CN107090162A - A kind of power distribution station electric power cabinet glass steel surface plate material and preparation method thereof - Google Patents
A kind of power distribution station electric power cabinet glass steel surface plate material and preparation method thereof Download PDFInfo
- Publication number
- CN107090162A CN107090162A CN201710479805.2A CN201710479805A CN107090162A CN 107090162 A CN107090162 A CN 107090162A CN 201710479805 A CN201710479805 A CN 201710479805A CN 107090162 A CN107090162 A CN 107090162A
- Authority
- CN
- China
- Prior art keywords
- parts
- electric power
- surface plate
- steel surface
- plate material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of power distribution station electric power cabinet glass steel surface plate material, include the raw material of following parts by weight：60 70 parts of thermoset synthetic resin, 68 parts of Nano filling, 8 12 parts of glass fibre, 46 parts of furane resins bonding agent, 24 parts of polytetrafluoroethylene (PTFE), 12 parts of glass microballoon, 0.5 0.9 parts of graphite powder, 37 parts of processing aid, 8 15 parts of polyvinyl butyral resin, 35 parts of metal packing.Its density of the glass steel surface plate material of the present invention is small, lightweight, hardness is high, good toughness, electrical insulating property are good, with preferable fire resistance, corrosion resistance and wearability；While the preparation method of the insulating coating material of the present invention, its material cost is relatively low, raw material is easy to get and technique concise, industrialized production easy to operate and realize, with higher practical value and good application prospect.
Description
Technical field
The present invention relates to electric power distributing cabinet technical field, and in particular to a kind of power distribution station electric power cabinet glass steel surface plate material
And preparation method thereof.
Background technology
Current electric power cabinet shell is mainly what is be made of cold-rolled steel sheet or stainless steel plate, and the intensity of cold-rolled steel sheet is very high,
Surface-brightening, but toughness, solderability are poor, it is harder, crisp, it if there is solder skip, then can intake, cause first device inside electric power cabinet
Fire is scrapped or even occurred to part, there is potential safety hazard.Stainless steel plate has enough intensity, there is fabulous plasticity again, and hardness is not yet
Height, is easy to processing, but is due to be chronically at outdoor, and environment is poor, so corrosion resistance can not meet use demand well,
So that the service life of electric power cabinet is shorter, the acid rain formed after especially raining has extremely strong corrosivity to electric power cabinet outer surface,
Once electric power cabinet is corroded, power system will face great danger.Other electric power cabinet is used to carry high voltage power supply, mesh
Preceding electric power cabinet is generally iron sheet and makes shell, particularly in the dry north, and often because dust friction produces electrostatic, this is just
High voltage power supply electric power cabinet is caused extremely easily to occur fire hazard, consequence is hardly imaginable.And the density of stainless steel plate is larger, peace
Wasted time and energy during dress, electrical insulating property is poor, there is also potential safety hazard.
On the other hand, at present, electric power cabinet anticorrosion material mainly makes sheet material with plastics, and plastics are the macromolecule of synthesis
Compound, can freely change body styles.Plastics are the material to synthesize or condensation reaction is polymerized using raw material monomer,
It is made up of the additive such as synthetic resin and filler, plasticizer, stabilizer, lubricant, colorant, its main component is synthesis tree
Fat.Above-mentioned anticorrosion material typically is provided with certain Corrosion Protection, but mechanical performance, heat endurance and fire resistance are often
Expected requirement is not reached；The anticorrosive index of also some anticorrosion materials is unqualified, for example, acid and alkali corrosion can only be prevented, or
Person can only prevent irradiation, and various indexs tend not to take into account.
The content of the invention
For the defect of prior art, it is an object of the invention to provide a kind of power distribution station electric power cabinet glass steel surface sheet material
Material, its density of the glass steel surface plate material is small, lightweight, hardness is high, good toughness, electrical insulating property are good, with preferable fire resistance,
Corrosion resistance and wearability；While the preparation method of the insulating coating material of the present invention, its material cost is relatively low, raw material is easy to get,
And technique is concise, industrialized production easy to operate and realize, with higher practical value and good application prospect.
