CN107157043A - A kind of secondary metal jewel and preparation method thereof - Google Patents
A kind of secondary metal jewel and preparation method thereof Download PDFInfo
- Publication number
- CN107157043A CN107157043A CN201710339914.4A CN201710339914A CN107157043A CN 107157043 A CN107157043 A CN 107157043A CN 201710339914 A CN201710339914 A CN 201710339914A CN 107157043 A CN107157043 A CN 107157043A
- Authority
- CN
- China
- Prior art keywords
- jewel
- metal
- particle
- preparation
- natural
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of secondary metal jewel and preparation method thereof, secondary metal jewel of the invention, including following weight parts raw material：25 75 parts of 50 parts of jewel particle, metal and its alloy；Its preparation method includes：（1）13 kinds of jewel particles are selected to pass through natural air drying or low temperature drying after cleaning, sorting, magnitude classification；（2）One layer of 0.1 thick high temperature resistance protective layer of 0.3mm, natural air drying or low temperature drying are brushed on well-graded jewel particle；（3）The jewel particle handled well is placed in into place mat according to design requirement has in the mould of casting model powder；（4）By raw metal high-temperature fusion, point molten metal is gradually poured into mould, is stripped after after metal cooling, produces metal jewel shaping blank；（5）By metal jewel shaping blank it is cleaved, design, sizing, polishing, polishing, produce；Rationally, preparation method is simple, enriches ornaments, handicraft species, wide market for inventive formulation.
Description
Technical field
The invention belongs to natural gemstone technical field of regeneration, and in particular to a kind of secondary metal jewel and preparation method thereof.
Background technology
The copper existed in nature with pure nature is also known as native copper, is created on Black Warrior volcanic rock grotto and crack
In, and the metal symbiosis such as gold, silver, and its it is rare, therefore be of great rarity, reserve value is high.And also have a kind of day in nature
Metal jewel of the right metal together with jewel growth, the structure of this jewel is very special, is pressed from both sides to the eye in jade
There is native metal, when being like volcano eruption, flowed into the point molten metal in a flash that jewel splits in jewel gap and moment
Formed by cooling, this jewel was both gentle agile with jewel, the noble aesthetic feeling with native metal, be it is a kind of very
Unique collectibles.Due to this metal jewel in nature it is very rare, be worth very high, but be constrained to resource and have
Limit, it is impossible to meet the demand of numerous collectors, or even many people do not know the presence for having this jewel, can not be given birth to it yet
Produce consumer ornaments and handicraft.
Because metal jewel is also substantially unknown by the people at present, if preparing various handicrafts using this metal jewel
Or ornaments, the demand of numerous collectors can be met, the vacancy of the such raw material process product of in the market can be filled up again, is enriched
The species of ornaments.Therefore, a kind of preparation method of secondary metal jewel is researched and developed very necessary.
The content of the invention
The purpose of the present invention is extremely limited aiming at metal jewel mineral resources natural in current nature, it is impossible to full
Numerous collectors of foot and there is provided a kind of secondary metal jewel and preparation method thereof the problem of consumer demand.Gold of the invention
Category jewel can fill up the vacancy of in the market metal lapidarist product, enrich ornaments species, and market prospects are boundless.
A kind of secondary metal jewel of the present invention, includes the raw material of following weight parts：Jewel particle：50 parts, metal and its
Alloy：25-75 parts.
The jewel particle is the tailing from natural gemstone or synthetic gem, the natural gemstone or synthetic gem
For jade, ruby, sapphire, emerald, golden green opal, opal, aquamarine, spinelle, blue crystal, olivine, Tuo Pa
Stone, garnet, moonstone, Australia jade, lapis lazuli, malachite, turquoise, purple dragon are brilliant, Dongling it is beautiful in any one or a few,
Certainly the selection of natural gemstone or synthetic gem is not limited to mentioned kind in the present invention, jewel present in any nature,
It may be incorporated for preparing metal jewel of the present invention.
The metal and its alloy are that copper alloy, kirsite, titanium alloy, stainless steel alloy, gold and billon, platinum and platinum are closed
Any one in gold, silver and silver alloy, palladium and palldium alloy.Various metals content impurity indexs in the metal and its alloy
The requirement of International Environmental Protection regulation standard all should be reached.
