CN107130755A - A kind of environmentally friendly combined wall board of novel glass fiber - Google Patents
A kind of environmentally friendly combined wall board of novel glass fiber Download PDFInfo
- Publication number
- CN107130755A CN107130755A CN201710301224.XA CN201710301224A CN107130755A CN 107130755 A CN107130755 A CN 107130755A CN 201710301224 A CN201710301224 A CN 201710301224A CN 107130755 A CN107130755 A CN 107130755A
- Authority
- CN
- China
- Prior art keywords
- parts
- epoxy resin
- glass fibre
- weight
- wall board
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention belongs to household building materials field, and in particular to a kind of environmentally friendly combined wall board of novel glass fiber, including internal surface layer, middle level and outer coversheet, the internal surface layer are made up of the raw material of following parts by weight：15~20 parts of 48~56 parts of continuous glass fibre, 6~10 parts of brominated epoxy resin, 18~24 parts of makrolon and vinyl ester resin, the middle level is made up of the raw material of following parts by weight：60~66 parts of continuous glass fibre, 12~16 parts of epoxy resin, 18~24 parts of M-phthalic acid type unsaturated polyester (UP), the outer coversheet is made up of the raw material of following parts by weight：15~20 parts of 48~56 parts of continuous glass fibre, 6~10 parts of brominated epoxy resin, 18~24 parts of makrolon and vinyl ester resin, also disclose its preparation method.The present invention effectively reduces pernicious gas content in wallboard, while having prevented the performance defect that existing wooden wallboard is present from source, reduces unnecessary trouble.
Description
Technical field
The invention belongs to household building materials field, and in particular to a kind of environmentally friendly combined wall board of novel glass fiber.
Background technology
With being showing improvement or progress day by day for social economy and scientific and technological level, requirement of the people to home decoration is also improved constantly.Due to
Original cement wall surface lacks the feature of stereo decoration, or when needing that space is simply separated indoors, generally requires to make
Operation is carried out with certain decorative wall panels.Decorative wall panels classification has a lot, has by material structure point：Solid wood wallboard, reinforcing are compound
Wooden wallboard and at present most popular glass wallboard etc..Solid wood wallboard is the ornament materials formed after timber drying, processing,
With decorative pattern naturally, comfortable foot feeling, using it is safe the characteristics of, be the ideal material of the wall surfacings such as bedroom, parlor, study.And
The weakness of solid wood wallboard is the poor durability to moist and sunlight, and humidity makes natural timber expand, and parching can shrink on the contrary,
Slot even flexing is thus caused to tilt, the life given people brings inconvenience.It is in recent years to strengthen wood composite wallboard
Popular wall covering, is after log crushing, glue, preservative, additive to be dosed, through hot press HTHP compression process
Into, therefore it has broken the physical arrangement of log, overcomes the weakness of log stability difference, but adding due to a large amount of adhesive glues
Plus, there is larger environmentally friendly hidden danger, formaldehyde and other harmful substance contents are higher, have impact on the physical and mental health of people.Glass wall
Plate is attractive in appearance, but the metope sense of reality is poor, and is unfavorable for protecting privacy.
Therefore, the product homogeneity of current household building materials market is serious, and the performance and environmental-protecting performance of product are difficult
To get both, it would be highly desirable to research and develop a kind of new material to fill a hole in the market.
The content of the invention
In view of the above-mentioned problems, the invention provides a kind of environmentally friendly combined wall board of novel glass fiber, effectively reducing in wallboard has
Evil gas content, while having prevented the performance defect that existing wooden wallboard is present from source, reduces unnecessary trouble.
To solve problem above, the present invention is achieved through the following technical solutions：
A kind of environmentally friendly combined wall board of novel glass fiber, including internal surface layer, middle level and outer coversheet are designed, wherein, the internal surface layer
It is made up of the raw material of following parts by weight：48~56 parts of continuous glass fibre, 6~10 parts of brominated epoxy resin, makrolon 18~
24 parts and 15~20 parts of vinyl ester resin, the middle level is made up of the raw material of following parts by weight：Continuous glass fibre 60~66
Part, 12~16 parts of epoxy resin, 18~24 parts of M-phthalic acid type unsaturated polyester (UP), the outer coversheet by following parts by weight original
Material is made：48~56 parts of continuous glass fibre, 6~10 parts of brominated epoxy resin, 18~24 parts of makrolon and vinyl esters tree
15~20 parts of fat.