The present invention solves technical problem and adopted the following technical scheme that：
The invention provides a kind of power distribution station electric power cabinet glass steel surface plate material, include the raw material of following parts by weight：
It is 60-70 parts of thermoset synthetic resin, 6-8 parts of Nano filling, 8-12 parts of glass fibre, 4-6 parts of furane resins bonding agent, poly-
2-4 parts of tetrafluoroethene, 1-2 parts of glass microballoon, 0.5-0.9 parts of graphite powder, 3-7 parts of processing aid, polyvinyl butyral resin 8-15
Part, 3-5 parts of metal packing.
Preferably, the power distribution station electric power cabinet includes the raw material of following parts by weight with glass steel surface plate material：
65 parts of thermoset synthetic resin, 7 parts of Nano filling, 10 parts of glass fibre, 5 parts of furane resins bonding agent, polytetrafluoroethylene (PTFE) 3
Part, 1.5 parts of glass microballoon, 0.7 part of graphite powder, 5 parts of processing aid, 11 parts of polyvinyl butyral resin, 4 parts of metal packing.
Preferably, the thermoset synthetic resin is by epoxy resin, phenolic resin and vinyl ester resin, according to weight ratio
3:1:The mixture of 2 compositions.
Preferably, the Nano filling is nano silicon, nano-calcium carbonate, nano titanium oxide, according to Ou Chongliang
Than 3:2:The mixture of 0.5 composition.
Preferably, the glass microballoon is hollow glass micropearl, and the particle size range of the hollow glass micropearl is 50-100
Micron.
Preferably, the processing aid is that plasticizer, stabilizer, curing agent compare 3 according to weight:1:The mixture of 2 compositions,
The plasticizer is the fat of phosphorus benzene bis-acid potassium two, and the stabilizer is triphenyl phosphite, and the curing agent is triethylene tetramine.
Preferably, the metal packing copper powder, iron powder and tungsten powder, compare 3 according to weight:1:The mixture of 2 compositions, the gold
Belong to the fineness of powder between 300-400 mesh.
The present invention also provides a kind of preparation method of power distribution station electric power cabinet glass steel surface plate material, comprises the following steps：
Step one, each component raw material is weighed on request；
Step 2, Nano filling, glass fibre, glass microballoon, graphite powder, metal packing, furane resins bonding agent are mixed and added
Enter mixer, stir 10-20 minutes, speed of agitator is 350-450r/min, obtains mixture A；
Step 3, thermoset synthetic resin, polytetrafluoroethylene (PTFE), polyvinyl butyral resin are mixed and add the reaction with mixer
In kettle, in the case where temperature is 60-70 DEG C, stir 8-10 minutes, speed of agitator is 200-300r/min, adds processing aid and step
The rapid two mixture A prepared, are warming up to 100-120 DEG C, continue to stir 10-18 minutes, and the mixture B after stirring is sent into double spiral shells
Bar extruder, barrel and head temperature are 170-180 DEG C, and screw speed is 60-80r/min, and extrudate pours into the mold plate, natural
The power distribution station electric power cabinet glass steel surface plate material that cooling and shaping is invented.
Preferably, the power distribution station electric power cabinet is with the preparation process of glass steel surface plate material：
Step one, each component raw material is weighed on request；
Step 2, Nano filling, glass fibre, glass microballoon, graphite powder, metal packing, furane resins bonding agent are mixed and added
Enter mixer, stir 15 minutes, speed of agitator is 400r/min, obtains mixture A；
Step 3, thermoset synthetic resin, polytetrafluoroethylene (PTFE), polyvinyl butyral resin are mixed and add the reaction with mixer
It is at 65 DEG C, to stir 9 minutes, speed of agitator is 250r/min, add prepared by processing aid and step 2 in temperature in kettle
Mixture A, is warming up to 110 DEG C, continues to stir 14 minutes, the mixture B after stirring is sent into double screw extruder, barrel and machine
Head temperature is 175 DEG C, and screw speed is 70r/min, and extrudate pours into the mold plate, the power distribution station that natural cooling sizing is invented
Electric power cabinet glass steel surface plate material.
