CN107164968A - A kind of efficient Anti-ultraviolet Garment Fabric and preparation method thereof - Google Patents
A kind of efficient Anti-ultraviolet Garment Fabric and preparation method thereof Download PDFInfo
- Publication number
- CN107164968A CN107164968A CN201710379851.5A CN201710379851A CN107164968A CN 107164968 A CN107164968 A CN 107164968A CN 201710379851 A CN201710379851 A CN 201710379851A CN 107164968 A CN107164968 A CN 107164968A
- Authority
- CN
- China
- Prior art keywords
- ultraviolet
- parts
- fabric
- fiber
- efficient anti
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses efficient Anti-ultraviolet Garment Fabric and preparation method thereof, composition and its parts by weight are：30 ~ 40 parts of long-staple cotton fiber, 15 ~ 25 parts of polyester fiber, 10 ~ 15 parts of flaxen fiber, 5 ~ 10 parts of silk fiber, 1 ~ 5 part of ultraviolet light screener, 1 ~ 5 part of thickener, 1 ~ 5 part of polyethylene glycol, 5 ~ 10 parts of coating agent.Have the beneficial effect that：The various proportioning components of garment material of the present invention rationally, with good moisture absorption, dissipate wet and ventilative function, feel is smooth plentiful, to no skin irritation, makes skin feel more comfortable；Fabric is nontoxic, non-stimulated, harmless, and uv-shielding capacity is stable, not the influence of heated, light or other materials；Rate of ultraviolet shield is high, continuation is strong, can all band shielding ultraviolet rays, effective acting time is long, and clothing is than the ability still with higher absorption ultraviolet in the case of relatively thin and of light color, it is easy to popularization and application.
Description
Technical field
The present invention relates to garment material field, more particularly to a kind of efficient Anti-ultraviolet Garment Fabric and preparation method thereof.
Background technology
Through the ultraviolet of atmosphere, part is reflected, is partly absorbed, and the transmission clothing also having is radiated at the person
Body, the excessive ultraviolet of irradiation can injure skin, so as to threaten people's healthy.As divided by wavelength size, it is ultraviolet
Line can be divided into three classes：Near ultraviolet band（UVA）, middle ultraviolet band（UVB）, extreme ultraviolet region（UVC）, wherein extreme ultraviolet region
Amount of radiation is maximum.After UVA irradiates epidermis, the mRNA and protein expression of I type and III procollagen type are inhibited in epidermis, subtract
The quantity of few epidermis inner fiber cell, suppresses the synthesis of collagen, and increases the decomposition of elastin laminin, improves collagen
The activity of catabolic enzyme matrix metalloproteinase, so as to cause cutis laxa thus produce wrinkle.In addition, UVB irradiation can allow
Skin photoage.The maximum ultraviolet of harm surely belongs to short wave ultraviolet, and it will can cut positioned at endonuclear DNA molecular chain
It is disconnected, there is the enzyme for repairing power that the DNA of chain rupture can resile, if the repair ability of enzyme is poor, can cause to suffer from cutaneum carcinoma.
Fortunately, the ozone layer positioned at the km of overhead 10 ~ 50 can absorb short wave ultraviolet, and cause it can not reach ground.But
It is the modern science and technology continued to develop, the continuous of temperature increases, and the industrialization of the mankind constantly destroys the extraatmospheric ozone of earth's surface
Layer, has increasing ultraviolet to be irradiated to human body through ozone layer, and ultraviolet harm is increasing, more and more substantially, ultraviolet
The importance of line protection is also increasingly highlighted, for working in the wild, out on tours, the also people on plateau, uvioresistant weaving
Product are very important.Concern of the people to uvioresistant product is more and more, and at home and abroad in the market has ultraviolet ray resistant textiles
There is the huge application prospect heart.
