CN109553868A - Encapsulated material in the floor a kind of high abrasion TPV and preparation method thereof - Google Patents
Encapsulated material in the floor a kind of high abrasion TPV and preparation method thereof Download PDFInfo
- Publication number
- CN109553868A CN109553868A CN201811477261.7A CN201811477261A CN109553868A CN 109553868 A CN109553868 A CN 109553868A CN 201811477261 A CN201811477261 A CN 201811477261A CN 109553868 A CN109553868 A CN 109553868A
- Authority
- CN
- China
- Prior art keywords
- parts
- floor
- tpv
- elastomer
- encapsulated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of encapsulated material in the floor TPV, and in parts by weight, preparing raw material includes following component: 20-50 parts of vulcanizable elastomer, 10-30 parts of rubber elastomer, 10-20 parts of fibrous material, 20.1-35.5 parts of other auxiliary agents;The rubber elastomer includes vinyl peroxide modified thermoplastic elastomer (TPE).The present invention has good water-fast, sun-proof, damage resistant and anti-pollution characteristic;Environmental protection of the invention and safety, can be realized light-weighted transformation.
Description
Technical field
The present invention relates to polymeric material fields, more specifically encapsulated material in the floor a kind of high abrasion TPV and preparation method thereof.
Background technique
Thermoplastic dynamic perduren (TPV) refers to that rubber and thermoplastic make rubber sulphur during melt blending
Change, the macromolecular elastomer material that sulfureted rubber forms in continuous thermoplastic phase as dispersed phase distribution.TPV not only has
There are the good machine-shaping feature of thermoplastic, elastic characteristic also excellent with vulcanized rubber.With traditional rubber material
Compare, TPV has and can form repeatedly, the characteristics of leftover pieces and waste can recycle, in addition, TPV also have it is good
Insulating properties, impact resistance, heat-resisting quantity, weatherability and good processing performance, therefore, TPV are that current development speed is very fast
One of high molecular material kind.
Currently, the encapsulated material in floor is mainly using the encapsulated material of PVC, however PVC floor is encapsulated that there are many lack in performance
It falls into, needs user to avoid solarization, avoid steam, also want periodic maintenance, therefore just gradually substituted by the floor TPV is encapsulated.However,
PVC floor is not encapsulated scratch-resistant, in order to enhance scratch-resistant performance just necessary sacrificial surface wear-resisting property, in addition, over time,
It has part formaldehyde to release from floor, be detrimental to health;Using over time, floor it is encapsulated between floor paint with
And the adhesive force between floor paint and floor can be deteriorated, and the problem of will appear cracking.
Therefore, this field needs to develop a kind of encapsulated material in the floor novel high wear-resistant TPV, be able to solve it is wear-resisting with it is scratch-resistant it
Between contradiction, it can be ensured that safety and environmental protection, while fire-proof and water-proof is sun-proof.
Summary of the invention
In order to solve the above-mentioned technical problem, the first aspect of the present invention provides a kind of encapsulated material in the floor TPV, according to weight
Part meter, preparing raw material includes following component:
20-50 parts of vulcanizable elastomer, 10-30 parts of rubber elastomer, 10-20 parts of fibrous material, other auxiliary agents 20.1-
35.5 parts;The rubber elastomer includes vinyl peroxide modified thermoplastic elastomer (TPE).
As a kind of perferred technical scheme, the rubber elastomer is polypropylene, polyethylene, polystyrene, ethylene-the third
Alkene copolymer, acrylonitrile-butadiene-styrene copolymer, styrene-acrylonitrile copolymer, polymethyl methacrylate, poly- pair
The combination of one or more of terephtha-late, vinyl peroxide modified polypropylene, polycarbonate.
As a kind of perferred technical scheme, the vulcanizable elastomer can be it is any suitably can vulcanised elastomeric
Body.
As a kind of perferred technical scheme, the vinyl peroxide modified polypropylene is dimethylvinylsiloxy ethyl-acetylene
Base hydroperoxides modified polypropene.
As a kind of perferred technical scheme, the weight ratio of the rubber elastomer and fibrous material is (1-3): (1-2).
As a kind of perferred technical scheme, the fibrous material includes carbon fibre material and Polyester Fibers.
As a kind of perferred technical scheme, the weight ratio of the carbon fibre material and Polyester Fibers is 1:2.
As a kind of perferred technical scheme, in parts by weight, other described auxiliary agents include 5-10 parts of plasticizer, compatible
10-15 parts of agent, 5-10 parts and vulcanizing agent 0.1-0.5 parts of filler.
To solve the above-mentioned problems, the second aspect of the present invention provides a kind of preparation method of encapsulated material in the floor TPV, packet
Containing following steps:
S1: the vulcanizable elastomer of formula ratio, rubber elastomer are stirred evenly, and plasticizer, vulcanizing agent and compatible is added
Agent stirs evenly, and fibrous material is added, stirs evenly;
S2: the obtained mixed material of S1 is added in the hopper of double screw extruder, the filler of formula ratio is added, is melted
Melt blending, extruding pelletization obtains the encapsulated material in the floor TPV.
As a kind of perferred technical scheme, each temperature setting of the Screw Extrusion is 170-175 DEG C of feeding section, leading portion
195-198 DEG C, 185-190 DEG C of middle section, 180-185 DEG C of back segment temperature.