A kind of preparation method of secondary metal jewel of the present invention, is made up of following step successively：
（1）Select 1-3 kind jewel particles standby by natural air drying after cleaning, sorting, magnitude classification or low temperature drying；
（2）The thick high temperature resistance protective layers of one layer of 0.1-0.3mm are brushed on well-graded jewel particle, natural air drying or low temperature dry
It is dry standby；The high temperature resistance protective layer is aqueous inorganic nano paint；
（3）Select step（2）In the jewel particle handled well, being placed in place mat according to design requirement has standby in the mould of casting model powder
With；
（4）By raw metal high-temperature fusion, point molten metal is gradually uniformly poured into jewel mould, taken off after after metal cooling
Mould, produces metal jewel shaping blank；
（5）By metal jewel shaping blank it is cleaved, design, sizing, polishing, polishing, produce.
According to the preparation method of the metal jewel of the present invention, the species of two kinds of metal jewels is mainly prepared, one kind is metal
Jewel artifacts, one kind is metal gem ornament, and its specific preparation method is otherwise varied, is specifically described below.
1. the preparation method of metal lapidarist product：Selected jewel particle is that selection 1-3 kind particle sizes are different
Jewel particle, after one layer of high temperature resistance protective layer of its external coating, place mat is placed at random to be had in the mould of casting model powder, is used
When point molten metal is cast, point molten metal need to flood jewel particle, be stripped after after metal cooling, you can obtain metal jewel base
Material, metal jewel shaping blank made from the method is applied to prepare various metal lapidarist product, can be according to its shape facility
Various artifacts, hand are processed into part etc., can be certainly also used to be processed into various metal gem ornaments.
One of classical dispensing of metal lapidarist product：Selected jewel particle is brilliant from Khotan jade, emerald, point
The tailing of stone；The raw metal is to use copper alloy, is made up of the raw material of following weight percent：Copper 50%, aluminium
15%, zinc 15%, iron 15%, tin 5%.
The two of the classical dispensing of metal lapidarist product：Selected jewel particle is to select emerald, sapphire, described
Raw metal is using 18K gold.
The three of the classical dispensing of metal lapidarist product：Selected jewel particle is to select lapis lazuli, malachite, described
Raw metal is to use brass alloys H68.
The four of the classical dispensing of metal lapidarist product：Selected jewel particle is to select olivine, turquoise, described
Raw metal is to use thousand pure silvers.
The five of metal lapidarist product classics dispensing：Selected jewel particle is ruby, and the raw metal is to adopt
Use thousand pure golds.
2. the preparation method of metal gem ornament：Selected jewel particle is a kind of uniform sheet of particle size of selection
Material, after one layer of high temperature resistance protective layer of its external coating, neat insertion place mat has in the mould of casting model powder, using metal
When fused solution is cast, the casting amount of point molten metal is the 1/7-1/2 of jewel particle height, is stripped after after metal cooling, you can
Metal jewel blank is obtained, such a metal jewel blank is due to being exactly to select raw material of uniform size in sorting, in die-filling tool
When be neat arrangement insertion casting model powder, therefore, the blank obtained after casting metals is that top is jewel, and root is metal
Metal jewel, metal jewel shaping blank prepared by the method is adapted to the various metal gem ornaments of processing, can after cutting
To be processed into various pendants, necklace, bangle, the ornaments such as foot chain.
One of classical dispensing of metal gem ornament：Selected jewel particle is from natural blue crystal leftover pieces, institute
It is to use kirsite to state raw metal, is made up of the raw material of following weight percent：Zinc 50%, copper 10%, aluminium 40%.
The two of the classical dispensing of metal gem ornament：Selected jewel particle is to select natural moonstone leftover pieces, institute
It is using thousand sufficient platinums to state raw metal.
The three of the classical dispensing of metal gem ornament：Selected jewel particle is, the metal brilliant from natural purple dragon
Raw material is to use brass H62.
The four of the classical dispensing of metal gem ornament：Selected jewel particle is, the metal beautiful from natural Australia
Raw material is to use brass H68.