Prior art such as Authorization Notice No. is the B of CN 103835140 Chinese invention patent, discloses a kind of antiultraviolet
Fabric, the fabric includes fabric and is coated in the ultraviolet resistant layer of fabric nexine, and ultraviolet resistant layer is coffee
Thickness 0.05mm ~ 0.3mm of the blended layer of powder and polyester, wherein ultraviolet resistant layer, the particle diameter of coffee powder is 0.5 μm ~ 5 μ
The mass ratio of m, coffee powder and polyester is 2:10~5:10.The fabric has that UV resistance effect is good, noxious material do not decomposed, anti-
The features such as bacterium eliminates the unusual smell, but comfort level is not enough, it is improper to be used for clothes.
The content of the invention
It is an object of the invention to provide a kind of uv resistance can strong, water-fastness, good permeability, wear and comfortable efficiently prevents
Ultraviolet garment material and preparation method thereof.
The present invention is directed to the problem of being mentioned in above-mentioned technology, and the technical scheme taken is：A kind of efficient ultra violet resistant clothes
Fabric, composition and its parts by weight are：30 ~ 40 parts of long-staple cotton fiber, 15 ~ 25 parts of polyester fiber, 10 ~ 15 parts of flaxen fiber, silk fibroin
5 ~ 10 parts of dimension, 1 ~ 5 part of ultraviolet light screener, 1 ~ 5 part of thickener, 1 ~ 5 part of polyethylene glycol, 5 ~ 10 parts of coating agent.Ultraviolet screener
Agent is nano titanium oxide, nano zine oxide and protein peptides, and its mass ratio is 1:0.5~2:0.01 ~ 0.03, the amino of protein peptides
Acid sequence is HSHSYSRCYCRCLRCRVLHPGCVNCYRCSR, and the ultraviolet light screener can not only strengthen the UV resistance of fabric
Line, and the structure of bacteria cell wall can also be destroyed, change the permeability of bacteria cell wall, fabric is produced in preparation process
Bacterium it is lethal and nontoxic because normal osmotic pressure can not be kept, it is harmless；Coating agent is water-soluble urethane, and it contains admittedly
Measure as 25 ~ 30%.Above-mentioned garment material has stronger UV resistance ability, and ultraviolet resistance is persistent, clothing than it is relatively thin simultaneously
And it is of light color in the case of still have higher absorption ultraviolet ability；Gas permeability, the thermal diffusivity of clothing are improved, it is water-fast
Wash, pliability is high, dress is comfortable, and to no skin irritation.
A kind of preparation method of efficient Anti-ultraviolet Garment Fabric, preparation process is：
Base fabric prepares：Long-staple cotton fiber, polyester fiber, flaxen fiber, silk fiber are weighed by formula ratio, mixing is mixed to form fine
Dimension, is put into knitting braider, the formula woven base fabric for weaving and setting through computer, is washed again with cold water after hot water treatment, iron
Ironing, the various proportioning components of the base fabric rationally, with good moisture absorption, dissipate wet and ventilative function, heat transfer heat conduction is fast, suitable people
The excretion and secretion of body skin, feel are smooth plentiful, to no skin irritation, with good flexibility, make skin feel more
Plus it is comfortable；
It is prepared by coating slurry：Formula ratio ultraviolet light screener, polyethylene glycol mixing are taken, is stirred until homogeneous, adds coating agent, protein peptides
And thickener, stirring is to being well mixed, and the slurry has very high chemical stability and heat endurance, nontoxic, non-stimulated,
It is harmless, do not chemically react, do not influenceed by light and heat with other auxiliary agents, good dispersion is difficult to reunite, do not influenceed
The mechanical property of fabric；
Coating：Coating slurry is poured on and is fixed in the base fabric of coating machine clamping plate, makes to scrape hymenotome and base fabric contact portion is all uniformly divided
Coating slurry is furnished with, is at the uniform velocity promoted using hymenotome is scraped, a knifing shaping is baked, gained fabric ultraviolet screener again after prebake
Rate is high, continuation is strong, can all band shielding ultraviolet rays, effective acting time is long, extends fabric service life, will not produce not
The compound of sharp health, even if clothing is than the energy still with higher absorption ultraviolet in the case of relatively thin and of light color
Power, it is easy to popularization and application.