As a kind of perferred technical scheme, the system of the dimethyl ethenyl acetenyl hydroperoxides modified polypropene
Preparation Method comprises the following steps:
Epoxy -4 vinyl cyclohexene and polypropylene are weighed in reaction kettle by weight 1:4, is stirred evenly, and ring is added
The initiator of oxygen -4 vinyl cyclohexene and the 2-3% of polypropylene total weight keeps bath temperature at 50-60 DEG C, stirs 30-
50min is warming up to 70-80 DEG C, continues to stir 3-5h, obtains dimethyl ethenyl acetenyl hydroperoxides modified polypropene.
The beneficial effects of the present invention are:
The present invention has good water-fast, sun-proof, damage resistant and anti-pollution characteristic;Environmental protection of the invention and safety, Neng Goushi
Existing light-weighted transformation.
Specific embodiment
For the purpose of following detailed description, it should be understood that the present invention can be used various substitutions variation and step it is suitable
Sequence, unless specifically stated on the contrary.In addition, being indicated in the case where in addition in any operational instances or otherwise pointing out
Such as all numbers of the amount of ingredient used in description and claims should be understood in all cases by term
" about " it modifies.Therefore, unless indicated to the contrary, the numerical parameter otherwise illustrated in the following description and appended dependent claims is root
The approximation changed according to the expected performance of the invention to be obtained.It is at least not intended to for the applicable of doctrine of equivalents being limited in
In the scope of the claims, each numerical parameter should at least be given up according to the number of the effective digital of report and by the way that application is common
Enter technology to explain.
Although illustrating that broad range of numberical range and parameter of the invention are approximations, listed in specific example
Numerical value is reported as accurately as possible.However, any numerical value inherently includes the standard deviation by finding in its each self-test measurement
The certain errors necessarily led to.
In addition, it should be understood that any numberical range as described herein, which is intended to include, is included into all subranges therein.Example
Such as, the range of " 1 to 10 " is intended to include all sub- models between (and including) described minimum value 1 and the maximum value 10
It encloses, that is, there is the minimum value equal to or more than 1 and the maximum value equal to or less than 10.
To solve the above-mentioned problems, the first aspect of the present invention provides a kind of encapsulated material in the floor TPV, comprising such as the following group
Point:
20-50 parts of vulcanizable elastomer, 10-30 parts of rubber elastomer, 10-20 parts of fibrous material, other auxiliary agents 20.1-
35.5 parts;The rubber elastomer includes vinyl peroxide modified thermoplastic elastomer (TPE).
In a preferred embodiment, the encapsulated material in the floor TPV includes following component:
30-40 parts of vulcanizable elastomer, 15-25 parts of rubber elastomer, 12-18 parts of fibrous material, other auxiliary agents 24.2-
32.4 parts;The rubber elastomer includes vinyl peroxide modified thermoplastic elastomer (TPE).
In preferred embodiment, the encapsulated material in the floor TPV includes following component:
35 parts of vulcanizable elastomer, 18 parts of rubber elastomer, 15 parts of fibrous material, 28.3 parts of other auxiliary agents;The rubber
Elastomer includes vinyl peroxide modified thermoplastic elastomer (TPE).
Any suitable vulcanizable elastomer can operate with the present invention.In a particular embodiment, described can
Vulcanized elastomer is ethylene/alpha-olefin/polyenoid terpolymer;In a preferred embodiment, the alpha-olefin be propylene and
The combination of one or both of 1- butylene, the polyenoid are one of dicyclopentadiene, Isosorbide-5-Nitrae-hexadiene or multiple combinations;?
In preferred embodiment, the vulcanizable elastomer is ethylene/propylene/dicyclopentadiene terpolymer;More into one
It walks in preferred embodiment, the vulcanizable elastomer is the ethylene/propylene/dicyclopentadiene of the copolymerization of 1:1:1 by weight
Terpolymer.
In a particular embodiment, the rubber elastomer is that polypropylene, polyethylene, polystyrene, ethylene-propylene are total
Polymers, styrene-acrylonitrile copolymer, polymethyl methacrylate, gathers to benzene two acrylonitrile-butadiene-styrene copolymer
The combination of one or more of formic acid fourth diester, vinyl peroxide modified polypropylene, polycarbonate;In preferred embodiment party
In formula, the rubber elastomer is polypropylene, polystyrene, ethylene-propylene copolymer, acrylonitrile-butadiene-styrene (ABS) copolymerization
The combination of one or more of object, polybutylene terephthalate, vinyl peroxide modified polypropylene, polycarbonate;?
In preferred embodiment, the rubber elastomer is polypropylene, polystyrene, ethylene-propylene copolymer, acrylic nitrile-butadiene
Diene-styrene copolymer, polybutylene terephthalate, vinyl peroxide modified polypropylene, one in polycarbonate
Kind or several combinations;In embodiment still more preferably, the rubber elastomer is vinyl peroxide modified benzene
Propylene.
In a particular embodiment, the vinyl peroxide modified propenyl benzene is dimethyl ethenyl acetenyl hydrogen
Peroxide modified polypropylene.
In a particular embodiment, the weight ratio of the rubber elastomer and fibrous material is (1-3): (1-2);Excellent
In the embodiment of choosing, the weight ratio of the rubber elastomer and fibrous material is (1-2): (1-1.5);More preferably implementing
In mode, the weight ratio of the rubber elastomer and fibrous material is 2:1.
In a particular embodiment, the fibrous material includes carbon fibre material and Polyester Fibers;Preferred
In embodiment, the weight ratio of the carbon fibre material and Polyester Fibers is 1:2.
