CN107098627A - Enhanced concrete permeable brick of a kind of carbon fiber cinder aggregate and preparation method thereof - Google Patents
Enhanced concrete permeable brick of a kind of carbon fiber cinder aggregate and preparation method thereof Download PDFInfo
- Publication number
- CN107098627A CN107098627A CN201710280484.3A CN201710280484A CN107098627A CN 107098627 A CN107098627 A CN 107098627A CN 201710280484 A CN201710280484 A CN 201710280484A CN 107098627 A CN107098627 A CN 107098627A
- Authority
- CN
- China
- Prior art keywords
- carbon fiber
- permeable brick
- water
- aggregate
- cinder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses enhanced concrete permeable brick of a kind of carbon fiber cinder aggregate and preparation method thereof, the high-temperature medium that the present invention has in itself using melted gangue carries out carbonization treatment to the carbon fiber precursor fiber after pre-oxidation treatment, this method for preparing carbon fiber reduces energy consumption, and realize effective combination of carbon fiber and slag, avoid the not good defect of minute yardstick carbon fiber dispersiveness, it is easier to realize the large-scale promotion application of the material of fibre reinforced, again with aluminium powder, serpentine slag, the materials such as additive act synergistically, the water-permeable brick that this carbon fiber cinder aggregate, which is the water-permeable brick for preparing of base-material, to be prepared than traditional aggregate is more excellent in intensity and water penetration, obtained concrete segment high-strength light, heat absorption insulation, noise reduction is permeable, pressure-proof and snap-resistent, it is more economical and practical, the performance requirement of modern ground surface material can be met.
Description
Technical field
The present invention relates to building material technical field, more particularly to a kind of enhanced concrete of carbon fiber-cinder aggregate are saturating
Water brick and preparation method thereof.
Background technology
Concrete permeable brick is unified overall as formed by surface of aggregate parcel cement slurry, and cellular knot is presented in inside
Structure, belongs to skeleton gap structure.As a kind of Functional road pavement material, its special alveolate texture soil possesses rain
Permeance property is avenged, surface gathered water is on the one hand eliminated, the pressure of city flood fighting draining and pipeline dredging is alleviated, supplements in time
Groundwater resources, reduce setting of ground；In addition, by the evaporation of moisture in brick inside aperture, reducing the suction of urban ground heat energy
Receive and tropical island effect, effectively reduce the noise pollution in city, compared with other traditional ground pavement materials, concrete permeable
Brick undoubtedly has more prominent ecological environment benefit.But require higher road surface in some road loads, water-permeable brick it is strong
Degree and water penetration need further lifting, could meet actual production living needs.
The annual substantial amounts of slag discharge of China, which is stored up, not only occupies substantial amounts of soil, and serious dirt is also caused to environment
Dye, it is the direct approach for solving this problem that slag, which is recycled,.There are some researches show slag is entrained in concrete permeable brick
The compression strength and water penetration of material can be improved simultaneously, with good application prospect.Due to slag be under the condition of high temperature it is rapid
Obtained after cold, be the massive losses to slag sensible heat, and can all cause secondary pollution, and slag in processing procedure to empty gas and water
The preparation process of powder is a kind of process of high energy consumption, is badly in need of the utilization means that developing more saves high level.If can be effective by its
Applied in concrete permeable brick, and optimize corresponding process parameters, will greatly subtract on the basis of proof strength with water penetration
Few corresponding production stage, reduces energy consumption.
The content of the invention
There is provided a kind of enhanced concrete permeable of carbon fiber-cinder aggregate for the defect that makes up prior art by the present invention
Brick and preparation method thereof.
The present invention is achieved by the following technical solutions：
A kind of enhanced concrete permeable brick of carbon fiber-cinder aggregate, includes the raw material of following parts by weight：Carbon fiber-slag bone
Expect 80-115, flyash 5-10, cement 20-35, polycarboxylic-acid buck agent 0.1-0.5, aluminium powder 0.1-0.5, serpentine tailing slag
Powder 8-12, desulfurated plaster 3-8, additive 0.5-1, water 13.5-22.5.
Described carbon fiber-cinder aggregate is the water after the pre- oxysome of carbon fiber precursor fiber and melted gangue batch mixing 1-5min
Quench and crush the pellet that obtained particle diameter is 5-20mm after handling again.
Described carbon fiber precursor fiber is one kind in pitch fibers, polyacrylonitrile fibre.
