CN107090646A - A kind of greening wall auxiliary material function three-dimensional spacer fabric technology of preparing - Google Patents
A kind of greening wall auxiliary material function three-dimensional spacer fabric technology of preparing Download PDFInfo
- Publication number
- CN107090646A CN107090646A CN201710227730.9A CN201710227730A CN107090646A CN 107090646 A CN107090646 A CN 107090646A CN 201710227730 A CN201710227730 A CN 201710227730A CN 107090646 A CN107090646 A CN 107090646A
- Authority
- CN
- China
- Prior art keywords
- minutes
- incubated
- dyeing
- terylene
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of greening wall auxiliary material function three-dimensional spacer fabric preparation method, comprise the technical steps that:Weaving, sizing, dyeing and finishing, shaping.The present invention is coordinated by the combination and rear whole technique adaptable therewith of plurality of raw materials, so as to obtain it is a kind of with 3-D solid structure and it is fire-retardant it is ageing-resistant can effect wiping fabric, utilize the combination of different material functionally, make the fabric that there is ageing-resistant effect, the characteristic of different material is played by the design of institutional framework, especially 3-D solid structure can effectively mitigate weight, reach optimal afforestation effect.
Description
Technical field
The present invention relates to field of textiles, and in particular to a kind of greening wall auxiliary material prepares skill with function three-dimensional spacer fabric
Art.
Background technology
With the improvement of people's life quality, also gradually being increased sharply to demand of the city in terms of clean.Especially mist in recent years
The influence of haze, for the rush of demand of the environment-friendly engineerings such as air cleaning, increase green coverage is to improve air quality, keep air
Moisture reduces the effective measures of haze.Cultivate cultivated area it is limited in the case of, rational effective utilization space, with sky
Between to change the mode of plane be practicable.The invention of this material is short for the usage cycles of existing greening covering material at present, makes
With proposing in the case of not convenient, the weight of green material application can be effectively reduced, the load-bearing burden of building body is reduced, simultaneously because
Design is controllable, can be made to measure according to different building constructions, with good operability.Using fire-retardant, weatherability material
Material, which prepare, can significantly extend the service life of product, reduce greening cost.
The content of the invention
It is an object of the invention to provide a kind of greening wall auxiliary material function three-dimensional spacer fabric technology of preparing, by many
The combination and weaving process adaptable therewith for planting raw material coordinate, so as to obtain a kind of with weatherability, anti-flaming function, pass through face
Material organizational structure design realizes rational distribution, reduces the weight of fabric, adds permeability, can be conducive to vegetation
Growth.
To achieve the above object, the present invention provides a kind of greening wall auxiliary material function three-dimensional spacer fabric technology of preparing,
It is constituted and mass percentage content is:Flame-retardant polypropylene or polyamide fibre or terylene 10-40%, uvioresistant polypropylene or polyamide fibre or
Person terylene 10-40%, high viscosity (high-strength) polypropylene fibre or polyamide fibre or terylene 10-40%, anti-electrostatic polyester or polyamide fibre 10-
40%.
The present invention uses the model that the specification of fibrous raw material can be DTY and FDY, wherein Denier number (being abbreviated as D)
Enclose for 20-300D, the scope of head number (being abbreviated as F) is 1-300F, and single fiber Denier range is 1-20D.
The fibrous raw material that processing method of the present invention is used is DTY or FDY flame-retardant polypropylenes or polyamide fibre or terylene, anti-purple
Outer polypropylene fibre or polyamide fibre or terylene, high viscosity (high-strength) polypropylene fibre or polyamide fibre or terylene, anti-electrostatic polyester or polyamide fibre;Should
Processing method is comprised the technical steps that:Weaving, sizing, dyeing and finishing, shaping.
The setting temperature of setting process involved in the present invention is 120~200 DEG C, and sizing speed is 15~25m/min.
Dyeing and finishing technology of the present invention is comprised the technical steps that:Enter dye vat (dyeing temperature be 90-140 DEG C), (temperature is for drying
100-180 DEG C), washing, drying (temperature is 100-180 DEG C) adds softening agent to handle according to conventional fabric processing method.
The temperature control that the present invention states dyeing is:Initial temperature is 25-35 DEG C, and 80- is heated to 1-3 DEG C/min
90 DEG C, 3-8 minutes are incubated, then 100-120 DEG C is heated to 2-3 DEG C/min, 3-8 minutes are incubated, then with 1-3 DEG C/min of heating
To 125-140 DEG C, 20-40 minutes are incubated, then 100-120 DEG C is cooled to 0.5-1.5 DEG C/min, 3-8 minutes are incubated, then with
1-3 DEG C/min is cooled to 70-90 DEG C, is incubated 15-40 minutes, is finally cooled to 30-50 DEG C with 1.5-4 DEG C/min.
