CN107216743A - 一种石墨烯类膨胀型低烟防火涂料及其制备方法 - Google Patents

一种石墨烯类膨胀型低烟防火涂料及其制备方法 Download PDF

Info

Publication number
CN107216743A
CN107216743A CN201710549464.1A CN201710549464A CN107216743A CN 107216743 A CN107216743 A CN 107216743A CN 201710549464 A CN201710549464 A CN 201710549464A CN 107216743 A CN107216743 A CN 107216743A
Authority
CN
China
Prior art keywords
parts
expansion type
graphene
fireproof coating
smoke
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710549464.1A
Other languages
English (en)
Inventor
李洪飞
冯伟华
刘雪莲
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Beijing University of Chemical Technology
Original Assignee
Beijing University of Chemical Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Beijing University of Chemical Technology filed Critical Beijing University of Chemical Technology
Priority to CN201710549464.1A priority Critical patent/CN107216743A/zh
Publication of CN107216743A publication Critical patent/CN107216743A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种石墨烯类膨胀型低烟防火涂料及其制备方法，属于功能涂料范畴。其特征是以水性成膜基体(100份)，膨胀型阻燃剂(200份‑250份)，钛白粉(20份‑30份)，石墨烯类物质(10‑5‑10‑4)，助剂(1份‑2份)，水(200份‑250份)，将这些物质按照一定配比混合研磨成涂料。本发明的效果在于燃烧初期，均匀致密发泡，后期形成了一种隔火隔热的包状炭层结构，耐燃时间长，机械强度大，耐水耐候性好，涂层表面光滑，制备工艺流程简单，便于操作。该防火涂料属于水性涂料范畴，低烟低毒，属于绿色环保涂料。该涂料可广泛用于木结构、钢结构，纤维织物等领域。

Description

一种石墨烯类膨胀型低烟防火涂料及其制备方法
技术领域
本发明涉及一种防火涂料的制备，尤其是一种石墨烯类膨胀型低烟防火涂料的制备。
背景技术
众所周知，木材与钢结构的应用已遍及各个行业，而火灾的发生大部分与木结构、钢结构本身的破坏密切相关，若在外表面附加一层保护膜，那么火灾就不易发生，为此，防火涂料的存在是相当有效且有意义的。
膨胀型防火涂料是由基体，阻燃体系、添加剂(颜料、填料)以及各种助剂组成。在高温火焰的作用下，涂料层熔融，发泡，膨胀，形成蜂窝状的包状炭化层结构，并放出难燃气体，冲淡氧气的浓度，起到隔火隔热的作用。而水性防火涂料，不仅满足国家环保的要求，而且价格低廉，性能显著，故而越来越受到研究者与厂商的重视。
本发明采用水性成膜物作为基体，钛白粉作为高温填料，在燃烧的过程当中，析出附着在炭层表面，起到隔火隔热的作用，在此是一种非常受欢迎的一种高温填料，而石墨烯类化学物质具有阻燃抑烟的作用，在国家越来越重视环境安全与人身安全的情况下，减少烟雾的产生，已势在必行，毕竟在火灾中死亡的人，85％以上都是因为毒烟而窒息死亡。
发明内容
本发明的目的在于提高现有防火涂料的耐燃抑烟性能，提供一种优于传统防火涂料的石墨烯类膨胀型防火涂料。
本发明的目的可以通过以下技术方案来实现：
该防火涂料的组分及含量：
水性成膜基体(100份)，膨胀型阻燃剂(200份-250份)，钛白粉(20份-30份)，石墨烯类物质(10-5-10-4)，助剂(1份-2份)，水(200份-250份)。
本发明水性成膜基体为丙烯酸乳液，水性聚氨酯，环氧树脂其中的一种。
本发明所述的膨胀型阻燃剂为三聚氰酸螺环磷酸酯、螺环磷酸酯酰胺其中的一种。
本发明所述的钛白粉为金红石型钛白粉，锐钛型钛白粉的其中一种。
本发明所述的助剂包含成膜助剂，分散剂，增稠剂，流平剂，消泡剂。
本发明所述的石墨烯类物质为石墨烯，氧化石墨烯或它们的复配物。
该发明包括以下步骤：
(1)按照以下组分配比备料：水性成膜基体(100份)，膨胀型阻燃剂(200份-250份)，钛白粉(20份-30份)，石墨烯类物质(10-5-10-4)，助剂(1份-2份)，水(200份-250份)。
(2)将水，防火助剂，填料混合均匀，放入转速为1400r/min的研磨机中研磨30min，然后将水性成膜基体以及助剂加入，在搅拌仪中低速搅拌30min，过筛出料，制得石墨烯类膨胀型低烟防火涂料。
本发明的优点：
本发明所用到的水性成膜基体，为水性环保基料，对环境无污染。
本发明所用的高温填料钛白粉，会在燃烧过程当中析出，附着在炭层表面，提高炭化层强度，隔绝了热量的传导，延长了耐燃时间。
本发明所用的石墨烯类物质具有阻燃抑烟的效果，且用量极少，降低成本，添加入防火涂料后，烟释放量明显降低。
具体实施方式
实例一：
各组分含量：
硅丙乳液(100份)，三聚氰酸螺环磷酸酯(200份)，金红石型钛白粉(20份)，石墨烯(0.03份)，助剂(1份)，水(200份)。
制备方法：
将水，防火助剂，填料混合均匀，放入转速为1400r/min的研磨机中研磨30min，然后将硅丙乳液以及助剂加入，在搅拌仪中低速搅拌30min，过筛出料，制得石墨烯类膨胀型低烟防火涂料。
实例二：
水性聚氨酯(100份)，季戊四醇双磷酸酯蜜铵盐(200份)，锐钛型钛白粉(25份)，氧化石墨烯(1份)，助剂(1份)，水(230份)。
制备方法：
将水，防火助剂，填料混合均匀，放入转速为1400r/min的研磨机中研磨30min，然后将水性聚氨酯以及助剂加入，在搅拌仪中低速搅拌30min，过筛出料，制得石墨烯类膨胀型低烟防火涂料。
实例三：
环氧树脂(100份)，螺环磷酸酯酰胺(230份)，金红石型钛白粉(30份)，石墨烯与氧化石墨烯复配物(1份)，助剂(1份)，水(250份)。
制备方法：
将水，防火助剂，填料混合均匀，放入转速为1400r/min的研磨机中研磨30min，然后将环氧树脂以及助剂加入，在搅拌仪中低速搅拌30min，过筛出料，制得石墨烯类膨胀型低烟防火涂料。