Wherein, the bath raio of 70 ~ 80 DEG C of hot water temperature in base fabric preparation process, base fabric and aquae destillata is 1:40 ~ 50, during processing
Between be 20 ~ 30 minutes；Coating layer thickness in coating step is 0.1 ~ 0.5mm, and prebake temperature is 85 ~ 95 DEG C, and the time is 2 ~ 5 points
Clock, baking temperature is 120 ~ 140 DEG C, and the time is 2 ~ 5 minutes.
Compared with prior art, the advantage of the invention is that：1）The various proportioning components of garment material of the present invention rationally, have
Good moisture absorption, dissipate wet with ventilative function, feel is smooth plentiful, to no skin irritation, with good flexibility, makes flesh
Skin feels more comfortable；2）Fabric is nontoxic, non-stimulated, harmless, and uv-shielding capacity is stable, be not heated, light or other
The influence of material；3）The fabric rate of ultraviolet shield is high, continuation is strong, being capable of all band shielding ultraviolet rays, effective acting time
It is long, extend fabric service life, will not produce the compound of unfavorable health, clothing is than in the case of relatively thin and of light color
Still have higher absorption ultraviolet ability, it is easy to popularization and application.
Embodiment
Below by embodiment, the invention will be further described：
Embodiment 1：
Efficient Anti-ultraviolet Garment Fabric, composition and its parts by weight are：35 parts of long-staple cotton fiber, 18 parts of polyester fiber, flaxen fiber
12 parts, 8 parts of silk fiber, 3 parts of ultraviolet light screener, 2 parts of thickener, 4 parts of polyethylene glycol, 6 parts of coating agent.Ultraviolet light screener
For nano titanium oxide, nano zine oxide and protein peptides, its mass ratio is 1:0.5:0.01, the amino acid sequence of protein peptides is
HSHSYSRCYCRCLRCRVLHPGCVNCYRCSR, the ultraviolet light screener can not only strengthen the antiultraviolet of fabric, but also
Can destroy the structure of bacteria cell wall, change the permeability of bacteria cell wall, make the bacterium that fabric is produced in preparation process because
Normal osmotic pressure can not be kept and lethal and nontoxic, it is harmless；Coating agent is water-soluble urethane, its solid content is 25 ~
30%。
The preparation method of efficient Anti-ultraviolet Garment Fabric, preparation process is：
1）Base fabric prepares：Long-staple cotton fiber, polyester fiber, flaxen fiber, silk fiber are weighed by formula ratio, mixing is mixed to form fine
Dimension, is put into knitting braider, the formula woven base fabric for weaving and setting through computer, is washed again with cold water after hot water treatment, iron
Ironing, the various proportioning components of the base fabric rationally, with good moisture absorption, dissipate wet and ventilative function, heat transfer heat conduction is fast, suitable people
The excretion and secretion of body skin, feel are smooth plentiful, to no skin irritation, with good flexibility, make skin feel more
Plus it is comfortable；
2）It is prepared by coating slurry：Formula ratio ultraviolet light screener, polyethylene glycol mixing are taken, is stirred until homogeneous, adds coating agent, albumen
Peptide and thickener, stirring is to being well mixed, and the slurry has very high chemical stability and heat endurance, nontoxic, non-stimulated, right
Human body is harmless, does not chemically react, is not influenceed by light and heat with other auxiliary agents, good dispersion, is difficult to reunite, does not influence face
The mechanical property of material；
3）Coating：Step 2 gained coating slurry is poured on and is fixed in the base fabric of coating machine clamping plate, makes to scrape hymenotome and base fabric contact site
Divide and be all evenly distributed with coating slurry, at the uniform velocity promoted using hymenotome is scraped, a knifing shaping is baked, gained fabric again after prebake
Rate of ultraviolet shield is high, continuation is strong, can all band shielding ultraviolet rays, effective acting time is long, extends fabric service life,
The compound of unfavorable health will not be produced, even if clothing is than still having higher absorption in the case of relatively thin and of light color
The ability of ultraviolet, it is easy to popularization and application.