In a particular embodiment, other described auxiliary agents include 5-10 parts of plasticizer, and 10-15 parts of compatilizer, filler
5-10 parts and vulcanizing agent 0.1-0.5 parts;In a preferred embodiment, other described auxiliary agents include 6-9 parts of plasticizer, compatilizer
12-14 parts, 6-9 parts and vulcanizing agent 0.2-0.4 parts of filler;In preferred embodiment, other described auxiliary agents include increasing
8 parts of agent of modeling, 13 parts of compatilizer, 7 parts and 0.3 part of vulcanizing agent of filler.
In a particular embodiment, the plasticizer is dioctyl phthalate, dibutyl phthalate, adjacent benzene
The combination of one or more of dicarboxylate, dioctyl sebacate;In a preferred embodiment, the plasticizer is neighbour
The combination of one or both of dioctyl phthalate, dibutyl phthalate;In preferred embodiment, the increasing
Modeling agent is dibutyl phthalate.
In a particular embodiment, the compatilizer is polypropylene grafted maleic anhydride, polypropylene grafted carboxylic acid, chlorination
The combination of one or more of polypropylene and Research of Grafting Malaic Anhydride Onto Polyethylene;In a preferred embodiment, the compatilizer is
The combination of one or both of polypropylene grafted maleic anhydride and polypropylene grafted carboxylic acid.Grafting rate is 0.8%-1.5%, is melted
Melting index is 1-10g/10min;In a preferred embodiment, grafting rate 1.2%, melt index 6g/10min.It connects
Branch means are conventional technical means in the art, are not required specifically.
In a particular embodiment, the filler is one of calcium carbonate, silica, talcum powder, kaolin
Or multiple combinations;In a preferred embodiment, the filler is one of silica, talcum powder and kaolin or more
Kind combination;In preferred embodiment, the filler is silica.
In a particular embodiment, the vulcanizing agent is DCP crosslinking agent.
In order to solve the above-mentioned technical problem, the second aspect of the present invention provides a kind of preparation side of encapsulated material in the floor TPV
Method comprises the following steps:
S1: the vulcanizable elastomer of formula ratio, rubber elastomer are stirred evenly, and plasticizer, vulcanizing agent and compatible is added
Agent stirs evenly, and fibrous material is added, stirs evenly;
S2: the obtained mixed material of S1 is added in the hopper of double screw extruder, the filler of formula ratio is added, is melted
Melt blending, extruding pelletization obtains the encapsulated material in the floor TPV.
In the present invention, it has been found that using dimethyl ethenyl acetenyl hydroperoxides modified polypropene conduct
The elastic rubbery body of TPV, can enhance the encapsulated damage resistant ability in floor, and possible reason is dimethyl ethenyl acetenyl
Hydroperoxides modified polypropene can reduce encapsulated surface tension, so that the coefficient of friction for reducing encapsulated surface changes to reach
The effect of the scratch resistant performance of kind material surface.
In order to achieve the effect that enhance scratch resistant performance, need to reduce the skin-friction coefficient of cover material, however in day
Often in life, after reducing skin-friction coefficient, user is when in use it is possible that easy the problems such as slipping, therefore, inventor
It joined carbon fiber in the cover material of floor to be modified the entire floor TPV cover material, not by the distinctive structure of carbon fiber
But the water-resistant capacity of whole system can be enhanced, can more enhance skin-friction coefficient, utilize dimethyl ethenyl acetenyl hydrogen peroxide
The reasonable compounding of compound modified polypropene and carbon fiber can enhance the encapsulated damage resistant ability in floor and enhance surface
Coefficient of friction.However inventor has found in research and development, not arbitrary addition is all up double effects, only in caoutchouc elasticity
The weight ratio of body and fibrous material is (1-3): when (1-2), can overcome technology resistance.
For floor, formaldehyde can be contained during fabrication and installation, common floor glue can only be from the one of floor
Face prevents, over time, formaldehyde being come out from the gap on side floor slowly, chronic hazard the body of people
Body health.Polyester fiber is the synthetic fibers as made of binary acid and dihydric alcohol polycondensation, abbreviation PET fiber.On the one hand, of the invention
In by addition polyester fiber, during copolymerization, between polyester fiber, carbon fiber and modified polypropene rubber elastomer
It entwines mutually, to form a fine and close network structure, zero volatilization of formaldehyde can be ensured in terms of front and side two.
In addition, fine and close structure also effectively prevents the absorption and volatilization of moisture in floor, thus the wet rate that rises of the drying shrinkage for reducing floor,
The stabilization for maintaining ground plate bulk, significantly extends the service life on floor.Apply also being found surprisingly that, when control caoutchouc elasticity
The weight ratio of body and fibrous material is that 2:1 can be perfect when the weight ratio of carbon fibre material and Polyester Fibers is 1:2
Solve the problems, such as that the encapsulated stickiness between floor paint in the floor as caused by the special construction of carbon fiber is not fine, possibility
The reason of be, the weight ratio of rubber elastomer and fibrous material be 2:1, the weight ratio of carbon fibre material and Polyester Fibers
When for 1:2, it is copolymerized each other, the group in molecule can be with main matter polyurethane resin and epoxy resin in floor paint
Between have an effect power, to enhance the encapsulated adhesive force between floor paint in the floor TPV, so as to avoid due to solarization and
The migration of caused floor paint small molecular, and the case where gradually floor paint is caused to crack.
