CN105925044A - Fiber-reinforced plastic panel for environment-friendly power distribution cabinet and production method thereof - Google Patents
Fiber-reinforced plastic panel for environment-friendly power distribution cabinet and production method thereof Download PDFInfo
- Publication number
- CN105925044A CN105925044A CN201610414945.7A CN201610414945A CN105925044A CN 105925044 A CN105925044 A CN 105925044A CN 201610414945 A CN201610414945 A CN 201610414945A CN 105925044 A CN105925044 A CN 105925044A
- Authority
- CN
- China
- Prior art keywords
- parts
- reinforced plastic
- plastic panel
- power distribution
- distribution cabinet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a fiber-reinforced plastic panel for an environment-friendly power distribution cabinet and a production method thereof. The fiber-reinforced plastic panel is made from 35-55 parts of epoxy resin, 20-25 parts of fluororesin, 40-50 parts of reinforcing fiber, 15-25 parts of diatomite, 8-15 parts of polyvinyl butyral, 6-10 parts of cobalt naphthenate styrene, 5-10 parts of cyclohexanone peroxide, 2-4 parts of polyester resin, 4-8 parts of titanium dioxide, 3-9 parts of triethylamine, 4-8 parts of aluminum oxide, 2-4 parts of a dispersant, 1-5 parts of a defoaming agent, 3-6 parts of a plasticizer, 1-5 parts of a stabilizer, and 2-8 parts of a curing agent. The panel produced from the above materials in a scientific ratio is low in density, light in weight, high in hardness, good in toughness and good in electrical insulation, has good fire resistance, corrosion resistance, wear resistance and antistatic property, is time- and labor-efficient to mount, is safe and reliable and enables a longer life for a power cabinet.
Description
Technical field
The present invention relates to glass reinforced plastic panel manufacture technology field, be specifically related to a kind of environmental protection power distribution cabinet glass reinforced plastic panel and preparation method thereof.
Background technology
Current electric power cabinet shell is mainly made with cold-rolled steel sheet or corrosion resistant plate, and the intensity of cold-rolled steel sheet is the highest, surface-brightening, but toughness, solderability are poor, harder, crisp, if there is solder skip, then can intake, cause the components and parts within electric power cabinet to scrap even breaking out of fire, there is potential safety hazard.Corrosion resistant plate has enough intensity, there is again fabulous plasticity, hardness is the highest, it is simple to processing, but owing to being chronically at outdoor, environment is poor, so corrosion resistance can not meet use demand well so that the service life of electric power cabinet is shorter, the acid rain formed after especially raining has extremely strong corrosivity to electric power cabinet outer surface, once electric power cabinet is corroded, and power system will face great danger.Other electric power cabinet is used for carrying high voltage power supply, current electric power cabinet is generally iron sheet and makes shell, particularly in the dry north, often due to dust friction produces electrostatic, this results in high voltage power supply electric power cabinet and is extremely susceptible to fire hazard, and consequence is hardly imaginable.And the density of corrosion resistant plate is relatively big, wastes time and energy during installation, electrical insulating property is poor, there is also potential safety hazard.
Summary of the invention
For solving the problems referred to above, the invention provides a kind of environmental protection power distribution cabinet glass reinforced plastic panel and preparation method thereof.
For achieving the above object, the technical scheme that the present invention takes is:
A kind of environmental protection power distribution cabinet glass reinforced plastic panel and preparation method thereof, is prepared from including by the raw material of following weight portion: epoxy resin 35-55 part, fluororesin 20-25 part, reinforcing fiber 40-50 part, kieselguhr 15-25 part, polyvinyl butyral resin 8-15 part, naphthoic acid cobalt styrene 6-10 part, cyclohexanone peroxide 5-10 part, polyester resin 2-4 part, titanium dioxide 4-8 part, triethylamine 3-9 part, aluminium sesquioxide 4-8 part, dispersant 2-4 part, defoamer 1-5 part, plasticizer 3-6 part, stabilizer 1-5 part and firming agent 2-8 part.
Further, one or more during described reinforcing fiber is carbon fiber, glass fibre, polyethylene fibre.
Further, described plasticizer is phosphorus benzene bis-acid potassium two fat, and described stabilizer is triphenyl phosphite, and described firming agent is triethylene tetramine.