Beneficial effect
The present invention is coordinated by the combination and weaving process adaptable therewith of plurality of raw materials, so as to obtain a kind of with work(
Energy combined effect, the fabric that light weight durable is used is especially suitable for the exploitation of wall greening material product.
Embodiment
With reference to specific embodiment, the invention will be further described.Following examples are only used for clearly saying
Bright technical scheme, and can not be limited the scope of the invention with this.
Embodiment 1
With 40 parts by weight of high-viscosity polyester DTYs, 10 parts by weight uvioresistant terylene, 10 parts by weight flame-resistant terylene DTY and 40 weights
It is fibrous raw material to measure part anti-electrostatic polyester FDY, and designed material is made by weaving, sizing, dyeing and finishing, sewing tech.
The specification of the high viscosity polyester DTY is 150D/144F, and the specification of the uvioresistant terylene is 150D/72F, institute
The specification for stating flame-resistant terylene DTY is 100D/48F, and the specification of the anti-electrostatic polyester FDY is 150D/144F.
The setting temperature of the setting process is 200 DEG C, and sizing speed is 20m/min.
The dyeing and finishing technology is comprised the technical steps that:Enter dye vat (dyeing temperature is 130 DEG C), (temperature is 150 for drying
DEG C), washing, drying (temperature is 150 DEG C), softening agent is handled using tannic acid.
The composition and mass parts for the dyestuff that the dyeing is used for:The mass parts of cationic yellow 0.04, cationic red
Blue 0.022 mass parts of 0.0152 mass parts, cation, the mass parts of 98% glacial acetic acid 0.5.The temperature control of the dyeing
For:Initial temperature is 30 DEG C, and 70 DEG C are heated to 2 DEG C/min, is incubated 5 minutes, then is heated to 115 DEG C, guarantor with 1.5 DEG C/min
Temperature 5 minutes, then 130 DEG C are heated to 2 DEG C/min, 30 minutes are incubated, then 100 DEG C are cooled to 1 DEG C/min, 5 minutes are incubated,
70 DEG C are cooled to 1.5 DEG C/min again, 20 minutes is incubated, is finally cooled to 35 DEG C with 2 DEG C/min.
Specific aim performance detection has been carried out to gained fabric, it is as a result as follows:
Test event | Test foundation | Properties of product | Standard requirement |
It is fire-retardant | Limited oxygen index | 28 | More than 27 |
It is antistatic | GB/T 12703-2008 | 3.6s | ≤15s |
It is ageing-resistant | GB/T16422.3-1997 | Radiate mechanical property reduction by 6% | ≤ 10% |
Embodiment 2
With 30 parts by weight of high-viscosity polyester DTYs, 20 parts by weight uvioresistant terylene, 30 parts by weight flame-resistant terylene DTY and 20 weights
It is fibrous raw material to measure part anti-electrostatic polyester FDY, and designed material is made by weaving, sizing, dyeing and finishing, sewing tech.
The specification of the high viscosity polyester DTY is 150D/144F, and the specification of the uvioresistant terylene is 150D/72F, institute
The specification for stating flame-resistant terylene DTY is 100D/48F, and the specification of the anti-electrostatic polyester FDY is 150D/144F.
The setting temperature of the setting process is 200 DEG C, and sizing speed is 20m/min.
The dyeing and finishing technology is comprised the technical steps that:Enter dye vat (dyeing temperature is 130 DEG C), (temperature is 150 for drying
DEG C), washing, drying (temperature is 150 DEG C), softening agent is handled using tannic acid.
