CN103647081B - The preparation method of ascorbic acid modified graphite - Google Patents
The preparation method of ascorbic acid modified graphite Download PDFInfo
- Publication number
- CN103647081B CN103647081B CN201310568784.3A CN201310568784A CN103647081B CN 103647081 B CN103647081 B CN 103647081B CN 201310568784 A CN201310568784 A CN 201310568784A CN 103647081 B CN103647081 B CN 103647081B
- Authority
- CN
- China
- Prior art keywords
- graphite
- ascorbic acid
- acid modified
- mixture
- modified graphite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention provides a kind of preparation method of ascorbic acid modified graphite, belong to chemical cell preparation field.The present invention by after potassium permanganate and native graphite are carried out oxidation processes, then carries out ultrasonic, sintering with ascorbic acid, obtains a kind of negative material of ascorbic acid modified graphite.The modified graphite that method provided by the invention is prepared is the complex carbon material with nucleocapsid structure, improve the chemical property of graphite material, not only can improve the compatibility of electrode and electrolyte, in cyclic process subsequently, stop the insertion of solvent, reduce irreversible loss; And its external sheath thing secures graphite flake, at Li
+when deintercalation changes graphite volume repeatedly, stop coming off of graphite linings.
Description
Technical field
The invention belongs to chemical cell preparation field, particularly relate to a kind of preparation method of ascorbic acid modified graphite.
Background technology
Native graphite is widely used as the negative material of lithium ion battery, but the compatibility of native graphite and electrolyte is poor, in embedding/de-lithium process, easily there is the stripping of graphite linings and cause cycle performance to decline, thus limiting the application of pure natural graphite in lithium ion battery.
Along with the extensively universal of various small-sized portable electronic product and electric bicycle and development, the commercial development of New Generation of Electric Vehicle (EV), hybrid vehicle (HEV), has higher requirement to the energy density of lithium ion battery and performance.Traditional carbon-based negative electrode material all can not meet the needs of Novel cathode material for lithium ion battery of future generation in specific capacity, specific energy, and therefore the carbon-based negative electrode material of development of new has very important meaning.
Summary of the invention
A preparation method for ascorbic acid modified graphite, is characterized in that comprising the following steps:
(1) with potassium permanganate, native graphite is carried out oxidation processes, obtain mixture A;
(2) mixture A and ascorbic acid are mixed in proportion, and carry out ultrasonic disperse in deionized water, obtain mixture B;
(3) mixture B is carried out drying, then carburizing sintering 2 ~ 4 hours under the inert gas shielding of 700 DEG C ~ 900 DEG C, obtains described ascorbic acid modified graphite.
Preferably, the mass ratio of the native graphite described in step (1) and potassium permanganate is 1:(0.05 ~ 0.2).
Preferably, the oxidation processes described in step (1) comprises the following steps: oxidizing temperature is 800 DEG C ~ 1000 DEG C, and oxidization time is 10 ~ 40 seconds.
Preferably, the mass ratio of the mixture A described in step (2) and ascorbic acid is 2:(0.5 ~ 1).
Beneficial effect of the present invention is as follows:
1. the present invention adopts ascorbic acid modified graphite, and ascorbic acid has advantages such as being extensively easy to get, cheap, can reduce the cost of modified graphite, reduces it produces battery cost as negative material further.
2. with the modified graphite that method provided by the invention is prepared from, at high-graphitized carbon material surface coated one deck ascorbic acid amorphous carbon material, prepare the complex carbon material with nucleocapsid structure, improve the chemical property of graphite material, not only can improve the compatibility of electrode and electrolyte, in cyclic process subsequently, stop the insertion of solvent, reduce irreversible loss; And its external sheath thing secures graphite flake, at Li
+when deintercalation changes graphite volume repeatedly, stop coming off of graphite linings.
Embodiment
Below in conjunction with specific embodiment, the present invention is described in detail.Following examples will contribute to those skilled in the art and understand the present invention further, but not limit the present invention in any form.It should be pointed out that to those skilled in the art, without departing from the inventive concept of the premise, some distortion and improvement can also be made.These all belong to protection scope of the present invention.
embodiment 1
A preparation method for ascorbic acid modified graphite, is characterized in that comprising the following steps:
(1) be 1:0.05 mixing by the mass ratio of native graphite and potassium permanganate, at temperature is 800 DEG C, oxidation processes 40 seconds, obtains mixture A;
(2) by mixture A and ascorbic acid be the ratio mixing of 2:1 in mass ratio, and carry out ultrasonic disperse in deionized water, obtain mixture B;
(3) mixture B is carried out drying, then carburizing sintering 3 ~ 4 hours under the inert gas shielding of 700 DEG C ~ 800 DEG C, obtains described ascorbic acid modified graphite.
embodiment 2
A preparation method for ascorbic acid modified graphite, is characterized in that comprising the following steps:
(1) be 1:0.2 mixing by the mass ratio of native graphite and potassium permanganate, at temperature is 1000 DEG C, oxidation processes 10 seconds, obtains mixture A;
(2) by mixture A and ascorbic acid be the ratio mixing of 2:0.8 in mass ratio, and carry out ultrasonic disperse in deionized water, obtain mixture B;
(3) mixture B is carried out drying, then carburizing sintering 2 ~ 3 hours under the inert gas shielding of 800 DEG C ~ 900 DEG C, obtains described ascorbic acid modified graphite.
embodiment 3
A preparation method for ascorbic acid modified graphite, is characterized in that comprising the following steps:
(1) be 1:0.1 mixing by the mass ratio of native graphite and potassium permanganate, at temperature is 900 DEG C, oxidation processes 30 seconds, obtains mixture A;
(2) by mixture A and ascorbic acid be the ratio mixing of 2:0.5 in mass ratio, and carry out ultrasonic disperse in deionized water, obtain mixture B;
(3) mixture B is carried out drying, then carburizing sintering 2.5 hours under the inert gas shielding of 750 DEG C ~ 850 DEG C, obtains described ascorbic acid modified graphite.
Claims (1)
1. a preparation method for ascorbic acid modified graphite, is characterized in that comprising the following steps:
(1) with potassium permanganate, native graphite is carried out oxidation processes, obtain mixture A;
(2) mixture A and ascorbic acid are mixed in proportion, and carry out ultrasonic disperse in deionized water, obtain mixture B;
(3) mixture B is carried out drying, then carburizing sintering 2 ~ 4 hours under the inert gas shielding of 700 DEG C ~ 900 DEG C, obtains described ascorbic acid modified graphite;
Wherein, the mass ratio of the native graphite described in step (1) and potassium permanganate is 1:(0.05 ~ 0.2);
Oxidation processes described in step (1) comprises the following steps: oxidizing temperature is 800 DEG C ~ 1000 DEG C, and oxidization time is 10 ~ 40 seconds;
The mass ratio of the mixture A described in step (2) and ascorbic acid is 2:(0.5 ~ 1).