CN107099064A - A kind of solid tyre rubber and preparation method - Google Patents
A kind of solid tyre rubber and preparation method Download PDFInfo
- Publication number
- CN107099064A CN107099064A CN201710410068.0A CN201710410068A CN107099064A CN 107099064 A CN107099064 A CN 107099064A CN 201710410068 A CN201710410068 A CN 201710410068A CN 107099064 A CN107099064 A CN 107099064A
- Authority
- CN
- China
- Prior art keywords
- parts
- solid tyre
- rubber
- preparation
- tyre rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of solid tyre rubber and preparation method, the rubber includes following component:Natural rubber, nitrile rubber, polybutadiene, hydroxy-ethyl acrylate, graphene, nano titanium oxide, stearic acid, age resistor, vulcanizing agent, coupling agent, filler.Preparation method includes:First polymer is placed in banbury and plasticated, graphene, hydroxy-ethyl acrylate, silane coupler is then added and continues to knead, then sequentially add after remaining ingredient completes mixing and carry out dumping, obtain the solid tyre rubber.The rubber not only has preferable molding effect, and also with the performance such as preferable wear-resisting, anticorrosion, weather-proof, for the preparation of solid tyre, guarantee is provided for the safe handling of automobile.
Description
Technical field
The present invention relates to solid tyre technical field, and in particular to a kind of solid tyre rubber and preparation method.
Background technology
Tire is as the key fitment of automobile, and it is inevitable to wear and tear in use, puncture rear gas leakage, is particularly
Occur tyre explosion situation in the automobile run at high speed, easily cause the major accident of car crash.Therefore each production man is to wheel
The security of tire, the feature of environmental protection, energy saving requirement are being improved constantly.In order to prevent tire from exploding, existing automobile all generally makes
Tubeless vehicle wheel is used, tubeless vehicle wheel is progressively promoted the use of in load-carrying vehicle national requirements.Solid tyre is general all negative in height
Used under lotus, it is desirable to which sizing material there are enough resistance to pressures and wearability, with sufficiently high stress at definite elongation, higher hardness, low
Permanent deformation and good wearability, and continuing to develop with society, people get over to the multi-functional of tire, high security requirement
Come higher, and determine that the rubber of tyre performance turns into the emphasis of research, choose suitable rubber and be modified processing to reach city
Field demand is significant.
Therefore, researching and developing one kind has preferable molding effect, is had by the tyre rubber with preferable performance
It is significant, the demand of existing market is also complied with, with preferable application prospect.
The content of the invention
For defect of the prior art, it is an object of the invention to provide a kind of solid tyre rubber and preparation method,
The rubber not only has preferable molding effect, also with the performance such as preferable wear-resisting, anticorrosion, weather-proof, for reality
The preparation of heart tire, guarantee is provided for the safe handling of automobile.
The present invention solves technical problem and adopted the following technical scheme that:
The present invention relates to each raw material of a kind of solid tyre rubber, including following parts by weight:35 ~ 50 parts of natural rubber, butyronitrile
5 ~ 12 parts of rubber, 10 ~ 20 parts of polybutadiene, 9 ~ 18 parts of hydroxy-ethyl acrylate, 2 ~ 7 parts of graphene, 5 ~ 8 parts of nano titanium oxide,
6 ~ 13 parts of stearic acid, 3 ~ 9 parts of age resistor, 5 ~ 10 parts of vulcanizing agent, 6 ~ 10 parts of coupling agent, 15 ~ 23 parts of filler.
Preferably, 46 parts of the natural rubber, 8 parts of nitrile rubber, 15 parts of polybutadiene, 17 parts of hydroxy-ethyl acrylate, stone
Black 5 parts of alkene, 6 parts of nano titanium oxide, 10 parts of stearic acid, 6 parts of age resistor, 8 parts of vulcanizing agent, 7 parts of coupling agent, 18 parts of filler.
Preferably, the filler is talcum powder, the mixture of high viscous Concave-convex clay rod, and wherein both weight ratios are
1:0.8~1.2.
Preferably, natural attapulgite clay is purified, obtained after thermal activation by the high viscous attapulgite
Product.
Preferably, the coupling agent is silane coupler.
The invention further relates to a kind of method for preparing solid tyre rubber, comprise the following steps:
(1)It is the close of 70 ~ 85 turns/min to weigh natural rubber, nitrile rubber and polybutadiene respectively to be added to rotating speed according to proportioning
In mill, plasticate 80 ~ 100s under the conditions of 58 ~ 63 DEG C, obtains mixture a1;
(2)Graphene, hydroxy-ethyl acrylate, silane coupler are added into mixture a1 to continue to knead 80 ~ 90 seconds, are then added again
Enter nano titanium oxide, age resistor and filler and carry out mixing 80 ~ 90 seconds, room temperature is cooled in air;
(3)By step(2)In elastomeric compound be added in banbury, add vulcanizing agent, stearic acid, knead 50 ~ 55 seconds, carry stone roller
5 ~ 10 seconds, ram was kneaded 35 ~ 45 seconds, is carried out dumping after completing mixing, is obtained the solid tyre rubber.