The composition and mass parts for the dyestuff that the dyeing is used for:The mass parts of cationic yellow 0.04, cationic red
Blue 0.022 mass parts of 0.0152 mass parts, cation, the mass parts of 98% glacial acetic acid 0.5.The temperature control of the dyeing
For:Initial temperature is 30 DEG C, and 70 DEG C are heated to 2 DEG C/min, is incubated 5 minutes, then is heated to 115 DEG C, guarantor with 1.5 DEG C/min
Temperature 5 minutes, then 130 DEG C are heated to 2 DEG C/min, 30 minutes are incubated, then 100 DEG C are cooled to 1 DEG C/min, 5 minutes are incubated,
70 DEG C are cooled to 1.5 DEG C/min again, 20 minutes is incubated, is finally cooled to 35 DEG C with 2 DEG C/min.
Specific aim performance detection has been carried out to gained fabric, it is as a result as follows:
Test event | Test foundation | Properties of product | Standard requirement |
It is fire-retardant | Limited oxygen index | 29 | More than 27 |
It is antistatic | GB/T 12703-2008 | 6.9s | ≤15s |
It is ageing-resistant | GB/T16422.3-1997 | Radiate mechanical property reduction by 2% | ≤ 10% |
Embodiment 3
With 10 parts by weight of high-viscosity polyester DTYs, 40 parts by weight uvioresistant terylene, 40 parts by weight flame-resistant terylene DTY and 10 weights
It is fibrous raw material to measure part anti-electrostatic polyester FDY, and designed material is made by weaving, sizing, dyeing and finishing, sewing tech.
The specification of the high viscosity polyester DTY is 150D/144F, and the specification of the uvioresistant terylene is 150D/72F, institute
The specification for stating flame-resistant terylene DTY is 100D/48F, and the specification of the anti-electrostatic polyester FDY is 150D/144F.
The setting temperature of the setting process is 200 DEG C, and sizing speed is 20m/min.
The dyeing and finishing technology is comprised the technical steps that:Enter dye vat (dyeing temperature is 130 DEG C), (temperature is 150 for drying
DEG C), washing, drying (temperature is 150 DEG C), softening agent is handled using tannic acid.
The composition and mass parts for the dyestuff that the dyeing is used for:The mass parts of cationic yellow 0.04, cationic red
Blue 0.022 mass parts of 0.0152 mass parts, cation, the mass parts of 98% glacial acetic acid 0.5.The temperature control of the dyeing
For:Initial temperature is 30 DEG C, and 70 DEG C are heated to 2 DEG C/min, is incubated 5 minutes, then is heated to 115 DEG C, guarantor with 1.5 DEG C/min
Temperature 5 minutes, then 130 DEG C are heated to 2 DEG C/min, 30 minutes are incubated, then 100 DEG C are cooled to 1 DEG C/min, 5 minutes are incubated,
70 DEG C are cooled to 1.5 DEG C/min again, 20 minutes is incubated, is finally cooled to 35 DEG C with 2 DEG C/min.
Specific aim performance detection has been carried out to gained fabric, it is as a result as follows:
Claims (5)
1. a kind of greening wall auxiliary material function three-dimensional spacer fabric preparation method, processing technology step is followed successively by:Weave, determine
Type, dyeing and finishing, shaping, it is characterised in that including following component and weight ratio:Flame-retardant polypropylene or polyamide fibre or terylene 10-40%,
Uvioresistant polypropylene or polyamide fibre or terylene 10-40%, high viscosity are high-strength polypropylene fibre or polyamide fibre or terylene 10-40%, are resisted
Electrostatic terylene or polyamide fibre 10-40%.
2. the method as described in claim 1, it is characterised in that setting temperature is 120~200 DEG C, sizing speed is 15~
25m/min。
3. the method as described in claim 1, it is characterised in that dyeing and finishing technology is comprised the technical steps that:Enter dye vat dyeing temperature
Spend for 90-140 DEG C, drying temperature is 100-180 DEG C;Then wash again, then drying temperature is 100-180 DEG C, according to conventional face
Material processing method adds softening agent to handle.
4. method as claimed in claim 3, it is characterised in that the temperature control of dyeing is:Initial temperature is 25-35
DEG C, 80-90 DEG C is heated to 1-3 DEG C/min, 3-8 minutes are incubated;100-120 DEG C is heated to 2-3 DEG C/min again, 3- is incubated
8 minutes;125-140 DEG C is heated to 1-3 DEG C/min again, 20-40 minutes are incubated;It is cooled to again with 0.5-1.5 DEG C/min
100-120 DEG C, it is incubated 3-8 minutes;70-90 DEG C is cooled to 1-3 DEG C/min again, 15-40 minutes are incubated, finally with 1.5-4
DEG C/min it is cooled to 30-50 DEG C.
5. the method as described in claim 1, it is characterised in that the specification of fibrous raw material is DTY and FDY, wherein Denier
The scope that number is abbreviated as D is 20-300D, and the scope that head number is abbreviated as F is 1-300F, and single fiber Denier range is 1-20D.