved, the cycle performance of graphite is further improved.
Description
The application is application number:2015102660462, the applying date:05 month 2015 22 days, denomination of invention:It is a kind of porous
Graphite dopping and the divisional application of the preparation method of carbon coating graphite cathode material.
Technical field
The present invention relates to lithium ion battery negative material, and in particular to a kind of porous graphite doping and carbon coating graphite cathode
The preparation method of material.
Background technology
With the development of automobile industry, the exhaustion of the non-renewable fossil fuel such as oil, natural gas is of increasing concern, empty
Gas pollutes and room temperature effect also turns into global problem.To solve energy problem, low-carbon environment-friendly is realized, based on current energy skill
The development level of art, electric vehicle engineering is increasingly becoming the emphasis direction of global economic development, the U.S., Japan, Germany, China etc.
The national fuel vehicle of limitation in succession is used, and greatly develops electric car.It is used as the core component of electric automobile --- electrokinetic cell is also met
Big good opportunity to develop is carried out.Electrokinetic cell refers to the battery applied to electric car, including lithium ion battery, lead-acid battery, combustion
Expect battery etc., wherein, lithium ion battery is because with specific energy is high, specific power is big, self discharge is few, service life length and security are good
The advantages of, it has also become the emphasis of current various countries' development.
Lithium ion battery is as the remarkable new generation of green high-energy battery of performance, and it has, and high voltage, energy density are big, follow
The distinguishing feature such as ring performance is good, self discharge is small, memory-less effect, operating temperature range are wide.Present lithium ion cell electrode material
Expect that positive electrode is mainly LiCoO2、LiNiO2And LiMn2O4Deng.Co systems toxicity is larger, and Ni systems synthesis condition is harsh, Mn systems
Jahn-Teller effect cycle performances are bad.LiFePO4Being acknowledged as comparing in lithium ion battery of future generation has before application
One of positive electrode of scape.However, the security of negative pole is then often ignored by people, current lithium ion battery negative material is main
It is carbon material.
And there is relatively low lithium insertion/deintercalation current potential as the graphite type material of lithium ion battery negative material, it is suitable
Reversible capacity and aboundresources, it is cheap the advantages of, be more satisfactory lithium ion battery negative material.But there is also head for it
Secondary discharging efficiency is low, cycle performance is poor, it is selectively high to electrolyte the shortcomings of, be restricted graphite material application.To understand
The certainly disadvantages mentioned above of graphite material, people are modified processing to graphite by various methods, and the method generally used at present is
Carbon coating method.Yang Ruizhi etc. exists《Resin carbon coated graphite as lithium ion battery negative electrode research》(《Journal of Inorganic Materials》,
2000,15(4):712—718)In with liquid-phase impregnation process in natural flake graphite Surface coating phenolic resin, filled with constant current,
Electric discharge, powder microelectrode cyclic voltammetry has investigated charging-discharging performances.Test result indicates that, thermally treated phenolic resin carbon
Coated graphite material puts that a capacity is higher, and cycle life is longer, can as high performance lithium ion battery negative material.He Ming
Deng《The preparation of resin carbon-coated graphite and its chemical property》(《Battery》, 2003,3(5):281—284)In in day
Right micro crystal graphite particle surface coats one layer of resin carbon, and cladding processing can reduce the appearance irreversible first of natural micro crystal graphite
Amount, using first mixing and then scattered method coated graphite, inside is natural micro crystal graphite, and outside is 1~2 μm of phenolic resin
Pyrolytic carbon layer.The irreversible capacity that lithium ion experimental cell measures natural micro crystal graphite is 14%, the irreversible capacity of coated graphite
For 7%.Cladding processing can largely reduce the irreversible capacity of natural micro crystal graphite.Chen Meng etc. exists《Pitch-coating is natural
The preparation of graphite and performance study》(《Battery industry》, 2007,12(5):298—302)Using liquid phase coating method, pitch is split
Carbon coating is solved on natural spherical plumbago, to improve its cycle performance.Test result indicates that, native graphite after pitch-coating,
Irreversible capacity loss has been reduced to 32.5mAh/g from 125.5mAh/g, and specific capacity is brought up to from 290.8mAh/g
365.3mAh/g, the capability retention after 50 circulations has brought up to 93.66% from 55.4%, effectively improves following for native graphite
Ring performance.
