CN107141689A - A kind of TPE plastics and preparation method thereof - Google Patents
A kind of TPE plastics and preparation method thereof Download PDFInfo
- Publication number
- CN107141689A CN107141689A CN201710368298.5A CN201710368298A CN107141689A CN 107141689 A CN107141689 A CN 107141689A CN 201710368298 A CN201710368298 A CN 201710368298A CN 107141689 A CN107141689 A CN 107141689A
- Authority
- CN
- China
- Prior art keywords
- parts
- tpe plastics
- tpe
- preparation
- epdm
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of TPE plastics and preparation method thereof, the TPE plastics include the composition of following parts by weight：30 parts of SEBS20,20 25 parts of EPDM, 10 15 parts of PP, 5 10 parts of glass fibre, 5 15 parts of elastomer, 10 parts of PA661,20 parts of TPV10,20 35 parts of white oil.Its preparation method is filled with white oil stirring for first SEBS, EPDM are put into mixer, is stirred after adding PP, PA66, TPV, glass fibre and elastomer addition mixer after abundant oil suction, then add mixture into double screw extruder extruding pelletization.Using the TPE plastics made by the present invention, cheap, high yield rate, function admirable, safety and environmental protection.
Description
Technical field
The present invention relates to a kind of TPE plastics and preparation method thereof, belong to plastics arts.
Background technology
As economic develops rapidly, enhancing and product requirement of the mankind to environmental consciousness must be improved constantly, and people are to height
It is required that plastics demand it is increasing.And TPE is a kind of high resiliency with rubber, high intensity, high resilience, having again to note
The biomaterials of processing are moulded, with asepsis environment-protecting, there is excellent coloring, weatherability and temperature tolerance, processing characteristics is superior, can be with
Recycle, and the matrix material coating and bonding such as PP, PC, PS, ABS can also be separately formed, and TPE both has thermoplastic
Processing characteristics, there is the physical property of vulcanization rubber again, be the advantageous combination of plastics and rubber advantage, therefore big
Wantonly capture the manor for being pertaining only to vulcanize rubber originally.But the price of the TPE is still higher, yield rate is relatively low, need to improve.
The content of the invention
It is an object of the present invention to provide a kind of cheap, high yield rate, function admirable, the TPE plastics of safety and environmental protection and its
Preparation method.
The technical solution adopted by the present invention is：
A kind of TPE plastics, it includes the composition of following parts by weight：The TPE plastics include the composition of following parts by weight：
SEBS20-30 parts, 20-25 parts of EPDM, 10-15 parts of PP, 5-10 parts of glass fibre, 5-15 parts of elastomer, PA661-10 parts,
TPV10-20 parts, 20-35 parts of white oil.
It is a kind of prepare above-mentioned TPE plastics method be：First SEBS, EPDM are put into mixer, white oil stirring is filled with, treats
PP, PA66, TPV, glass fibre and elastomer addition mixer are added after abundant oil suction to stir, then are added mixture into double
Screw extruder extruding pelletization.
The method have the advantages that：The present invention TPE plastics are cheap, high yield rate, function admirable, environmental protection, antistatic.
Embodiment
Embodiment：
A kind of TPE plastics, it includes the composition of following parts by weight：The TPE plastics include the composition of following parts by weight：
25 parts of SEBS, 20 parts of EPDM, 10 parts of PP, 8 parts of glass fibre, 10 parts of elastomer, 6 parts of PA66,15 parts of TPV, white oil 30
Part.
It is a kind of prepare above-mentioned TPE plastics method be：First SEBS, EPDM are put into mixer, white oil stirring is filled with, treats
PP, PA66, TPV, glass fibre and elastomer addition mixer are added after abundant oil suction to stir, then are added mixture into double
Screw extruder extruding pelletization.
Certainly the above embodiments merely illustrate the technical concept and features of the present invention, and its object is to allow be familiar with technique
People can understand present disclosure and implement according to this, it is not intended to limit the scope of the present invention.It is all according to this hair
Equivalent transformation or modification that the Spirit Essence of bright main technical schemes is done, should all be included within the scope of the present invention.
Claims (2)
1. a kind of TPE plastics, it is characterised in that it includes the composition of following parts by weight：The TPE plastics include following parts by weight
Composition：SEBS20-30 parts, 20-25 parts of EPDM, 10-15 parts of PP, 5-10 parts of glass fibre, 5-15 parts of elastomer, PA661-
10 parts, TPV10-20 parts, 20-35 parts of white oil.
2. TPE plastics according to claim 1, it is characterised in that：Its preparation method is that SEBS, EPDM first are put into stirring
In machine, white oil stirring is filled with, mixer stirring is added after adding PP, PA66, TPV, glass fibre and elastomer after abundant oil suction
Uniformly, then double screw extruder extruding pelletization is added mixture into.