The five of the classical dispensing of metal gem ornament：Selected jewel particle is to select natural sapphire, the metal
Raw material is to use thousand pure silvers.
The secondary metal jewel of the present invention, selected jewel particle is the tailing of natural gemstone or synthetic cut stone,
The offcut of natural gemstone is preferably used, using the tailing of natural gemstone, the work of jewel in itself on the one hand can be lifted
Skill is worth, and makes shaped article quality more preferably, quality is more excellent, and makings is more outstanding, on the other hand can accomplish the abundant profit of resource
With making originally rare natural gemstone resource not be wasted.
Raw metal selected by the secondary metal jewel of the present invention is copper alloy, kirsite, titanium alloy, stainless steel are closed
Gold, gold and billon, platinum and platinum alloy, silver and silver alloy, palladium and palldium alloy in any one, the selection of above-mentioned raw metal
Can be according to the design of product, selection is worth the jewel matched with it and matched, and above-mentioned raw metal is used equally for
Handicraft and jewellery trade, all should meet the International Environmental Protection regulation standard requirement of handicraft and jewellery trade.
The preparation method of the secondary metal jewel of the present invention is inventor after five years, by constantly experiment, total
Tying-in tests what is drawn afterwards, because the particularity of raw material for gem, and many jewels can be burst at once when suddenly encountering high temperature,
After being cast using point molten metal, seldom purpose product can only obtain（This may be also that native metal jewel mineral resources are dilute
Scarce main cause）.Inventor carefully studies by the several years, finds finally first by jewel particle using aqueous inorganic nanometer material
Expect after being protected, then cast with point molten metal, metal jewel can be obtained after cooling.Certainly, with science skill
Selected high temperature resistance protective layer can also use other raw materials in the progress of art, the present invention, be poured as long as can reach in metal
During casting, raw material for gem is not burst.
The secondary metal jewel of the present invention, the tailing and gold produced when being using natural gemstone or synthetic gem processing
Belong to raw material as major ingredient, it is obtained on the raw material for gem protected in advance by high temperature resistant by the way that point molten metal is cast to, it
The unique aesthetic feeling being had is that all artifacts and ornaments are lacked on the market at present, is also with very high reduction day
People are understood, understanding metal jewel has positive effect by the value of right metal jewel.The metal jewel of the present invention can basis
The different choice of raw material for gem and raw metal, makes a variety of various forms of combination products, greatly enrich handicraft and
The species of ornaments, has filled up the market vacancy, with high market value and economic benefit.
Brief description of the drawings
Fig. 1 is the arrangement schematic diagram of jewel particle in a mold when prepared by metal lapidarist product of the present invention；
Fig. 2 is the arrangement schematic diagram of jewel particle in a mold when prepared by metal gem ornament of the present invention.
In figure：1-casting model powder, 2-point molten metal, 3-jewel particle, 4-mould.
Embodiment
The preparation method of the metal jewel of the present invention is illustrated below by embodiment, following embodiments are only to use
To explain the present invention, the invention is not limited in any way.
Following embodiment 1-5 are exemplified by preparing metal lapidarist product, to explain in detail the present invention.
Embodiment 1
A kind of secondary metal jewel of the present embodiment, includes the raw material of following weight parts：Jewel particle：50 parts, metal and its conjunction
Gold：75 parts.
Described jewel particle is the natural Khotan jade of selection, natural emerald, three kinds of raw materials of natural spinelle, and it neutralizes field
Jade accounts for 50%, emerald 40%, spinelle 10%.
The raw metal is to use copper alloy, is made up of the raw material of following weight percent：Copper 50%, aluminium 15%,
Zinc 15%, iron 15%, tin 5%.
