CN107164761A - Printed matter manufacture craft with metal sheet - Google Patents
Printed matter manufacture craft with metal sheet Download PDFInfo
- Publication number
- CN107164761A CN107164761A CN201710254286.XA CN201710254286A CN107164761A CN 107164761 A CN107164761 A CN 107164761A CN 201710254286 A CN201710254286 A CN 201710254286A CN 107164761 A CN107164761 A CN 107164761A
- Authority
- CN
- China
- Prior art keywords
- metal sheet
- printed matter
- parts
- manufacture craft
- present
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of printed matter manufacture craft with metal sheet, includes following steps：（1）Metal sheet is taken, and metal sheet is etched using chemical solution, to obtain required pattern；（2）The metal sheet for completing etching is fixed on the surface of printed matter；（3）Aluminum coated steel is carried out to the surface of printed matter so that a transparent protective film is formed on the surface of printed matter, transparent protective film covers all metal sheet.Present invention process main feature is combined with the three-decker of printed matter base material, etch process metal sheet and later stage overlay film；Etching metal sheet can make full use of electric conductivity, magnetic, pliability etc., the multi-effects such as wire netting, circuit line, high-strength bending-resistant, extraordinary embossment are further designed on the basis of paper substrate three-decker, the present invention is realized is different from existing way from principle, material and processing procedure many-side, the progress of technique is realized, is that enterprise brings huge economic benefit.
Description
Technical field
The present invention relates to printed matter art, a kind of printed matter manufacture craft with metal sheet is referred in particular to.
Background technology
In printed matter surface, the stereo relief effect for forming projection is relatively common, is traditionally used in packaging industry
Hit convex making, but hit that convex technique production efficiency itself is not high, precision is general.Need mold（Copper mold or aluminum dipping form, also there is resin mold
Tool etc.）, using gold stamping film material, aluminium film colour and luster effect are transferred on printed matter with HTHP principle, and is formed
The stereoeffect of paper pattern.Gold stamping and hit the existing decades history of convex technique, development runs into bottleneck, it is difficult to reach what is more optimized
Effect and raising production efficiency.
The content of the invention
In view of this, in view of the existing deficiencies of the prior art, its main purpose is to provide a kind of band metal sheet to the present invention
Printed matter manufacture craft, it can effectively solve the problem of existing printed matter technique effect is single.
To achieve the above object, the present invention is using following technical scheme：
A kind of printed matter manufacture craft with metal sheet, includes following steps：
（1）Metal sheet is taken, and metal sheet is etched using chemical solution, to obtain required pattern；
（2）The metal sheet for completing etching is fixed on the surface of printed matter；
（3）Aluminum coated steel is carried out to the surface of printed matter so that a transparent protective film is formed on the surface of printed matter, it is transparency protected
Film covers all metal sheet.
As a kind of preferred scheme, the metal sheet is stainless steel or copper material thin slice.
It is used as a kind of preferred scheme, the model SUS200-400 of the stainless steel.
As a kind of preferred scheme, the thickness of the metal sheet is 0.04-1.0mm.
As a kind of preferred scheme, the chemical solution includes following material composition：50% 50-60 parts of nitric acid, 32% salt
Sour 35-40 parts, 25-30 parts of stannous acid, 15-20 parts of ferric trichloride, 8-10 parts of caprolactam, 80-100 parts of water.
As a kind of preferred scheme, the metal sheet is fixed on the surface of printed matter by gum or positioning method.
As a kind of preferred scheme, the overlay film is aqueous overlay film or uses UV glazings.
The present invention has clear advantage and beneficial effect compared with prior art, specifically, by above-mentioned technical proposal
Understand：
Present invention process main feature is combined with the three-layered node of printed matter base material, etch process metal sheet and later stage overlay film
Structure, reaches and is different from gold stamping and hits convex extraordinary effect, is different from gold stamping and hits convex equipment and making technology and efficiency；Erosion
Electric conductivity, magnetic, pliability etc. can be made full use of by carving metal sheet, and one is more entered on the basis of paper substrate three-decker
Step is designed to the multi-effects such as wire netting, circuit line, high-strength bending-resistant, extraordinary embossment, the present invention realize from principle, material and
Processing procedure many-side is different from existing way, realizes the progress of technique, is that enterprise brings huge economic benefit.
