CN107099069A - A kind of anti-static and abrasion-resistant solid tyre fetal rhythm and preparation method - Google Patents
A kind of anti-static and abrasion-resistant solid tyre fetal rhythm and preparation method Download PDFInfo
- Publication number
- CN107099069A CN107099069A CN201710410080.1A CN201710410080A CN107099069A CN 107099069 A CN107099069 A CN 107099069A CN 201710410080 A CN201710410080 A CN 201710410080A CN 107099069 A CN107099069 A CN 107099069A
- Authority
- CN
- China
- Prior art keywords
- parts
- fetal rhythm
- solid tyre
- abrasion
- static
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of anti-static and abrasion-resistant solid tyre fetal rhythm and preparation method, the tire includes following component:Nitrile rubber, butadiene-styrene rubber, natural rubber, acrylic resin, silane coupler, graphene, white carbon, carbon black, glass fibre, bamboo-carbon fibre, nano silicon, activated zinc oxide, age resistor, accelerator, vulcanizing agent, filler.Preparation method includes:It will first be kneaded in rubber raw materials banbury, remaining ingredient then added in batches and is kneaded, dumping is carried out after completing mixing, then pours into mould to be molded, obtain forming tire;Polished at normal temperatures, remove foreign matter, produce the solid tyre fetal rhythm.The tire fetal rhythm not only has preferable anti-wear performance, substantially increases the service life of tire, also with preferable antistatic effect, guarantee is provided for the safe handling of automobile.
Description
Technical field
The present invention relates to solid tyre technical field, and in particular to a kind of anti-static and abrasion-resistant solid tyre fetal rhythm and preparation side
Method.
Background technology
Tire is as the key fitment of automobile, and it is inevitable to wear and tear in use, puncture rear gas leakage, is particularly
Occur tyre explosion situation in the automobile run at high speed, easily cause the major accident of car crash.Therefore each production man is to wheel
The security of tire, the feature of environmental protection, energy saving requirement are being improved constantly.In order to prevent tire from exploding, existing automobile all generally makes
Tubeless vehicle wheel is used, tubeless vehicle wheel is progressively promoted the use of in load-carrying vehicle national requirements.Solid tyre is general all negative in height
Used under lotus, it is desirable to which sizing material there are enough resistance to pressures and wearability, with sufficiently high stress at definite elongation, higher hardness, low
Permanent deformation and good wearability, and continuing to develop with society, people get over to the multi-functional of tire, high security requirement
Come higher, wherein the antistatic behaviour of tire turns into one of emphasis of concern, effectively improves the antistatic behaviour and electromagnetism of tire
Shielding action is significant for the safe handling of automobile.
Therefore, a kind of solid tyre that there is preferable anti-wear performance, there is preferable antistatic property again is researched and developed
It is significant, the demand of existing market is also complied with, with preferable application prospect.
The content of the invention
For defect of the prior art, it is an object of the invention to provide a kind of anti-static and abrasion-resistant solid tyre fetal rhythm and system
Preparation Method, the tire fetal rhythm not only has preferable anti-wear performance, the service life of tire is substantially increased, also with preferable
Antistatic effect, provide guarantee for the safe handling of automobile.
The present invention solves technical problem and adopted the following technical scheme that:
The present invention relates to each raw material of a kind of anti-static and abrasion-resistant solid tyre fetal rhythm, including following parts by weight:Nitrile rubber 30 ~ 50
Part, 20 ~ 40 parts of butadiene-styrene rubber, 25 ~ 50 parts of natural rubber, 30 ~ 45 parts of acrylic resin, 10 ~ 20 parts of silane coupler, graphene
3 ~ 10 parts, 33 ~ 46 parts of white carbon, 5 ~ 12 parts of carbon black, 8 ~ 16 parts of glass fibre, 11 ~ 15 parts of bamboo-carbon fibre, nano silicon 14
~ 22 parts, 10 ~ 15 parts of activated zinc oxide, 6 ~ 9 parts of age resistor, 5 ~ 10 parts of accelerator, 8 ~ 13 parts of vulcanizing agent, 15 ~ 25 parts of filler.