Preferably, the step(2)Middle melting temperature is 110 ~ 120 DEG C.
Preferably, the step(2)In to put forward the elastomeric compound temperature before stone roller be 110 ~ 120 DEG C, the melting temperature after ram is
130~140℃。
Preferably, the step(2)The preparation method of high viscous Concave-convex clay rod is in middle filler:
Take natural attapulgite to be crushed and cross 200 mesh sieves, add the water of 10 ~ 20 times of attapulgite quality, stirring forms outstanding
Mud scum is starched, and takes upper suspension centrifugal treating 10min in 3000 turns/min centrifuge, is filtered by vacuum;By filtration cakes torrefaction simultaneously
800 DEG C ~ 900 DEG C of Muffle 3 ~ 4h of kiln roasting is placed in, cools down, produces the high viscous Concave-convex clay rod.
Compared with prior art, the present invention has following beneficial effect:
(1)Solid tyre rubber of the present invention, not only with preferable molding effect, also with preferably wear-resisting, anti-
The performance such as burn into is weather-proof, for the preparation of solid tyre, guarantee is provided for the safe handling of automobile.
(2)High viscous Concave-convex clay rod is added with solid tyre rubber of the present invention, with preferable viscosity
And plasticity, the bonding uniformity between each raw material can be effectively improved, the mechanical property of rubber is improved, is applied to wheel
Viviparity production, can effectively improve the safety in utilization of tire.
(3)Graphene composition is added with solid tyre rubber of the present invention, because graphene has lamella conjugation
Structure, is layering to form the anticorrosive coat of densification, can effectively suppress infiltration and infiltration of the water to coating;Further, since graphite
The excellent mechanical property of alkene and electromagnetic property so that modified rubber polymer not only has preferable anticorrosion, permeation-proof
Water is acted on, and also with preferable wear-resisting, scraping and wiping resistance performance and preferable effectiveness, the addition of graphene is efficiently solved
The problem of white carbon packing material accumulation of static electricity so that the tire prepared using the present invention has preferably antistatic and resistance to
Grind the effect of scratch-resistant.
(4)The preparation technology of solid tyre rubber of the present invention is simple, mild condition, is adapted to industrialization promotion life
Production.
Embodiment
With reference to specific embodiment, the present invention is expanded on further.These embodiments be merely to illustrate the present invention and without
In limitation the scope of the present invention.The experimental method of unreceipted actual conditions in the following example, generally according to normal condition, for example
Sambrook equimoleculars are cloned:Laboratory manual(New York:Cold Spring Harbor Laboratory Press,
1989)Described in condition, or according to the condition proposed by manufacturer.
Embodiment 1:
A kind of solid tyre rubber and preparation method of the preferred embodiment of the present invention;
The solid tyre rubber, is prepared from by each raw material of following parts by weight:
46 parts of natural rubber, 8 parts of nitrile rubber, 15 parts of polybutadiene, 17 parts of hydroxy-ethyl acrylate, 5 parts of graphene, nano-silica
Change 6 parts of titanium, 10 parts of stearic acid, 6 parts of age resistor, 8 parts of vulcanizing agent, 7 parts of coupling agent, 18 parts of filler.
The filler is talcum powder, the mixture of high viscous Concave-convex clay rod, and wherein both weight ratios are 1:0.9.
The high viscous attapulgite is the product for purifying natural attapulgite clay, obtaining after thermal activation.
The coupling agent is silane coupler.
The method that the present invention prepares solid tyre rubber, comprises the following steps:
(1)Natural rubber, nitrile rubber and polybutadiene are weighed respectively according to proportioning is added to the banburying that rotating speed is 80 turns/min
In machine, plasticate 90s under the conditions of 60 DEG C, obtains mixture a1;
(2)Graphene, hydroxy-ethyl acrylate, silane coupler are added into mixture a1 to continue to knead 90s, are then added and are received
Rice titanium dioxide, age resistor and filler carry out being cooled to room temperature in mixing 90s, air;
(3)By step(2)In elastomeric compound be added in banbury, add vulcanizing agent, stearic acid, knead 50s, carry stone roller 10s,
Ram kneads 40s, carries out dumping after completing mixing, obtains the solid tyre rubber.
Step(2)Middle melting temperature is 120 DEG C.