Compared with prior art, the present invention has following beneficial effect：
（1）A kind of power distribution station electric power cabinet glass steel surface plate material of the present invention, by being reasonably formulated, makes obtained panel material
Material, density is small, lightweight, and hardness is high, and good toughness, electrical insulating property is good, with preferable fire resistance, corrosion resistance, wearability and
Anti-static ability, it is time saving and energy saving during installation, it is safe and reliable, extend the service life of electric power cabinet.
（2）A kind of power distribution station electric power cabinet glass steel surface plate material of the present invention, polytetrafluoroethylene (PTFE), the polyvinyl alcohol of addition
Butyral, the two compound action can keep excellent mechanical property, self-lubricating, acid-alkali-corrosive-resisting is non-ignitable, in wider frequency rate
In the range of dielectric constant and dielectric loss it is all very low, and breakdown voltage, specific insulation and arc resistance are all higher, pass through
The parts by weight ratio of polytetrafluoroethylene (PTFE) and furane resins bonding agent is adjusted, can make to prepare during panel material and have between each raw material
There is good amalgamation.
（3）The processing aid that a kind of power distribution station electric power cabinet of the present invention is added with glass steel surface plate material is mainly thickening
Agent, dispersant, curing agent, levelling agent, defoamer, a few person's compound actions the insulating coating material film forming of the present invention can be made fine and close and
Flexible, elasticity is good, and hardness is moderate, and film layer is transparent, and caking property is good, and adhesive force is extremely strong, with outstanding static state and dynamically formed membrane matter
Amount, strong shock resistance；Film layer melt drop temperature is high, is amenable to the strong sunlight irradiation of long-time and hyperthermia radiation without disappearing, gently
Degree friction is not damaged.
（4）A kind of power distribution station electric power cabinet of the present invention is with glass steel surface plate material using thermoset synthetic resin as matrix material
Material, aids in various additives, can improve the combination property of panel material, so as to improve the security of electric power cabinet and reliable
Property, extend the service life of electric power cabinet.
（5）The glass fibre heatproof that a kind of power distribution station electric power cabinet of the present invention is added with glass steel surface plate material is high, non-ignitable,
Anti- corruption, heat-insulated, tensile strength is high, and electrical insulating property is good, the glass microballoon of addition, effective heat-insulated corrosion resistant for improving panel material
Corrosion energy, can make them complementary, improve the combination property of panel, so as to improve the safety and reliability of electric power cabinet, extend
The service life of electric power cabinet；While the preparation method of the insulating coating material of the present invention, its material cost is relatively low, raw material is easy to get,
And technique is concise, industrialized production easy to operate and realize, with higher practical value and good application prospect.
Embodiment
With reference to specific embodiment, the technical scheme in the embodiment of the present invention is clearly and completely described, shown
So, described embodiment is only a part of embodiment of the invention, rather than whole embodiments.Based on the reality in the present invention
Example is applied, the every other embodiment that those of ordinary skill in the art are obtained under the premise of creative work is not made all belongs to
In the scope of protection of the invention.
Embodiment 1.
A kind of power distribution station electric power cabinet glass steel surface plate material of the present embodiment, includes the raw material of following parts by weight：
60 parts of thermoset synthetic resin, 6 parts of Nano filling, 8 parts of glass fibre, 4 parts of furane resins bonding agent, polytetrafluoroethylene (PTFE) 2
Part, 1 part of glass microballoon, 0.5 part of graphite powder, 3 parts of processing aid, 8 parts of polyvinyl butyral resin, 3 parts of metal packing.
Thermoset synthetic resin in the present embodiment is by epoxy resin, phenolic resin and vinyl ester resin, according to weight
Than 3:1:The mixture of 2 compositions.
Nano filling in the present embodiment is nano silicon, nano-calcium carbonate, nano titanium oxide, according to Ou Chongliang
Than 3:2:The mixture of 0.5 composition.
Glass microballoon in the present embodiment is hollow glass micropearl, and the particle size range of the hollow glass micropearl is 50-100
Micron.
Processing aid in the present embodiment is plasticizer, stabilizer, curing agent compare 3 according to weight:1:The mixing of 2 compositions
Thing, the plasticizer is the fat of phosphorus benzene bis-acid potassium two, and the stabilizer is triphenyl phosphite, and the curing agent is triethylene four
Amine.
