CN107151528A - A kind of two component polyurethane steric hammer varnish - Google Patents

A kind of two component polyurethane steric hammer varnish Download PDF

Info

Publication number
CN107151528A
CN107151528A CN201710443805.7A CN201710443805A CN107151528A CN 107151528 A CN107151528 A CN 107151528A CN 201710443805 A CN201710443805 A CN 201710443805A CN 107151528 A CN107151528 A CN 107151528A
Authority
CN
China
Prior art keywords
component
hammer
steric
varnish
dimethylbenzene
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710443805.7A
Other languages
Chinese (zh)
Inventor
王辉
赵云鹏
王占庭
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Kangrui High-Tech New Material Technology Engineering Co Ltd
Original Assignee
Anhui Kangrui High-Tech New Material Technology Engineering Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Kangrui High-Tech New Material Technology Engineering Co Ltd filed Critical Anhui Kangrui High-Tech New Material Technology Engineering Co Ltd
Priority to CN201710443805.7A priority Critical patent/CN107151528A/en
Publication of CN107151528A publication Critical patent/CN107151528A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of two component polyurethane steric hammer varnish, it is mixed by component A and component B, described component A by following mass percent material composition：Alkyd resin 45 65%；Non-floating type aluminum paste 2 6%；Hammer agent 0.05 0.6%；Dimethylbenzene 15 25%；Toluene 5 10%；Butyl acetate 3 10%；Mallear stria mill base 5 15%；Thixotropic agent 0.5 0.8%；Described component B by following mass percent material composition：Trimethylolpropane 8 11%；Toluene di-isocyanate(TDI) 35 41%；Butyl acetate 25 35%；It is dehydrated dimethylbenzene 15 25%；It is dehydrated higher boiling flux 5 8%；Antioxidant 5 10%.Described component A and component B mixed proportions are 3:1.The present invention is using alkyd resin as main film forming matter, and extensively, cost is relatively low, stable processing technique for raw material sources, paint film air drying is rapid, and gloss is high, and adhesive force is strong, and anti-corrosive properties are good, mallear stria third dimension is strong, has protection and decoration double effects concurrently, has broad application prospects.

