CN107099224A - A kind of sports equipment protects paint vehicle coating process - Google Patents
A kind of sports equipment protects paint vehicle coating process Download PDFInfo
- Publication number
- CN107099224A CN107099224A CN201710304459.4A CN201710304459A CN107099224A CN 107099224 A CN107099224 A CN 107099224A CN 201710304459 A CN201710304459 A CN 201710304459A CN 107099224 A CN107099224 A CN 107099224A
- Authority
- CN
- China
- Prior art keywords
- parts
- paint vehicle
- sports equipment
- coating process
- protection paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of sports equipment protects paint vehicle coating process, is related to paint vehicle technical field, and (1) will protect paint vehicle to be sufficiently stirred for；Described protection paint vehicle is prepared from by the component of following parts by weight meter：30~40 parts of aqueous saturated polyester resins, 1~2 part of ammonia nertralizer, 4~5 parts of milky white adhesives, 0.2~0.4 part of beeswax, 0.2~0.3 part of defoamer, 0.3~0.4 part of thickener, 0.1~0.2 part of petroleum coke powder, 40~50 parts of aqueous white slurries, 18~25 parts of deionized waters；(2) liquid after stirring is heated, its temperature is reached 20~30 DEG C；(3) protection paint vehicle is sprayed on sports equipment, the coating thickness of protection paint vehicle is controlled at 10~100 μm；(4) sports equipment is taken out, sprays coagulant solution, continue 2~5 minutes；(5) sports equipment carried out after step (4) is dried or dried.Environmental Safety of the present invention, pollution-free, hardness is high, be not easy to scratch, and is easy to production, and service life is long.
Description
Technical field：
The present invention relates to paint vehicle technical field, and in particular to a kind of sports equipment protects paint vehicle coating process.
Background technology：
In recent years, environment for human survival is increasingly severe, and atmosphere pollution is also on the rise.With the earth be faced with it is more and more tighter
High atmosphere pollution, control of the Overseas Government to paint vehicle product Volatile organic emissions is also increasingly strict.China is locomotory apparatus
Material big producer, the requirement of particularly safety cap protective paint is very high, still, and presently commercially available paint vehicle volatility is stronger, taste compared with
Greatly, indices are unsatisfactory for the relevant laws and regulations of American-European countries, also do not meet the current development prospect of China.
The content of the invention：
The technical problems to be solved by the invention are to overcome existing technological deficiency that there is provided a kind of Environmental Safety, no dirt
Dye, hardness is high, be not easy the sports equipment protection paint vehicle coating process of scuffing.
The technical problems to be solved by the invention are realized using following technical scheme：
A kind of sports equipment protects paint vehicle coating process, it is characterised in that：
(1) protection paint vehicle is sufficiently stirred for；Described protection paint vehicle is prepared from by the component of following parts by weight meter：30~
40 parts of aqueous saturated polyester resins, 1~2 part of ammonia nertralizer, 4~5 parts of milky white adhesives, 0.2~0.4 part of beeswax, 0.2~0.3 part disappears
Infusion, 0.3~0.4 part of thickener, 0.1~0.2 part of petroleum coke powder, 40~50 parts of aqueous white slurries, 18~25 parts of deionized waters；
(2) liquid after stirring is heated, its temperature is reached 20~30 DEG C；
(3) protection paint vehicle is sprayed on sports equipment, the coating thickness of protection paint vehicle is controlled at 10~100 μm；
(4) sports equipment is taken out, sprays coagulant solution, continue 2~5 minutes；
(5) sports equipment carried out after step (4) is dried or dried.
Described thickener includes 6-8 parts of hydroxylmethyl cellulose, 2~4 parts of bentonite, 3~4 parts of apatite, sea by weight
1~2 part of 3~4 parts of afrodite powder and cornstarch.