Metal packing copper powder, iron powder and tungsten powder in the present embodiment, compare 3 according to weight:1:The mixture of 2 compositions, it is described
The fineness of metal powder is between 300-400 mesh.
A kind of power distribution station electric power cabinet preparation method of glass steel surface plate material of the present embodiment, comprises the following steps：
Step one, each component raw material is weighed on request；
Step 2, Nano filling, glass fibre, glass microballoon, graphite powder, metal packing, furane resins bonding agent are mixed and added
Enter mixer, stir 10 minutes, speed of agitator is 350r/min, obtains mixture A；
Step 3, thermoset synthetic resin, polytetrafluoroethylene (PTFE), polyvinyl butyral resin are mixed and add the reaction with mixer
It is at 60 DEG C, to stir 8 minutes, speed of agitator is 200r/min, add prepared by processing aid and step 2 in temperature in kettle
Mixture A, is warming up to 100 DEG C, continues to stir 10 minutes, the mixture B after stirring is sent into double screw extruder, barrel and machine
Head temperature is 170 DEG C, and screw speed is 60r/min, and extrudate pours into the mold plate, the power distribution station that natural cooling sizing is invented
Electric power cabinet glass steel surface plate material.
Embodiment 2.
A kind of power distribution station electric power cabinet glass steel surface plate material of the present embodiment, includes the raw material of following parts by weight：
70 parts of thermoset synthetic resin, 8 parts of Nano filling, 12 parts of glass fibre, 6 parts of furane resins bonding agent, polytetrafluoroethylene (PTFE) 4
Part, 2 parts of glass microballoon, 0.9 part of graphite powder, 7 parts of processing aid, 15 parts of polyvinyl butyral resin, 5 parts of metal packing.
Thermoset synthetic resin in the present embodiment is by epoxy resin, phenolic resin and vinyl ester resin, according to weight
Than 3:1:The mixture of 2 compositions.
Nano filling in the present embodiment is nano silicon, nano-calcium carbonate, nano titanium oxide, according to Ou Chongliang
Than 3:2:The mixture of 0.5 composition.
Glass microballoon in the present embodiment is hollow glass micropearl, and the particle size range of the hollow glass micropearl is 50-100
Micron.
Processing aid in the present embodiment is plasticizer, stabilizer, curing agent compare 3 according to weight:1:The mixing of 2 compositions
Thing, the plasticizer is the fat of phosphorus benzene bis-acid potassium two, and the stabilizer is triphenyl phosphite, and the curing agent is triethylene four
Amine.
Metal packing copper powder, iron powder and tungsten powder in the present embodiment, compare 3 according to weight:1:The mixture of 2 compositions, it is described
The fineness of metal powder is between 300-400 mesh.
A kind of power distribution station electric power cabinet preparation method of glass steel surface plate material of the present embodiment, comprises the following steps：
Step one, each component raw material is weighed on request；
Step 2, Nano filling, glass fibre, glass microballoon, graphite powder, metal packing, furane resins bonding agent are mixed and added
Enter mixer, stir 20 minutes, speed of agitator is 450r/min, obtains mixture A；
Step 3, thermoset synthetic resin, polytetrafluoroethylene (PTFE), polyvinyl butyral resin are mixed and add the reaction with mixer
In kettle, in the case where temperature is 70 DEG C, stir 10 minutes, speed of agitator is 300r/min, add processing aid and be prepared by step 2
Mixture A, be warming up to 120 DEG C, continue to stir 18 minutes, the mixture B after stirring is sent into double screw extruder, barrel and
Head temperature is 180 DEG C, and screw speed is 80r/min, and extrudate pours into the mold plate, the distribution that natural cooling sizing is invented
Stand electric power cabinet glass steel surface plate material.
Embodiment 3.
A kind of power distribution station electric power cabinet glass steel surface plate material of the present embodiment, includes the raw material of following parts by weight：
65 parts of thermoset synthetic resin, 7 parts of Nano filling, 10 parts of glass fibre, 5 parts of furane resins bonding agent, polytetrafluoroethylene (PTFE) 3
Part, 1.5 parts of glass microballoon, 0.7 part of graphite powder, 5 parts of processing aid, 11 parts of polyvinyl butyral resin, 4 parts of metal packing.