Hydrophilic surface than hydrophobic surface more resistant to dirt, it is encapsulated for general floor for, hydrophobic effect is preferably
Plate cover material anti-pollution characteristic is worse, and the preferable floor cover material hydrophobic effect of anti-pollution characteristic is poor, and the present invention can solve
Certainly resistant and hydrophobic contradiction, the reason is that because the dimethyl ethenyl acetenyl hydroperoxides used in the present invention are modified poly-
Propylene has hydroxyl again while with alkylene, therefore can enhance the antistatic effect on the floor TPV cover material surface,
So that the present invention have both it is extremely hydrophobic and extremely resistant the effect of.
In a particular embodiment, each temperature setting of the Screw Extrusion is 170-175 DEG C of feeding section, leading portion 195-
198 DEG C, 185-190 DEG C of middle section, 180-185 DEG C of back segment temperature;In a preferred embodiment, each temperature of the Screw Extrusion is set
It is set to 170-174 DEG C of feeding section, 196-197 DEG C of leading portion, 186-189 DEG C of middle section, 181-184 DEG C of back segment temperature;Further
In preferred embodiment, each temperature setting of Screw Extrusion be 173 DEG C of feeding section, 196 DEG C of leading portion, 187 DEG C of middle section, back segment
183 DEG C of temperature.
In a particular embodiment, the preparation side of the dimethyl ethenyl acetenyl hydroperoxides modified polypropene
Method comprises the following steps:
Epoxy -4 vinyl cyclohexene and polypropylene are weighed in reaction kettle by weight 1:4, is stirred evenly, and ring is added
The initiator of oxygen -4 vinyl cyclohexene and the 2-3% of polypropylene total weight keeps bath temperature at 50-60 DEG C, stirs 30-
50min is warming up to 70-80 DEG C, continues to stir 3-5h, obtains dimethyl ethenyl acetenyl hydroperoxides modified polypropene.
In a preferred embodiment, the preparation side of the dimethyl ethenyl acetenyl hydroperoxides modified polypropene
Method comprises the following steps:
Epoxy -4 vinyl cyclohexene and polypropylene are weighed in reaction kettle by weight 1:4, is stirred evenly, and ring is added
The initiator of oxygen -4 vinyl cyclohexene and the 2-3% of polypropylene total weight keeps bath temperature at 52-58 DEG C, stirs 35-
45min is warming up to 72-78 DEG C, continues to stir 3.5-4.5h, obtains dimethyl ethenyl acetenyl hydroperoxides modified poly- third
Alkene.The initiator is KPS initiator.
In preferred embodiment, the preparation of the dimethyl ethenyl acetenyl hydroperoxides modified polypropene
Method comprises the following steps:
Epoxy -4 vinyl cyclohexene and polypropylene are weighed in reaction kettle by weight 1:4, is stirred evenly, and ring is added
2% initiator of oxygen -4 vinyl cyclohexene and polypropylene total weight keeps bath temperature at 55 DEG C, stirs 40min, rises
Temperature continues to stir 4h, obtains dimethyl ethenyl acetenyl hydroperoxides modified polypropene to 75 DEG C.The initiator is
KPS initiator.
Illustrate below with reference to specific embodiment.
Embodiment
Embodiment 1
The first aspect of embodiment 1 provides a kind of encapsulated material in the floor TPV, and in parts by weight, preparing raw material includes such as
Lower component:
35 parts of vulcanizable elastomer, 18 parts of rubber elastomer, 15 parts of fibrous material, 28.3 parts of other auxiliary agents;The rubber
Elastomer includes vinyl peroxide modified thermoplastic elastomer (TPE);The vulcanizable elastomer is the copolymerization of 1:1:1 by weight
Ethylene/propylene/dicyclopentadiene terpolymer;The rubber elastomer is vinyl peroxide modified propenyl benzene;Institute
The weight ratio for stating rubber elastomer and fibrous material is 2:1;The fibrous material includes carbon fibre material and Polyester Fibers;
The weight ratio of the carbon fibre material and Polyester Fibers is 1:2;Other described auxiliary agents include 8 parts of plasticizer, compatilizer 13
Part, 7 parts and 0.3 part of vulcanizing agent of filler;The plasticizer is dibutyl phthalate;The compatilizer is polypropylene grafted
Maleic anhydride, grafting rate 1.2%, melt index 6g/10min;The filler is silica.
The second aspect of embodiment 1 provides a kind of preparation method of encapsulated material in the floor TPV, comprises the following steps:
S1: the vulcanizable elastomer of formula ratio, rubber elastomer are stirred evenly, and plasticizer, vulcanizing agent and compatible is added
Agent stirs evenly, and fibrous material is added, stirs evenly;
S2: the obtained mixed material of S1 is added in the hopper of double screw extruder, the filler of formula ratio is added, is melted
Melt blending, extruding pelletization obtains the encapsulated material in the floor TPV.
Each temperature setting of Screw Extrusion be 173 DEG C of feeding section, 196 DEG C of leading portion, 187 DEG C of middle section, back segment temperature 183
℃。
The third aspect of embodiment 1 provides the preparation side of dimethyl ethenyl acetenyl hydroperoxides modified polypropene
Method comprises the following steps:
Epoxy -4 vinyl cyclohexene and polypropylene are weighed in reaction kettle by weight 1:4, is stirred evenly, and ring is added
2% initiator of oxygen -4 vinyl cyclohexene and polypropylene total weight keeps bath temperature at 55 DEG C, stirs 40min, rises
Temperature continues to stir 4h, obtains dimethyl ethenyl acetenyl hydroperoxides modified polypropene to 75 DEG C.The initiator is
KPS initiator.