A kind of sports equipment protects the preparation method of paint vehicle coating process, it is characterised in that：
1) 24-25 parts of aqueous saturated polyester resins are added into container, be then stirred with high speed dispersor, while stirring
Ammonia nertralizer is progressively added dropwise, after mixing speed is 500r/min-900r/min, 3-5min, test mixing liquid pH value is in 7.5-
Between 8.5, stop stirring, carry out next step operation；
2) the whole millings of solid material are handled, then all solid materials is added progress breast is sufficiently mixed in container
Change is handled, 60 DEG C of emulsifying temperature during emulsification, emulsification stirring speed 2000r/min, emulsification times 15min；
3) aqueous white slurry and milky white adhesive are added into container again, deionized water is eventually adding, continues scattered 10-15 points
Clock, test pH value is made paint vehicle between 7.5-8.5.
The aqueous white slurry is to be prepared from according to the following steps：
1) titanium dioxide, dispersant, defoamer, cosolvent, deionized water, ammonia nertralizer are mixed by proportioning, mixed
Liquid；
2) mixed liquor is stirred into mixing under high speed dispersion agent, mixing speed is 1000r/min-1500r/min, during stirring
Between 0.3-0.7h, obtain stir liquid；
3) stirring liquid is inserted in horizontal sand mill, bead mill is handled 3-5 times, aqueous white slurry is made.
Described defoamer includes wooden 2~4 parts of triethanolamine, 2~4 parts of triisopropanolamine and ethylene glycol 3~7 by weight
Part.
The ammonia nertralizer is formic acid or acetic acid.
Described defoamer by weight include 2~4 parts of polyoxyethylene polyoxy propyl alcohol amidogen ether, have 1-3 parts of silicone emulsion and
2~4 parts of high-carbon polyol fatty acid.
Described coagulator is that calcium chloride, Arabic gum, ethanol and concentration are that 50% coal acid solution is mixed.
Viscosity foot of the invention, intensity is high, and rate of drying is fast, it is not easy to drop.The defoamer of the present invention not only has efficient
Froth breaking effect, improve the uniformity, and play paint vehicle rapid draing and meanwhile strengthen paint vehicle dry after intensity and hardness purpose,
Thickener in the present invention can also strengthen paint vehicle bond and the intensity of itself, be encounter hard object also will not be broken
It is rotten.The preparation method of the present invention makes by milling, emulsification and under specific temperature, time, and paint vehicle fineness, the uniformity are high,
Be conducive to improving the performance of product.
1st, aqueous paint vehicle economy of the invention, durable, especially this aqueous paint vehicle uses water as solvent and decentralized medium,
It is diluted with water and can be used, almost pollution-free to air, it is to avoid the poisonous and harmful property of organic solvent, environmental protection, energy-conservation is strong
Health；
2nd, aqueous paint vehicle of the invention is by the use of aqueous saturated polyester resin as matrix resin, the paint film have hardness height,
The advantages of flexible, impact resistance, UV resistant；Aqueous white slurry in aqueous paint vehicle can be used for the paint for preparing different colours
Material, the paint vehicle gloss made is bright-coloured, and service life is long；
3rd, the preparation method step of paint vehicle of the invention is simple, short the time required to preparation process, is given birth to beneficial to large-scale industry
Production, application, and the aqueous paint vehicle environmental protection that the preparation method is prepared, can promote the steady of China's sports equipment industry
Step, sound development, strengthen the competitiveness of China's sports equipment.
The beneficial effects of the invention are as follows：Environmental Safety of the present invention, pollution-free, hardness is high, be not easy to scratch, and is easy to life
Production, service life is long.
Embodiment：
In order that technological means, creation new feature, reached purpose and effect that the present invention is realized are easy to understand, below
With reference to instantiation, the present invention is expanded on further.
Embodiment 1
A kind of sports equipment protects paint vehicle coating process, it is characterised in that：
(1) protection paint vehicle is sufficiently stirred for；Protection paint vehicle is prepared from by the component of following parts by weight meter：30 parts aqueous full
And polyester resin, 1 part of ammonia nertralizer, 4 parts of milky white adhesives, 0.2 part of beeswax, 0.2 part of defoamer, 0.3 part of thickener, 0.1 part of oil
Coke powder, 40 parts of aqueous white slurries, 18 parts of deionized waters；
(2) liquid after stirring is heated, its temperature is reached 20~30 DEG C；
(3) protection paint vehicle is sprayed on sports equipment, the coating thickness of protection paint vehicle is controlled at 10~100 μm；
(4) sports equipment is taken out, sprays coagulant solution, continue 2~5 minutes；
(5) sports equipment carried out after step (4) is dried or dried.
