CN107114975B - A kind of pearl ceramic cup production technology - Google Patents
A kind of pearl ceramic cup production technology Download PDFInfo
- Publication number
- CN107114975B CN107114975B CN201710325749.7A CN201710325749A CN107114975B CN 107114975 B CN107114975 B CN 107114975B CN 201710325749 A CN201710325749 A CN 201710325749A CN 107114975 B CN107114975 B CN 107114975B
- Authority
- CN
- China
- Prior art keywords
- pearl
- cup
- powder
- ceramic
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention proposes a kind of pearl ceramic cup production technologies, it is characterized by: the pearl ceramic cup includes cup body and pearl health-care layer, the inner wall of the cup body is equipped with pearl powder heath care layer, the production technology of the pearl ceramic cup specifically includes following processing step: pearl mineral powder pretreatment, the production of cup body ceramic body, the production of pearl powder heath care layer green body, cup body forms by a firing, finished product processing and etc., the present invention, which is utilized, is arranged pearl bisque in the internal layer of cup body, during capable of making daily drinking-water, it takes into micro pearl powder, long-term drinking has certain health-care effect to human body, utilize discarded pearl and its particle, it is processed into the material of ceramic material, pearl powder minerals utilization is increased to the texture of porcelain into ceramic, hardness, with light transmittance etc., cup body tire matter can be made pure, glaze is smooth, simple process is feasible, Safety and environmental protection, resource maximally utilize.
Description
[technical field]
The present invention relates to a kind of technical field of ceramic cup, especially a kind of pearl ceramic cup production technology.
[background technique]
What is generated in fresh water pearl industry does not conform to the regenerations such as grain pearl, discarded pearl particles, Pearl by one
Fixed limitation, the main component of pearl are calcium carbonate, and the mineral of calcium carbonate can be substantially reduced the burning of product in Production of Ceramics
Temperature processed increases the texture, hardness and light transmittance of porcelain, therefore pearl powder minerals utilization can be improved into ceramic
The performance of ceramics；Pearl powder has certain health-care effect simultaneously:
One, pearl delays senescence to human body, and long term usage keeps your whole body skin carefully white, adheres to making face with tens milligrams of pearls sooner or later
Skin care powder is made in portion's massage, and skin can be obvious white after 1 year, and face presents transparent white.It can be reduced in the every pearl powder in the sky of navel
Facial spot；
Two, it clears liver and improve vision.Pearl takes away Liver Channel orally, and eye illness, pearl eyesight are controlled in external application；
Three, it replenishes the calcium；The effect of adjusting the human bodies ph values such as gastric acid hematic acid uric acid, pearl are in alkalescent, and long term usage must make blood in weak
Alkalinity, be not afraid of mosquito improve skin immune function controlling, neutralize gastric acid can stomach invigorating, because increase blood calcium thus have anti-allergic effects.From change
Learning angle analysis pearl long term usage must have good health and a long life；
Four, tranquilizing mind, yin-nourishing relieve dizziness, high fever, infantile convulsions, epilepsy, etc., and heat-clearing falls phlegm, and " peace soul, only passes out semen, gonorrhoea, and solution acne treats poison, and " long term usage is able to maintain
Awake brains, makes the Quality advance of sleep, and medical research is beneficial to heart disease；
Five, morning and evening buccal pearl powder can control mouth disease such as dispute and fester, and pharyngitis, odontitis etc. has antiinflammation, also
Protect tooth effect；
Cup is frequently used in daily life as daily necessity, can be daily by pearl bisque is arranged in cup
It is taken during drinking-water into micro pearl powder, there is certain health-care effect to human body, therefore propose a kind of pearl ceramic cup production
Technique.
[summary of the invention]
The object of the invention is to solve the problems of the prior art, a kind of pearl ceramic cup production technology is proposed, in cup
Pearl bisque is arranged in the internal layer of body, during capable of making daily drinking-water, takes into micro pearl powder, long-term drinking has one to human body
Fixed health-care effect increases texture, hardness and light transmittance of porcelain etc., simultaneously by pearl powder minerals utilization into ceramic
Using hollow double-layer cup body structure, avoid cup body temperature excessively high, it is convenient empty-handedly to take cup.
