CN107163538A - 一种手机外壳用塑料及其制备方法 - Google Patents
一种手机外壳用塑料及其制备方法 Download PDFInfo
- Publication number
- CN107163538A CN107163538A CN201710506133.XA CN201710506133A CN107163538A CN 107163538 A CN107163538 A CN 107163538A CN 201710506133 A CN201710506133 A CN 201710506133A CN 107163538 A CN107163538 A CN 107163538A
- Authority
- CN
- China
- Prior art keywords
- parts
- plastic
- mobile phone
- mixture
- following
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种手机外壳用塑料,属于手机技术领域,包括以下重量份的原料:聚碳酸脂70‑75份、丙烯腈‑丁二烯‑苯乙烯共聚物30‑34份、苯乙烯‑马来酸酐共聚物10‑14份、玻璃纤维8‑10份、钢纤维12‑15份、碳纤维7‑9份、铸石粉5‑9份、增塑剂2‑4份、抗氧剂1‑2份、润滑剂5‑7份、阻燃剂6‑8份;本发明还公开了一种手机外壳用塑料的制备方法;本发明制备简单,具有较佳地强度,耐磨性好,耐热耐酸碱。
Description
技术领域
本发明涉及手机技术领域,具体的说,涉及了一种手机外壳用塑料及其制备方法。
背景技术
手机外壳主要由金属或塑料制成。金属手机外壳具有质感良好、强度高的优点,但是它存在造价高、不易加工、有信号问题、不易着色以及工艺复杂和生产效率低等问题,故其在市场上就很难占据优势。而塑料手机外壳的价格低廉、易于加工、着色容易、绝缘、对信号的影响小,且其成型方法主要是注塑和压制等,生产效率高,可大规模生产,因而在市场上的占有率相对较高。
但目前的手机外壳强度低,容易折断,耐磨性较差,所以需要一种手机外壳用塑料来解决上述问题。
在公开号为CN104877327A的专利文件中,公开了一种塑料手机外壳的制造方法,涉及手机配件技术领域,包括以下步骤:按重量份数称出:聚碳酸酯65-80份,丙烯腈-丁二烯-苯乙烯共聚物25-35份,甲基丙烯酸-丁二烯-苯乙烯共聚物4-6份,苯乙烯-马来酸酐共聚物6-10份,阻燃剂6-10份,纳米β-碳化硅22-30份,镍粉6-10份,聚苯胺液体6-10份;先将纳米β-碳化硅、镍粉和聚苯胺液体混合均匀,烘干后制成料粒;预热混料机,加入料粒和剩余的原料混合均匀,将混合物料加入到挤出机中,经熔融挤出造粒;将造粒料干燥后加入注塑机,注塑机加热保压后,将熔融物料推入模具中,制成手机外壳。该发明解决了现有塑料手机外壳强度低和防辐射性能差的问题;但该发明的强度仍然能够进一步加强。
发明内容
本发明的目的在于克服上述现有技术的不足,提供了一种手机外壳用塑料及其制备方法,制备简单,具有较佳地强度,耐磨性好,耐热耐酸碱。
本发明提供的一种手机外壳用塑料,包括以下重量份的原料:
聚碳酸脂70-75份、丙烯腈-丁二烯-苯乙烯共聚物30-34份、苯乙烯-马来酸酐共聚物10-14份、玻璃纤维8-10份、钢纤维12-15份、碳纤维7-9份、铸石粉5-9份、增塑剂2-4份、抗氧剂1-2份、润滑剂5-7份、阻燃剂6-8份。
作为优选,玻璃纤维、钢纤维和碳纤维的长度均为0.8-1mm,直径均为0.3-0.6mm;铸石粉的目数为200-300目。
作为优选,增塑剂为邻苯二甲酸二正辛酯、邻苯二甲酸二环己酯、邻苯二甲酸二异丁酯、邻苯二甲酸二异壬酯、邻苯二甲酸二异癸酯的一种或二种以上的混合物。
作为优选,抗氧剂为亚磷酸酯和双2,6-二叔丁基酚的混合物,两者之间的重量比为3:1。
作为优选,润滑剂为硅油、白油、硬脂酸、硬脂酸丁酯、油酰胺、乙撑双硬脂酰胺的一种或二种以上的混合物。
作为优选,阻燃剂为三氧化二锑、氢氧化镁、氢氧化铝和磷酸三丁酯的混合物,四者之间的重量比为2:1:1:3。
本发明还提供了一种手机外壳用塑料的制备方法,包括以下步骤:
(1)、按上述重量份称取各种原料;