More clearly to illustrate the architectural feature and effect of the present invention, come below in conjunction with the accompanying drawings with specific embodiment to this hair
It is bright to be described in detail.
Brief description of the drawings
Fig. 1 is the sectional view of the preferred embodiments of the invention.
Accompanying drawing identifier declaration：
10th, metal sheet 20, printed matter
30th, gum 40, transparent protective film.
Embodiment
Present invention is disclosed a kind of printed matter manufacture craft with metal sheet, include following steps：
（1）Metal sheet 10 is taken, and metal sheet 10 is etched using chemical solution, to obtain required pattern；It is described
Metal sheet 10 is stainless steel or copper material thin slice, when it is stainless steel, the model SUS200-400 of the stainless steel.And
And, the thickness of the metal sheet 10 is 0.04-1.0mm.And, the chemical solution includes following material composition：50% nitre
Sour 50-60 parts, 35-40 parts of 32% hydrochloric acid, 25-30 parts of stannous acid, 15-20 parts of ferric trichloride, 8-10 parts of caprolactam, water
80-100 parts.
（2）The metal sheet 10 for completing etching is fixed on the surface of printed matter 20；In the present embodiment, the metal
Sheet material 10 is fixed on by gum 30 or positioning method on the surface of printed matter 20, can be in printed matter when using positioning method
20 surface opens up caulking groove, and metal sheet 10 is embedded in caulking groove and positioned.
（3）Aluminum coated steel is carried out to the surface of printed matter 20 so that a transparent protective film is formed on the surface of printed matter 20
40, transparent protective film 40 covers all metal sheet 10.In the present embodiment, the overlay film is aqueous overlay film or used on UV
Light.
The present invention is described in further detail with multiple embodiments below：
Embodiment 1
A kind of printed matter manufacture craft with metal sheet, includes following steps：
（1）Metal sheet 10 is taken, and metal sheet 10 is etched using chemical solution, to obtain required pattern；It is described
Metal sheet 10 is stainless steel, its model SUS400.Also, the thickness of the metal sheet 10 is 0.06mm.And, it is described
Chemical solution includes following material composition：50% 50 parts of nitric acid, 38 parts of 32% hydrochloric acid, stannous sour 28 parts, ferric trichloride 15
Part, 8 parts of caprolactam, 100 parts of water.
（2）The metal sheet 10 for completing etching is fixed on the surface of printed matter 20；In the present embodiment, the metal
Sheet material 10 is fixed on by gum 30 or positioning method on the surface of printed matter 20.
（3）Aluminum coated steel is carried out to the surface of printed matter 20 so that a transparent protective film is formed on the surface of printed matter 20
40, transparent protective film 40 covers all metal sheet 10.In the present embodiment, the overlay film is aqueous overlay film or used on UV
Light.
The test of surface gloss is carried out to product obtained above, its method of testing is to use vancometer, is obtained
Glossiness is 80%, realizes good metal surface gloss, and can keep for a long time.
Embodiment 2
A kind of printed matter manufacture craft with metal sheet, includes following steps：
（1）Metal sheet 10 is taken, and metal sheet 10 is etched using chemical solution, to obtain required pattern；It is described
Metal sheet 10 is copper material thin slice.Also, the thickness of the metal sheet 10 is 0.04mm.And, the chemical solution includes
There is following material composition：50% 60 parts of nitric acid, 36 parts of 32% hydrochloric acid, 25 parts of stannous acid, 17 parts of ferric trichloride, caprolactam
8.5 parts, 80 parts of water.
（2）The metal sheet 10 for completing etching is fixed on the surface of printed matter 20；In the present embodiment, the metal
Sheet material 10 is fixed on by gum 30 or positioning method on the surface of printed matter 20.