Description

A kind of two component polyurethane steric hammer varnish
Technical field
The invention belongs to coating processing technique field, and in particular to a kind of two component polyurethane steric hammer varnish.
Background technology
Hammer paint is a kind of stronger novelty finish of dicoration, recently as the improvement of people's living standards, decorates idea Be continually changing, the application of steric hammer varnish is more and more wider, is mainly used in the application on the surfaces such as all kinds of instrument, instrument, antitheft door. Hammer trace decorative pattern of the coating surface of hammer paint like left by hammering iron plate, with colour harmony, the features such as decorative pattern is attractive in appearance.Meanwhile, Hammer paint can cover the out-of-flatness defect of ground, the pre-treatment work polished with putty be eliminated, so applicability is very strong.But mesh Preceding existing hammer paint has that hammer tone effect is unstable, the high defect of production cost.
The content of the invention
The technical problems to be solved by the invention are to provide a kind of two component polyurethane steric hammer varnish.
The technical problems to be solved by the invention are realized using following technical scheme：
A kind of two component polyurethane steric hammer varnish, it is mixed by component A and component B, and described component A is by following quality The material composition of percentage：Alkyd resin 45-65%；Non-floating type aluminum paste 2-6%；Hammer agent 0.05-0.6%；Dimethylbenzene 15- 25%；Toluene 5-10%；Butyl acetate 3-10%；Mallear stria mill base 5-15%；Thixotropic agent 0.5-0.8%；
Described component B by following mass percent material composition：Trimethylolpropane 8-11%；Toluene di-isocyanate(TDI) 35- 41%；Butyl acetate 25-35%；It is dehydrated dimethylbenzene 15-25%；It is dehydrated higher boiling flux 5-8%；Antioxidant 5-10%.
Described component A and component B mixed proportions are 3:1.
The beneficial effects of the invention are as follows：A kind of two component polyurethane steric hammer varnish is provided, with alkyd resin and three hydroxyl first Base propane is main film forming matter, and extensively, cost is relatively low, stable processing technique for raw material sources, and paint film air drying is rapid, gloss Height, adhesive force is strong, and anti-corrosive properties are good, and mallear stria third dimension is strong, has protection and decoration double effects concurrently, has broad application prospects.
Embodiment
In order that the technical means, the inventive features, the objects and the advantages of the present invention are easy to understand, tie below Specific embodiment is closed, the present invention is expanded on further.
Embodiment 1：
A kind of two component polyurethane steric hammer varnish, by the material composition of following mass percent：Alkyd resin 45%；Non-floating type Aluminum paste 2%；Hammer agent 0.05%；Dimethylbenzene 25%；Toluene 10%；Butyl acetate 3%；Mallear stria mill base 14.4%；Thixotropic agent 0.55%；
Described component B by following mass percent material composition：Trimethylolpropane 8%；Toluene di-isocyanate(TDI) 35%；Vinegar Acid butyl ester 30%；It is dehydrated dimethylbenzene 15%；It is dehydrated higher boiling flux 5%；Antioxidant 7%.
Embodiment 2：
A kind of two component polyurethane steric hammer varnish, by the material composition of following mass percent：Alkyd resin 55%；Non-floating type Aluminum paste 3%；Hammer agent 0.3%；Dimethylbenzene 20%；Toluene 5%；Butyl acetate 10%；Mallear stria mill base 6%；Thixotropic agent 0.7%；
Described component B by following mass percent material composition：Trimethylolpropane 9%；Toluene di-isocyanate(TDI) 40%；Vinegar Acid butyl ester 25%；It is dehydrated dimethylbenzene 15%；It is dehydrated higher boiling flux 6%；Antioxidant 5%.
Embodiment 3：
A kind of two component polyurethane steric hammer varnish, by the material composition of following mass percent：Alkyd resin 60%；Non-floating type Aluminum paste 6%；Hammer agent 0.4%；Dimethylbenzene 15%；Toluene 5%；Butyl acetate 3%；Mallear stria mill base 10%；Thixotropic agent 0.6%；
Described component B by following mass percent material composition：Trimethylolpropane 11%；Toluene di-isocyanate(TDI) 38%； Butyl acetate 25%；It is dehydrated dimethylbenzene 15%；It is dehydrated higher boiling flux 6%；Antioxidant 5%.
Described component A and component B mixed proportions are 3:1.
The general principle and principal character and advantages of the present invention of the present invention has been shown and described above.The technology of the industry Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the simply explanation described in above-described embodiment and specification is originally The principle of invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its Equivalent thereof.

Claims (2)

1. a kind of two component polyurethane steric hammer varnish, it is characterised in that：It is mixed by component A and component B, described group Divide A by the material composition of following mass percent：Alkyd resin 45-65%；Non-floating type aluminum paste 2-6%；Hammer agent 0.05- 0.6%；Dimethylbenzene 15-25%；Toluene 5-10%；Butyl acetate 3-10%；Mallear stria mill base 5-15%；Thixotropic agent 0.5-0.8%；
Described component B by following mass percent material composition：Trimethylolpropane 8-11%；Toluene di-isocyanate(TDI) 35- 41%；Butyl acetate 25-35%；It is dehydrated dimethylbenzene 15-25%；It is dehydrated higher boiling flux 5-8%；Antioxidant 5-10%.
2. a kind of dual-component polyurethane steric hammer varnish according to claim 1, it is characterised in that：Described component A and Component B mixed proportions are 3:1.
CN201710443805.7A 2017-06-13 2017-06-13 A kind of two component polyurethane steric hammer varnish Pending CN107151528A (en)