Step(2)In to put forward the elastomeric compound temperature before stone roller be 120 DEG C, melting temperature after ram is 135 DEG C.
Step(2)The preparation method of high viscous Concave-convex clay rod is in middle filler:
Take natural attapulgite to be crushed and cross 200 mesh sieves, add the water of 16 times of attapulgite quality, stirring forms suspension mud
Slurry, takes upper suspension centrifugal treating 10min in 3000 turns/min centrifuge, is filtered by vacuum;Filtration cakes torrefaction is placed in
800 DEG C of Muffle kiln roasting 4h, cooling, produces the high viscous Concave-convex clay rod.
Embodiment 2:
A kind of solid tyre rubber and preparation method of the preferred embodiment of the present invention;
The solid tyre rubber, is prepared from by each raw material of following parts by weight:
35 parts of natural rubber, 5 parts of nitrile rubber, 10 parts of polybutadiene, 9 parts of hydroxy-ethyl acrylate, 2 parts of graphene, nano-silica
Change 5 parts of titanium, 6 parts of stearic acid, 3 parts of age resistor, 5 parts of vulcanizing agent, 6 parts of coupling agent, 15 parts of filler.
The filler is talcum powder, the mixture of high viscous Concave-convex clay rod, and wherein both weight ratios are 1:0.8.
The high viscous attapulgite is the product for purifying natural attapulgite clay, obtaining after thermal activation.
The coupling agent is silane coupler.
The method that the present invention prepares solid tyre rubber, comprises the following steps:
(1)Natural rubber, nitrile rubber and polybutadiene are weighed respectively according to proportioning is added to the banburying that rotating speed is 70 turns/min
In machine, plasticate 100s under the conditions of 58 DEG C, obtains mixture a1;
(2)Graphene, hydroxy-ethyl acrylate, silane coupler are added into mixture a1 to continue to knead 80 seconds, are then added
Nano titanium oxide, age resistor and filler carry out mixing 80 seconds, and room temperature is cooled in air;
(3)By step(2)In elastomeric compound be added in banbury, add vulcanizing agent, stearic acid, knead 50 seconds, carry stone roller 5
Second, ram is kneaded 35 seconds, is carried out dumping after completing mixing, is obtained the solid tyre rubber.
Step(2)Middle melting temperature is 110 DEG C.
Step(2)In to put forward the elastomeric compound temperature before stone roller be 110 DEG C, melting temperature after ram is 130 DEG C.
Step(2)The preparation method of high viscous Concave-convex clay rod is in middle filler:
Take natural attapulgite to be crushed and cross 200 mesh sieves, add the water of 10 times of attapulgite quality, stirring forms suspension mud
Slurry, takes upper suspension centrifugal treating 10min in 3000 turns/min centrifuge, is filtered by vacuum;Filtration cakes torrefaction is placed in
800 DEG C of Muffle kiln roasting 4h, cooling, produces the high viscous Concave-convex clay rod.
Embodiment 3:
A kind of solid tyre rubber and preparation method of the preferred embodiment of the present invention;
The solid tyre rubber, is prepared from by each raw material of following parts by weight:
50 parts of natural rubber, 12 parts of nitrile rubber, 20 parts of polybutadiene, 18 parts of hydroxy-ethyl acrylate, part, nanometer two of graphene 7
8 parts of titanium oxide, 13 parts of stearic acid, 9 parts of age resistor, 10 parts of vulcanizing agent, 10 parts of coupling agent, 23 parts of filler.
The filler is talcum powder, the mixture of high viscous Concave-convex clay rod, and wherein both weight ratios are 1:1.2.
The high viscous attapulgite is the product for purifying natural attapulgite clay, obtaining after thermal activation.
The coupling agent is silane coupler.
The method that the present invention prepares solid tyre rubber, comprises the following steps:
(1)Natural rubber, nitrile rubber and polybutadiene are weighed respectively according to proportioning is added to the banburying that rotating speed is 85 turns/min
In machine, plasticate 80s under the conditions of 63 DEG C, obtains mixture a1;
(2)Graphene, hydroxy-ethyl acrylate, silane coupler are added into mixture a1 to continue to knead 90 seconds, are then added
Nano titanium oxide, age resistor and filler carry out mixing 90 seconds, and room temperature is cooled in air;
(3)By step(2)In elastomeric compound be added in banbury, add vulcanizing agent, stearic acid, knead 55 seconds, carry stone roller 10
Second, ram is kneaded 45 seconds, is carried out dumping after completing mixing, is obtained the solid tyre rubber.
Step(2)Middle melting temperature is 120 DEG C.
Step(2)In to put forward the elastomeric compound temperature before stone roller be 120 DEG C, melting temperature after ram is 140 DEG C.
