CN107129656A - A kind of wear resistant type plastic floor - Google Patents
A kind of wear resistant type plastic floor Download PDFInfo
- Publication number
- CN107129656A CN107129656A CN201710508770.0A CN201710508770A CN107129656A CN 107129656 A CN107129656 A CN 107129656A CN 201710508770 A CN201710508770 A CN 201710508770A CN 107129656 A CN107129656 A CN 107129656A
- Authority
- CN
- China
- Prior art keywords
- parts
- wear resistant
- resistant type
- substrate
- type plastic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of wear resistant type plastic floor, it is characterised in that：It is made up of following raw material and its mass fraction：30 40 parts of phenolic resin；Polypropylene 20 30；10 20 parts of polyvinyl chloride；20 30 parts of calcium carbonate；25 parts of plastics reinforcing agent；Plastics；5 10 parts of magnesium carbonate；10 15 parts of clay；58 parts of coupling agent；After above-mentioned raw materials are well mixed, heated mixed at high speed is extruded into plastic pellet, then extruded compound, compression molding, cooling, traction are substrate, and surface decoration layer and substrate are complex as into finished product using waterproof binder.Wear resistant type plastic floor prepared by the present invention, wearability is good, long lifespan, and resistance to old oxidation susceptibility is excellent.
Description
Technical field
The present invention relates to a kind of wear resistant type plastic floor, belong to plastic products technology field.
Background technology
It is used for family in the market, the floor that office occupancy is decorated is typically to use solid wooden floor board or composite floor board.It is real
Timber floor need to consume substantial amounts of timber, and expensive, though its have the advantages that it is wear-resisting, laying using rear water resistance it is poor,
And it is easy to crack, warp.Composite floor board be using wood chip, adhesive is blended is extruded from.Though it has light, cheap
The advantages of, but water resistance, wearability are poor, and mechanical performance is low, unstable, can equally warp, decorative effect is poor, use after circuitous water
Short life, is difficult to be liked receiving by people.
The content of the invention
In order to overcome the above-mentioned deficiencies of the prior art, the invention provides a kind of wear resistant type plastic floor, it is by following
Raw material and its mass fraction composition：30-40 parts of phenolic resin；Polypropylene 20-30；10-20 parts of polyvinyl chloride；Calcium carbonate 20-30
Part；2-5 parts of plastics reinforcing agent；Plastics；5-10 parts of magnesium carbonate；10-15 parts of clay；5-8 parts of coupling agent；
After above-mentioned raw materials are well mixed, heated mixed at high speed is extruded into plastic pellet, then extruded compound, compression molding, cold
But, traction is substrate, and surface decoration layer and substrate are complex as into finished product using waterproof binder.
Advantageous effects of the present invention：Wear resistant type plastic floor prepared by the present invention, wearability is good, long lifespan, resistance to old oxygen
Change excellent performance.
Embodiment
With reference to embodiment, the invention will be further described.
Embodiment 1
A kind of wear resistant type plastic floor, it is made up of following raw material and its mass fraction：30-40 parts of phenolic resin；Polypropylene
20；10 parts of polyvinyl chloride；20 parts of calcium carbonate；2 parts of plastics reinforcing agent；Plastics；5 parts of magnesium carbonate；10 parts of clay；5 parts of coupling agent；
After above-mentioned raw materials are well mixed, heated mixed at high speed is extruded into plastic pellet, then extruded compound, compression molding, cold
But, traction is substrate, and surface decoration layer and substrate are complex as into finished product using waterproof binder.
Embodiment 2
A kind of wear resistant type plastic floor, it is made up of following raw material and its mass fraction：40 parts of phenolic resin；Polypropylene 30；
20 parts of polyvinyl chloride；30 parts of calcium carbonate；5 parts of plastics reinforcing agent；Plastics；10 parts of magnesium carbonate；15 parts of clay；5 parts of coupling agent；
After above-mentioned raw materials are well mixed, heated mixed at high speed is extruded into plastic pellet, then extruded compound, compression molding, cold
But, traction is substrate, and surface decoration layer and substrate are complex as into finished product using waterproof binder.
Claims (1)
1. a kind of wear resistant type plastic floor, it is characterised in that：It is made up of following raw material and its mass fraction：Phenolic resin
30-40 parts；Polypropylene 20-30；10-20 parts of polyvinyl chloride；20-30 parts of calcium carbonate；2-5 parts of plastics reinforcing agent；Plastics；Magnesium carbonate
5-10 parts；10-15 parts of clay；5-8 parts of coupling agent；
After above-mentioned raw materials are well mixed, heated mixed at high speed is extruded into plastic pellet, then extruded compound, compression molding, cold
But, traction is substrate, and surface decoration layer and substrate are complex as into finished product using waterproof binder.