Preferably, 45 parts of the nitrile rubber, 36 parts of butadiene-styrene rubber, 44 parts of natural rubber, 35 parts of acrylic resin, silane
16 parts of coupling agent, 8 parts of graphene, 40 parts of white carbon, 6 parts of carbon black, 12 parts of glass fibre, 14 parts of bamboo-carbon fibre, nanometer titanium dioxide
20 parts of silicon, 13 parts of activated zinc oxide, 8 parts of age resistor, 7 parts of accelerator, 10 parts of vulcanizing agent, 20 parts of filler.
Preferably, the filler is nano-calcium carbonate, high viscous Concave-convex clay rod, and wherein both weight ratios are 1:
0.5~1.5。
Preferably, natural attapulgite clay is purified, obtained after thermal activation by the high viscous attapulgite
Product.
The invention further relates to a kind of method for preparing anti-static and abrasion-resistant solid tyre fetal rhythm, comprise the following steps:
(1)Nitrile rubber, butadiene-styrene rubber, natural rubber are weighed respectively according to proportioning, and are placed on mixing 2 minutes in banbury
More than, then by bamboo-carbon fibre, white carbon, carbon black be added in banbury continue knead 30 ~ 40 seconds after, add graphene,
Acrylate, silane coupler continue to knead 80 ~ 90 seconds, then add zinc oxide, nano silicon, glass fibre, anti-
Old agent and filler carry out mixing 80 ~ 90 seconds, and room temperature is cooled in air;
(2)By step(1)In elastomeric compound be added in banbury, add accelerator, vulcanizing agent, knead 50 ~ 55 seconds, carry stone roller
5 ~ 10 seconds, ram was kneaded 35 ~ 45 seconds, is carried out dumping after completing mixing, then is poured into mould to be molded, obtain briquetting roller
Tire;(3)By step(2)Forming tire polished at normal temperatures, remove foreign matter, produce the solid tyre fetal rhythm.
Preferably, the step(1)Middle melting temperature is 120 ~ 130 DEG C.
Preferably, the step(2)In to put forward the elastomeric compound temperature before stone roller be 125 ~ 135 DEG C, the melting temperature after ram is
150~160℃。
Preferably, the step(2)The preparation method of high viscous Concave-convex clay rod is in middle filler:
Take natural attapulgite to be crushed and cross 200 mesh sieves, add the water of 10 ~ 20 times of attapulgite quality, stirring forms outstanding
Mud scum is starched, and takes upper suspension 5 ~ 10min of centrifugal treating in 3000 ~ 5000 turns/min centrifuge, is filtered by vacuum;By filter cake
The dry Muffle 3 ~ 4h of kiln roasting for being placed in 800 DEG C ~ 900 DEG C, cooling produces the high viscous Concave-convex clay rod.
Compared with prior art, the present invention has following beneficial effect:
(1)Anti-static and abrasion-resistant solid tyre fetal rhythm of the present invention, not only with preferable anti-wear performance, substantially increases wheel
The service life of tire, also acts on preferable antistatic effect and electrostatic screen, guarantee is provided for the safe handling of automobile.
(2)In anti-static and abrasion-resistant solid tyre fetal rhythm of the present invention be added with high viscous Concave-convex clay rod, with compared with
Good viscosity and plasticity, can effectively improve the bonding uniformity between each raw material, improve the fastness of tire.
(3)Graphene composition is added with anti-static and abrasion-resistant solid tyre fetal rhythm of the present invention, because graphene has
Lamella conjugated structure, is layering to form the anticorrosive coat of densification, can effectively suppress infiltration and infiltration of the water to coating;In addition,
Due to the excellent mechanical property of graphene and electromagnetic property so that modified rubber polymer not only has preferable anti-corrosion
Erosion, anti-permeable effect, also with preferable wear-resisting, scraping and wiping resistance performance and preferable effectiveness, the addition of graphene is also
The problem of efficiently solving white carbon packing material accumulation of static electricity, improves the antistatic effect of tire.
(4)The preparation technology of anti-static and abrasion-resistant solid tyre fetal rhythm of the present invention is simple, mild condition, is adapted to industrialization
Promote production.
Embodiment
With reference to specific embodiment, the present invention is expanded on further.These embodiments be merely to illustrate the present invention and without
In limitation the scope of the present invention.The experimental method of unreceipted actual conditions in the following example, generally according to normal condition, for example
Sambrook equimoleculars are cloned:Laboratory manual(New York:Cold Spring Harbor Laboratory Press,
1989)Described in condition, or according to the condition proposed by manufacturer.