Embodiment 2
The first aspect of embodiment 2 provides a kind of encapsulated material in the floor TPV, and in parts by weight, preparing raw material includes such as
Lower component:
20 parts of vulcanizable elastomer, 10 parts of rubber elastomer, 10 parts of fibrous material, 20.1 parts of other auxiliary agents;The rubber
Elastomer includes vinyl peroxide modified thermoplastic elastomer (TPE);The vulcanizable elastomer is the copolymerization of 1:1:1 by weight
Ethylene/propylene/dicyclopentadiene terpolymer;The rubber elastomer is vinyl peroxide modified propenyl benzene;Institute
The weight ratio for stating rubber elastomer and fibrous material is 2:1;The fibrous material includes carbon fibre material and Polyester Fibers;
The weight ratio of the carbon fibre material and Polyester Fibers is 1:2;Other described auxiliary agents include 5 parts of plasticizer, compatilizer 10
Part, 5 parts and 0.1 part of vulcanizing agent of filler;The plasticizer is dibutyl phthalate;The compatilizer is polypropylene grafted
Maleic anhydride, grafting rate 1.2%, melt index 6g/10min;The filler is silica.
The second aspect of embodiment 2 provides a kind of preparation method of encapsulated material in the floor TPV, and the preparation method is the same as that of Example 1.
The third aspect of embodiment 2 provides the preparation side of dimethyl ethenyl acetenyl hydroperoxides modified polypropene
Method, the preparation method is the same as that of Example 1.
Embodiment 3
The first aspect of embodiment 3 provides a kind of encapsulated material in the floor TPV, and in parts by weight, preparing raw material includes such as
Lower component:
50 parts of vulcanizable elastomer, 30 parts of rubber elastomer, 20 parts of fibrous material, 35.5 parts of other auxiliary agents;The rubber
Elastomer includes vinyl peroxide modified thermoplastic elastomer (TPE);The vulcanizable elastomer is the copolymerization of 1:1:1 by weight
Ethylene/propylene/dicyclopentadiene terpolymer;The rubber elastomer is vinyl peroxide modified propenyl benzene;Institute
The weight ratio for stating rubber elastomer and fibrous material is 2:1;The fibrous material includes carbon fibre material and Polyester Fibers;
The weight ratio of the carbon fibre material and Polyester Fibers is 1:2;Other described auxiliary agents include 10 parts of plasticizer, compatilizer 15
Part, 10 parts and 0.5 part of vulcanizing agent of filler;The plasticizer is dibutyl phthalate;The compatilizer connects for polypropylene
Branch maleic anhydride, grafting rate 1.2%, melt index 6g/10min;The filler is silica.
The second aspect of embodiment 3 provides a kind of preparation method of encapsulated material in the floor TPV, and the preparation method is the same as that of Example 1.
The third aspect of embodiment 3 provides the preparation side of dimethyl ethenyl acetenyl hydroperoxides modified polypropene
Method, the preparation method is the same as that of Example 1.
Embodiment 4
The first aspect of embodiment 4 provides a kind of encapsulated material in the floor TPV, and in parts by weight, preparing raw material includes such as
Lower component:
35 parts of vulcanizable elastomer, 18 parts of rubber elastomer, 28.3 parts of other auxiliary agents;The rubber elastomer includes ethylene
Base peroxide modified thermoplastic elastomer (TPE);The ethylene/propene that the vulcanizable elastomer is copolymerized for 1:1:1 by weight/bis-
Dicyclopentadiene terpolymers;The rubber elastomer is vinyl peroxide modified propenyl benzene;The rubber elastomer with
The weight ratio of fibrous material is 2:1;The fibrous material includes carbon fibre material and Polyester Fibers;The carbon fibre material
Weight ratio with Polyester Fibers is 1:2;Other described auxiliary agents include 8 parts of plasticizer, 13 parts of compatilizer, 7 parts of filler and
0.3 part of vulcanizing agent;The plasticizer is dibutyl phthalate;The compatilizer is polypropylene grafted maleic anhydride, grafting
Rate is 1.2%, melt index 6g/10min;The filler is silica.
The second aspect of embodiment 4 provides a kind of preparation method of encapsulated material in the floor TPV, comprises the following steps:
S1: the vulcanizable elastomer of formula ratio, rubber elastomer are stirred evenly, and plasticizer, vulcanizing agent and compatible is added
Agent stirs evenly, and stirs evenly;
S2: the obtained mixed material of S1 is added in the hopper of double screw extruder, the filler of formula ratio is added, is melted
Melt blending, extruding pelletization obtains the encapsulated material in the floor TPV.
Each temperature setting of Screw Extrusion be 173 DEG C of feeding section, 196 DEG C of leading portion, 187 DEG C of middle section, back segment temperature 183
℃。
The third aspect of embodiment 4 provides the preparation side of dimethyl ethenyl acetenyl hydroperoxides modified polypropene
Method, the preparation method is the same as that of Example 1.
Embodiment 5
The first aspect of embodiment 5 provides a kind of encapsulated material in the floor TPV, and in parts by weight, preparing raw material includes such as
Lower component:
35 parts of vulcanizable elastomer, 18 parts of rubber elastomer, 15 parts of fibrous material, 28.3 parts of other auxiliary agents;The rubber
Elastomer includes vinyl peroxide modified thermoplastic elastomer (TPE);The vulcanizable elastomer is the copolymerization of 1:1:1 by weight
Ethylene/propylene/dicyclopentadiene terpolymer;The rubber elastomer is propenyl benzene;The rubber elastomer and fiber
The weight ratio of material is 2:1;The fibrous material includes carbon fibre material and Polyester Fibers;The carbon fibre material and poly-
The weight ratio of ester fiber material is 1:2;Other described auxiliary agents include 8 parts of plasticizer, and 13 parts of compatilizer, 7 parts of filler and vulcanization
0.3 part of agent;The plasticizer is dibutyl phthalate;The compatilizer is polypropylene grafted maleic anhydride, and grafting rate is
1.2%, melt index 6g/10min;The filler is silica.