Claims (7)

1.一种石墨烯类膨胀型低烟防火涂料制备方法，其特征在于：该防火涂料的组分及含量：
水性成膜基体(100份)，膨胀型阻燃剂(200份-250份)，钛白粉(20份-30份)，石墨烯类物质(10-5-10-4)，助剂(1份-2份)，水(200份-250份)。
2.根据权利要求书1所述的石墨烯类膨胀型低烟防火涂料，其特征在于，所述的水性成膜基体为水性丙烯酸乳液，水性聚氨酯，水性环氧树脂其中的一种。
3.根据权利要求书1所述的石墨烯类膨胀型低烟防火涂料，其特征在于，所述的膨胀型阻燃剂为三聚氰酸螺环磷酸酯、螺环磷酸酯酰胺其中的一种。
4.根据权利要求书1所述的石墨烯类膨胀型低烟防火涂料，其特征在于，所述的钛白粉为金红石型钛白粉，锐钛型钛白粉其中的一种。
5.根据权利要求书1所述的石墨烯类膨胀型低烟防火涂料，其特征在于，所述的助剂包含成膜助剂，分散剂，增稠剂，流平剂，消泡剂。
6.根据权利要求书1所述的石墨烯类膨胀型低烟防火涂料，其特征在于，所述的石墨烯物质为石墨烯，氧化石墨烯或其复配物。
7.根据权利要求书1所述的螺环磷酸酯类膨胀型低烟防火涂料，其特征在于，该方法包括以下步骤：
(1)按照以下组分配比备料：水性成膜基体(100份)，膨胀型阻燃剂(200份-250份)，钛白粉(20份-30份)，石墨烯类物质(10-5-10-4)，助剂(1份-2份)，水(200份-250份)。
(2)将水，防火助剂，填料混合均匀，放入转速为1400r/min的研磨机中研磨30min，然后将水性成膜基体以及助剂加入，在搅拌仪中低速搅拌30min，过筛出料，制得石墨烯类膨胀型低烟防火涂料。
CN201710549464.1A 2017-07-07 2017-07-07 一种石墨烯类膨胀型低烟防火涂料及其制备方法 Pending CN107216743A (zh)