Referring to Fig. 1, a kind of preparation method of secondary metal jewel of the present embodiment is made up of following step successively：
（1）Natural Khotan jade, natural emerald, natural spinelle leftover pieces are cleaned, sorting, natural wind after magnitude classification
Dry or low temperature drying is standby；
（2）The thick high temperature resistance protective layers of one layer of 0.1-0.3mm, natural air drying or low temperature are brushed on well-graded jewel particle 3
Dry for standby；The high temperature resistance protective layer is aqueous inorganic nano paint；It is to be opened using the pure and fresh technology of Shandong cloud in the present embodiment
Send out the clear board aqueous inorganic nano paint of cloud of Co., Ltd's production；
（3）Select step（2）In the different jewel particle 3 of the particle size handled well, place mat is placed at random casting model powder 1
It is standby in mould 4；
（4）By raw metal high-temperature fusion, point molten metal 2 is gradually uniformly poured into broken up to flooding jewel in jewel mould
Material, is stripped after after metal cooling, produces metal jewel shaping blank；
（5）By metal jewel shaping blank it is cleaved, design, sizing, polishing, polishing, produce.
Embodiment 2
A kind of secondary metal jewel of the present embodiment, includes the raw material of following weight parts：Jewel particle：50 parts, metal and its conjunction
Gold：70 parts.
Described jewel particle is the natural emerald of selection, wherein two kinds of raw materials of natural sapphire, emerald 60%, Lan Bao
Stone 40%.
The raw metal is using 18K gold.
A kind of preparation method of secondary metal jewel of the present embodiment, is made up of following step successively：
（1）Natural emerald, natural sapphire leftover pieces are cleaned, sorting, natural air drying or low temperature dry after magnitude classification
It is dry standby；
（2）The thick high temperature resistance protective layers of one layer of 0.1-0.3mm are brushed on well-graded jewel particle, natural air drying or low temperature dry
It is dry standby；The high temperature resistance protective layer is aqueous inorganic nano paint；It is to use the pure and fresh technological development of Shandong cloud in the present embodiment
The clear board aqueous inorganic nano paint of cloud of Co., Ltd's production；
（3）Select step（2）In the different jewel particle of the particle size handled well, place mat is placed at random the mould of casting model powder
It is standby in tool；
（4）Point molten metal is gradually uniformly poured into raw metal high-temperature fusion up to flooding jewel particle in jewel mould,
It is stripped after after metal cooling, produces metal jewel shaping blank；
（5）By metal jewel shaping blank it is cleaved, design, sizing, polishing, polishing, produce.
Embodiment 3
A kind of secondary metal jewel of the present embodiment, includes the raw material of following weight parts：Jewel particle：50 parts, metal and its conjunction
Gold：60 parts.
Described jewel particle is the natural lapis lazuli of selection, wherein two kinds of raw materials of natural malachite, lapis lazuli 70%, peacock
Stone 30%.
The raw metal is to use brass H68（Copper 68%, zinc 32%）.
A kind of preparation method of secondary metal jewel of the present embodiment, is made up of following step successively：
（1）Natural lapis lazuli, natural malachite leftover pieces are cleaned, sorting, natural air drying or low temperature dry after magnitude classification
It is dry standby；
（2）The thick high temperature resistance protective layers of one layer of 0.1-0.3mm are brushed on well-graded jewel particle, natural air drying or low temperature dry
It is dry standby；The high temperature resistance protective layer is aqueous inorganic nano paint；It is to use the pure and fresh technological development of Shandong cloud in the present embodiment
The clear board aqueous inorganic nano paint of cloud of Co., Ltd's production；
（3）Select step（2）In the different jewel particle of the particle size handled well, place mat is placed at random the mould of casting model powder
It is standby in tool；
（4）Point molten metal is gradually uniformly poured into raw metal high-temperature fusion up to flooding jewel particle in jewel mould,
It is stripped after after metal cooling, produces metal jewel shaping blank；
（5）By metal jewel shaping blank it is cleaved, design, sizing, polishing, polishing, produce.
Embodiment 4
A kind of secondary metal jewel of the present embodiment, includes the raw material of following weight parts：Jewel particle：50 parts, metal and its conjunction
Gold：70 parts.
Described jewel particle is the natural olivine of selection, wherein two kinds of raw materials of natural turquoise, olivine 70%, green pine
Stone 30%.
The raw metal is to use thousand pure silvers.