Embodiment 1:
A kind of anti-static and abrasion-resistant solid tyre fetal rhythm and preparation method of the preferred embodiment of the present invention;
The anti-static and abrasion-resistant solid tyre fetal rhythm, is prepared from by each raw material of following parts by weight:
45 parts of nitrile rubber, 36 parts of butadiene-styrene rubber, 44 parts of natural rubber, 35 parts of acrylic resin, 16 parts of silane coupler, graphite
8 parts of alkene, 40 parts of white carbon, 6 parts of carbon black, 12 parts of glass fibre, 14 parts of bamboo-carbon fibre, 20 parts of nano silicon, active oxidation
13 parts of zinc, 8 parts of age resistor, 7 parts of accelerator, 10 parts of vulcanizing agent, 20 parts of filler.
The filler is nano-calcium carbonate, high viscous Concave-convex clay rod, and wherein both weight ratios are 1:1.2.
The high viscous attapulgite is the product for purifying natural attapulgite clay, obtaining after thermal activation.
The method that the present invention prepares anti-static and abrasion-resistant solid tyre fetal rhythm, comprises the following steps:
(1)Nitrile rubber, butadiene-styrene rubber, natural rubber are weighed respectively according to proportioning, and are placed on mixing 2 minutes in banbury
More than, then bamboo-carbon fibre, white carbon, carbon black are added in banbury after continuing to knead 30 seconds, add graphene, propylene
Acid esters, silane coupler continue to knead 80 seconds, then add zinc oxide, nano silicon, glass fibre, age resistor and fill out
Fill agent and carry out mixing 80 seconds, room temperature is cooled in air;
(2)By step(1)In elastomeric compound be added in banbury, add accelerator, vulcanizing agent, knead 50 seconds, carry stone roller 10
Second, ram is kneaded 40 seconds, is carried out dumping after completing mixing, then is poured into mould to be molded, obtain forming tire;(3)Will
Step(2)Forming tire polished at normal temperatures, remove foreign matter, produce the solid tyre fetal rhythm.
Step(1)Middle melting temperature is 125 DEG C.
Step(2)In to put forward the elastomeric compound temperature before stone roller be 130 DEG C, melting temperature after ram is 150 DEG C.
Step(2)The preparation method of high viscous Concave-convex clay rod is in middle filler:
Take natural attapulgite to be crushed and cross 200 mesh sieves, add the water of 15 times of attapulgite quality, stirring forms suspension mud
Slurry, takes upper suspension centrifugal treating 10min in 4000 turns/min centrifuge, is filtered by vacuum;Filtration cakes torrefaction is placed in
800 DEG C of Muffle kiln roasting 4h, cooling, produces the high viscous Concave-convex clay rod.
Embodiment 2:
A kind of anti-static and abrasion-resistant solid tyre fetal rhythm and preparation method of the preferred embodiment of the present invention;
The anti-static and abrasion-resistant solid tyre fetal rhythm, is prepared from by each raw material of following parts by weight:
30 parts of nitrile rubber, 20 parts of butadiene-styrene rubber, 25 parts of natural rubber, 30 parts of acrylic resin, 10 parts of silane coupler, graphite
3 parts of alkene, 33 parts of white carbon, 5 parts of carbon black, 8 parts of glass fibre, 11 parts of bamboo-carbon fibre, 14 parts of nano silicon, activated zinc oxide
10 parts, 6 parts of age resistor, 5 parts of accelerator, 8 parts of vulcanizing agent, 15 parts of filler.
The filler is nano-calcium carbonate, high viscous Concave-convex clay rod, and wherein both weight ratios are 1:0.5.
The high viscous attapulgite is the product for purifying natural attapulgite clay, obtaining after thermal activation.
The method that the present invention prepares anti-static and abrasion-resistant solid tyre fetal rhythm, comprises the following steps:
(1)Nitrile rubber, butadiene-styrene rubber, natural rubber are weighed respectively according to proportioning, and are placed on mixing 2 minutes in banbury
More than, then bamboo-carbon fibre, white carbon, carbon black are added in banbury after continuing to knead 30 seconds, add graphene, propylene
Acid esters, silane coupler continue to knead 80 seconds, then add zinc oxide, nano silicon, glass fibre, age resistor and fill out
Fill agent and carry out mixing 80 seconds, room temperature is cooled in air;
(2)By step(1)In elastomeric compound be added in banbury, add accelerator, vulcanizing agent, knead 50 seconds, carry stone roller 5
Second, ram is kneaded 35 seconds, is carried out dumping after completing mixing, then is poured into mould to be molded, obtain forming tire;(3)Will
Step(2)Forming tire polished at normal temperatures, remove foreign matter, produce the solid tyre fetal rhythm.