The content of the invention
The technical problems to be solved by the invention are to provide a kind of porous graphite doping and carbon coating graphite cathode material
Preparation method, it is therefore intended that the problems such as solving poor graphite high-rate charge-discharge capability and anti-electrolyte organic solvent poor compatibility,
Improve the cycle performance of discharge and recharge.
The present invention solve the technical scheme that is used of above-mentioned technical problem for:A kind of porous graphite doping and carbon coating graphite
The preparation method of negative material, it is characterised in that comprise the following steps:
(1)Configuration concentration is 1~12 mg/mL potassium permanganate solution, adds graphite and carries out oxidation pore-creating, washing and drying is obtained
To porous graphite;Step(1)In graphite be native graphite, particle diameter D50≤5 μm, specific surface area >=10m2/g;
(2)According to porous graphite:Graphite=(0.02~0.1):1 ratio, while adding according to 5~20% ratio of graphite weight
Enter a certain amount of carbon matrix precursor, be well mixed, obtain porous graphite and graphite and carbon matrix precursor composite granule;Step(2)In
Graphite be Delanium or native graphite, particle diameter D50 is between 5~25 μm, specific surface area≤6m2/ g, tap density >=0.7g/
cm3;Step(2)Described in carbon matrix precursor be sodium cellulose glycolate, polyvinyl alcohol, phenolic resin, epoxy resin, grape
Mixture more than one or both of sugar, starch, pitch;
(3)Under nitrogen protection, the composite granule in step (2) is heated to 700~950 DEG C with 2~10 DEG C/min heatings,
And continue 3~20 hours, cool down to after room temperature, pulverize and sieve, that is, obtain porous graphite doping and carbon coating graphite cathode material
Material.
Compared with prior art, the advantage of the invention is that porous graphite doping improves the conductance of graphite with carbon coating
Rate, obtained porous graphite doping is high with carbon coating graphite cathode material specific capacity, and good cycle can be widely applied to various
Lithium ion battery.Meanwhile, preparation method of the invention is with low cost, and technique is simple, is suitable for large-scale industrial production.
The problem of high rate capability that porous carbon can solve graphite to the doping vario-property of graphite is poor, it is porous due to doping
Carbon serves the effect of electric transmission cushion in graphite material, therefore improves the cycle performance and high magnification of graphite material
The introducing of the other carbon material of charge and discharge point performance can effectively suppress common embedding effect of the electrolyte to graphite, and raising graphite resists organic molten
Agent erosiveness, further improves the cycle performance of graphite.
Embodiment
The present invention is described in further detail below in conjunction with specific embodiment.
Embodiment 1
A kind of porous graphite doping and the preparation method of carbon coating graphite cathode material, comprise the following steps:
(1)5 mg/mL potassium permanganate solution is prepared, by 50g native graphite(Particle diameter D50:3.63 μm, specific surface area:
12.51m2/g)Be added in solution, then oxidation processes 60min is washed with water to neutrality, then dry for standby;
(2)According to porous graphite:Graphite(D50:10.82 μm, specific surface area:6.1m2/ g, tap density:0.96g/cm3)=
0.02:1 ratio, while adding a certain amount of carbon matrix precursor according to the ratio of graphite weight 5%(Pitch powder), it is well mixed,
Obtain porous graphite and graphite and carbon matrix precursor composite granule;
(3)Under nitrogen protection, the composite granule in step (2) is heated to 950 DEG C with 10 DEG C/min heatings, and it is small to continue 3
When, cool down to after room temperature, pulverize and sieve, that is, obtain porous graphite doping and carbon coating graphite cathode material.
Embodiment 2
A kind of porous graphite doping and the preparation method of carbon coating graphite cathode material, comprise the following steps:
(1)10 mg/mL potassium permanganate solution is prepared, by 50g native graphite(Particle diameter D50:5.42 μm, specific surface area:
18.12m2/g)Be added in solution, then oxidation processes 30min is washed with water to neutrality, then dry for standby;
(2)According to porous graphite:Graphite(D50:17.21 μm, specific surface area:5.8m2/ g, tap density:0.85g/cm3)=
0.1:1 ratio, while adding a certain amount of carbon matrix precursor according to the ratio of graphite weight 10%(Phenolic resin powder), mixing
Uniformly, porous graphite and graphite and carbon matrix precursor composite granule are obtained;
(3)Under nitrogen protection, the composite granule in step (2) is heated to 900 DEG C with 5 DEG C/min heatings, and it is small to continue 5
When, cool down to after room temperature, pulverize and sieve, that is, obtain porous graphite doping and carbon coating graphite cathode material.