A kind of preparation method of secondary metal jewel of the present embodiment, is made up of following step successively：
（1）Natural olivine, natural turquoise leftover pieces are cleaned, sorting, natural air drying or low temperature dry after magnitude classification
It is dry standby；
（2）The thick high temperature resistance protective layers of one layer of 0.1-0.3mm are brushed on well-graded jewel particle, natural air drying or low temperature dry
It is dry standby；The high temperature resistance protective layer is aqueous inorganic nano paint；It is to use the pure and fresh technological development of Shandong cloud in the present embodiment
The clear board aqueous inorganic nano paint of cloud of Co., Ltd's production；
（3）Select step（2）In the different jewel particle of the particle size handled well, place mat is placed at random the mould of casting model powder
It is standby in tool；
（4）Point molten metal is gradually uniformly poured into raw metal high-temperature fusion up to flooding jewel particle in jewel mould,
It is stripped after after metal cooling, produces metal jewel shaping blank；
（5）By metal jewel shaping blank it is cleaved, design, sizing, polishing, polishing, produce.
Embodiment 5
A kind of secondary metal jewel of the present embodiment, includes the raw material of following weight parts：Jewel particle：50 parts, metal and its conjunction
Gold：75 parts.
Described jewel particle is selection natural ruby.
The raw metal is to use thousand pure golds.
A kind of preparation method of secondary metal jewel of the present embodiment, is made up of following step successively：
（1）Natural ruby leftover pieces are cleaned, sorting, natural air drying or low temperature drying are standby after magnitude classification；
（2）The thick high temperature resistance protective layers of one layer of 0.1-0.3mm are brushed on well-graded jewel particle, natural air drying or low temperature dry
It is dry standby；The high temperature resistance protective layer is aqueous inorganic nano paint；It is to use the pure and fresh technological development of Shandong cloud in the present embodiment
The clear board aqueous inorganic nano paint of cloud of Co., Ltd's production；
（3）Select step（2）In the different jewel particle of the particle size handled well, place mat is placed at random the mould of casting model powder
It is standby in tool；
（4）Point molten metal is gradually uniformly poured into raw metal high-temperature fusion up to flooding jewel particle in jewel mould,
It is stripped after after metal cooling, produces metal jewel shaping blank；
（5）By metal jewel shaping blank it is cleaved, design, sizing, polishing, polishing, produce.
Following embodiment 6-10 are exemplified by preparing metal gem ornament, to explain in detail the present invention.
Embodiment 6
A kind of secondary metal jewel of the present embodiment, includes the raw material of following weight parts：Jewel particle：50 parts, metal and its conjunction
Gold：25 parts.
Described jewel particle is the natural blue crystal of selection.
The raw metal is to use kirsite, is made up of the raw material of following weight percent：Zinc 50%, copper 10%,
Aluminium 40%.
Referring to Fig. 2, a kind of preparation method of secondary metal jewel of the present embodiment is made up of following step successively：
（1）Select natural sapphire particle standby by natural air drying after cleaning, sorting, magnitude classification or low temperature drying；
（2）The thick high temperature resistance protective layers of one layer of 0.1-0.3mm, natural air drying or low temperature are brushed on well-graded jewel particle 3
Dry for standby；The high temperature resistance protective layer is aqueous inorganic nano paint；
（3）Select step（2）In the long 20-22mm that handles well, the wide 8-10mm blue crystal material of sheet, neat insertion place mat
Have in the mould 4 of casting model powder 1, it is standby；
（4）By raw metal high-temperature fusion, point molten metal 2 is gradually uniformly poured into jewel mould, point molten metal is poured
Casting amount is the 1/4 of jewel particle height, is stripped after after metal cooling, produces metal jewel shaping blank；
（5）By metal jewel shaping blank it is cleaved, design, sizing, polishing, polishing, produce.
Embodiment 7
A kind of secondary metal jewel of the present embodiment, includes the raw material of following weight parts：Jewel particle：50 parts, metal and its conjunction
Gold：30 parts.
Described jewel particle is the natural moonstone of selection.
The raw metal is to use thousand pure silvers.