(2)、将上述原料加入到高速混合机内,混合4-6min,得到混合物;
(3)、将步骤(2)中的混合物加入到双螺杆挤出机挤出造粒,得到粒料;
(4)、将粒料干燥,然后用注塑机注射加工成型。
其中,
步骤(3)中的双螺杆挤出机的温度为:第一段180℃,第二段240℃,第三段250℃,第四段235℃。
步骤(4)干燥的方法为:在90℃的烘箱内干燥30min。
本发明的一种手机外壳用塑料及其制备方法,制备简单,具有较佳地强度,耐磨性好,耐热耐酸碱,具体的有益效果如下:
(1)、聚碳酸脂和丙烯腈-丁二烯-苯乙烯共聚物的混合能保证塑料的高强度;苯乙烯-马来酸酐共聚物作为增容剂,能改善聚碳酸脂和丙烯腈-丁二烯-苯乙烯共聚物的相容性;
(2)、铸石粉能加强塑料的耐磨、耐酸碱性能;钢纤维能大大提高塑料的物理强度;玻璃纤维能提高塑料的冲击强度和韧性,也提高了耐热能力;碳纤维具有良好的导电导热性能、电磁屏蔽性好、耐高温、耐腐蚀、强度高,能大大增强塑料的性能;
(3)、增塑剂、抗氧剂、润滑剂和阻燃剂这些添加剂能改善塑料的性能;
(4)、本发明各种原料对应比例的混合使得塑料具有强度高,耐磨性好,耐热耐酸碱等特点;并且制备方法简单,能稳定、有效地制备出手机外壳用塑料。
具体实施方式
以下结合具体实施例对发明作进一步详细的描述。
实施例1
本实施例的一种手机外壳用塑料,包括以下重量份的原料:
聚碳酸脂70份、丙烯腈-丁二烯-苯乙烯共聚物30份、苯乙烯-马来酸酐共聚物10份、玻璃纤维8份、钢纤维12份、碳纤维7份、铸石粉5份、增塑剂2份、抗氧剂1份、润滑剂5份、阻燃剂6份。
本实施例中,玻璃纤维、钢纤维和碳纤维的长度均为0.8mm,直径均为0.3mm;铸石粉的目数为200目。
本实施例中,增塑剂为邻苯二甲酸二正辛酯、邻苯二甲酸二环己酯、邻苯二甲酸二异丁酯、邻苯二甲酸二异壬酯、邻苯二甲酸二异癸酯的混合物。
本实施例中,抗氧剂为亚磷酸酯和双2,6-二叔丁基酚的混合物,两者之间的重量比为3:1。
本实施例中,润滑剂为硅油、白油、硬脂酸、硬脂酸丁酯、油酰胺、乙撑双硬脂酰胺的混合物。
本实施例中,阻燃剂为三氧化二锑、氢氧化镁、氢氧化铝和磷酸三丁酯的混合物,四者之间的重量比为2:1:1:3。
本实施例还提供了一种手机外壳用塑料的制备方法,包括以下步骤:
(1)、按上述重量份称取各种原料;
(2)、将上述原料加入到高速混合机内,混合4min,得到混合物;
(3)、将步骤(2)中的混合物加入到双螺杆挤出机挤出造粒,得到粒料;
(4)、将粒料干燥,然后用注塑机注射加工成型。
其中,
步骤(3)中的双螺杆挤出机的温度为:第一段180℃,第二段240℃,第三段250℃,第四段235℃。
步骤(4)干燥的方法为:在90℃的烘箱内干燥30min。
实施例2
本实施例的一种手机外壳用塑料,包括以下重量份的原料:
聚碳酸脂73份、丙烯腈-丁二烯-苯乙烯共聚物32份、苯乙烯-马来酸酐共聚物12份、玻璃纤维9份、钢纤维14份、碳纤维8份、铸石粉7份、增塑剂3份、抗氧剂1.5份、润滑剂6份、阻燃剂7份。
本实施例中,玻璃纤维、钢纤维和碳纤维的长度均为0.9mm,直径均为0.5mm;铸石粉的目数为300目。
本实施例中,增塑剂为邻苯二甲酸二正辛酯、邻苯二甲酸二环己酯、邻苯二甲酸二异丁酯、邻苯二甲酸二异壬酯、邻苯二甲酸二异癸酯的混合物。
本实施例中,抗氧剂为亚磷酸酯和双2,6-二叔丁基酚的混合物,两者之间的重量比为3:1。
本实施例中,润滑剂为硅油、白油、硬脂酸、硬脂酸丁酯、油酰胺、乙撑双硬脂酰胺的混合物。
本实施例中,阻燃剂为三氧化二锑、氢氧化镁、氢氧化铝和磷酸三丁酯的混合物,四者之间的重量比为2:1:1:3。
本实施例还提供了一种手机外壳用塑料的制备方法,包括以下步骤:
(1)、按上述重量份称取各种原料;
(2)、将上述原料加入到高速混合机内,混合5min,得到混合物;
(3)、将步骤(2)中的混合物加入到双螺杆挤出机挤出造粒,得到粒料;
(4)、将粒料干燥,然后用注塑机注射加工成型。
其中,
步骤(3)中的双螺杆挤出机的温度为:第一段180℃,第二段240℃,第三段250℃,第四段235℃。
步骤(4)干燥的方法为:在90℃的烘箱内干燥30min。
实施例3
本实施例的一种手机外壳用塑料,包括以下重量份的原料:
聚碳酸脂75份、丙烯腈-丁二烯-苯乙烯共聚物34份、苯乙烯-马来酸酐共聚物14份、玻璃纤维10份、钢纤维15份、碳纤维9份、铸石粉9份、增塑剂4份、抗氧剂2份、润滑剂7份、阻燃剂8份。
本实施例中,玻璃纤维、钢纤维和碳纤维的长度均为1mm,直径均为0.6mm;铸石粉的目数为300目。
本实施例中,增塑剂为邻苯二甲酸二正辛酯、邻苯二甲酸二环己酯、邻苯二甲酸二异丁酯、邻苯二甲酸二异壬酯、邻苯二甲酸二异癸酯的混合物。
本实施例中,抗氧剂为亚磷酸酯和双2,6-二叔丁基酚的混合物,两者之间的重量比为3:1。
本实施例中,润滑剂为硅油、白油、硬脂酸、硬脂酸丁酯、油酰胺、乙撑双硬脂酰胺的混合物。
本实施例中,阻燃剂为三氧化二锑、氢氧化镁、氢氧化铝和磷酸三丁酯的混合物,四者之间的重量比为2:1:1:3。
本实施例还提供了一种手机外壳用塑料的制备方法,包括以下步骤:
(1)、按上述重量份称取各种原料;
(2)、将上述原料加入到高速混合机内,混合6min,得到混合物;
(3)、将步骤(2)中的混合物加入到双螺杆挤出机挤出造粒,得到粒料;
(4)、将粒料干燥,然后用注塑机注射加工成型。
其中,
步骤(3)中的双螺杆挤出机的温度为:第一段180℃,第二段240℃,第三段250℃,第四段235℃。
步骤(4)干燥的方法为:在90℃的烘箱内干燥30min。
实施例1-3的检测结果如下:
实施例1 | 实施例2 | 实施例3 | |
断裂强度,MPa | 201 | 204 | 208 |
断裂伸长率,% | 2.5 | 2.5 | 2.6 |
抗冲击强度,J/mm2 | 22.0 | 22.3 | 22.7 |
弯曲强度,MPa | 138.7 | 138.8 | 139.3 |
以公开号为CN104877327A的专利文件中实施例1作为对比例,对比例的拉伸强度73.2MPa,弯曲强度131.6 MPa。
所以实施例1-3具有较佳地物理强度。
以上所述仅是本发明的优选实施方式,本发明的保护范围并不仅局限于上述实施例,凡属于本发明思路下的技术方案均属于本发明的保护范围。应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明原理前提下的若干改进和润饰,这些改进和润饰也应视为本发明的保护范围。
Claims (9)
1.一种手机外壳用塑料,其特征在于:包括以下重量份的原料:
聚碳酸脂70-75份、丙烯腈-丁二烯-苯乙烯共聚物30-34份、苯乙烯-马来酸酐共聚物10-14份、玻璃纤维8-10份、钢纤维12-15份、碳纤维7-9份、铸石粉5-9份、增塑剂2-4份、抗氧剂1-2份、润滑剂5-7份、阻燃剂6-8份。
2.根据权利要求1所述的手机外壳用塑料,其特征在于:玻璃纤维、钢纤维和碳纤维的长度均为0.8-1mm,直径均为0.3-0.6mm;铸石粉的目数为200-300目。
3.根据权利要求1所述的手机外壳用塑料,其特征在于:增塑剂为邻苯二甲酸二正辛酯、邻苯二甲酸二环己酯、邻苯二甲酸二异丁酯、邻苯二甲酸二异壬酯、邻苯二甲酸二异癸酯的一种或二种以上的混合物。
4.根据权利要求1所述的手机外壳用塑料,其特征在于:抗氧剂为亚磷酸酯和双2,6-二叔丁基酚的混合物,两者之间的重量比为3:1。
5.根据权利要求1所述的手机外壳用塑料,其特征在于:润滑剂为硅油、白油、硬脂酸、硬脂酸丁酯、油酰胺、乙撑双硬脂酰胺的一种或二种以上的混合物。
6.根据权利要求1所述的手机外壳用塑料,其特征在于:阻燃剂为三氧化二锑、氢氧化镁、氢氧化铝和磷酸三丁酯的混合物,四者之间的重量比为2:1:1:3。
7.根据权利要求1-6任意一项所述的一种手机外壳用塑料的制备方法,其特征在于:包括以下步骤:
(1)、按上述重量份称取各种原料;
(2)、将上述原料加入到高速混合机内,混合4-6min,得到混合物;
(3)、将步骤(2)中的混合物加入到双螺杆挤出机挤出造粒,得到粒料;
(4)、将粒料干燥,然后用注塑机注射加工成型。
8.根据权利要求7所述的手机外壳用塑料的制备方法,其特征在于:步骤(3)中的双螺杆挤出机的温度为:第一段180℃,第二段240℃,第三段250℃,第四段235℃。
9.根据权利要求7所述的手机外壳用塑料的制备方法,其特征在于:步骤(4)干燥的方法为:在90℃的烘箱内干燥30min。