The bath raio of 80 DEG C of hot water temperature in above-mentioned steps 1, base fabric and aquae destillata is 1:40, processing time is 30 minutes；Step
Coating layer thickness in rapid 3 is 0.2mm, and prebake temperature is 90 DEG C, and the time is 3 minutes；Baking temperature is 120 DEG C, and the time is 3 points
Clock.
The Uvr Protective Fabric fabric is subjected to anti-ultraviolet property test, its UPF is obtained（UPF）For
63.7, near ultraviolet ray wave band transmitance（UVA）For 2.5%.
Embodiment 2：
Efficient Anti-ultraviolet Garment Fabric, composition and its parts by weight are：40 parts of long-staple cotton fiber, polyester fiber 17, flaxen fiber 11
Part, 8 parts of silk fiber, 4 parts of ultraviolet light screener, 3 parts of thickener, 4 parts of polyethylene glycol, 7 parts of coating agent.Ultraviolet light screener is
Nano titanium oxide, nano zine oxide and protein peptides, its mass ratio are 1:1:0.01, the amino acid sequence of protein peptides is
HSHSYSRCYCRCLRCRVLHPGCVNCYRCSR, the ultraviolet light screener can not only strengthen the antiultraviolet of fabric, but also
Can destroy the structure of bacteria cell wall, change the permeability of bacteria cell wall, make the bacterium that fabric is produced in preparation process because
Normal osmotic pressure can not be kept and lethal and nontoxic, it is harmless；Coating agent is water-soluble urethane, its solid content is 25 ~
30%。
The preparation method of efficient Anti-ultraviolet Garment Fabric, preparation process is：
1）Base fabric prepares：Long-staple cotton fiber, polyester fiber, flaxen fiber, silk fiber are weighed by formula ratio, mixing is mixed to form fine
Dimension, is put into knitting braider, the formula woven base fabric for weaving and setting through computer, is washed again with cold water after hot water treatment, iron
Ironing, the various proportioning components of the base fabric rationally, with good moisture absorption, dissipate wet and ventilative function, heat transfer heat conduction is fast, suitable people
The excretion and secretion of body skin, feel are smooth plentiful, to no skin irritation, with good flexibility, make skin feel more
Plus it is comfortable；
2）It is prepared by coating slurry：Formula ratio ultraviolet light screener, polyethylene glycol mixing are taken, is stirred until homogeneous, adds coating agent, albumen
Peptide and thickener, stirring is to being well mixed, and the slurry has very high chemical stability and heat endurance, nontoxic, non-stimulated, right
Human body is harmless, does not chemically react, is not influenceed by light and heat with other auxiliary agents, good dispersion, is difficult to reunite, does not influence face
The mechanical property of material；
3）Coating：Step 2 gained coating slurry is poured on and is fixed in the base fabric of coating machine clamping plate, makes to scrape hymenotome and base fabric contact site
Divide and be all evenly distributed with coating slurry, at the uniform velocity promoted using hymenotome is scraped, a knifing shaping is baked, gained fabric again after prebake
Rate of ultraviolet shield is high, continuation is strong, can all band shielding ultraviolet rays, effective acting time is long, extends fabric service life,
The compound of unfavorable health will not be produced, even if clothing is than still having higher absorption in the case of relatively thin and of light color
The ability of ultraviolet, it is easy to popularization and application.
The bath raio of 70 DEG C of hot water temperature in above-mentioned steps 1, base fabric and aquae destillata is 1:45, processing time is 25 minutes；Step
Coating layer thickness in rapid 3 is 0.4mm, and prebake temperature is 95 DEG C, and the time is 2 minutes；Baking temperature is 140 DEG C, and the time is 2 points
Clock.