The second aspect of embodiment 5 provides a kind of preparation method of encapsulated material in the floor TPV, comprises the following steps, preparation
Step is the same as embodiment 1.
Embodiment 6
The first aspect of embodiment 6 provides a kind of encapsulated material in the floor TPV, and in parts by weight, preparing raw material includes such as
Lower component:
35 parts of vulcanizable elastomer, 18 parts of rubber elastomer, 15 parts of fibrous material, 28.3 parts of other auxiliary agents;The rubber
Elastomer includes vinyl peroxide modified thermoplastic elastomer (TPE);The vulcanizable elastomer is the copolymerization of 1:1:1 by weight
Ethylene/propylene/dicyclopentadiene terpolymer;The rubber elastomer is vinyl peroxide modified propenyl benzene;Institute
The weight ratio for stating rubber elastomer and fibrous material is 1:4;The fibrous material includes carbon fibre material and Polyester Fibers;
The weight ratio of the carbon fibre material and Polyester Fibers is 1:2;Other described auxiliary agents include 8 parts of plasticizer, compatilizer 13
Part, 7 parts and 0.3 part of vulcanizing agent of filler;The plasticizer is dibutyl phthalate;The compatilizer is polypropylene grafted
Maleic anhydride, grafting rate 1.2%, melt index 6g/10min;The filler is silica.
The second aspect of embodiment 6 provides a kind of preparation method of encapsulated material in the floor TPV, comprises the following steps, preparation
Step is the same as embodiment 1.
The third aspect of embodiment 6 provides the preparation side of dimethyl ethenyl acetenyl hydroperoxides modified polypropene
Method, the preparation method is the same as that of Example 1.
Embodiment 7
The first aspect of embodiment 7 provides a kind of encapsulated material in the floor TPV, and in parts by weight, preparing raw material includes such as
Lower component:
35 parts of vulcanizable elastomer, 18 parts of rubber elastomer, 15 parts of fibrous material, 28.3 parts of other auxiliary agents;The rubber
Elastomer includes vinyl peroxide modified thermoplastic elastomer (TPE);The vulcanizable elastomer is the copolymerization of 1:1:1 by weight
Ethylene/propylene/dicyclopentadiene terpolymer;The rubber elastomer is vinyl peroxide modified propenyl benzene;Institute
The weight ratio for stating rubber elastomer and fibrous material is 2:1;The fibrous material includes carbon fibre material and Polyester Fibers;
The weight ratio of the carbon fibre material and Polyester Fibers is 1:2;Other described auxiliary agents include 20 parts of plasticizer, compatilizer 5
Part, 3 parts and 2.3 parts of vulcanizing agent of filler;The plasticizer is dibutyl phthalate;The compatilizer is polypropylene grafted
Maleic anhydride, grafting rate 1.2%, melt index 6g/10min;The filler is silica.
The second aspect of embodiment 7 provides a kind of preparation method of encapsulated material in the floor TPV, comprises the following steps, preparation
Step is the same as embodiment 1.
The third aspect of embodiment 7 provides the preparation side of dimethyl ethenyl acetenyl hydroperoxides modified polypropene
Method, the preparation method is the same as that of Example 1.
Embodiment 8
The first aspect of embodiment 8 provides a kind of encapsulated material in the floor TPV, and in parts by weight, preparing raw material includes such as
Lower component:
35 parts of vulcanizable elastomer, 18 parts of rubber elastomer, 15 parts of fibrous material, 28.3 parts of other auxiliary agents;The rubber
Elastomer includes vinyl peroxide modified thermoplastic elastomer (TPE);The vulcanizable elastomer is the copolymerization of 1:1:1 by weight
Ethylene/propylene/dicyclopentadiene terpolymer;The rubber elastomer is vinyl peroxide modified propenyl benzene;Institute
The weight ratio for stating rubber elastomer and fibrous material is 2:1;The fibrous material is Polyester Fibers;Other described auxiliary agent packets
Include 8 parts of plasticizer, 13 parts of compatilizer, 7 parts and 0.3 part of vulcanizing agent of filler;The plasticizer is dibutyl phthalate;Institute
Stating compatilizer is polypropylene grafted maleic anhydride, grafting rate 1.2%, melt index 6g/10min;The filler is
Silica.
The second aspect of embodiment 8 provides a kind of preparation method of encapsulated material in the floor TPV, comprises the following steps, preparation
Step is the same as embodiment 1.
The third aspect of embodiment 8 provides the preparation side of dimethyl ethenyl acetenyl hydroperoxides modified polypropene
Method, the preparation method is the same as that of Example 1.
