CN107090345A - A kind of lubricating fluid assembled for solid tyre and preparation method - Google Patents
A kind of lubricating fluid assembled for solid tyre and preparation method Download PDFInfo
- Publication number
- CN107090345A CN107090345A CN201710410081.6A CN201710410081A CN107090345A CN 107090345 A CN107090345 A CN 107090345A CN 201710410081 A CN201710410081 A CN 201710410081A CN 107090345 A CN107090345 A CN 107090345A
- Authority
- CN
- China
- Prior art keywords
- parts
- lubricating fluid
- assembled
- solid tyre
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of lubricating fluid assembled for solid tyre and preparation method, the lubricating fluid includes following component：Mineral base oil, lithium base grease, olein, corrosion inhibitor, biocide mildewcide, emulsifying agent, antioxidant, water.Preparation method includes：Biocide mildewcide is extracted first, lyophilized freeze-dried powder is obtained；Then by mineral base oil, it is placed in 30 ~ 40 DEG C of reactors, sequentially adds each component, after being well mixed, shearing is scattered, obtains the lubricating fluid.The installation that the lubricating fluid is applied to solid tyre is assembled, and can be played preferable lubrication, effectively be prevented tire wear and rim deformation, with preferable application value.
Description
Technical field
The present invention relates to solid tyre mounting technology field, and in particular to it is a kind of for solid tyre assemble lubricating fluid and
Preparation method.
Background technology
Tire is the important component in automobile running system, can play a part of supporting vehicle body, buffering foreign impacts, realize with
The contact on road surface and the driving performance for ensureing vehicle.The assembling process of tire, is exactly that the ground connection on various vehicles is rolled into annulus
Shape elastic rubber product, under certain pressure and lubricating condition, in alloy rim.Either original equipped tyre or replacement
Tire, although assembling it is simple to operate, still, assembling quality on the life-span of tire and vehicle handling quality influence it is very big,
Cause the attention of Automobile Enterprises.
Solid tyre is preferably moistened in assembling process because its hardness is higher, it is necessary to coat one layer of lubricity, adaptability
Lubrication prescription, prevents from causing damage to tyre surface and rim deformation.At present, domestic there is no this assembles what is used suitable for this tire
Lubricant, and external product is then expensive, and saving production cost is not utilized.
Usually, lubricating fluid is used in various process, to reduce the frictional resistance on contact surface, slow down its abrasion,
Mainly play lubrication, cooling, antirust, cleaning etc..Especially, in the assembling process of automobile tire, when by various vehicles
Ground connection roll annular elastic rubber product, under certain pressure and lubricating condition, when in alloy rim, it is necessary to
One layer of lubricating fluid is smeared at tire bead position, to reduce dress tire resistance, just dress the blowing pressure and the damage to tire, is not influenceed
The dynamic balancing of tire and air-tightness.Because the lubricating fluid used with aluminium alloy wheel rim and rubber tyre while contact, this is required
Lubricating fluid should also possess preferable aluminium alloy rust-preventing characteristic and rubber compatibility on the basis of lubrication anti-attrition effect is played.
Therefore, research and develop a kind of suitable for solid tyre assembling process, lubricating fluid with preferable lubricant effect
It is significant, the demand of existing market is also complied with, with preferable application prospect.
The content of the invention
For defect of the prior art, it is an object of the invention to provide a kind of lubricating fluid assembled for solid tyre and
Preparation method, the installation that the lubricating fluid is applied to solid tyre is assembled, and can play preferable lubrication, effectively prevents wheel
Tire weares and teares and rim deformation, with preferable application value.
The present invention solves technical problem and adopted the following technical scheme that：
The present invention relates to a kind of lubricating fluid assembled for solid tyre, include each raw material of following parts by weight：Mineral base oil
20 ~ 40 parts, 9 ~ 18 parts of lithium base grease, 13 ~ 20 parts of olein, 10 ~ 15 parts of corrosion inhibitor, 6 ~ 10 parts of biocide mildewcide,
12 ~ 17 parts of emulsifying agent, 5 ~ 10 parts of antioxidant, 20 ~ 30 parts of water.
Preferably, 35 parts of the mineral base oil, 16 parts of lithium base grease, 18 parts of olein, 12 parts of corrosion inhibitor,
9 parts of biocide mildewcide, 15 parts of emulsifying agent, 7 parts of antioxidant, 28 parts of water.
Preferably, the corrosion inhibitor is any of boric acid, Boratex, triethanolamine borate.