It is preferred that, the internal surface layer is made up of the raw material of following parts by weight：52 parts of continuous glass fibre, brominated epoxy resin
18 parts of 8 parts, 21 parts of makrolon and vinyl ester resin, the middle level is made up of the raw material of following parts by weight：Continuous glass fibers
Dimension 63 parts, 14 parts of epoxy resin, 21 parts of M-phthalic acid type unsaturated polyester (UP), the outer coversheet by following parts by weight raw material system
Into：18 parts of 52 parts of continuous glass fibre, 8 parts of brominated epoxy resin, 21 parts of makrolon and vinyl ester resin.
It is preferred that, the thickness ratio between the internal surface layer, middle level and outer coversheet is 1:(1.5~1.8):1.
It is preferred that, the makrolon is bisphenol-a polycarbonate.
It is preferred that, it is additionally provided with wear-resisting decorative layer on the surface of the internal surface layer and outer coversheet.
It is preferred that, the wear-resisting decorative layer has the facing paper of silica membrane for deposition.
The preparation method of the environmentally friendly combined wall board of above-mentioned novel glass fiber, comprises the following steps：
(1) preparation of internal surface layer：By the brominated epoxy resin, makrolon and vinyl ester resin heating and melting and mix
After closing uniformly, the continuous glass fibre is impregnated using gained mixed with resin liquid, laying is then carried out in a mold；
(2) preparation in middle level：By the epoxy resin and M-phthalic acid type unsaturated polyester (UP) heating and melting and stir mixed
After closing uniformly, the continuous glass fibre is impregnated using gained mixed with resin liquid, then on inner coversheet material
Carry out laying；
(3) preparation of outer coversheet：After the vinyl ester resin heating and melting, using gained resin liquid to the company
Continuous glass fibre is impregnated, and laying is then carried out on middle layer material；
(4) hot-press solidifying：Mould is placed in hot press, first 10~15min of precompressed at 2~3MPa, 150~160 DEG C,
Then, pressurize is molded 150~180min then at 5~6MPa, 250~260 DEG C, finally the natural cooling under the conditions of 1~2MPa
30min；
(5) prepared by laminated material：A certain amount of nano-attapulgite stone is added in deionized water, and adds a certain amount of NaCl,
After stirring, ultrasonically treated 8~10 minutes, ultrasonic frequency was 50~55KHz, then filters, dries, obtains material of fitting
Material；Weight ratio between the nano-attapulgite stone, deionized water, NaCl is 1：(6~8)：(0.08~0.10)；
(6) wear-resisting decorative layer laminating：Laminated material obtained by step (5) is compared 1 with weight:0.8~1.0 dipping brominated epoxy
Resin, then by its uniform paving to the surface of latter two surface layer of hot-press solidifying, thickness is 1.2~1.6mm, and wear-resisting decorative layer is pasted
Close thereon, carry out being split after hot pressing, natural cooling again in 200~210 DEG C, slot, that is, obtain combined wall board of the present invention.
The present invention has following positive beneficial effect：
Combined wall board of the present invention health, environmental protection, content of formaldehyde as little as below 0.1mg/L, and stability is good, be not afraid of it is moist,
Water logging, corrosion-resistant, good heat insulating, and sound-absorbing damping, excellent noise reduction effect.
(1) present invention is configured in interior outer coversheet using the resin of science, can be reduced the dust pollution in process, be made behaviour
The suction of excessive dust is avoided as personnel, is reduced to healthy influence.In addition, the unsaturated double-bond position of vinyl ester resin
In the end of polymer molecular chain, very vivaciously, do not influenceed during solidification by spatial obstacle, and the R group in resin chain can be with
Ester bond is shielded, the chemical-resistance and stability to hydrolysis resistance of ester bond are improved, while in resin chainSecondary hydroxylWith glass fibre it
Between the wellability and caking property that have had, so as to improve the intensity of composite.
(2) present invention, can in the load middle level of combined wall board epoxy resin mixing M-phthalic acid type unsaturated polyester (UP)
Make have preferable mechanical property, toughness after solidification, significantly improve modulus of elasticity, wallboard is born certain shearing should
Power, and have the ester bond on excellent decay resistance, isophthalic polyester strand sterically hindered by M-phthalic acid
The protection of effect, it is not easy to attacked by water and other various corrosive mediums.
(3) present invention is used as the laminating medium material of wear-resisting decorative layer by the use of nano-attapulgite stone material and brominated epoxy resin
Material, can not only significantly improve laminating firmness, improve service life, moreover it is possible to play flame retardant effect, largely avoid fire
Calamity spreads.
Embodiment
Following embodiment facilitates a better understanding of the present invention, but does not limit the present invention.Experiment in following embodiments
Method, is conventional method unless otherwise specified.Test material used in following embodiments, is certainly unless otherwise specified
Conventional chemical reagent shop is commercially available.