To achieve the above object, the invention proposes a kind of pearl ceramic cup production technologies, it is characterised in that: the pearl
Ceramic cup includes cup body and pearl health-care layer, and the inner wall of the cup body is equipped with pearl powder heath care layer, the life of the pearl ceramic cup
Production. art specifically includes following processing step:
Step 1: the pearl cleaned up or broken pearl particles the pretreatment of pearl mineral powder: being subjected to crushing and processing
To less than 1000 mesh little particle, the temperature lower calcination by Pearl at 300-350 DEG C, at such a temperature keep the temperature 2.5-4 it is small
When, by container of the Pearl feeding containing phosphoric acid treatment fluid after primary treatment, after reaction to pH value is 5-7, stand 12-
It obtains aqueous powder within 15 hours, then aqueous powder is washed with water, remove soluble intermediate material, calcined again after dry
To pearl mineral powder, classification processing is carried out to pearl mineral powder after cooling；
Step 2: cup body ceramic body production: by pearl mineral powder, china clay, kaolin, feldspar powder, silver nitrate and water
Ceramic material is obtained after mixing, and is processed into inner cup ceramic body；
Step 3: the production of pearl powder heath care layer green body: the pearl cleaned up being subjected to crushing and processing to less than 1800 mesh are small
The pearl health-care powder of particle, the temperature lower calcination by Pearl at 300-350 DEG C keep the temperature 2.5-4 hours at such a temperature, will
Pearl health-care layer pug is obtained after pearl health-care powder, china clay, kaolin and water mixing, pug is coated to inner cup ceramic body
Inner wall, and it is processed into the inner cup green body with heath care layer；
Step 4: cup body forms by a firing: inner cup ceramic body being formed by a firing by 1180-1230 DEG C, is obtained after cooling interior
Cup semi-finished product；
Step 5: semi-finished product sanding and polishing and air-dry, glazing then carried out to the outer wall of cup body, 1050-1150 DEG C
It forms within low-firing 5-8 hours.
As preferred: the 0.5-2% with a thickness of cup body integral thickness of the pearl powder heath care layer.
As preferred: inner cup ceramic body is made of the raw material of following mass component in the step 2: pearl mineral powder
20-40 parts, 15-20 parts of china clay, 50-60 parts of kaolin, 5-20 parts of feldspar powder, 0.02-0.05 parts of silver nitrate, water 100-200
Part.
As preferred: pearl mineral powder forms: less than 500 mesh by the raw material of following mass component in the step 2
Grain: 500-800 mesh particle: particle=1:4:2 of 800-1000 mesh, the feldspar powder are made of the raw material of lower mass component:
Potassium feldspar: albite=1:1.
As preferred: pearl health-care layer pug is made of the raw material of following mass component in the step 3: pearl health-care powder
40-80 parts, 15-30 parts of china clay, 20-40 parts of kaolin and 70-120 parts of water.
As preferred: pearl health-care powder forms: less than 500 mesh particles by the raw material of following mass component in the step 3:
500-1000 mesh particle: particle=4:2:1 of 1000-1800 mesh.
As preferred: further including outer cup on the outside of the cup body, air chamber, institute are equipped between the cup body and outer cup
The bottom of a cup outer wall for stating cup body is equipped with annular protrusion, and the bottom of a cup inner wall of the outer cup is equipped with annular groove, the annular protrusion with
Annular groove is bonding, and the upper end of the cup body is equipped with cup edge connector, and the lower wall path length of the cup edge connector is greater than cup body
Path length, the lower wall of the cup edge connector offers link slot, and the upper end of the outer cup and link slot are bonding.
Beneficial effects of the present invention: the present invention, which is utilized, is arranged pearl bisque in the internal layer of cup body, can make daily drank water
Cheng Zhong takes into micro pearl powder, and long-term drinking has certain health-care effect to human body, using discarded pearl and its particle,
It is processed into the material of ceramic material, pearl powder minerals utilization is increased to the texture, hardness and light transmittance of porcelain into ceramic
Deng can make that cup body tire matter is pure, glaze is smooth, simple process is feasible, safety and environmental protection, and resource maximally utilizes.