Preferably, the biocide mildewcide includes each raw material of following parts by weight：10 ~ 22 parts of rheum officinale, 6 ~ 15 parts of climbing groundsel,
8 ~ 17 parts of Asian puccoon, 10 ~ 20 parts of black false hellebore, 5 ~ 12 parts of the Chinese bulbul, 9 ~ 17 parts of Chinese gall, 12 ~ 23 parts of Salvia japonica, 9 ~ 16 parts of Huang Fen.
Preferably, the emulsifying agent is any of polyvinyl alcohol, polyoxyethylene ester.
Preferably, the antioxidant is in butylated hydroxy anisole, dibutyl hydroxy toluene, TBHQ
It is any.
The invention further relates to a kind of method for preparing the lubricating fluid assembled for solid tyre, comprise the following steps：
（1）Each composition for weighing biocide mildewcide respectively according to proportioning is crushed and crosses 200 mesh sieves, is then well mixed, will mix
Thing is placed in apparatus,Soxhlet's, is extracted 4 ~ 6h in the in the mixed solvent mixing of second alcohol and water, is obtained extract solution, and extract solution is dense
Contract, freeze, obtain freeze-dried powder, it is standby；
（2）Mineral base oil is weighed according to proportioning, is placed in reactor, 30 ~ 40 DEG C is heated to, lithium is then added into reactor
Base grease, olein, corrosion inhibitor, antioxidant, mix 20 ~ 30min, then add biocide mildewcide jelly
Dry powder, emulsifying agent and water, after being well mixed, are placed in the cutter that rotating speed is 2000 ~ 2500 turns/min and shear 20 ~ 30min, i.e.,
Obtain the lubricating fluid.
Preferably, the step（1）The addition of middle mixed solvent is 10 ~ 20 times of mixture powder weight, wherein second
The volume ratio of alcohol and water is 1：0.8~1.5.
Preferably, the step（1）Middle Extracting temperature is 75 ~ 80 DEG C.
Compared with prior art, the present invention has following beneficial effect：
（1）The lubricating fluid of the present invention assembled for solid tyre, the installation applied to solid tyre is assembled, and can be played
Preferable lubrication, effectively prevents tire wear and rim deformation, improves property easy for installation, while extending making for tire
With the life-span, with preferable application value.
（2）It is of the present invention for solid tyre assemble lubricating fluid in added with anticorrosive, antioxidant and
Biocide mildewcide etc. is acted synergistically, and can not only form certain adsorbed film on contact surface in tyre assembling process, and aluminium is closed
Golden wheel rim plays corrosion protection effect, moreover it is possible to effectively prevents the denaturation of lubricant and the erosion of bacterium, is provided for the use of tire
The environment of one safety, extends the service life of tire.
（3）The antibacterial mildew inhibitor added in the lubricating fluid of the present invention assembled for solid tyre is pure Chinese medicine composition,
On the one hand it is capable of the bacterium of active surface surface of tyre, mould to grow, improves rubber service life, on the other hand do not result in rubber
The aging of glue and the corrosion of wheel rim, with preferable application value.
（4）The preparation technology of the present invention for being used for the lubricating fluid that solid tyre is assembled is simple, mild condition, is adapted to industry
Change and promote production.
Embodiment
With reference to specific embodiment, the present invention is expanded on further.These embodiments be merely to illustrate the present invention and without
In limitation the scope of the present invention.The experimental method of unreceipted actual conditions in the following example, generally according to normal condition, for example
Sambrook equimoleculars are cloned：Laboratory manual（New York:Cold Spring Harbor Laboratory Press,
1989）Described in condition, or according to the condition proposed by manufacturer.
Embodiment 1：
A kind of lubricating fluid assembled for solid tyre and preparation method of the preferred embodiment of the present invention；
The lubricating fluid assembled for solid tyre, is prepared from by each raw material of following parts by weight：
35 parts of mineral base oil；
16 parts of lithium base grease；
18 parts of olein；
12 parts of corrosion inhibitor；
9 parts of biocide mildewcide；
15 parts of emulsifying agent；
7 parts of antioxidant；
28 parts of water.
The corrosion inhibitor is Boratex.
The biocide mildewcide includes each raw material of following parts by weight：20 parts of rheum officinale, 12 parts of climbing groundsel, 15 parts of Asian puccoon, lamb's-quarters
15 parts of reed, 7 parts of the Chinese bulbul, 12 parts of Chinese gall, 18 parts of Salvia japonica, 13 parts of Huang Fen.
The emulsifying agent is polyvinyl alcohol.
The antioxidant is butylated hydroxy anisole.