Embodiment 1
A kind of environmentally friendly combined wall board of novel glass fiber, including internal surface layer, middle level and outer coversheet, thickness ratio is 1:1.6:1, its
In, the internal surface layer is made up of the raw material of following parts by weight：52 parts of continuous glass fibre, 8 parts of brominated epoxy resin, polymer with bis phenol A
18 parts of 21 parts of carbonic ester and vinyl ester resin, the middle level is made up of the raw material of following parts by weight：63 parts of continuous glass fibre,
14 parts of epoxy resin, 21 parts of M-phthalic acid type unsaturated polyester (UP), the outer coversheet is made up of the raw material of following parts by weight：Continuously
18 parts of 52 parts of glass fibre, 8 parts of brominated epoxy resin, 21 parts of bisphenol-a polycarbonate and vinyl ester resin.
Wear-resisting decorative layer is additionally provided with the surface of the internal surface layer and outer coversheet, the wear-resisting decorative layer is that deposition has dioxy
The facing paper of SiClx film.
The preparation method of the environmentally friendly combined wall board of above-mentioned novel glass fiber, comprises the following steps：
(1) preparation of internal surface layer：By the brominated epoxy resin, makrolon and vinyl ester resin heating and melting and mix
After closing uniformly, the continuous glass fibre is impregnated using gained mixed with resin liquid, laying is then carried out in a mold；
(2) preparation in middle level：By the epoxy resin and M-phthalic acid type unsaturated polyester (UP) heating and melting and stir mixed
After closing uniformly, the continuous glass fibre is impregnated using gained mixed with resin liquid, then on inner coversheet material
Carry out laying；
(3) preparation of outer coversheet：After the vinyl ester resin heating and melting, using gained resin liquid to the company
Continuous glass fibre is impregnated, and laying is then carried out on middle layer material；
(4) hot-press solidifying：Mould is placed in hot press, first the precompressed 12min at 2.5MPa, 155 DEG C, then, then
5.5MPa, pressurize shaping 165min at 255 DEG C, finally the natural cooling 30min under the conditions of 1.5MPa；
(5) prepared by laminated material：A certain amount of nano-attapulgite stone is added in deionized water, and adds a certain amount of NaCl,
After stirring, ultrasonically treated 9 minutes, ultrasonic frequency was 53KHz, then filters, dries, obtains laminated material；It is described to receive
Weight ratio between rice attapulgite, deionized water, NaCl is 1：7：0.09；
(6) wear-resisting decorative layer laminating：Laminated material obtained by step (5) is compared 1 with weight:0.9 dipping brominated epoxy resin,
Then it is uniformly spread to the surface of latter two surface layer of hot-press solidifying, thickness is 1.4mm, by the laminating of wear-resisting decorative layer thereon, in
205 DEG C carry out being split after hot pressing, natural cooling again, slot, that is, obtain combined wall board of the present invention.The ring of gained combined wall board
The other E0 of safeguarding grades, tensile strength：659MPa, tensile modulus of elasticity 61GPa, bending strength 774MPa, modulus of elasticity in static bending 35GPa.
Embodiment 2
A kind of environmentally friendly combined wall board of novel glass fiber, including internal surface layer, middle level and outer coversheet, thickness ratio is 1:1.5:1, its
In, the internal surface layer is made up of the raw material of following parts by weight：56 parts of continuous glass fibre, 6 parts of brominated epoxy resin, polymer with bis phenol A
15 parts of 18 parts of carbonic ester and vinyl ester resin, the middle level is made up of the raw material of following parts by weight：60 parts of continuous glass fibre,
16 parts of epoxy resin, 24 parts of M-phthalic acid type unsaturated polyester (UP), the outer coversheet is made up of the raw material of following parts by weight：Continuously
15 parts of 56 parts of glass fibre, 6 parts of brominated epoxy resin, 18 parts of bisphenol-a polycarbonate and vinyl ester resin.
Wear-resisting decorative layer is additionally provided with the surface of the internal surface layer and outer coversheet, the wear-resisting decorative layer is that deposition has dioxy
The facing paper of SiClx film.