A kind of preparation method of secondary metal jewel of the present embodiment, is made up of following step successively：
（1）Select natural moonstone particle standby by natural air drying after cleaning, sorting, magnitude classification or low temperature drying；
（2）The thick high temperature resistance protective layers of one layer of 0.1-0.3mm are brushed on well-graded jewel particle, natural air drying or low temperature dry
It is dry standby；The high temperature resistance protective layer is aqueous inorganic nano paint；
（3）Select step（2）In the long 50-55mm that handles well, wide 12-15mm sheets moonlight stone material, neat insertion place mat
Have standby in the mould of casting model powder；
（4）By raw metal high-temperature fusion, point molten metal is gradually uniformly poured into jewel mould, the casting of point molten metal
Measure as the 1/7 of jewel particle height, be stripped after after metal cooling, produce metal jewel shaping blank；
（5）By metal jewel shaping blank it is cleaved, design, sizing, polishing, polishing, produce.
Embodiment 8
A kind of secondary metal jewel of the present embodiment, includes the raw material of following weight parts：Jewel particle：50 parts, metal and its conjunction
Gold：25 parts.
Described jewel particle is that the natural purple dragon of selection is brilliant.
The raw metal is to use brass H62（Copper 62%, zinc 38%）.
A kind of preparation method of secondary metal jewel of the present embodiment, is made up of following step successively：
（1）The natural purple dragon of selection is brilliant standby by natural air drying after cleaning, sorting, magnitude classification or low temperature drying；
（2）The thick high temperature resistance protective layers of one layer of 0.1-0.3mm are brushed on well-graded jewel particle, natural air drying or low temperature dry
It is dry standby；The high temperature resistance protective layer is aqueous inorganic nano paint；
（3）Select step（2）In the long 15-17mm that handles well, the wide uniform flaky materials of 6-8mm, neat insertion place mat has
It is standby in the mould of casting model powder；
（4）By raw metal high-temperature fusion, point molten metal is gradually uniformly poured into jewel mould, the casting of point molten metal
Measure as the 1/2 of jewel particle height, be stripped after after metal cooling, produce metal jewel shaping blank；
（5）By metal jewel shaping blank it is cleaved, design, sizing, polishing, polishing, produce.
Embodiment 9
A kind of secondary metal jewel of the present embodiment, includes the raw material of following weight parts：Jewel particle：50 parts, metal and its conjunction
Gold：25 parts.
Described jewel particle is that the natural Australia of selection is beautiful.
The raw metal is using silver 925.
A kind of preparation method of secondary metal jewel of the present embodiment, is made up of following step successively：
（1）Select natural Australia beautiful standby by natural air drying after cleaning, sorting, magnitude classification or low temperature drying；
（2）The thick high temperature resistance protective layers of one layer of 0.1-0.3mm are brushed on well-graded jewel particle, natural air drying or low temperature dry
It is dry standby；The high temperature resistance protective layer is aqueous inorganic nano paint；
（3）Select step（2）In the long 45-50mm that handles well, wide 10-12mm flaky materials, neat insertion place mat has casting
It is standby in the mould of sand；
（4）By raw metal high-temperature fusion, point molten metal is gradually uniformly poured into jewel mould, the casting of point molten metal
Measure as the 1/7 of jewel particle height, be stripped after after metal cooling, produce metal jewel shaping blank；
（5）By metal jewel shaping blank it is cleaved, design, sizing, polishing, polishing, produce.
Embodiment 10
A kind of secondary metal jewel of the present embodiment, includes the raw material of following weight parts：Jewel particle：50 parts, metal and its conjunction
Gold：35 parts.
Described jewel particle is selection synthetic sapphire.
The raw metal is to use brass H68（Copper 68%, zinc 62%）.
A kind of preparation method of secondary metal jewel of the present embodiment, is made up of following step successively：
（1）Select synthetic sapphire standby by natural air drying after cleaning, sorting, magnitude classification or low temperature drying；
（2）The thick high temperature resistance protective layers of one layer of 0.1-0.3mm are brushed on well-graded jewel particle, natural air drying or low temperature dry
It is dry standby；The high temperature resistance protective layer is aqueous inorganic nano paint；
（3）Select step（2）In the long 25-30mm that handles well, wide 12-15mm flaky materials, neat insertion place mat has casting
It is standby in the mould of sand；
（4）By raw metal high-temperature fusion, point molten metal is gradually uniformly poured into jewel mould, the casting of point molten metal
Measure as the 1/2 of jewel particle height, be stripped after after metal cooling, produce metal jewel shaping blank；
（5）By metal jewel shaping blank it is cleaved, design, sizing, polishing, polishing, produce.
