CN101544490B - 室内超薄型钢结构无机防火涂料 - Google Patents

室内超薄型钢结构无机防火涂料 Download PDF

Info

Publication number
CN101544490B
CN101544490B CN2009100113935A CN200910011393A CN101544490B CN 101544490 B CN101544490 B CN 101544490B CN 2009100113935 A CN2009100113935 A CN 2009100113935A CN 200910011393 A CN200910011393 A CN 200910011393A CN 101544490 B CN101544490 B CN 101544490B
Authority
CN
China
Prior art keywords
powder
parts
steel structure
coating
fireproof coating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN2009100113935A
Other languages
English (en)
Other versions
CN101544490A (zh
Inventor
王德洪
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN2009100113935A priority Critical patent/CN101544490B/zh
Publication of CN101544490A publication Critical patent/CN101544490A/zh
Application granted granted Critical
Publication of CN101544490B publication Critical patent/CN101544490B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及室内超薄型钢结构无机防火涂料，其特征在于是由下述成分按重量份配比组成，粉料包括硅石粉、镁石粉、膨润土、滑石粉组成，液料为硅酸钠，制法是：将粉料和液料按照一定比例配合用搅拌器搅拌均匀成乳白色液体后，即可涂装。本发明的有益效果是：1)、防火程度高：普通涂料最高温度达800℃，本产品最高温度达1300-1400℃。2)、环保：无毒、无味、无有害气体释放。3)、阻燃：有隔离效应，阻止热传递，延缓钢结构升温功能，提高耐火极限。

Description

室内超薄型钢结构无机防火涂料
技术领域
本发明涉及建筑材料，尤其涉及室内超薄型钢结构无机防火涂料。
背景技术
目前，建筑材料中的涂料主要是应用在室内外，用于室内金属钢结构件上的涂料大多是有机材料制成的，在生产中有毒有味，一旦发生火灾，不防火而且还助燃。
发明内容
本发明的目的是提供一种无毒、无味，而且有防火功能的室内超薄型钢结构无机防火涂料的配制方法。
室内超薄型钢结构无机防火涂料，其特征在于是由下述成分按重量份配比组成。
粉料：硅石粉 200～400目 含SiO2≥98.72％，3～12份；
镁石粉 200～400目 含MgO≥32％，10～30份；
膨润土 200～400目 含SiO2≥71.8％，2～8份；
滑石粉 200～400目 含SiO2≥59.3％，1～5份；
钛白粉 200～400目 灼烧失重0.5％，1～5份；
液料：硅酸钠 30～50份；其模数3.0-3.3，浓度为40-45波美度；
制法是：粉料和液料按照1∶1.1～1.5重量比例配合，用搅拌器搅拌均匀成乳白色液体后，即可涂装。
本发明的作用原理：
1)钢结构受热后，涂层中释放结晶水从而膨胀成致密均匀高度氧釉面层，隔热阻止热传递，延缓钢结构升温的功能，有提高耐火极限的作用。以前钢结构的耐火极限为20-30min，涂刷此涂料后，钢结构的耐火极限为90min。
2)石英粉(硅石粉)熔点在1710℃在本发明中起到骨架作用；在本专利的其它成分中，选定了滑石、菱镁石做原料，滑石在900℃时分解出结合水，在1200℃以上重新结晶成顽火辉石，放出SiO2；原料中加入膨润土，火灾受热后，有明显的“发泡”现象。“泡体”和涂层形成屏障来隔绝热源与钢结构之间的直接接触，形成绝密均匀的氧釉保护层，此产品不含有机物，无有害气体释放。
本发明的有益效果是：1)、防火程度高：普通涂料最高温度达800℃，本产品最高温度达1300-1400℃。2)、环保：无毒、无味、无有害气体释放。3)、阻燃：有隔离效应，阻止热传递，延缓钢结构升温功能，提高耐火极限。
具体实施方式
实施例1
室内超薄型钢结构无机防火涂料，是由下述成分按重量份配比组成。
粉料：硅石粉 4.1份；
镁石粉 20份；
膨润土 5份；
滑石粉 2.1份；
钛白粉 2.1份；
液料：硅酸钠 39.96份。
制法是：将粉料和液料混合，其重量比例为1∶1.2，用搅拌器搅拌均匀成乳白色液体后，即可涂装。
实施例2
室内超薄型钢结构无机防火涂料，是由下述成分按重量份配比组成。
粉料：硅石粉 3.1份；
镁石粉 18份；
膨润土 7份；
滑石粉 1.5份；
钛白粉 1.5份；
液料：硅酸钠 46.65份。
制法是：将粉料和液料混合，其重量比例为1∶1.5，用搅拌器搅拌均匀成乳白色液体后，即可涂装。
实施例3
室内超薄型钢结构无机防火涂料，是由下述成分按重量份配比组成。
粉料：硅石粉 12份；
镁石粉 10份；
膨润土 2份；
滑石粉 4份；
钛白粉 1.2份；
液料：硅酸钠 37.96。
制法是：将粉料和液料混合，其重量比例为1∶1.3，，用搅拌器搅拌均匀成乳白色液体后，即可涂装。
实施例4
室内超薄型钢结构无机防火涂料，是由下述成分按重量份配比组成。
粉料：硅石粉 8份；
镁石粉 26.5份；
膨润土 3份；
滑石粉 4.5份；
钛白粉 3份；
液料：硅酸钠49.5份。
制法是：将粉料和液料混合，其重量比例为1∶1.1，，用搅拌器搅拌均匀成乳白色液体后，即可涂装。
上述实施例中，各成分的技术指标如下：
粉料：硅石粉 200～400目 含SiO2≥98.72％；
镁石粉 200～400目 含MgO≥32％；
膨润土 200～400目 含SiO2≥71.8％；
滑石粉 200～400目 含SiO2≥59.3％；
钛白粉 200～400目 灼烧失重0.5％；
液料：硅酸钠(Na2SiO3)；其模数(即SiO2/Na2O比值)范围在3.0-3.3之间，浓度为40-45波美度。

Claims (1)

1.室内超薄型钢结构无机防火涂料，其特征在于是由下述成分按重量份配比组成：
粉料：硅石粉 200～400目 含SiO2≥98.72％，3～12份；
      镁石粉 200～400目 含MgO≥32％，10～30份；
      膨润土 200～400目 含SiO2≥71.8％，2～8份；
      滑石粉 200～400目 含SiO2≥59.3％，1～5份；
      钛白粉 200～400目 灼烧失重0.5％，1～5份；
液料：硅酸钠 30～50份；其模数3.0-3.3，浓度为40-45波美度；
制法是：粉料和液料按照1∶1.1～1.5重量比例配合，用搅拌器搅拌均匀成乳白色液体后，即可涂装。
CN2009100113935A 2009-04-30 2009-04-30 室内超薄型钢结构无机防火涂料 Expired - Fee Related CN101544490B (zh)