CN107090198A - 一种复合防火玻璃防火液及其制备方法 - Google Patents
一种复合防火玻璃防火液及其制备方法 Download PDFInfo
- Publication number
- CN107090198A CN107090198A CN201710479815.6A CN201710479815A CN107090198A CN 107090198 A CN107090198 A CN 107090198A CN 201710479815 A CN201710479815 A CN 201710479815A CN 107090198 A CN107090198 A CN 107090198A
- Authority
- CN
- China
- Prior art keywords
- parts
- fire
- glass
- fireproof
- composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明公开了一种复合防火玻璃防火液，属于防火玻璃技术领域，包括以下重量份的原料：钾水玻璃20‑40份、水100份、氰基丙烯酸酯8‑10份、二羟基聚二甲基硅氧烷5‑7份、十二醇脂3‑7份、季戊四醇0.2‑0.5份、环氧大豆油1‑4份、三氧化二铝12‑15份、陶粒11‑13份、混合偶联剂0.5‑1份、稳定剂2‑4份、触变剂0.2‑0.4份、增稠剂2‑5份、杀菌剂1‑2份；本发明还公开了一种复合防火玻璃防火液的制备方法；本发明制备简单，防火耐高温能力强，粘着力强，具有优异的机械性能。
Description
技术领域
本发明涉及防火玻璃技术领域，具体的说，涉及了一种复合防火玻璃防火液及其制备方法。
背景技术
安全玻璃是一种重要的新型建筑材料，主要分为钢化玻璃、夹层玻璃、防弹玻璃、防盗玻璃、防火玻璃、夹丝玻璃、防护玻璃及贴膜玻璃；防火玻璃是一种具有防火功能的建筑外墙或门窗玻璃，它在1000℃火焰冲击下能保持较长时间不炸裂，从而有效地阻止火焰与烟雾的蔓延，有利于第一时间发现火情，保证受灾人群有足够长的时间撤离现场，并为救灾工作争取了时间，是目前最有效最安全的防火类玻璃产品；防火玻璃分为复合防火玻璃和单片防火玻璃，复合防火玻璃是指将两片或两片以上的普通平板玻璃用透明防火胶粘剂粘结而成的玻璃或者喷涂复合防火玻璃液的玻璃，复合防火玻璃具有耐火完整性和耐火隔热性，还具有机械强度高、抗折、抗压等良好性能，复合防火玻璃遇到火灾时其防火胶层会迅速发泡膨胀形成坚硬绝热的耐火隔热泡沫层，大量吸收火灾产生的热量，有效阻断火焰，隔绝高温及有害气体，同时防火胶层还可以粘结破碎的玻璃片，以保持整体的完整性；防火胶层的性能决定着复合防火玻璃的性能，而防火胶层是由防火液固化而成，故防火液是否具有较好的性能决定着复合防火玻璃是否具有较好的防火性能。
而目前的防火液固化而成的防火胶在防火性能方面存在着不足，比如在公开号为CN103317783A的专利中，公开了一种复合防火玻璃合片液、其制备方法及复合防火玻璃，属于安全玻璃领域领域，所述复合防火玻璃合片液，以重量份计，其原料由以下物质组成：钾水玻璃25-150份、去离子水100份、成炭剂0.2-1份、成炭助剂0.1-0.5份、消泡剂0.01-0.05份、增塑剂0.1-0.2份、流平剂0.1-0.2份、交联剂0.1-0.5份。本发明通过改进合片液配方，使合片液各组分之间产生协同效应，消除了复合防火玻璃夹层的气泡，制备出透过率为82-83%、防火时间可高达95min左右的高性能无微泡复合防火玻璃；但该防火液存在着防火、耐高温性能一般、黏度不足等问题。
发明内容
本发明的目的在于克服上述现有技术的不足，提供了一种复合防火玻璃防火液及其制备方法，制备简单，防火耐高温能力强，粘着力强。
本发明提供的一种复合防火玻璃防火液，包括以下重量份的原料：
钾水玻璃20-40份、水100份、氰基丙烯酸酯8-10份、二羟基聚二甲基硅氧烷5-7份、十二醇脂3-7份、季戊四醇0.2-0.5份、环氧大豆油1-4份、三氧化二铝12-15份、陶粒11-13份、混合偶联剂0.5-1份、稳定剂2-4份、触变剂0.2-0.4份、增稠剂2-5份、杀菌剂1-2份。
作为优选，陶粒的粒径为0.01mm-0.05mm，三氧化二铝的目数为400-500目。