The weight ratio of the pre- oxysome of described carbon fiber precursor fiber and melted gangue is 1:10.
Described additive is mixed by molasses alcohol waste liquid 80-90%, surfactant 10-20%.
A kind of preparation method of the described enhanced concrete permeable brick of carbon fiber-cinder aggregate is：First by addition to water
Each raw material premix are uniform, then add water, continue to stir mixing 3-5min, will then be suppressed in batch mixing feeding shaping brick machine
Shaping, the adobe standard curing after shaping produced described water-permeable brick finished product to 28 day age.
Compared with prior art, it is an advantage of the current invention that the high-temperature medium having in itself using melted gangue is to through pre-
Carbon fiber precursor fiber after oxidation processes carries out carbonization treatment, and this method for preparing carbon fiber reduces energy consumption, and
Realize effective combination of carbon fiber and slag, it is to avoid the not good defect of minute yardstick carbon fiber dispersiveness, it is easier to realize carbon
The large-scale promotion application of fibre-reinforced material, then acted synergistically with the material such as aluminium powder, serpentine slag, additive, it is made
Water-permeable brick than traditional cinder aggregate for base-material water-permeable brick in intensity and water penetration more excellent, obtained concrete
Building block high-strength light, heat absorption are incubated, noise reduction is permeable, pressure-proof and snap-resistent, more economical and practical, can meet the performance of modern ground surface material
It is required that.
Embodiment
A kind of enhanced concrete permeable brick of carbon fiber-cinder aggregate, includes the raw material of following parts by weight：Carbon is fine
Dimension-cinder aggregate 95, flyash 7.5, cement 27.5, polycarboxylic-acid buck agent 0.25, aluminium powder 0.25, serpentine tailing ground-slag
10th, desulfurated plaster 5.5, additive 0.75, water 17.5.
Wherein carbon fiber-cinder aggregate be after Water Quenching after the pre- oxysome of polyacrylonitrile and melted gangue batch mixing 1min again
The particle diameter that grinding is obtained is 12.mm pellet, and the weight ratio of itself and melted gangue is 1:10.
Wherein additive is compounded and formed by molasses alcohol waste liquid 80%, surfactant 20%.
The preparation method of the embodiment concrete segment is：It is first that each raw material premix in addition to water are uniform, then add
Water, continues to stir mixing 4min, then will be compressing in batch mixing feeding shaping brick machine, and the adobe standard curing after shaping is extremely
28 day age, produce described water-permeable brick finished product.
Claims (6)
1. the enhanced concrete permeable brick of a kind of carbon fiber-cinder aggregate, it is characterised in that include the raw material of following parts by weight：
Carbon fiber-cinder aggregate 80-115, flyash 5-10, cement 20-35, polycarboxylic-acid buck agent 0.1-0.5, aluminium powder 0.1-0.5,
Serpentine tailing ground-slag 8-12, desulfurated plaster 3-8, additive 0.5-1, water 13.5-22.5.
2. the enhanced concrete permeable brick of as claimed in claim 1 a kind of carbon fiber-cinder aggregate, it is characterised in that described
Carbon fiber-cinder aggregate be with being broken again after Water Quenching after melted gangue batch mixing 1-5min by the pre- oxysome of carbon fiber precursor fiber
Broken obtained particle diameter is 5-20mm pellet.
3. the enhanced concrete permeable brick of as claimed in claim 2 a kind of carbon fiber-cinder aggregate, it is characterised in that described
Carbon fiber precursor fiber be pitch fibers, polyacrylonitrile fibre in one kind.
4. the enhanced concrete permeable brick of as claimed in claim 2 a kind of carbon fiber-cinder aggregate, it is characterised in that carbon is fine
The weight ratio for tieing up the pre- oxysome of precursor fiber and melted gangue is 1:10.
5. the enhanced concrete permeable brick of as claimed in claim 1 a kind of carbon fiber-cinder aggregate, it is characterised in that described
Additive be by molasses alcohol waste liquid 80-90%, surfactant 10-20%.
6. a kind of preparation method of the enhanced concrete permeable brick of as claimed in claim 1 carbon fiber-cinder aggregate, its feature
It is, it is first that each raw material premix in addition to water are uniform, water is then added, continues to stir mixing 3-5min, then send batch mixing
Enter to be molded compressing in brick machine, adobe standard curing after shaping to 28 day age, produce described water-permeable brick finished product.