（3）Aluminum coated steel is carried out to the surface of printed matter 20 so that a transparent protective film is formed on the surface of printed matter 20
40, transparent protective film 40 covers all metal sheet 10.In the present embodiment, the overlay film is aqueous overlay film or used on UV
Light.
The test of surface gloss is carried out to product obtained above, its method of testing is to use vancometer, is obtained
Glossiness is 85%, realizes good metal surface gloss, and can keep for a long time.
Embodiment 3
A kind of printed matter manufacture craft with metal sheet, includes following steps：
（1）Metal sheet 10 is taken, and metal sheet 10 is etched using chemical solution, to obtain required pattern；It is described
Metal sheet 10 is stainless steel, its model SUS200.Also, the thickness of the metal sheet 10 is 0.04mm.And, it is described
Chemical solution includes following material composition：50% 52 parts of nitric acid, 35 parts of 32% hydrochloric acid, stannous sour 30 parts, ferric trichloride 18
Part, 10 parts of caprolactam, 90 parts of water.
（2）The metal sheet 10 for completing etching is fixed on the surface of printed matter 20；In the present embodiment, the metal
Sheet material 10 is fixed on by gum 30 or positioning method on the surface of printed matter 20.
（3）Aluminum coated steel is carried out to the surface of printed matter 20 so that a transparent protective film is formed on the surface of printed matter 20
40, transparent protective film 40 covers all metal sheet 10.In the present embodiment, the overlay film is aqueous overlay film or used on UV
Light.
The test of surface gloss is carried out to product obtained above, its method of testing is to use vancometer, is obtained
Glossiness is 82%, realizes good metal surface gloss, and can keep for a long time.
Embodiment 4
A kind of printed matter manufacture craft with metal sheet, includes following steps：
（1）Metal sheet 10 is taken, and metal sheet 10 is etched using chemical solution, to obtain required pattern；It is described
Metal sheet 10 is stainless steel, its model SUS300.Also, the thickness of the metal sheet 10 is 1.0mm.And, it is described
Chemical solution includes following material composition：50% 55 parts of nitric acid, 40 parts of 32% hydrochloric acid, stannous sour 26 parts, ferric trichloride 16
Part, 9.5 parts of caprolactam, 85 parts of water.
（2）The metal sheet 10 for completing etching is fixed on the surface of printed matter 20；In the present embodiment, the metal
Sheet material 10 is fixed on by gum 30 or positioning method on the surface of printed matter 20.
（3）Aluminum coated steel is carried out to the surface of printed matter 20 so that a transparent protective film is formed on the surface of printed matter 20
40, transparent protective film 40 covers all metal sheet 10.In the present embodiment, the overlay film is aqueous overlay film or used on UV
Light.
The test of surface gloss is carried out to product obtained above, its method of testing is to use vancometer, is obtained
Glossiness is 83%, realizes good metal surface gloss, and can keep for a long time.
Embodiment 5
A kind of printed matter manufacture craft with metal sheet, includes following steps：
（1）Metal sheet 10 is taken, and metal sheet 10 is etched using chemical solution, to obtain required pattern；It is described
Metal sheet 10 is copper material thin slice.Also, the thickness of the metal sheet 10 is 01.0mm.And, the chemical solution includes
There is following material composition：50% 58 parts of nitric acid, 37 parts of 32% hydrochloric acid, 27 parts of stannous acid, 20 parts of ferric trichloride, caprolactam 9
Part, 95 parts of water.
（2）The metal sheet 10 for completing etching is fixed on the surface of printed matter 20；In the present embodiment, the metal
Sheet material 10 is fixed on by gum 30 or positioning method on the surface of printed matter 20.
（3）Aluminum coated steel is carried out to the surface of printed matter 20 so that a transparent protective film is formed on the surface of printed matter 20
40, transparent protective film 40 covers all metal sheet 10.In the present embodiment, the overlay film is aqueous overlay film or used on UV
Light.