Thermoset synthetic resin in the present embodiment is by epoxy resin, phenolic resin and vinyl ester resin, according to weight
Than 3:1:The mixture of 2 compositions.
Nano filling in the present embodiment is nano silicon, nano-calcium carbonate, nano titanium oxide, according to Ou Chongliang
Than 3:2:The mixture of 0.5 composition.
Glass microballoon in the present embodiment is hollow glass micropearl, and the particle size range of the hollow glass micropearl is 50-100
Micron.
Processing aid in the present embodiment is plasticizer, stabilizer, curing agent compare 3 according to weight:1:The mixing of 2 compositions
Thing, the plasticizer is the fat of phosphorus benzene bis-acid potassium two, and the stabilizer is triphenyl phosphite, and the curing agent is triethylene four
Amine.
Metal packing copper powder, iron powder and tungsten powder in the present embodiment, compare 3 according to weight:1:The mixture of 2 compositions, it is described
The fineness of metal powder is between 300-400 mesh.
A kind of power distribution station electric power cabinet preparation method of glass steel surface plate material of the present embodiment, comprises the following steps：
Step one, each component raw material is weighed on request；
Step 2, Nano filling, glass fibre, glass microballoon, graphite powder, metal packing, furane resins bonding agent are mixed and added
Enter mixer, stir 15 minutes, speed of agitator is 400r/min, obtains mixture A；
Step 3, thermoset synthetic resin, polytetrafluoroethylene (PTFE), polyvinyl butyral resin are mixed and add the reaction with mixer
It is at 65 DEG C, to stir 9 minutes, speed of agitator is 250r/min, add prepared by processing aid and step 2 in temperature in kettle
Mixture A, is warming up to 110 DEG C, continues to stir 14 minutes, the mixture B after stirring is sent into double screw extruder, barrel and machine
Head temperature is 175 DEG C, and screw speed is 70r/min, and extrudate pours into the mold plate, the power distribution station that natural cooling sizing is invented
Electric power cabinet glass steel surface plate material.
Power distribution station electric power cabinet prepared by various embodiments above is as follows with the performance test results of glass steel surface plate material：
| Compressive strength MPa | Flexibility MPa | Impact strength KJ/m2 | |
| Embodiment 1 | 25 | 308 | 197 |
| Embodiment 2 | 26 | 310 | 193 |
| Embodiment 3 | 25 | 310 | 192 |
| Comparative example | 20 | 270 | 178 |
A kind of power distribution station electric power cabinet of the present invention is with glass steel surface plate material its density is small, lightweight, hardness is high, good toughness, electricity
Good insulating, with preferable fire resistance, corrosion resistance and wearability；While the preparation side of the insulating coating material of the present invention
Method, its material cost is relatively low, raw material is easy to get and technique concise, industrialized production easy to operate and realize, with higher practicality
Value and good application prospect.
It is obvious to a person skilled in the art that the invention is not restricted to the details of above-mentioned one exemplary embodiment, Er Qie
In the case of without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, no matter
From the point of view of which point, embodiment all should be regarded as exemplary, and be nonrestrictive, the scope of the present invention is by appended power
Profit is required rather than described above is limited, it is intended that all in the implication and scope of the equivalency of claim by falling
Change is included in the present invention.
Moreover, it will be appreciated that although the present specification is described in terms of embodiments, not each embodiment is only wrapped
Containing an independent technical scheme, this narrating mode of specification is only that for clarity, those skilled in the art should
Using specification as an entirety, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
It may be appreciated other embodiment.
Claims (9)
1. a kind of power distribution station electric power cabinet glass steel surface plate material, it is characterised in that include the raw material of following parts by weight：
It is 60-70 parts of thermoset synthetic resin, 6-8 parts of Nano filling, 8-12 parts of glass fibre, 4-6 parts of furane resins bonding agent, poly-
2-4 parts of tetrafluoroethene, 1-2 parts of glass microballoon, 0.5-0.9 parts of graphite powder, 3-7 parts of processing aid, polyvinyl butyral resin 8-15
Part, 3-5 parts of metal packing.