The method that the present invention prepares solid tyre assembling lubricating fluid, comprises the following steps：
（1）Each composition for weighing biocide mildewcide respectively according to proportioning is crushed and crosses 200 mesh sieves, is then well mixed, will mix
Thing is placed in apparatus,Soxhlet's, under the conditions of 78 DEG C, and 5h is extracted in the in the mixed solvent mixing of second alcohol and water, obtains extract solution, will
Extract solution is concentrated, freezed, and obtains freeze-dried powder, standby；
（2）Mineral base oil is weighed according to proportioning, is placed in reactor, 40 DEG C are heated to, lithium base is then added into reactor
Lubricating grease, olein, corrosion inhibitor, antioxidant, mix 30min, then add biocide mildewcide freeze-dried powder,
Emulsifying agent and water, after being well mixed, are placed in the cutter that rotating speed is 2000 turns/min and shear 30min, produce the lubricating fluid.
The step（1）The addition of middle mixed solvent is 18 times of mixture powder weight, the wherein body of ethanol and water
Product is than being 1：1.2.
Embodiment 2：
A kind of lubricating fluid assembled for solid tyre and preparation method of the preferred embodiment of the present invention；
The lubricating fluid assembled for solid tyre, is prepared from by each raw material of following parts by weight：
20 parts of mineral base oil；
9 parts of lithium base grease；
13 parts of olein；
10 parts of corrosion inhibitor；
6 parts of biocide mildewcide；
12 parts of emulsifying agent；
5 parts of antioxidant；
20 parts of water.
The corrosion inhibitor is any of boric acid, Boratex, triethanolamine borate.
The biocide mildewcide includes each raw material of following parts by weight：10 parts of rheum officinale, 6 parts of climbing groundsel, 8 parts of Asian puccoon, black false hellebore
10 parts, 5 parts of the Chinese bulbul, 9 parts of Chinese gall, 12 parts of Salvia japonica, 9 parts of Huang Fen.
The emulsifying agent is polyoxyethylene ester.
The antioxidant is dibutyl hydroxy toluene.
The method that the present invention prepares solid tyre assembling lubricating fluid, comprises the following steps：
（1）Each composition for weighing biocide mildewcide respectively according to proportioning is crushed and crosses 200 mesh sieves, is then well mixed, will mix
Thing is placed in apparatus,Soxhlet's, under the conditions of 75 DEG C, and 6h is extracted in the in the mixed solvent mixing of second alcohol and water, obtains extract solution, will
Extract solution is concentrated, freezed, and obtains freeze-dried powder, standby；
（2）Mineral base oil is weighed according to proportioning, is placed in reactor, 30 DEG C are heated to, lithium base is then added into reactor
Lubricating grease, olein, corrosion inhibitor, antioxidant, mix 30min, then add biocide mildewcide freeze-dried powder,
Emulsifying agent and water, after being well mixed, are placed in the cutter that rotating speed is 2000 turns/min and shear 30min, produce the lubricating fluid.
The step（1）The addition of middle mixed solvent is 10 times of mixture powder weight, the wherein body of ethanol and water
Product is than being 1：0.8.
Embodiment 3：
A kind of lubricating fluid assembled for solid tyre and preparation method of the preferred embodiment of the present invention；
The lubricating fluid assembled for solid tyre, is prepared from by each raw material of following parts by weight：
40 parts of mineral base oil；
18 parts of lithium base grease；
20 parts of olein；
15 parts of corrosion inhibitor；
10 parts of biocide mildewcide；
17 parts of emulsifying agent；
10 parts of antioxidant；
30 parts of water.
The corrosion inhibitor is boric acid.
The biocide mildewcide includes each raw material of following parts by weight：22 parts of rheum officinale, 15 parts of climbing groundsel, 17 parts of Asian puccoon, lamb's-quarters
20 parts of reed, 12 parts of the Chinese bulbul, 17 parts of Chinese gall, 23 parts of Salvia japonica, 16 parts of Huang Fen.
The emulsifying agent is polyvinyl alcohol.
The antioxidant is TBHQ.
The method that the present invention prepares solid tyre assembling lubricating fluid, comprises the following steps：
（1）Each composition for weighing biocide mildewcide respectively according to proportioning is crushed and crosses 200 mesh sieves, is then well mixed, will mix
Thing is placed in apparatus,Soxhlet's, under the conditions of 80 DEG C, and 4h is extracted in the in the mixed solvent mixing of second alcohol and water, obtains extract solution, will
Extract solution is concentrated, freezed, and obtains freeze-dried powder, standby；
（2）Mineral base oil is weighed according to proportioning, is placed in reactor, 40 DEG C are heated to, lithium base is then added into reactor
Lubricating grease, olein, corrosion inhibitor, antioxidant, mix 20min, then add biocide mildewcide freeze-dried powder,
Emulsifying agent and water, after being well mixed, are placed in the cutter that rotating speed is 2500 turns/min and shear 20min, produce the lubricating fluid.