The preparation method of the environmentally friendly combined wall board of above-mentioned novel glass fiber, comprises the following steps：
(1) preparation of internal surface layer：By the brominated epoxy resin, makrolon and vinyl ester resin heating and melting and mix
After closing uniformly, the continuous glass fibre is impregnated using gained mixed with resin liquid, laying is then carried out in a mold；
(2) preparation in middle level：By the epoxy resin and M-phthalic acid type unsaturated polyester (UP) heating and melting and stir mixed
After closing uniformly, the continuous glass fibre is impregnated using gained mixed with resin liquid, then on inner coversheet material
Carry out laying；
(3) preparation of outer coversheet：After the vinyl ester resin heating and melting, using gained resin liquid to the company
Continuous glass fibre is impregnated, and laying is then carried out on middle layer material；
(4) hot-press solidifying：Mould is placed in hot press, first the precompressed 10min at 2MPa, 160 DEG C, then, then
5MPa, pressurize shaping 150min at 260 DEG C, finally the natural cooling 30min under the conditions of 1MPa；
(5) prepared by laminated material：A certain amount of nano-attapulgite stone is added in deionized water, and adds a certain amount of NaCl,
After stirring, ultrasonically treated 10 minutes, ultrasonic frequency was 50KHz, then filters, dries, obtains laminated material；It is described to receive
Weight ratio between rice attapulgite, deionized water, NaCl is 1：8：0.08；
(6) wear-resisting decorative layer laminating：Laminated material obtained by step (5) is compared 1 with weight:1.0 dipping brominated epoxy resins,
Then it is uniformly spread to the surface of latter two surface layer of hot-press solidifying, thickness is 1.2mm, by the laminating of wear-resisting decorative layer thereon, in
210 DEG C carry out being split after hot pressing, natural cooling again, slot, that is, obtain combined wall board of the present invention.The ring of gained combined wall board
The other E0 of safeguarding grades, tensile strength：638MPa, tensile modulus of elasticity 57GPa, bending strength 756MPa, modulus of elasticity in static bending 34GPa.
Embodiment 3
A kind of environmentally friendly combined wall board of novel glass fiber, including internal surface layer, middle level and outer coversheet, thickness ratio is 1:1.8:1, its
In, the internal surface layer is made up of the raw material of following parts by weight：48 parts of continuous glass fibre, 10 parts of brominated epoxy resin, polymer with bis phenol A
20 parts of 24 parts of carbonic ester and vinyl ester resin, the middle level is made up of the raw material of following parts by weight：66 parts of continuous glass fibre,
12 parts of epoxy resin, 18 parts of M-phthalic acid type unsaturated polyester (UP), the outer coversheet is made up of the raw material of following parts by weight：Continuously
20 parts of 48 parts of glass fibre, 10 parts of brominated epoxy resin, 24 parts of bisphenol-a polycarbonate and vinyl ester resin.
Wear-resisting decorative layer is additionally provided with the surface of the internal surface layer and outer coversheet, the wear-resisting decorative layer is that deposition has dioxy
The facing paper of SiClx film.
The preparation method of the environmentally friendly combined wall board of above-mentioned novel glass fiber, comprises the following steps：
(1) preparation of internal surface layer：By the brominated epoxy resin, makrolon and vinyl ester resin heating and melting and mix
After closing uniformly, the continuous glass fibre is impregnated using gained mixed with resin liquid, laying is then carried out in a mold；
(2) preparation in middle level：By the epoxy resin and M-phthalic acid type unsaturated polyester (UP) heating and melting and stir mixed
After closing uniformly, the continuous glass fibre is impregnated using gained mixed with resin liquid, then on inner coversheet material
Carry out laying；
(3) preparation of outer coversheet：After the vinyl ester resin heating and melting, using gained resin liquid to the company
Continuous glass fibre is impregnated, and laying is then carried out on middle layer material；
(4) hot-press solidifying：Mould is placed in hot press, first the precompressed 15min at 3MPa, 150 DEG C, then, then
6MPa, pressurize shaping 180min at 250 DEG C, finally the natural cooling 30min under the conditions of 2MPa；
(5) prepared by laminated material：A certain amount of nano-attapulgite stone is added in deionized water, and adds a certain amount of NaCl,
After stirring, ultrasonically treated 8 minutes, ultrasonic frequency was 55KHz, then filters, dries, obtains laminated material；It is described to receive
Weight ratio between rice attapulgite, deionized water, NaCl is 1：6：0.10；
(6) wear-resisting decorative layer laminating：Laminated material obtained by step (5) is compared 1 with weight:0.8 dipping brominated epoxy resin,
Then it is uniformly spread to the surface of latter two surface layer of hot-press solidifying, thickness is 1.6mm, by the laminating of wear-resisting decorative layer thereon, in
200 DEG C carry out being split after hot pressing, natural cooling again, slot, that is, obtain combined wall board of the present invention.The ring of gained combined wall board
The other E0 of safeguarding grades, tensile strength：651MPa, tensile modulus of elasticity 60GPa, bending strength 768MPa, modulus of elasticity in static bending 34GPa.