Feature and advantage of the invention will be described in detail by embodiment combination attached drawing
[Detailed description of the invention]
Fig. 1 is the cross section structure schematic diagram for inventing a kind of first embodiment of pearl ceramic cup production technology；
Fig. 2 is the cross section structure schematic diagram for inventing a kind of second embodiment of pearl ceramic cup production technology.
[specific embodiment]
Refering to fig. 1, a kind of pearl ceramic cup production technology of Fig. 2 present invention, it is characterised in that: the pearl ceramic cup includes
Cup body 1 and pearl health-care layer 2, the inner wall of the cup body 1 are equipped with pearl powder heath care layer 2, the pearl powder heath care layer 2 with a thickness of
The production technology of the 0.5-2% of 1 integral thickness of cup body, the pearl ceramic cup specifically include following processing step:
Step 1: the pearl cleaned up or broken pearl particles the pretreatment of pearl mineral powder: being subjected to crushing and processing
To less than 1000 mesh little particle, the temperature lower calcination by Pearl at 300-350 DEG C, at such a temperature keep the temperature 2.5-4 it is small
When, by container of the Pearl feeding containing phosphoric acid treatment fluid after primary treatment, after reaction to pH value is 5-7, stand 12-
It obtains aqueous powder within 15 hours, then aqueous powder is washed with water, remove soluble intermediate material, calcined again after dry
To pearl mineral powder, classification processing is carried out to pearl mineral powder after cooling；
Step 2: cup body ceramic body production: by pearl mineral powder, china clay, kaolin, feldspar powder, silver nitrate and water
Ceramic material is obtained after mixing, and is processed into inner cup ceramic body；
Step 3: the production of pearl powder heath care layer green body: the pearl cleaned up being subjected to crushing and processing to less than 1800 mesh are small
The pearl health-care powder of particle, the temperature lower calcination by Pearl at 300-350 DEG C keep the temperature 2.5-4 hours at such a temperature, will
Pearl health-care layer pug is obtained after pearl health-care powder, china clay, kaolin and water mixing, pug is coated to inner cup ceramic body
Inner wall, and it is processed into the inner cup green body with heath care layer；
Step 4: cup body forms by a firing: inner cup ceramic body being formed by a firing by 1180-1230 DEG C, is obtained after cooling interior
Cup semi-finished product；
Step 5: semi-finished product sanding and polishing and air-dry, glazing then carried out to the outer wall of cup body, 1050-1150 DEG C
It forms within low-firing 5-8 hours.
Inner cup ceramic body is made of the raw material of following mass component in the step 2: 20-40 parts of pearl mineral powder,
15-20 parts of china clay, 50-60 parts of kaolin, 5-20 parts of feldspar powder, 0.02-0.05 parts of silver nitrate, 100-200 parts of water.The step
Pearl mineral powder forms: less than 500 mesh particles: 500-800 mesh particle: 800- by the raw material of following mass component in rapid 2
Particle=1:4:2 of 1000 mesh, the feldspar powder are made of the raw material of lower mass component: potassium feldspar: albite=1:1.Institute
It states pearl health-care layer pug in step 3 to be made of the raw material of following mass component: 40-80 parts of pearl health-care powder, china clay 15-30
Part, 20-40 parts of kaolin and 70-120 parts of water.Pearl health-care powder is made of the raw material of following mass component in the step 3: small
In 500 mesh particles: 500-1000 mesh particle: particle=4:2:1 of 1000-1800 mesh.
The outside of the cup body 1 further includes outer cup 3, and air chamber 32 is equipped between the cup body 1 and outer cup 3, described
The bottom of a cup outer wall of cup body 1 is equipped with annular protrusion 11, and the bottom of a cup inner wall of the outer cup 3 is equipped with annular groove 31, the convex annular
Rise 11 bonding with annular groove 31, the upper end of the cup body 1 is equipped with cup edge connector 4, the lower wall diameter of the cup edge connector 4
The long path length for being greater than cup body 1, the lower wall of the cup edge connector 4 offer link slot 41, the upper end of the outer cup 3 and connection
Slot 41 is bonding.