Thickener includes 6 parts of hydroxylmethyl cellulose, 2 parts of bentonite, 3 parts of apatite, 3 parts of sepiolite powder and corn by weight
1 part of starch.
A kind of sports equipment protects the preparation method of paint vehicle coating process
1) aqueous saturated polyester resin is added into container, is then stirred, progressively dripped while stirring with high speed dispersor
Ammonification nertralizer, after mixing speed is 500r/min, 3min, test mixing liquid pH value stops stirring between 7.5, carries out
Next step is operated；
2) the whole millings of solid material are handled, then all solid materials is added progress breast is sufficiently mixed in container
Change is handled, 60 DEG C of emulsifying temperature during emulsification, emulsification stirring speed 2000r/min, emulsification times 15min；
3) aqueous white slurry and milky white adhesive are added into container again, deionized water is eventually adding, continues scattered 10 minutes, surveys
PH value is tried between 7.5, that is, paint vehicle is made.
Aqueous white slurry is to be prepared from according to the following steps：
1) titanium dioxide, dispersant, defoamer, cosolvent, deionized water, ammonia nertralizer are mixed by proportioning, mixed
Liquid；
2) mixed liquor is stirred into mixing under high speed dispersion agent, mixing speed is 1000r/min, mixing time 0.3h, is obtained
To stirring liquid；
3) stirring liquid is inserted in horizontal sand mill, bead mill is handled 3 times, aqueous white slurry is made.
Defoamer includes 3 parts of wooden 2 parts of triethanolamine, 2 parts of triisopropanolamine and ethylene glycol by weight.
Ammonia nertralizer is formic acid.
Defoamer includes 2 parts of polyoxyethylene polyoxy propyl alcohol amidogen ether, has 1 part of silicone emulsion and high-carbon polyol fatty acid by weight
2 parts.
Coagulator is that calcium chloride, Arabic gum, ethanol and concentration are that 50% coal acid solution is mixed.
Embodiment two
The technical problems to be solved by the invention are realized using following technical scheme：
A kind of sports equipment protects paint vehicle coating process, it is characterised in that：
(1) protection paint vehicle is sufficiently stirred for；Protection paint vehicle is prepared from by the component of following parts by weight meter：35 parts aqueous full
And polyester resin, 1.5 parts of ammonia nertralizers, 4.5 parts of milky white adhesives, 0.3 part of beeswax, 0.25 part of defoamer, 0.35 part of thickener, 0.15
Part petroleum coke powder, 45 parts of aqueous whites slurries, 21 parts of deionized waters；
(2) liquid after stirring is heated, its temperature is reached 20~30 DEG C；
(3) protection paint vehicle is sprayed on sports equipment, the coating thickness of protection paint vehicle is controlled at 10~100 μm；
(4) sports equipment is taken out, sprays coagulant solution, continue 2~5 minutes；
(5) sports equipment carried out after step (4) is dried or dried.
Thickener by weight include 7 parts of hydroxylmethyl cellulose, 3 parts of bentonite, 3.5 parts of apatite, 3.5 parts of sepiolite powder and
1.5 parts of cornstarch.
A kind of sports equipment protects the preparation method of paint vehicle coating process,
1) aqueous saturated polyester resin is added into container, is then stirred, progressively dripped while stirring with high speed dispersor
Ammonification nertralizer, after mixing speed is 700r/min, 4min, test mixing liquid pH value stops stirring, under progress between 8
Single stepping；
2) the whole millings of solid material are handled, then all solid materials is added progress breast is sufficiently mixed in container
Change is handled, 60 DEG C of emulsifying temperature during emulsification, emulsification stirring speed 2000r/min, emulsification times 15min；
3) aqueous white slurry and milky white adhesive are added into container again, deionized water is eventually adding, continues scattered 13 minutes, surveys
PH value is tried between 8, that is, paint vehicle is made.