The present invention is described in detail above in conjunction with embodiment, still, person of ordinary skill in the field can
Understand, on the premise of present inventive concept is not departed from, the design parameter of each in above-described embodiment can also be changed, shape
Into multiple specific embodiments, it is the common excursion of the present invention, is no longer described in detail one by one herein.
Claims (8)
1. a kind of environmentally friendly combined wall board of novel glass fiber, including internal surface layer, middle level and outer coversheet, it is characterised in that the internal surface layer
It is made up of the raw material of following parts by weight：48~56 parts of continuous glass fibre, 6~10 parts of brominated epoxy resin, makrolon 18~
24 parts and 15~20 parts of vinyl ester resin, the middle level is made up of the raw material of following parts by weight：Continuous glass fibre 60~66
Part, 12~16 parts of epoxy resin, 18~24 parts of M-phthalic acid type unsaturated polyester (UP), the outer coversheet by following parts by weight original
Material is made：48~56 parts of continuous glass fibre, 6~10 parts of brominated epoxy resin, 18~24 parts of makrolon and vinyl esters tree
15~20 parts of fat.
2. the environmentally friendly combined wall board of novel glass fiber according to claim 1, it is characterised in that the internal surface layer is by following weight
The raw material of part is made：18 parts of 52 parts of continuous glass fibre, 8 parts of brominated epoxy resin, 21 parts of makrolon and vinyl ester resin,
The middle level is made up of the raw material of following parts by weight：63 parts of continuous glass fibre, 14 parts of epoxy resin, M-phthalic acid type insatiable hunger
With 21 parts of polyester, the outer coversheet is made up of the raw material of following parts by weight：52 parts of continuous glass fibre, 8 parts of brominated epoxy resin,
18 parts of 21 parts of makrolon and vinyl ester resin.
3. the environmentally friendly combined wall board of novel glass fiber according to claim 1, it is characterised in that：The internal surface layer, middle level and outer
Thickness ratio between surface layer is 1:(1.5~1.8):1.
4. the environmentally friendly combined wall board of novel glass fiber according to claim 1, it is characterised in that：The makrolon is bisphenol-A
Makrolon.
5. the environmentally friendly combined wall board of novel glass fiber according to claim 1, it is characterised in that：In the internal surface layer and outer coversheet
Surface be additionally provided with wear-resisting decorative layer.
6. the environmentally friendly combined wall board of novel glass fiber according to claim 5, it is characterised in that：The wear-resisting decorative layer is deposition
There is the facing paper of silica membrane.
7. the preparation method of novel glass fiber environmental protection combined wall board described in claim 1, it is characterised in that comprise the following steps：
(1) preparation of internal surface layer：By the brominated epoxy resin, makrolon and vinyl ester resin heating and melting and mix equal
After even, the continuous glass fibre is impregnated using gained mixed with resin liquid, laying is then carried out in a mold；
(2) preparation in middle level：By the epoxy resin and M-phthalic acid type unsaturated polyester (UP) heating and melting and to stir mixing equal
After even, the continuous glass fibre is impregnated using gained mixed with resin liquid, then carried out on inner coversheet material
Laying；
(3) preparation of outer coversheet：After the vinyl ester resin heating and melting, using gained resin liquid to the continuous glass
Glass fiber is impregnated, and laying is then carried out on middle layer material；
(4) hot-press solidifying：Mould is placed in hot press, first 10~15min of precompressed at 2~3MPa, 150~160 DEG C, so
Afterwards, pressurize is molded 150~180min then at 5~6MPa, 250~260 DEG C, finally the natural cooling under the conditions of 1~2MPa
30min。
8. preparation method according to claim 7, it is characterised in that further comprising the steps of：
(5) prepared by laminated material：A certain amount of nano-attapulgite stone is added in deionized water, and adds a certain amount of NaCl, is stirred
After uniform, ultrasonically treated 8~10 minutes, ultrasonic frequency was 50~55KHz, then filters, dries, obtains laminated material；Institute
It is 1 to state the weight ratio between nano-attapulgite stone, deionized water, NaCl：(6~8)：(0.08~0.10)；
(6) wear-resisting decorative layer laminating：Laminated material obtained by step (5) is compared 1 with weight:0.8~1.0 dipping brominated oxygen tree
Fat, then by its uniform paving to the surface of latter two surface layer of hot-press solidifying, thickness is 1.2~1.6mm, and wear-resisting decorative layer is fitted
Thereon, carry out being split after hot pressing, natural cooling again in 200~210 DEG C, slot, that is, obtain combined wall board of the present invention.