Step(1)Middle melting temperature is 120 DEG C.
Step(2)In to put forward the elastomeric compound temperature before stone roller be 125 DEG C, melting temperature after ram is 150 DEG C.
Step(2)The preparation method of high viscous Concave-convex clay rod is in middle filler:
Take natural attapulgite to be crushed and cross 200 mesh sieves, add the water of 10 times of attapulgite quality, stirring forms suspension mud
Slurry, takes upper suspension centrifugal treating 5min in 3000 turns/min centrifuge, is filtered by vacuum;Filtration cakes torrefaction is placed in
800 DEG C of Muffle kiln roasting 4h, cooling, produces the high viscous Concave-convex clay rod.
Embodiment 3:
A kind of anti-static and abrasion-resistant solid tyre fetal rhythm and preparation method of the preferred embodiment of the present invention;
The anti-static and abrasion-resistant solid tyre fetal rhythm, is prepared from by each raw material of following parts by weight:
50 parts of nitrile rubber, 40 parts of butadiene-styrene rubber, 50 parts of natural rubber, 45 parts of acrylic resin, 20 parts of silane coupler, graphite
10 parts of alkene, 46 parts of white carbon, 12 parts of carbon black, 16 parts of glass fibre, 15 parts of bamboo-carbon fibre, 22 parts of nano silicon, active oxygen
Change 15 parts of zinc, 9 parts of age resistor, 10 parts of accelerator, 13 parts of vulcanizing agent, 25 parts of filler.
The filler is nano-calcium carbonate, high viscous Concave-convex clay rod, and wherein both weight ratios are 1: 1.5.
The high viscous attapulgite is the product for purifying natural attapulgite clay, obtaining after thermal activation.
The method that the present invention prepares anti-static and abrasion-resistant solid tyre fetal rhythm, comprises the following steps:
(1)Nitrile rubber, butadiene-styrene rubber, natural rubber are weighed respectively according to proportioning, and are placed on mixing 2 minutes in banbury
More than, then bamboo-carbon fibre, white carbon, carbon black are added in banbury after continuing to knead 40 seconds, add graphene, propylene
Acid esters, silane coupler continue to knead 90 seconds, then add zinc oxide, nano silicon, glass fibre, age resistor and fill out
Fill agent and carry out mixing 90 seconds, room temperature is cooled in air;
(2)By step(1)In elastomeric compound be added in banbury, add accelerator, vulcanizing agent, knead 55 seconds, carry stone roller 10
Second, ram is kneaded 45 seconds, is carried out dumping after completing mixing, then is poured into mould to be molded, obtain forming tire;(3)Will
Step(2)Forming tire polished at normal temperatures, remove foreign matter, produce the solid tyre fetal rhythm.
Step(1)Middle melting temperature is 130 DEG C.
Step(2)In to put forward the elastomeric compound temperature before stone roller be 135 DEG C, melting temperature after ram is 160 DEG C.
Step(2)The preparation method of high viscous Concave-convex clay rod is in middle filler:
Take natural attapulgite to be crushed and cross 200 mesh sieves, add the water of 20 times of attapulgite quality, stirring forms suspension mud
Slurry, takes upper suspension centrifugal treating 10min in 5000 turns/min centrifuge, is filtered by vacuum;Filtration cakes torrefaction is placed in
900 DEG C of Muffle kiln roasting 3h, cooling, produces the high viscous Concave-convex clay rod.
In summary, anti-static and abrasion-resistant solid tyre fetal rhythm of the present invention, not only with preferable anti-wear performance, greatly
The big service life for improving tire, also acts on preferable antistatic effect and electrostatic screen, is the safe handling of automobile
There is provided guarantee.The preparation technology of anti-static and abrasion-resistant solid tyre fetal rhythm of the present invention is simple, mild condition, is adapted to industrialization
Promote production.
The specific embodiment of the present invention is described above.It is to be appreciated that the invention is not limited in above-mentioned
Particular implementation, those skilled in the art can make various deformations or amendments within the scope of the claims, this not shadow
Ring the substantive content of the present invention.