The step（1）The addition of middle mixed solvent is 20 times of mixture powder weight, the wherein body of ethanol and water
Product is than being 1：1.5.
In summary, the lubricating fluid of the present invention assembled for solid tyre, the installation applied to solid tyre is filled
Match somebody with somebody, preferable lubrication can be played, effectively prevent tire wear and rim deformation, improve property easy for installation, same to time delay
The service life of tire is grown, with preferable application value.The preparation technology of the lubricating fluid assembled for solid tyre
Simply, mild condition, is adapted to industrialization promotion production.
The specific embodiment of the present invention is described above.It is to be appreciated that the invention is not limited in above-mentioned
Particular implementation, those skilled in the art can make various deformations or amendments within the scope of the claims, this not shadow
Ring the substantive content of the present invention.
Claims (9)
1. a kind of lubricating fluid assembled for solid tyre, it is characterised in that：Each raw material including following parts by weight：Mineral base
20 ~ 40 parts of oil, 9 ~ 18 parts of lithium base grease, 13 ~ 20 parts of olein, 10 ~ 15 parts of corrosion inhibitor, biocide mildewcide 6 ~ 10
Part, 12 ~ 17 parts of emulsifying agent, 5 ~ 10 parts of antioxidant, 20 ~ 30 parts of water.
2. the lubricating fluid according to claim 1 assembled for solid tyre, it is characterised in that：The mineral base oil 35
It is part, 16 parts of lithium base grease, 18 parts of olein, 12 parts of corrosion inhibitor, 9 parts of biocide mildewcide, 15 parts of emulsifying agent, anti-oxidant
7 parts of agent, 28 parts of water.
3. the lubricating fluid according to claim 1 assembled for solid tyre, it is characterised in that：The corrosion inhibitor is boron
Any of acid, Boratex, triethanolamine borate.
4. the lubricating fluid according to claim 1 assembled for solid tyre, it is characterised in that：The biocide mildewcide bag
Include each raw material of following parts by weight：10 ~ 22 parts of rheum officinale, 6 ~ 15 parts of climbing groundsel, 8 ~ 17 parts of Asian puccoon, 10 ~ 20 parts of black false hellebore, the Chinese bulbul 5 ~
12 parts, 9 ~ 17 parts of Chinese gall, 12 ~ 23 parts of Salvia japonica, 9 ~ 16 parts of Huang Fen.
5. the lubricating fluid according to claim 1 assembled for solid tyre, it is characterised in that：The emulsifying agent is poly- second
Any of enol, polyoxyethylene ester.
6. the lubricating fluid according to claim 1 assembled for solid tyre, it is characterised in that：The antioxidant is fourth
Any of base BHA, dibutyl hydroxy toluene, TBHQ.
7. prepared by one kind be used for the method for the lubricating fluid that solid tyre is assembled, its feature as described in any one of claim 1 ~ 6
It is：Comprise the following steps：
（1）Each composition for weighing biocide mildewcide respectively according to proportioning is crushed and crosses 200 mesh sieves, is then well mixed, will mix
Thing is placed in apparatus,Soxhlet's, is extracted 4 ~ 6h in the in the mixed solvent mixing of second alcohol and water, is obtained extract solution, and extract solution is dense
Contract, freeze, obtain freeze-dried powder, it is standby；
（2）Mineral base oil is weighed according to proportioning, is placed in reactor, 30 ~ 40 DEG C is heated to, lithium is then added into reactor
Base grease, olein, corrosion inhibitor, antioxidant, mix 20 ~ 30min, then add biocide mildewcide jelly
Dry powder, emulsifying agent and water, after being well mixed, are placed in the cutter that rotating speed is 2000 ~ 2500 turns/min and shear 20 ~ 30min, i.e.,
Obtain the lubricating fluid.
8. the preparation method of the lubricating fluid according to claim 7 assembled for solid tyre, it is characterised in that：The step
Suddenly（1）The addition of middle mixed solvent is 10 ~ 20 times of mixture powder weight, and wherein the volume ratio of ethanol and water is 1：0.8~
1.5。
9. the preparation method of the lubricating fluid according to claim 7 assembled for solid tyre, it is characterised in that：The step
Suddenly（1）Middle Extracting temperature is 75 ~ 80 DEG C.