作为优选，触变剂为二氧化硅、氢化蓖麻油和聚乙烯蜡中的一种或二种以上的混合物；混合偶联剂为硅烷偶联剂和钛酸酯偶联剂的混合物，两者之间的比例为3:1。
作为优选，增稠剂为聚丙烯酸钠、聚氧化乙烯、聚乙烯吡咯烷酮、聚乙烯醇、低分子聚乙烯蜡、聚丙烯酰胺中的一种或二种以上的混合物。
作为优选，稳定剂包括紫外线吸收剂和自由基捕获剂，两者之间的比例为3:1，紫外线吸收剂为 2，4-二羟基二苯甲酮，自由基捕获剂为受阻胺光稳定剂。
作为优选，杀菌剂为过氧乙酸、苯甲酸钠、氢氧化铜、氧化亚铜的一种或二种以上的混合物。
本发明还提供了一种复合防火玻璃防火液的制备方法，包括以下步骤：
（1）、按上述重量份称取各种原料；
（2）、将上述原料加入到搅拌机内搅拌8-10min，静置5-10min，然后继续搅拌15-20min，过滤即可。
其中，
步骤（2）中搅拌机的转速为600-800r/min。
步骤（2）中温度控制在40-45℃。
本发明的一种复合防火玻璃防火液及其制备方法，制备简单，防火耐高温能力强，粘着力强，具体的有益效果如下：
（1）、氰基丙烯酸酯能够加强防火液的附着能力；二羟基聚二甲基硅氧烷能有效地消去防火液的微泡；十二醇脂可作为成膜助剂；季戊四醇为成炭剂，提高防火液的耐火、耐高温能力；环氧大豆油起到润滑、增塑、稳定的作用，增加防火液的耐候性、良好的机械性能；
（2）、三氧化二铝和陶粒的添加能大大提高防火液的耐高温、耐火能力；混合偶联剂、稳定剂、触变剂、增稠剂均能有效地提高防火液的各项性能，加强防火液的质量和寿命；杀菌剂能有效地防止细菌滋生；
（3）、制备方法简单、有效，本发明防火耐高温能力强，粘着力强，机械性能优异。
具体实施方式
以下结合具体实施例对发明作进一步详细的描述。
实施例1
本实施例的一种复合防火玻璃防火液，包括以下重量份的原料：
钾水玻璃20份、水100份、氰基丙烯酸酯8份、二羟基聚二甲基硅氧烷5份、十二醇脂3份、季戊四醇0.2份、环氧大豆油1份、三氧化二铝12份、陶粒11份、混合偶联剂0.5份、稳定剂2份、触变剂0.2份、增稠剂2份、杀菌剂1份。
本实施例中，陶粒的粒径为0.01mm，三氧化二铝的目数为400目。
本实施例中，触变剂为二氧化硅、氢化蓖麻油和聚乙烯蜡的混合物；混合偶联剂为硅烷偶联剂和钛酸酯偶联剂的混合物，两者之间的比例为3:1。
本实施例中，增稠剂为聚丙烯酸钠、聚氧化乙烯、聚乙烯吡咯烷酮、聚乙烯醇、低分子聚乙烯蜡、聚丙烯酰胺的混合物。
本实施例中，稳定剂包括紫外线吸收剂和自由基捕获剂，两者之间的比例为3:1，紫外线吸收剂为 2，4-二羟基二苯甲酮，自由基捕获剂为受阻胺光稳定剂。
本实施例中，杀菌剂为过氧乙酸、苯甲酸钠、氢氧化铜、氧化亚铜的混合物。
本实施例还提供了一种复合防火玻璃防火液的制备方法，包括以下步骤：
（1）、按上述重量份称取各种原料；
（2）、将上述原料加入到搅拌机内搅拌8min，静置5min，然后继续搅拌15min，过滤即可。
其中，
步骤（2）中搅拌机的转速为600r/min。
步骤（2）中温度控制在40℃。
实施例2
本实施例的一种复合防火玻璃防火液，包括以下重量份的原料：
钾水玻璃30份、水100份、氰基丙烯酸酯9份、二羟基聚二甲基硅氧烷6份、十二醇脂5份、季戊四醇0.3份、环氧大豆油3份、三氧化二铝13份、陶粒12份、混合偶联剂0.8份、稳定剂3份、触变剂0.3份、增稠剂4份、杀菌剂1.5份。
本实施例中，陶粒的粒径为0.03mm，三氧化二铝的目数为500目。
本实施例中，触变剂为二氧化硅、氢化蓖麻油和聚乙烯蜡的混合物；混合偶联剂为硅烷偶联剂和钛酸酯偶联剂的混合物，两者之间的比例为3:1。
本实施例中，增稠剂为聚丙烯酸钠、聚氧化乙烯、聚乙烯吡咯烷酮、聚乙烯醇、低分子聚乙烯蜡、聚丙烯酰胺的混合物。
本实施例中，稳定剂包括紫外线吸收剂和自由基捕获剂，两者之间的比例为3:1，紫外线吸收剂为 2，4-二羟基二苯甲酮，自由基捕获剂为受阻胺光稳定剂。
本实施例中，杀菌剂为过氧乙酸、苯甲酸钠、氢氧化铜、氧化亚铜的混合物。
本实施例还提供了一种复合防火玻璃防火液的制备方法，包括以下步骤：
（1）、按上述重量份称取各种原料；
（2）、将上述原料加入到搅拌机内搅拌9min，静置8min，然后继续搅拌18min，过滤即可。