Claims (8)
1. a kind of anti-static and abrasion-resistant solid tyre fetal rhythm, it is characterised in that:Each raw material including following parts by weight:Nitrile rubber 30
~ 50 parts, 20 ~ 40 parts of butadiene-styrene rubber, 25 ~ 50 parts of natural rubber, 30 ~ 45 parts of acrylic resin, 10 ~ 20 parts of silane coupler, stone
Black 3 ~ 10 parts of alkene, 33 ~ 46 parts of white carbon, 5 ~ 12 parts of carbon black, 8 ~ 16 parts of glass fibre, 11 ~ 15 parts of bamboo-carbon fibre, nanometer titanium dioxide
14 ~ 22 parts of silicon, 10 ~ 15 parts of activated zinc oxide, 6 ~ 9 parts of age resistor, 5 ~ 10 parts of accelerator, 8 ~ 13 parts of vulcanizing agent, filler 15 ~ 25
Part.
2. anti-static and abrasion-resistant solid tyre fetal rhythm according to claim 1, it is characterised in that:45 parts of the nitrile rubber,
36 parts of butadiene-styrene rubber, 44 parts of natural rubber, 35 parts of acrylic resin, 16 parts of silane coupler, 8 parts of graphene, 40 parts of white carbon,
6 parts of carbon black, 12 parts of glass fibre, 14 parts of bamboo-carbon fibre, 20 parts of nano silicon, 13 parts of activated zinc oxide, 8 parts of age resistor,
7 parts of accelerator, 10 parts of vulcanizing agent, 20 parts of filler.
3. anti-static and abrasion-resistant solid tyre fetal rhythm according to claim 1, it is characterised in that:The filler is nano-sized carbon
Sour calcium, high viscous Concave-convex clay rod, wherein both weight ratios are 1:0.5~1.5.
4. anti-static and abrasion-resistant solid tyre fetal rhythm according to claim 1, it is characterised in that:The height glues attapulgite
The product that natural attapulgite clay is purified, obtained after thermal activation.
5. the method that one kind prepares the anti-static and abrasion-resistant solid tyre fetal rhythm as described in any one of claim 1 ~ 4, its feature exists
In:Comprise the following steps:
(1)Nitrile rubber, butadiene-styrene rubber, natural rubber are weighed respectively according to proportioning, and are placed on mixing 2 minutes in banbury
More than, then by bamboo-carbon fibre, white carbon, carbon black be added in banbury continue knead 30 ~ 40 seconds after, add graphene,
Acrylate, silane coupler continue to knead 80 ~ 90 seconds, then add zinc oxide, nano silicon, glass fibre, anti-
Old agent and filler carry out mixing 80 ~ 90 seconds, and room temperature is cooled in air;
(2)By step(1)In elastomeric compound be added in banbury, add accelerator, vulcanizing agent, knead 50 ~ 55 seconds, carry stone roller
5 ~ 10 seconds, ram was kneaded 35 ~ 45 seconds, is carried out dumping after completing mixing, then is poured into mould to be molded, obtain briquetting roller
Tire;(3)By step(2)Forming tire polished at normal temperatures, remove foreign matter, produce the solid tyre fetal rhythm.
6. the preparation method of anti-static and abrasion-resistant solid tyre fetal rhythm according to claim 5, it is characterised in that:The step
(1)Middle melting temperature is 120 ~ 130 DEG C.
7. the preparation method of anti-static and abrasion-resistant solid tyre fetal rhythm according to claim 5, it is characterised in that:The step
(2)In to put forward the elastomeric compound temperature before stone roller be 125 ~ 135 DEG C, melting temperature after ram is 150 ~ 160 DEG C.
8. the preparation method of anti-static and abrasion-resistant solid tyre fetal rhythm according to claim 5, it is characterised in that:The step
(2)The preparation method of high viscous Concave-convex clay rod is in middle filler:
Take natural attapulgite to be crushed and cross 200 mesh sieves, add the water of 10 ~ 20 times of attapulgite quality, stirring forms outstanding
Mud scum is starched, and takes upper suspension 5 ~ 10min of centrifugal treating in 3000 ~ 5000 turns/min centrifuge, is filtered by vacuum;By filter cake
The dry Muffle 3 ~ 4h of kiln roasting for being placed in 800 DEG C ~ 900 DEG C, cooling produces the high viscous Concave-convex clay rod.