Above-described embodiment is used only for explaining the present invention, and the invention is not limited in any way, and anyone is according to this hair
The principle of bright claims prepares the metal lapidarist product similar with the present invention, is regarded as falling into the claims in the present invention
Protection domain.
Claims (10)
1. a kind of secondary metal jewel, it is characterised in that the raw material including following weight parts：Jewel particle：50 parts, metal and its
Alloy：25-75 parts.
2. a kind of secondary metal jewel according to claim 1, it is characterised in that：The jewel particle is from natural precious
The tailing of stone or synthetic gem, the natural gemstone or synthetic gem are jade, ruby, sapphire, emerald, Jin Lv
Opal, opal, aquamarine, spinelle, blue crystal, olivine, Topaz, garnet, moonstone, Australia jade, lapis lazuli, hole
Any one or a few during sparrow stone, turquoise, Dongling stone, purple dragon are brilliant.
3. a kind of secondary metal jewel according to claim 1, it is characterised in that：The metal and its alloy close for copper
Appointing in gold, kirsite, titanium alloy, stainless steel alloy, gold and billon, platinum and platinum alloy, silver and silver alloy, palladium and palldium alloy
Meaning is a kind of.
4. the preparation method of a kind of secondary metal jewel as described in claim 1 or 2 or 3, it is characterised in that successively by following
Step is constituted：
（1）Select 1-3 kind jewel particles standby by natural air drying after cleaning, sorting, magnitude classification or low temperature drying；
（2）The thick high temperature resistance protective layers of one layer of 0.1-0.3mm are brushed on well-graded jewel particle, natural air drying or low temperature dry
It is dry standby；The high temperature resistance protective layer is aqueous inorganic nano paint；
（3）Select step（2）In the jewel particle handled well, being placed in place mat according to design requirement has standby in the mould of casting model powder
With；
（4）By raw metal high-temperature fusion, point molten metal is gradually uniformly poured into jewel mould, taken off after after metal cooling
Mould, produces metal jewel shaping blank；
（5）By metal jewel shaping blank it is cleaved, design, sizing, polishing, polishing, produce.
5. a kind of preparation method of secondary metal jewel as claimed in claim 4, it is characterised in that：The jewel particle is choosing
The different jewel particle of 1-3 kind particle sizes is selected, after its external coating high temperature resistance protective layer, place mat is placed at random casting
Make in the mould of sand, when being cast using point molten metal, point molten metal need to flood jewel particle, metal made from the method is precious
Stone shaping blank is applied to manufacture metal lapidarist product.
6. a kind of preparation method of secondary metal jewel according to claim 5, it is characterised in that：The jewel particle is
From Khotan jade, emerald, ruby tailing；The raw metal is to use copper alloy, and copper alloy is by following weight
The raw material composition of percentage composition：Copper 50%, aluminium 15%, zinc 15%, iron 15%, tin 5%.
7. a kind of preparation method of secondary metal jewel according to claim 5, it is characterised in that：The jewel particle is
From emerald, sapphire, the raw metal is using 18K gold.
8. a kind of preparation method of secondary metal jewel as claimed in claim 4, it is characterised in that：The jewel particle is choosing
A kind of uniform flaky material of particle size is selected, after its external coating high temperature resistance protective layer, neat insertion place mat has casting
Make in the mould of sand, when being cast using point molten metal, the casting amount of point molten metal is the 1/7-1/2 of jewel particle height,
Metal jewel shaping blank made from the method is applied to manufacture metal gem ornament.
9. a kind of preparation method of secondary metal jewel according to claim 8, it is characterised in that：The jewel particle is
From natural blue crystal leftover pieces, the raw metal is to use kirsite, and kirsite is the original by following weight percent
Material composition：Zinc 50%, copper 10%, aluminium 40%.
10. a kind of preparation method of secondary metal jewel according to claim 8, it is characterised in that：The jewel particle
It is that the raw metal is to use platinum alloy from natural purple imperial crystal edge corner material.