Embodiment 1:
A kind of pearl ceramic cup production technology of the present invention, it is characterised in that: the pearl ceramic cup includes cup body 1 and pearl
Heath care layer 2, the inner wall of the cup body 1 are equipped with pearl powder heath care layer 2, the pearl powder heath care layer 2 it is whole thick with a thickness of cup body 1
The 1% of degree, the production technology of the pearl ceramic cup specifically includes following processing step:
Step 1: the pearl cleaned up or broken pearl particles the pretreatment of pearl mineral powder: being subjected to crushing and processing
To less than 1000 mesh little particle, the temperature lower calcination by Pearl at 300-350 DEG C, at such a temperature keep the temperature 2.5-4 it is small
When, by container of the Pearl feeding containing phosphoric acid treatment fluid after primary treatment, after reaction to pH value is 5-7, stand 12-
It obtains aqueous powder within 15 hours, then aqueous powder is washed with water, remove soluble intermediate material, calcined again after dry
To pearl mineral powder, classification processing is carried out to pearl mineral powder after cooling；
Step 2: cup body ceramic body production: by pearl mineral powder, china clay, kaolin, feldspar powder, silver nitrate and water
Obtain ceramic material after mixing, and be processed into inner cup ceramic body, the inner cup ceramic body by following mass component raw material
Composition: 25 parts of pearl mineral powder, 15 parts of china clay, 55 parts of kaolin, 10 parts of feldspar powder, 0.03 part of silver nitrate, 120 parts of water,
The pearl mineral powder forms: less than 500 mesh particles: 500-800 mesh particle: 800-1000 by the raw material of following mass component
Purpose particle=1:4:2, the feldspar powder are made of the raw material of lower mass component: potassium feldspar: albite=1:1；
Step 3: the production of pearl powder heath care layer green body: the pearl cleaned up being subjected to crushing and processing to less than 1800 mesh are small
The pearl health-care powder of particle, the temperature lower calcination by Pearl at 300-350 DEG C keep the temperature 2.5-4 hours at such a temperature, will
Pearl health-care layer pug is obtained after pearl health-care powder, china clay, kaolin and water mixing, pug is coated to inner cup ceramic body
Inner wall, and it is processed into the inner cup green body with heath care layer, the pearl health-care layer pug is made of the raw material of following mass component:
40 parts of pearl health-care powder, 25 parts of china clay, 20 parts of kaolin and 90 parts of water, the pearl health-care powder by following mass component raw material
Form: less than 500 mesh particles: 500-1000 mesh particle: particle=4:2:1 of 1000-1800 mesh；
Step 4: cup body forms by a firing: inner cup ceramic body being formed by a firing by 1180-1230 DEG C, is obtained after cooling interior
Cup semi-finished product；
Step 5: semi-finished product sanding and polishing and air-dry, glazing then carried out to the outer wall of cup body, 1050-1150 DEG C
It forms within low-firing 7 hours.