Embodiment 9
The first aspect of embodiment 9 provides a kind of encapsulated material in the floor TPV, and in parts by weight, preparing raw material includes such as
Lower component:
35 parts of vulcanizable elastomer, 18 parts of rubber elastomer, 15 parts of fibrous material, 28.3 parts of other auxiliary agents;The rubber
Elastomer includes vinyl peroxide modified thermoplastic elastomer (TPE);The vulcanizable elastomer is the copolymerization of 1:1:1 by weight
Ethylene/propylene/dicyclopentadiene terpolymer;The rubber elastomer is vinyl peroxide modified propenyl benzene;Institute
The weight ratio for stating rubber elastomer and fibrous material is 2:1;The fibrous material is Polyester Fibers;Other described auxiliary agent packets
Include 8 parts of plasticizer, 13 parts of compatilizer, 7 parts and 0.3 part of vulcanizing agent of filler;The plasticizer is dibutyl phthalate;Institute
Stating compatilizer is polypropylene grafted maleic anhydride, grafting rate 1.2%, melt index 6g/10min;The filler is
Silica.
The second aspect of embodiment 1 provides a kind of preparation method of encapsulated material in the floor TPV, comprises the following steps, preparation
Step is the same as embodiment 1.
The third aspect of embodiment 1 provides the preparation side of dimethyl ethenyl acetenyl hydroperoxides modified polypropene
Method, the preparation method is the same as that of Example 1.
Embodiment 10
The first aspect of embodiment 10 provides a kind of encapsulated material in the floor TPV, in parts by weight, prepares raw material with implementation
Example 1.
The second aspect of embodiment 10 provides a kind of preparation method of encapsulated material in the floor TPV, comprises the following steps:
S1: the vulcanizable elastomer of formula ratio, rubber elastomer are stirred evenly, and plasticizer, vulcanizing agent and compatible is added
Agent stirs evenly, and fibrous material is added, stirs evenly;
S2: the obtained mixed material of S1 is added in the hopper of double screw extruder, the filler of formula ratio is added, is melted
Melt blending, extruding pelletization obtains the encapsulated material in the floor TPV.
Each temperature setting of Screw Extrusion be 153 DEG C of feeding section, 206 DEG C of leading portion, 177 DEG C of middle section, back segment temperature 193
℃。
The third aspect of embodiment 10 provides the preparation of dimethyl ethenyl acetenyl hydroperoxides modified polypropene
Method, the preparation method is the same as that of Example 1.
Embodiment 11
The first aspect of embodiment 11 provides a kind of encapsulated material in the floor TPV, and in parts by weight, preparing raw material includes such as
Lower component:
35 parts of vulcanizable elastomer, 18 parts of rubber elastomer, 15 parts of fibrous material, 28.3 parts of other auxiliary agents;The rubber
Elastomer includes vinyl peroxide modified thermoplastic elastomer (TPE);The vulcanizable elastomer is the copolymerization of 1:1:1 by weight
Ethylene/propylene/dicyclopentadiene terpolymer;The rubber elastomer is vinyl peroxide modified propenyl benzene;Institute
The weight ratio for stating rubber elastomer and fibrous material is 2:1;The fibrous material includes carbon fibre material and Polyester Fibers;
The weight ratio of the carbon fibre material and Polyester Fibers is 1:1;Other described auxiliary agents include 8 parts of plasticizer, compatilizer 13
Part, 7 parts and 0.3 part of vulcanizing agent of filler;The plasticizer is dibutyl phthalate;The compatilizer is polypropylene grafted
Maleic anhydride, grafting rate 1.2%, melt index 6g/10min;The filler is silica.
The second aspect of embodiment 11 provides a kind of preparation method of encapsulated material in the floor TPV, comprises the following steps, preparation
Step is the same as embodiment 1.
The third aspect of embodiment 11 provides the preparation of dimethyl ethenyl acetenyl hydroperoxides modified polypropene
Method, the preparation method is the same as that of Example 1.
Performance test evaluation
1) peel strength test
It is placed on the floor TPV of embodiment 1-11 is encapsulated in the environment of temperature is -20 DEG C, no any physical property variation.
In addition after placing 30 in the environment of -20 DEG C, peel strength test is carried out, test uses the testing standard of GB2792, test knot
Fruit is shown in Table 1.
Table 1
2) damage resistant is tested
The plank that 11 block sizes are all the same with, thickness and flatness is taken, with coating TPV described in embodiment 1-11 respectively
Plate glue, testing standard ISO12137-2:1997, test equipment are pointed stylus type damage resistant tester, and sample coatings are consolidated
It is scheduled on sliding stand, it adjusts taring and hammers into shape so that when scriber has just contacted test plate (panel) surface, the load of scriber is 0.Selected load model
It encloses, tester is started with 10mm/s speed, be automatically stopped as the mobile 100mm of sliding stand, check whether coating scratches, if not having
Have, then adjust other load ranges, until scratching, at least surveys three times.
Critical load=(100-d)/100 × (Ff-Fi), unit g;
D stops mobile point for scriber and the distance between scuffing point, unit mm occurs to rigid;
FfFor the initial load of selected scriber load range, unit g;
FiFor the final load of selected scriber load range, unit g.
Test result is shown in Table 2, and 2 result of table is testing mean three times.
Table 2
3) skin-friction force is tested
Friction testing is carried out using the standard of GB10006, test result is shown in Table 3.
Table 3
Embodiment | Frictional force/N |
Embodiment 1 | 0.70 |
Embodiment 2 | 0.68 |
Embodiment 3 | 0.69 |
Embodiment 4 | 0.35 |
Embodiment 5 | 0.76 |
Embodiment 6 | 0.45 |
Embodiment 7 | 0.51 |
Embodiment 8 | 0.42 |
Embodiment 9 | 0.53 |
Embodiment 10 | 0.54 |
Embodiment 11 | 0.49 |
For PVC floor glue, excessive frictional force and too small frictional force are unsuitable for, and most suitable is in 0.5-
Between 0.7, increasing friction force as far as possible is proper in this range.