Aqueous white slurry is to be prepared from according to the following steps：
1) titanium dioxide, dispersant, defoamer, cosolvent, deionized water, ammonia nertralizer are mixed by proportioning, mixed
Liquid；
2) mixed liquor is stirred into mixing under high speed dispersion agent, mixing speed is 1250r/min, mixing time 0.5h, is obtained
To stirring liquid；
3) stirring liquid is inserted in horizontal sand mill, bead mill is handled 4 times, aqueous white slurry is made.
Defoamer includes 5 parts of wooden 3 parts of triethanolamine, 3 parts of triisopropanolamine and ethylene glycol by weight.
Ammonia nertralizer is acetic acid.
Defoamer includes 3 parts of polyoxyethylene polyoxy propyl alcohol amidogen ether, has 2 parts of silicone emulsion and high-carbon polyol fatty acid by weight
3 parts.
Coagulator is that calcium chloride, Arabic gum, ethanol and concentration are that 50% coal acid solution is mixed.
Embodiment 3
The technical problems to be solved by the invention are realized using following technical scheme：
A kind of sports equipment protects paint vehicle coating process, it is characterised in that：
(1) protection paint vehicle is sufficiently stirred for；Protection paint vehicle is prepared from by the component of following parts by weight meter：40 parts aqueous full
And polyester resin, 2 parts of ammonia nertralizers, 5 parts of milky white adhesives, 0.4 part of beeswax, 0.3 part of defoamer, 0.4 part of thickener, 0.2 part of oil
Coke powder, 50 parts of aqueous white slurries, 25 parts of deionized waters；
(2) liquid after stirring is heated, its temperature is reached 20~30 DEG C；
(3) protection paint vehicle is sprayed on sports equipment, the coating thickness of protection paint vehicle is controlled at 10~100 μm；
(4) sports equipment is taken out, sprays coagulant solution, continue 2~5 minutes；
(5) sports equipment carried out after step (4) is dried or dried.
Thickener includes 8 parts of hydroxylmethyl cellulose, 4 parts of bentonite, 4 parts of apatite, 4 parts of sepiolite powder and corn by weight
2 parts of starch.
A kind of sports equipment protects the preparation method of paint vehicle coating process,
1) 25 parts of aqueous saturated polyester resins are added into containers, are then stirred with high speed dispersor, while stirring by
Ammonia nertralizer is added dropwise in step, after mixing speed is 900r/min, 5min, and test mixing liquid pH value stops stirring between 8.5,
Carry out next step operation；
2) the whole millings of solid material are handled, then all solid materials is added progress breast is sufficiently mixed in container
Change is handled, 60 DEG C of emulsifying temperature during emulsification, emulsification stirring speed 2000r/min, emulsification times 15min；
3) aqueous white slurry and milky white adhesive are added into container again, deionized water is eventually adding, continues scattered 15 minutes, surveys
PH value is tried between 8.5, that is, paint vehicle is made.
Aqueous white slurry is to be prepared from according to the following steps：
1) titanium dioxide, dispersant, defoamer, cosolvent, deionized water, ammonia nertralizer are mixed by proportioning, mixed
Liquid；
2) mixed liquor is stirred into mixing under high speed dispersion agent, mixing speed is 1500r/min, mixing time 0.3-
0.7h, obtains stirring liquid；
3) stirring liquid is inserted in horizontal sand mill, bead mill is handled 5 times, aqueous white slurry is made.
Defoamer includes 7 parts of wooden 4 parts of triethanolamine, 4 parts of triisopropanolamine and ethylene glycol by weight.
Ammonia nertralizer is formic acid or acetic acid.
Defoamer includes 4 parts of polyoxyethylene polyoxy propyl alcohol amidogen ether, has 3 parts of silicone emulsion and high-carbon polyol fatty acid by weight
4 parts.
Coagulator is that calcium chloride, Arabic gum, ethanol and concentration are that 50% coal acid solution is mixed.