Embodiment 2:
A kind of pearl ceramic cup production technology of the present invention, it is characterised in that: the pearl ceramic cup includes cup body 1 and pearl
Heath care layer 2, the inner wall of the cup body 1 are equipped with pearl powder heath care layer 2, the pearl powder heath care layer 2 it is whole thick with a thickness of cup body 1
The 1% of degree, the outside of the cup body 1 further includes outer cup 3, and air chamber 32 is equipped between the cup body 1 and outer cup 3, described
The bottom of a cup outer wall of cup body 1 is equipped with annular protrusion 11, and the bottom of a cup inner wall of the outer cup 3 is equipped with annular groove 31, the convex annular
Rise 11 bonding with annular groove 31, the upper end of the cup body 1 is equipped with cup edge connector 4, the lower wall diameter of the cup edge connector 4
The long path length for being greater than cup body 1, the lower wall of the cup edge connector 4 offer link slot 41, the upper end of the outer cup 3 and connection
Slot 41 is bonding, and the production technology of the pearl ceramic cup specifically includes following processing step:
Step 1: the pearl cleaned up or broken pearl particles the pretreatment of pearl mineral powder: being subjected to crushing and processing
To less than 1000 mesh little particle, the temperature lower calcination by Pearl at 300-350 DEG C, at such a temperature keep the temperature 2.5-4 it is small
When, by container of the Pearl feeding containing phosphoric acid treatment fluid after primary treatment, after reaction to pH value is 5-7, stand 12-
It obtains aqueous powder within 15 hours, then aqueous powder is washed with water, remove soluble intermediate material, calcined again after dry
To pearl mineral powder, classification processing is carried out to pearl mineral powder after cooling；
Step 2: cup body ceramic body production: by pearl mineral powder, china clay, kaolin, feldspar powder, silver nitrate and water
Obtain ceramic material after mixing, and be processed into inner cup ceramic body, the inner cup ceramic body by following mass component raw material
Composition: 25 parts of pearl mineral powder, 15 parts of china clay, 55 parts of kaolin, 10 parts of feldspar powder, 0.03 part of silver nitrate, 120 parts of water,
The pearl mineral powder forms: less than 500 mesh particles: 500-800 mesh particle: 800-1000 by the raw material of following mass component
Purpose particle=1:4:2, the feldspar powder are made of the raw material of lower mass component: potassium feldspar: albite=1:1, described outer
The ceramic material of cup ceramic body is identical as the formula of cup body ceramic blank ceramic material；
Step 3: the production of pearl powder heath care layer green body: the pearl cleaned up being subjected to crushing and processing to less than 1800 mesh are small
The pearl health-care powder of particle, the temperature lower calcination by Pearl at 300-350 DEG C keep the temperature 2.5-4 hours at such a temperature, will
Pearl health-care layer pug is obtained after pearl health-care powder, china clay, kaolin and water mixing, pug is coated to inner cup ceramic body
Inner wall, and it is processed into the inner cup green body with heath care layer, the pearl health-care layer pug is made of the raw material of following mass component:
40 parts of pearl health-care powder, 25 parts of china clay, 20 parts of kaolin and 90 parts of water, the pearl health-care powder by following mass component raw material
Form: less than 500 mesh particles: 500-1000 mesh particle: particle=4:2:1 of 1000-1800 mesh；
Step 4: cup body forms by a firing: the inner cup green body with heath care layer is formed by a firing by 1180-1230 DEG C, it is cooling
After obtain inner cup semi-finished product, outer cup ceramic body is formed by a firing at 1200-1300 DEG C, obtains outer cup semi-finished product after cooling；
Step 5: semi-finished product reprocessing: inside and outside cup semi-finished product being subjected to sanding and polishing and are air-dried, then to outer cup semi-finished product
Glazing is carried out, 1050-1150 DEG C forms for low-firing 5-8 hours；
Step 6: viscous glutinous molding: by cup body in the corresponding mounting groove of outer cup, and being glued by bonding slurry
It closes, completes overall package.
The present invention, which is utilized, is arranged pearl bisque in the internal layer of cup body, during capable of making daily drinking-water, takes into micro pearl
Powder, long-term drinking there is certain health-care effect to be processed into the material of ceramic material using discarded pearl and its particle human body
Pearl powder minerals utilization, is increased the texture, hardness and light transmittance etc. of porcelain into ceramic, can make cup body tire matter by material
It is pure, glaze is smooth, simple process is feasible, and safety and environmental protection, resource maximally utilizes, while hollow double-layer cup body knot can be used
Structure avoids cup body temperature excessively high, convenient empty-handedly to take cup, and annular groove is arranged in the bottom of inner cup, can be quick group convenient for positioning
Dress.
Above-described embodiment is the description of the invention, is not limitation of the invention, after any pair of simple transformation of the present invention
Scheme all belong to the scope of protection of the present invention.