The test of surface gloss is carried out to product obtained above, its method of testing is to use vancometer, is obtained
Glossiness is 81%, realizes good metal surface gloss, and can keep for a long time.
Embodiment 6
A kind of printed matter manufacture craft with metal sheet, includes following steps：
（1）Metal sheet 10 is taken, and metal sheet 10 is etched using chemical solution, to obtain required pattern；It is described
Metal sheet 10 is stainless steel, when it is stainless steel, its model SUS300.Also, the thickness of the metal sheet 10 is
0.09mm.And, the chemical solution includes following material composition：50% 54 parts of nitric acid, 38 parts of 32% hydrochloric acid, stannous acid
29 parts, 19 parts of ferric trichloride, 8.4 parts of caprolactam, 88 parts of water.
（2）The metal sheet 10 for completing etching is fixed on the surface of printed matter 20；In the present embodiment, the metal
Sheet material 10 is fixed on by gum 30 or positioning method on the surface of printed matter 20.
（3）Aluminum coated steel is carried out to the surface of printed matter 20 so that a transparent protective film is formed on the surface of printed matter 20
40, transparent protective film 40 covers all metal sheet 10.In the present embodiment, the overlay film is aqueous overlay film or used on UV
Light.
The test of surface gloss is carried out to product obtained above, its method of testing is to use vancometer, is obtained
Glossiness is 84%, realizes good metal surface gloss, and can keep for a long time.
The design focal point of the present invention is：Present invention process main feature is combined with printed matter base material, etch process gold
Belong to the three-decker of sheet material and later stage overlay film, reach and be different from gold stamping and hit convex extraordinary effect, be different from gold stamping and hit convex
Equipment and making technology and efficiency；Etching metal sheet can make full use of electric conductivity, magnetic, pliability etc., in paper
A variety of effects such as wire netting, circuit line, high-strength bending-resistant, extraordinary embossment are further designed on the basis of Zhang Jicai three-deckers
Really, the present invention is realized is different from existing way from principle, material and processing procedure many-side, realizes the progress of technique, is that enterprise brings
Huge economic benefit.
The above described is only a preferred embodiment of the present invention, be not intended to limit the scope of the present invention,
Therefore any subtle modifications, equivalent variations and modifications that every technical spirit according to the present invention is made to above example, still
Belong in the range of technical solution of the present invention.
Claims (7)
1. a kind of printed matter manufacture craft with metal sheet, it is characterised in that：Include following steps：
（1）Metal sheet is taken, and metal sheet is etched using chemical solution, to obtain required pattern；
（2）The metal sheet for completing etching is fixed on the surface of printed matter；
（3）Aluminum coated steel is carried out to the surface of printed matter so that a transparent protective film is formed on the surface of printed matter, it is transparency protected
Film covers all metal sheet.
2. the printed matter manufacture craft according to claim 1 with metal sheet, it is characterised in that：The metal sheet is
Stainless steel or copper material thin slice.
3. the printed matter manufacture craft according to claim 2 with metal sheet, it is characterised in that：The type of the stainless steel
Number be SUS200-400.
4. the printed matter manufacture craft according to claim 1 with metal sheet, it is characterised in that：The metal sheet
Thickness is 0.04-1.0mm.
5. the printed matter manufacture craft according to claim 1 with metal sheet, it is characterised in that：The chemical solution bag
Following material composition is included：50% 50-60 parts of nitric acid, 35-40 parts of 32% hydrochloric acid, 25-30 parts of stannous acid, ferric trichloride 15-
20 parts, 8-10 parts of caprolactam, 80-100 parts of water.
6. the printed matter manufacture craft according to claim 1 with metal sheet, it is characterised in that：The metal sheet leads to
Cross gum or positioning method is fixed on the surface of printed matter.
7. the printed matter manufacture craft according to claim 1 with metal sheet, it is characterised in that：The overlay film is aqueous
Overlay film uses UV glazings.