The Uvr Protective Fabric fabric is subjected to anti-ultraviolet property test, its UPF is obtained（UPF）For
58.6, near ultraviolet ray wave band transmitance（UVA）For 3.2%.
Embodiment 3：
Efficient Anti-ultraviolet Garment Fabric, composition and its parts by weight are：32 parts of long-staple cotton fiber, 20 parts of polyester fiber, flaxen fiber
10 parts, 10 parts of silk fiber, 5 parts of ultraviolet light screener, 5 parts of thickener, 5 parts of polyethylene glycol, 8 parts of coating agent.Ultraviolet screener
Agent is nano titanium oxide, nano zine oxide and protein peptides, and its mass ratio is 1:0.5~2:0.01 ~ 0.03, the amino of protein peptides
Acid sequence is HSHSYSRCYCRCLRCRVLHPGCVNCYRCSR, and the ultraviolet light screener can not only strengthen the UV resistance of fabric
Line, and the structure of bacteria cell wall can also be destroyed, change the permeability of bacteria cell wall, fabric is produced in preparation process
Bacterium it is lethal and nontoxic because normal osmotic pressure can not be kept, it is harmless；Coating agent is water-soluble urethane, and it contains admittedly
Measure as 25 ~ 30%.
The preparation method of efficient Anti-ultraviolet Garment Fabric, preparation process is：
1）Base fabric prepares：Long-staple cotton fiber, polyester fiber, flaxen fiber, silk fiber are weighed by formula ratio, mixing is mixed to form fine
Dimension, is put into knitting braider, the formula woven base fabric for weaving and setting through computer, is washed again with cold water after hot water treatment, iron
Ironing, the various proportioning components of the base fabric rationally, with good moisture absorption, dissipate wet and ventilative function, heat transfer heat conduction is fast, suitable people
The excretion and secretion of body skin, feel are smooth plentiful, to no skin irritation, with good flexibility, make skin feel more
Plus it is comfortable；
2）It is prepared by coating slurry：Formula ratio ultraviolet light screener, polyethylene glycol mixing are taken, is stirred until homogeneous, adds coating agent, albumen
Peptide and thickener, stirring is to being well mixed, and the slurry has very high chemical stability and heat endurance, nontoxic, non-stimulated, right
Human body is harmless, does not chemically react, is not influenceed by light and heat with other auxiliary agents, good dispersion, is difficult to reunite, does not influence face
The mechanical property of material；
3）Coating：Step 2 gained coating slurry is poured on and is fixed in the base fabric of coating machine clamping plate, makes to scrape hymenotome and base fabric contact site
Divide and be all evenly distributed with coating slurry, at the uniform velocity promoted using hymenotome is scraped, a knifing shaping is baked, gained fabric again after prebake
Rate of ultraviolet shield is high, continuation is strong, can all band shielding ultraviolet rays, effective acting time is long, extends fabric service life,
The compound of unfavorable health will not be produced, even if clothing is than still having higher absorption in the case of relatively thin and of light color
The ability of ultraviolet, it is easy to popularization and application.
The bath raio of 78 DEG C of hot water temperature in above-mentioned steps 1, base fabric and aquae destillata is 1:42, processing time is 25 minutes；Step
Coating layer thickness in rapid 3 is 0.2mm, and prebake temperature is 90 DEG C, and the time is 3 minutes；Baking temperature is 120 DEG C, and the time is 5 points
Clock.
The Uvr Protective Fabric fabric is subjected to anti-ultraviolet property test, its UPF is obtained（UPF）For
53.7, near ultraviolet ray wave band transmitance（UVA）For 3.1%.
Routine operation in the operating procedure of the present invention is well known to those skilled in the art, herein without repeating.