Claims (7)
1. a kind of pearl ceramic cup production technology, the pearl ceramic cup includes cup body (1) and pearl health-care layer (2), the cup
The inner wall of body (1) is equipped with pearl powder heath care layer (2), it is characterised in that: comprises the technical steps that:
Step 1: the pearl cleaned up or broken pearl particles the pretreatment of pearl mineral powder: being subjected to crushing and processing to small
In the little particle of 1000 mesh, temperature lower calcination by Pearl at 300-350 DEG C keeps the temperature 2.5-4 hour at such a temperature, general
In container of the Pearl feeding containing phosphoric acid treatment fluid after primary treatment, after reaction to pH value is 5-7, it is small to stand 12-15
When obtain aqueous powder, then aqueous powder is washed with water, removes soluble intermediate material, it is dry after again calcining obtain treasure
Pearl mineral powder carries out classification processing to pearl mineral powder after cooling；
Step 2: the production of cup body ceramic body: pearl mineral powder, china clay, kaolin, feldspar powder, silver nitrate and water being mixed
After obtain ceramic material, and be processed into inner cup ceramic body；
Step 3: the pearl cleaned up the production of pearl powder heath care layer green body: being subjected to crushing and processing to less than 1800 mesh little particles
Pearl health-care powder, the temperature lower calcination by Pearl at 300-350 DEG C, at such a temperature keep the temperature 2.5-4 hours, by pearl
Pearl health-care layer pug is obtained after health-care powder, china clay, kaolin and water mixing, pug is coated in inner cup ceramic body
Wall, and it is processed into the inner cup green body with heath care layer；
Step 4: cup body forms by a firing: inner cup ceramic body being formed by a firing by 1180-1230 DEG C, inner cup half is obtained after cooling
Finished product；
Step 5: semi-finished product being subjected to sanding and polishing and are air-dried, glazing, 1050-1150 DEG C of low temperature then are carried out to the outer wall of cup body
It fires 5-8 hours and forms.
2. a kind of pearl ceramic cup production technology as described in claim 1, it is characterised in that: the pearl powder heath care layer (2)
The 0.5-2% with a thickness of cup body (1) integral thickness.
3. a kind of pearl ceramic cup production technology as described in claim 1, it is characterised in that: inner cup ceramics in the step 2
Green body is made of the raw material of following mass component: 20-40 parts of pearl mineral powder, 15-20 parts of china clay, 50-60 parts of kaolin, length
5-20 parts of mountain flour material, 0.02-0.05 parts of silver nitrate, 100-200 parts of water.
4. a kind of pearl ceramic cup production technology as described in claim 1, it is characterised in that: pearl mineral in the step 2
Powder forms: less than 500 mesh particles: 500-800 mesh particle: particle=1 of 800-1000 mesh by the raw material of following mass component:
4:2, the feldspar powder are made of the raw material of lower mass component: potassium feldspar: albite=1:1.
5. a kind of pearl ceramic cup production technology as described in claim 1, it is characterised in that: pearl health-care in the step 3
Layer pug be made of the raw material of following mass component: 40-80 parts of pearl health-care powder, 15-30 parts of china clay, 20-40 parts of kaolin and
70-120 parts of water.
6. a kind of pearl ceramic cup production technology as described in claim 1, it is characterised in that: pearl health-care in the step 3
Powder forms: less than 500 mesh particles: 500-1000 mesh particle: particle=4 of 1000-1800 mesh by the raw material of following mass component:
2:1。
7. a kind of pearl ceramic cup production technology as described in claim 1, it is characterised in that: the outside of the cup body (1) is also
Including outer cup (3), air chamber (12) are equipped between the cup body (1) and outer cup (3), the bottom of a cup outer wall of the cup body (1)
Equipped with annular protrusion (11), the bottom of a cup inner wall of the outer cup (3) is equipped with annular groove (31), the annular protrusion (11) and ring
Connected in star (31) is bonding, and the upper end of the cup body (1) is equipped with cup edge connector (4), the lower wall diameter of the cup edge connector (4)
The long path length for being greater than cup body (1), the lower wall of the cup edge connector (4) offer link slot (41), the outer cup (3) it is upper
It holds bonding with link slot (41).