Experimental data is obtained to embodiments of the invention progress experiment detection as shown in the table：
| Inspection content | Embodiment 1 | Embodiment 2 | Embodiment 3 |
| Amount of solid content (%) | 68 | 72 | 65 |
| Paint vehicle viscosity (s) | 149 | 150 | 152 |
| PH value | 7.9 | 7.8 | 7.8 |
| Coating dry film thickness (μm) | 25 | 26 | 23 |
| Fineness (μm) | 18 | 20 | 19 |
| Surface gloss | 91 | 95 | 89 |
| Aberration | 0.3 | 0.2 | 0.4 |
The general principle and principal character and advantages of the present invention of the present invention has been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the simply explanation described in above-described embodiment and specification is originally
The principle of invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (8)
1. a kind of sports equipment protects paint vehicle coating process, it is characterised in that：
(1) protection paint vehicle is sufficiently stirred for；Described protection paint vehicle is prepared from by the component of following parts by weight meter：30~40 parts
Aqueous saturated polyester resin, 1~2 part of ammonia nertralizer, 4~5 parts of milky white adhesives, 0.2~0.4 part of beeswax, 0.2~0.3 part of defoamer,
0.3~0.4 part of thickener, 0.1~0.2 part of petroleum coke powder, 40~50 parts of aqueous white slurries, 18~25 parts of deionized waters；
(2) liquid after stirring is heated, its temperature is reached 20~30 DEG C；
(3) protection paint vehicle is sprayed on sports equipment, the coating thickness of protection paint vehicle is controlled at 10~100 μm；
(4) sports equipment is taken out, sprays coagulant solution, continue 2~5 minutes；
(5) sports equipment carried out after step (4) is dried or dried.
2. a kind of sports equipment protection paint vehicle coating process according to claim 1, it is characterised in that：Described thickener
Include 6-8 parts of hydroxylmethyl cellulose, 2~4 parts of bentonite, 3~4 parts of apatite, 3~4 parts of sepiolite powder and corn by weight to form sediment
1~2 part of powder.
3. a kind of sports equipment protection paint vehicle coating process according to claim 1, it is characterised in that：
1) aqueous saturated polyester resin is added into container, is then stirred with high speed dispersor, ammonia is progressively added dropwise while stirring
Nertralizer, after mixing speed is 500r/min-900r/min, 3-5min, test mixing liquid pH value stops between 7.5-8.5
Only stir, carry out next step operation；
2) the whole millings of solid material are handled, then all solid materials is added and are sufficiently mixed in container at progress emulsification
Reason, 60 DEG C of emulsifying temperature during emulsification, emulsification stirring speed 2000r/min, emulsification times 15min；
3) aqueous white slurry and milky white adhesive are added into container again, deionized water is eventually adding, continues scattered 10-15 minutes, surveys
PH value is tried between 7.5-8.5, that is, paint vehicle is made.
4. a kind of sports equipment protection paint vehicle coating process according to claim 1, it is characterised in that the aqueous white
Slurry is to be prepared from according to the following steps：
1) titanium dioxide, dispersant, defoamer, cosolvent, deionized water, ammonia nertralizer are mixed by proportioning, obtains mixed liquor；
2) mixed liquor is stirred into mixing under high speed dispersion agent, mixing speed is 1000r/min-1500r/min, mixing time
0.3-0.7h, obtains stirring liquid；
3) stirring liquid is inserted in horizontal sand mill, bead mill is handled 3-5 times, aqueous white slurry is made.
5. a kind of sports equipment protection paint vehicle coating process according to claim 1, it is characterised in that：Described defoamer
Include 3~7 parts of wooden 2~4 parts of triethanolamine, 2~4 parts of triisopropanolamine and ethylene glycol by weight.
6. a kind of sports equipment protection paint vehicle coating process according to claim 1, it is characterised in that：The ammonia nertralizer
For formic acid or acetic acid.
7. a kind of sports equipment protection paint vehicle coating process according to claim 1, it is characterised in that：Described defoamer
Include 2~4 parts of polyoxyethylene polyoxy propyl alcohol amidogen ether by weight, have 2~4 parts of 1-3 parts of silicone emulsion and high-carbon polyol fatty acid.
8. a kind of sports equipment protection paint vehicle coating process according to claim 1, it is characterised in that：Described coagulator
It is that 50% coal acid solution is mixed for calcium chloride, Arabic gum, ethanol and concentration.