Technical scheme is described in detail embodiment described above, it should be understood that it is described above only
For the specific embodiment of the present invention, it is not intended to limit the invention, all any modifications made in the spirit of the present invention,
Supplement or similar fashion replacement etc., should be included in the scope of the protection.
SEQUENCE LISTING
<110>Sea salt sends Mortopl Science and Technology Ltd.
<120>A kind of efficient Anti-ultraviolet Garment Fabric and preparation method thereof
<130> 1
<160> 1
<170> PatentIn version 3.5
<210> 1
<211> 30
<212> PRT
<213>It is artificial synthesized go out
<400> 1
His Ser His Ser Tyr Ser Arg Cys Tyr Cys Arg Cys Leu Arg Cys Arg
1 5 10 15
Val Leu His Pro Gly Cys Val Asn Cys Tyr Arg Cys Ser Arg
20 25 30
Claims (8)
1. a kind of efficient Anti-ultraviolet Garment Fabric, it is characterised in that：Described fabric composition and its parts by weight are：Long-staple cotton is fine
30 ~ 40 parts of dimension, 15 ~ 25 parts of polyester fiber, 10 ~ 15 parts of flaxen fiber, 5 ~ 10 parts of silk fiber, 1 ~ 5 part of ultraviolet light screener, thickening
1 ~ 5 part of agent, 1 ~ 5 part of polyethylene glycol, 5 ~ 10 parts of coating agent.
2. a kind of efficient Anti-ultraviolet Garment Fabric according to claim 1, it is characterised in that：Described ultraviolet screener
Agent is nano titanium oxide, nano zine oxide and protein peptides, and its mass ratio is 1:0.5~2:0.01~0.03.
3. a kind of efficient Anti-ultraviolet Garment Fabric according to claim 1, it is characterised in that：Described ultraviolet screener
The amino acid sequence of protein peptides is HSHSYSRCYCRCLRCRVLHPGCVNCYRCSR in agent.
4. a kind of efficient Anti-ultraviolet Garment Fabric according to claim 1, it is characterised in that：Described coating agent is water
Dissolubility urethane, its solid content is 25 ~ 30%.
5. the preparation method of efficient Anti-ultraviolet Garment Fabric, it is characterised in that：Described preparation method comprising the step of be：
1）Base fabric prepares：Long-staple cotton fiber, polyester fiber, flaxen fiber, silk fiber are weighed by formula ratio, mixing is mixed to form fine
Dimension, is put into knitting braider, the formula woven base fabric for weaving and setting through computer, is washed again with cold water after hot water treatment, iron
Ironing is standby；
2）It is prepared by coating slurry：Formula ratio ultraviolet light screener, polyethylene glycol mixing are taken, is stirred until homogeneous, adds coating agent and increasing
Thick dose, stir to well mixed；
3）Coating：Step 2 gained coating slurry is poured on and is fixed in the base fabric of coating machine clamping plate, makes to scrape hymenotome and base fabric contact site
Divide and be all evenly distributed with coating slurry, at the uniform velocity promoted using hymenotome is scraped, a knifing shaping is baked, produced efficiently again after prebake
Anti-ultraviolet Garment Fabric.
6. the preparation method of efficient Anti-ultraviolet Garment Fabric according to claim 4, it is characterised in that：Described step
The bath raio of 70 ~ 80 DEG C of hot water temperature in 1, base fabric and aquae destillata is 1:40 ~ 50, processing time is 20 ~ 30 minutes.
7. the preparation method of efficient Anti-ultraviolet Garment Fabric according to claim 4, it is characterised in that：Described step
Coating layer thickness in 3 is 0.1 ~ 0.5mm.
8. the preparation method of efficient Anti-ultraviolet Garment Fabric according to claim 4, it is characterised in that：Described step
Prebake temperature in 3 is 85 ~ 95 DEG C, and the time is 2 ~ 5 minutes；Baking temperature is 120 ~ 140 DEG C, and the time is 2 ~ 5 minutes.