Step(2)The preparation method of high viscous Concave-convex clay rod is in middle filler:
Take natural attapulgite to be crushed and cross 200 mesh sieves, add the water of 20 times of attapulgite quality, stirring forms suspension mud
Slurry, takes upper suspension centrifugal treating 10min in 3000 turns/min centrifuge, is filtered by vacuum;Filtration cakes torrefaction is placed in
900 DEG C of Muffle kiln roasting 3h, cooling, produces the high viscous Concave-convex clay rod.
In summary, not only with preferable molding effect, also with the usability such as preferable wear-resisting, anticorrosion, weather-proof
Can, for the preparation of solid tyre, guarantee is provided for the safe handling of automobile.The system of solid tyre rubber of the present invention
Standby technique is simple, mild condition, is adapted to industrialization promotion production.
The specific embodiment of the present invention is described above.It is to be appreciated that the invention is not limited in above-mentioned
Particular implementation, those skilled in the art can make various deformations or amendments within the scope of the claims, this not shadow
Ring the substantive content of the present invention.
Claims (9)
1. a kind of solid tyre rubber, it is characterised in that:Each raw material including following parts by weight:35 ~ 50 parts of natural rubber, fourth
5 ~ 12 parts of nitrile rubber, 10 ~ 20 parts of polybutadiene, 9 ~ 18 parts of hydroxy-ethyl acrylate, 2 ~ 7 parts of graphene, nano titanium oxide 5 ~ 8
Part, 6 ~ 13 parts of stearic acid, 3 ~ 9 parts of age resistor, 5 ~ 10 parts of vulcanizing agent, 6 ~ 10 parts of coupling agent, 15 ~ 23 parts of filler.
2. solid tyre rubber according to claim 1, it is characterised in that:46 parts of the natural rubber, nitrile rubber 8
Part, 15 parts of polybutadiene, 17 parts of hydroxy-ethyl acrylate, 5 parts of graphene, 6 parts of nano titanium oxide, 10 parts of stearic acid, age resistor 6
Part, 8 parts of vulcanizing agent, 7 parts of coupling agent, 18 parts of filler.
3. solid tyre rubber according to claim 1, it is characterised in that:The filler is talcum powder, height is viscous recessed
The mixture of convex rod stone clay, wherein both weight ratios are 1:0.8~1.2.
4. solid tyre rubber according to claim 1, it is characterised in that:The high viscous attapulgite is will be natural recessed
The product that convex rod stone clay is purified, obtained after thermal activation.
5. solid tyre rubber according to claim 1, it is characterised in that:The coupling agent is silane coupler.
6. the method that one kind prepares the solid tyre rubber as described in any one of claim 1 ~ 5, it is characterised in that:Including such as
Lower step:
(1)It is the close of 70 ~ 85 turns/min to weigh natural rubber, nitrile rubber and polybutadiene respectively to be added to rotating speed according to proportioning
In mill, plasticate 80 ~ 100s under the conditions of 58 ~ 63 DEG C, obtains mixture a1;
(2)Graphene, hydroxy-ethyl acrylate, silane coupler are added into mixture a1 to continue to knead 80 ~ 90 seconds, are then added again
Enter nano titanium oxide, age resistor and filler and carry out mixing 80 ~ 90 seconds, room temperature is cooled in air;
(3)By step(2)In elastomeric compound be added in banbury, add vulcanizing agent, stearic acid, knead 50 ~ 55 seconds, carry stone roller
5 ~ 10 seconds, ram was kneaded 35 ~ 45 seconds, is carried out dumping after completing mixing, is obtained the solid tyre rubber.
7. the preparation method of solid tyre rubber according to claim 6, it is characterised in that:The step(2)In mix
It is 110 ~ 120 DEG C to refine temperature.
8. the preparation method of solid tyre rubber according to claim 6, it is characterised in that:The step(2)In carry
Elastomeric compound temperature before stone roller is 110 ~ 120 DEG C, and the melting temperature after ram is 130 ~ 140 DEG C.
9. the preparation method of solid tyre rubber according to claim 6, it is characterised in that:The step(2)In fill out
The preparation method for filling high viscous Concave-convex clay rod in agent is:
Take natural attapulgite to be crushed and cross 200 mesh sieves, add the water of 10 ~ 20 times of attapulgite quality, stirring forms outstanding
Mud scum is starched, and takes upper suspension centrifugal treating 10min in 3000 turns/min centrifuge, is filtered by vacuum;By filtration cakes torrefaction simultaneously
800 DEG C ~ 900 DEG C of Muffle 3 ~ 4h of kiln roasting is placed in, cools down, produces the high viscous Concave-convex clay rod.