其中，
步骤（2）中搅拌机的转速为700r/min。
步骤（2）中温度控制在43℃。
实施例3
本实施例的一种复合防火玻璃防火液，包括以下重量份的原料：
钾水玻璃40份、水100份、氰基丙烯酸酯10份、二羟基聚二甲基硅氧烷7份、十二醇脂7份、季戊四醇0.5份、环氧大豆油4份、三氧化二铝15份、陶粒13份、混合偶联剂1份、稳定剂4份、触变剂0.4份、增稠剂5份、杀菌剂2份。
本实施例中，陶粒的粒径为0.05mm，三氧化二铝的目数为500目。
本实施例中，触变剂为二氧化硅、氢化蓖麻油和聚乙烯蜡的混合物；混合偶联剂为硅烷偶联剂和钛酸酯偶联剂的混合物，两者之间的比例为3:1。
本实施例中，增稠剂为聚丙烯酸钠、聚氧化乙烯、聚乙烯吡咯烷酮、聚乙烯醇、低分子聚乙烯蜡、聚丙烯酰胺的混合物。
本实施例中，稳定剂包括紫外线吸收剂和自由基捕获剂，两者之间的比例为3:1，紫外线吸收剂为 2，4-二羟基二苯甲酮，自由基捕获剂为受阻胺光稳定剂。
本实施例中，杀菌剂为过氧乙酸、苯甲酸钠、氢氧化铜、氧化亚铜的混合物。
本实施例还提供了一种复合防火玻璃防火液的制备方法，包括以下步骤：
（1）、按上述重量份称取各种原料；
（2）、将上述原料加入到搅拌机内搅拌10min，静置10min，然后继续搅拌20min，过滤即可。
其中，
步骤（2）中搅拌机的转速为800r/min。
步骤（2）中温度控制在45℃。
以公开号为CN103317783A的专利实施例1作为对比例，实施例1-3中性能检测结果如下：
| 实施例1 | 实施例2 | 实施例3 | 对比例 | |
| 透过率，% | 83 | 83 | 84 | 82 |
| 防火时间，min | 121.5 | 120.8 | 119.6 | 83 |
| 表观质量 | 无微泡 | 无微泡 | 无微泡 | 无微泡 |
从上表可以看出，实施例1-3具有较佳地高温防火火能力。
以上所述仅是本发明的优选实施方式，本发明的保护范围并不仅局限于上述实施例，凡属于本发明思路下的技术方案均属于本发明的保护范围。应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明原理前提下的若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。
Claims (9)
1.一种复合防火玻璃防火液，其特征在于：包括以下重量份的原料：
钾水玻璃20-40份、水100份、氰基丙烯酸酯8-10份、二羟基聚二甲基硅氧烷5-7份、十二醇脂3-7份、季戊四醇0.2-0.5份、环氧大豆油1-4份、三氧化二铝12-15份、陶粒11-13份、混合偶联剂0.5-1份、稳定剂2-4份、触变剂0.2-0.4份、增稠剂2-5份、杀菌剂1-2份。
2.根据权利要求1所述的复合防火玻璃防火液，其特征在于：陶粒的粒径为0.01mm-0.05mm，三氧化二铝的目数为400-500目。
3.根据权利要求1所述的复合防火玻璃防火液，其特征在于：触变剂为二氧化硅、氢化蓖麻油和聚乙烯蜡中的一种或二种以上的混合物；混合偶联剂为硅烷偶联剂和钛酸酯偶联剂的混合物，两者之间的比例为3:1。
4.根据权利要求1所述的复合防火玻璃防火液，其特征在于：增稠剂为聚丙烯酸钠、聚氧化乙烯、聚乙烯吡咯烷酮、聚乙烯醇、低分子聚乙烯蜡、聚丙烯酰胺中的一种或二种以上的混合物。
5.根据权利要求1所述的复合防火玻璃防火液，其特征在于：稳定剂包括紫外线吸收剂和自由基捕获剂，两者之间的比例为3:1，紫外线吸收剂为 2，4-二羟基二苯甲酮，自由基捕获剂为受阻胺光稳定剂。
6.根据权利要求1所述的复合防火玻璃防火液，其特征在于：杀菌剂为过氧乙酸、苯甲酸钠、氢氧化铜、氧化亚铜的一种或二种以上的混合物。
7.根据权利要求1-6任意一项所述的一种复合防火玻璃防火液的制备方法，其特征在于：包括以下步骤：
（1）、按上述重量份称取各种原料；
（2）、将上述原料加入到搅拌机内搅拌8-10min，静置5-10min，然后继续搅拌15-20min，过滤即可。
8.根据权利要求7所述的复合防火玻璃防火液的制备方法，其特征在于：步骤（2）中搅拌机的转速为600-800r/min。
9.根据权利要求7所述的复合防火玻璃防火液的制备方法，其特征在于：步骤（2）中温度控制在40-45℃。