2. a kind of power distribution station electric power cabinet glass steel surface plate material according to claim 1, it is characterised in that the distribution
Electric power cabinet glass steel surface plate material of standing includes the raw material of following parts by weight：
65 parts of thermoset synthetic resin, 7 parts of Nano filling, 10 parts of glass fibre, 5 parts of furane resins bonding agent, polytetrafluoroethylene (PTFE) 3
Part, 1.5 parts of glass microballoon, 0.7 part of graphite powder, 5 parts of processing aid, 11 parts of polyvinyl butyral resin, 4 parts of metal packing.
3. a kind of power distribution station electric power cabinet glass steel surface plate material according to claim 1 or 2, it is characterised in that described
Thermoset synthetic resin compares 3 by epoxy resin, phenolic resin and vinyl ester resin according to weight:1:The mixture of 2 compositions.
4. a kind of power distribution station electric power cabinet glass steel surface plate material according to claim 1 or 2, it is characterised in that described
Nano filling is nano silicon, nano-calcium carbonate, nano titanium oxide, compares 3 according to Ou Chongliang:2:The mixing of 0.5 composition
Thing.
5. a kind of power distribution station electric power cabinet glass steel surface plate material according to claim 1 or 2, it is characterised in that described
Glass microballoon is hollow glass micropearl, and the particle size range of the hollow glass micropearl is 50-100 microns.
6. a kind of power distribution station electric power cabinet glass steel surface plate material according to claim 1 or 2, it is characterised in that described
Processing aid is plasticizer, stabilizer, curing agent compare 3 according to weight:1:The mixture of 2 compositions, the plasticizer is phosphorus benzene two
The fat of formic acid two, the stabilizer is triphenyl phosphite, and the curing agent is triethylene tetramine.
7. a kind of power distribution station electric power cabinet glass steel surface plate material according to claim 1 or 2, it is characterised in that described
Metal packing copper powder, iron powder and tungsten powder, compare 3 according to weight:1:The mixture of 2 compositions, the fineness of the metal powder is in 300-400
Between mesh.
8. a kind of method for preparing power distribution station electric power cabinet glass steel surface plate material as claimed in claim 1 or 2, its feature exists
In comprising the following steps：
Step one, each component raw material is weighed on request；
Step 2, Nano filling, glass fibre, glass microballoon, graphite powder, metal packing, furane resins bonding agent are mixed and added
Enter mixer, stir 10-20 minutes, speed of agitator is 350-450r/min, obtains mixture A；
Step 3, thermoset synthetic resin, polytetrafluoroethylene (PTFE), polyvinyl butyral resin are mixed and add the reaction with mixer
In kettle, in the case where temperature is 60-70 DEG C, stir 8-10 minutes, speed of agitator is 200-300r/min, adds processing aid and step
The rapid two mixture A prepared, are warming up to 100-120 DEG C, continue to stir 10-18 minutes, and the mixture B after stirring is sent into double spiral shells
Bar extruder, barrel and head temperature are 170-180 DEG C, and screw speed is 60-80r/min, and extrudate pours into the mold plate, natural
The power distribution station electric power cabinet glass steel surface plate material that cooling and shaping is invented.
9. a kind of preparation method of power distribution station electric power cabinet glass steel surface plate material according to claim 8, its feature exists
In the preparation process is：
Step one, each component raw material is weighed on request；
Step 2, Nano filling, glass fibre, glass microballoon, graphite powder, metal packing, furane resins bonding agent are mixed and added
Enter mixer, stir 15 minutes, speed of agitator is 400r/min, obtains mixture A；
Step 3, thermoset synthetic resin, polytetrafluoroethylene (PTFE), polyvinyl butyral resin are mixed and add the reaction with mixer
It is at 65 DEG C, to stir 9 minutes, speed of agitator is 250r/min, add prepared by processing aid and step 2 in temperature in kettle
Mixture A, is warming up to 110 DEG C, continues to stir 14 minutes, the mixture B after stirring is sent into double screw extruder, barrel and machine
Head temperature is 175 DEG C, and screw speed is 70r/min, and extrudate pours into the mold plate, the power distribution station that natural cooling sizing is invented
Electric power cabinet glass steel surface plate material.