4) anti-pollution characteristic is tested
Template made by embodiment 1-11 is tested using GB/T9780-2013.Grading system such as table 4 is wherein
X corresponding to level-oneIt is interiorValue is initial value of each stain application on coating, namely does not have any removal ability to the substance.
10 grades represent highest greasiness removal rate, are equivalent to the most spots of removal.
Table 4
It therefrom selects three kinds of vinegars, blue-black ink and spirit black pigment to test the sample of embodiment 1-11, survey
Test result is shown in Table 5.
Table 5
Embodiment | Vinegar | Blue-black ink | Spirit black pigment | Average score |
Embodiment 1 | 10 | 10 | 10 | 10 |
Embodiment 2 | 9 | 9 | 9 | 9 |
Embodiment 3 | 9 | 10 | 9 | 9.3 |
Embodiment 4 | 9 | 9 | 9 | 9 |
Embodiment 5 | 5 | 6 | 5 | 5.3 |
Embodiment 6 | 7 | 6 | 7 | 6.7 |
Embodiment 7 | 8 | 8 | 8 | 8 |
Embodiment 8 | 8 | 7 | 8 | 7.7 |
Embodiment 9 | 9 | 9 | 8 | 8.7 |
Embodiment 10 | 8 | 8 | 8 | 8 |
Embodiment 11 | 7 | 8 | 8 | 7.7 |
5) water resistance test
The plank that 11 block sizes are all the same with, thickness and flatness is taken, with coating TPV described in embodiment 1-11 respectively
Plate glue is placed in water, 25 ± 2 DEG C of water temperature after drying, and tests water resisting time, observation place plate sample surface water is no water stain infiltration
Into floor, test result is shown in Table 6.
Table 6
It may be noted that the foregoing is merely the preferable specific embodiments of the present invention, but protection scope of the present invention is not
Be confined to this, anyone skilled in the art in the technical scope disclosed by the present invention, the variation that can readily occur in or
Replacement, should be covered by the protection scope of the present invention.Therefore, protection scope of the present invention should be with the protection of claim
Subject to range.
Claims (10)
1. a kind of encapsulated material in the floor TPV, which is characterized in that in parts by weight, preparing raw material includes following component:
20-50 parts of vulcanizable elastomer, 10-30 parts of rubber elastomer, 10-20 parts of fibrous material, other auxiliary agents 20.1-35.5
Part;The rubber elastomer includes vinyl peroxide modified thermoplastic elastomer (TPE).
2. the encapsulated material in the floor TPV described in claim 1, which is characterized in that the rubber elastomer be polypropylene, polyethylene,
Polystyrene, ethylene-propylene copolymer, acrylonitrile-butadiene-styrene copolymer, styrene-acrylonitrile copolymer, poly- first
One of base methyl acrylate, polybutylene terephthalate, vinyl peroxide modified polypropylene, polycarbonate are several
Kind combination.
3. the encapsulated material in the floor TPV described in claim 1, which is characterized in that the vinyl peroxide modified polypropylene is
Dimethyl ethenyl acetenyl hydroperoxides modified polypropene.
4. the encapsulated material in the floor TPV described in claim 1, which is characterized in that the weight of the rubber elastomer and fibrous material
Than for (1-3): (1-2).
5. the encapsulated material in the floor TPV described in claim 1, which is characterized in that the fibrous material includes carbon fibre material and gathers
Ester fiber material.
6. the encapsulated material in the floor TPV described in claim 5, which is characterized in that the carbon fibre material and Polyester Fibers
Weight ratio is 1:2.
7. the encapsulated material in the floor TPV described in claim 1, which is characterized in that in parts by weight, other described auxiliary agents include increasing
Agent 5-10 parts of modeling, 10-15 parts of compatilizer, 5-10 parts and vulcanizing agent 0.1-0.5 parts of filler.
8. the preparation method of the described in any item encapsulated material in the floor TPV of claim 1-7, which is characterized in that comprise the following steps:
S1: the vulcanizable elastomer of formula ratio, rubber elastomer are stirred evenly, and plasticizer, vulcanizing agent and compatilizer is added, stirs
It mixes uniformly, fibrous material is added, stirs evenly;
S2: the obtained mixed material of S1 is added in the hopper of double screw extruder, the filler of formula ratio is added, melting is altogether
Mixed, extruding pelletization obtains the encapsulated material in the floor TPV.
9. the preparation method of the encapsulated material in the floor TPV according to any one of claims 8, which is characterized in that each temperature of Screw Extrusion is set
It is set to 170-175 DEG C of feeding section, 195-198 DEG C of leading portion, 185-190 DEG C of middle section, 180-185 DEG C of back segment temperature.
10. the encapsulated material in the floor TPV as claimed in claim 3, which is characterized in that the dimethyl ethenyl acetenyl hydroperoxidation
The preparation method of object modified polypropene, comprises the following steps:
Epoxy -4 vinyl cyclohexene and polypropylene are weighed in reaction kettle by weight 1:4, is stirred evenly, and epoxy -4- is added
The initiator of the 2-3% of vinylcyclohexene and polypropylene total weight keeps bath temperature at 50-60 DEG C, stirs 30-50min,
It is warming up to 70-80 DEG C, continues to stir 3-5h, obtains dimethyl ethenyl acetenyl hydroperoxides modified polypropene.