Embodiment 3
A kind of porous graphite doping and the preparation method of carbon coating graphite cathode material, comprise the following steps:
(1)8 mg/mL potassium permanganate solution is prepared, by 50g native graphite(Particle diameter D50:7.28 μm, specific surface area:
15.42m2/g)Be added in solution, then oxidation processes 50min is washed with water to neutrality, then dry for standby;
(2)According to porous graphite:Graphite(D50:8.14 μm, specific surface area:6.9m2/ g, tap density:1.04g/cm3)=
0.08:1 ratio, while adding a certain amount of carbon matrix precursor according to the ratio of graphite weight 7%(Epoxy resin powder), mixing
Uniformly, porous graphite and graphite and carbon matrix precursor composite granule are obtained;
(3)Under nitrogen protection, the composite granule in step (2) is heated to 850 DEG C with 8 DEG C/min heatings, and it is small to continue 6
When, cool down to after room temperature, pulverize and sieve, that is, obtain porous graphite doping and carbon coating graphite cathode material.
Comparative example 1
Undressed native graphite in embodiment 1.
Comparative example 2
Undressed Delanium in embodiment 2.
Electrochemical property test
For the performance for the modification lithium-ion battery graphite cathode material for examining the inventive method preparation, entered with half-cell method of testing
Row test, with above example and the negative material of comparative example:Acetylene black:PVDF(Kynoar)=95:2:3(Weight ratio),
Plus appropriate NMP(1-METHYLPYRROLIDONE)Pulpous state is tuned into, is coated on copper foil, negative pole is made within 8 hours through 110 DEG C of dryings of vacuum
Piece;Using metal lithium sheet as to electrode, electrolyte is 1mol/L LiPF6/EC+DEC+DMC=1:1:1, microporous polypropylene membrane be every
Film, is assembled into battery.Charging/discharging voltage is 0~2.0V, and charge-discharge velocity is 0.5C, and battery performance is carried out can test, test
It the results are shown in Table 1.
Table 1 for negative material in not be the same as Example and comparative example performance comparision
The general principle and principal character and advantages of the present invention of the present invention, the technical staff of the industry has been shown and described above
It should be appreciated that the present invention is not limited to the above embodiments, simply illustrate the present invention described in above-described embodiment and specification
Principle, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these change and
Improvement all fall within the protetion scope of the claimed invention, and the claimed scope of the invention is by appended claims and its equivalent
Thing is defined.
Claims (1)
1. a kind of porous graphite doping and the preparation method of carbon coating graphite cathode material, it is characterised in that comprise the following steps:
(1)Prepare porous graphite:Configuration concentration is 1-12mg/mL potassium permanganate solution, adds graphite and carries out oxidation pore-creating,
Washing and drying, obtains porous graphite;Step(1)In graphite be native graphite, particle diameter D50≤10 μm, specific surface area >=10m2/
g;
(2)It is prepared by graphite presoma:According to porous graphite:Graphite=(0.02~0.1):1 ratio, while according to graphite weight
5~20% ratio add a certain amount of carbon matrix precursor, be well mixed, obtain porous graphite and graphite and carbon matrix precursor is multiple
Close powder;Step(2)In graphite be Delanium or native graphite, particle diameter D50 is between 5~25 μm, specific surface area≤6m2/
G, tap density >=0.7g/cm3;Step(2)Described in carbon source presoma be sodium cellulose glycolate, polyvinyl alcohol, phenolic aldehyde
Mixture more than one or both of resin, epoxy resin, glucose, starch, pitch;
(3)High-temperature process:Under nitrogen protection, the powder of drying in step (2) is heated to 700 with 2~10 DEG C/min heatings
~950 DEG C, and continue 3-20 hours, cool down to after room temperature, pulverize and sieve, that is, obtain porous graphite doping and carbon coating graphite
Negative material.