Further, the preparation method of a kind of environmental protection power distribution cabinet glass reinforced plastic panel, comprise the steps:
S1, glass cleaning is clean, drying；
S2, will be polished at glass surface with electric polisher, reach mirror effect；Then uniform brushing releasing agent；
S3, weigh epoxy resin 35-55 part according to weight portion, fluororesin 20-25 part, reinforcing fiber 40-50 part, kieselguhr 15-25 part, polyvinyl butyral resin 8-15 part, naphthoic acid cobalt styrene 6-10 part, cyclohexanone peroxide 5-10 part, polyester resin 2-4 part, titanium dioxide 4-8 part, triethylamine 3-9 part, aluminium sesquioxide 4-8 part, dispersant 2-4 part, defoamer 1-5 part, plasticizer 3-6 part, stabilizer 1-5 part and firming agent 2-8 part add in stirring container, stir 10-20min at temperature is 30-55 DEG C；Obtain gumming solution；
S4, on the glass of step S2, the gumming solution of step S3 gained is uniformly brushed, the most at room temperature stand 10-15min, continue brushing gumming solution；
S5, finally by after step S4 gluing glass drying device dry after obtain surface should smooth, the glass reinforced plastic panel of flawless, uniform color.
Further, a kind of environmental protection power distribution cabinet glass reinforced plastic panel, is prepared from including by the raw material of following weight portion: epoxy resin 36-50 part, fluororesin 21-24 part, reinforcing fiber 45-58 part, kieselguhr 18-20 part, polyvinyl butyral resin 9-14 part, naphthoic acid cobalt styrene 7-9 part, cyclohexanone peroxide 6-9 part, polyester resin 3-4 part, titanium dioxide 5-7 part, triethylamine 4-8 part, aluminium sesquioxide 5-7 part, dispersant 2-4 part, defoamer 2-4 part, plasticizer 4-6 part, stabilizer 2-5 part and firming agent 4-7 part.
Further, a kind of environmental protection power distribution cabinet glass reinforced plastic panel, is prepared from including by the raw material of following weight portion: epoxy resin 39 parts, fluororesin 23 parts, reinforcing fiber 48 parts, 19 parts of kieselguhr, polyvinyl butyral resin 11 parts, naphthoic acid cobalt styrene 8 parts, cyclohexanone peroxide 6 parts, 4 parts of polyester resin, titanium dioxide 6 parts, triethylamine 5 parts, aluminium sesquioxide 6 parts, dispersant 3 parts, defoamer 3 parts, plasticizer 5 parts, stabilizer 4 parts and 6 parts of firming agent.
The present invention uses above-mentioned raw materials to carry out the proportioning combination of science, the panel prepared, density is little, lightweight, and hardness is high, good toughness, electrical insulating property is good, has preferable fire resistance, corrosion resistance, wearability and anti-static ability, time saving and energy saving during installation, safe and reliable, extend the service life of electric power cabinet.
Glass fibre heatproof is high, does not fires, anti-corruption, heat insulation, and tensile strength is high, and electrical insulating property is good, but property is crisp, and wearability is poor.Adhering with epoxy resin is strong, wearability is strong, resistance to water is strong, thermostability is strong, mechanicalness is strong, electrical insulating property is strong, chemical stability is strong, resistant of high or low temperature is strong, shrinkage factor is low, internal stress is low, good toughness；
Kieselguhr pH value is neutral, nontoxic, and suspendability is good, and absorption property is strong, and unit weight is light；
Fluororesin has the characteristics such as high and low temperature resistance, dielectric properties, chemical stability, weatherability, noninflammability, non-stick and the low coefficient of friction of excellence；
Firming agent can make panel rapid solidification in the preparation；
Detailed description of the invention
In order to make objects and advantages of the present invention clearer, below in conjunction with embodiment, the present invention is further elaborated.Should be appreciated that specific embodiment described herein, only in order to explain the present invention, is not intended to limit the present invention.
The present invention includes being prepared from by the raw material of following weight portion: epoxy resin 35-55 part, fluororesin 20-25 part, reinforcing fiber 40-50 part, kieselguhr 15-25 part, polyvinyl butyral resin 8-15 part, naphthoic acid cobalt styrene 6-10 part, cyclohexanone peroxide 5-10 part, polyester resin 2-4 part, titanium dioxide 4-8 part, triethylamine 3-9 part, aluminium sesquioxide 4-8 part, dispersant 2-4 part, defoamer 1-5 part, plasticizer 3-6 part, stabilizer 1-5 part and firming agent 2-8 part.
Described reinforcing fiber is one or more in carbon fiber, glass fibre, polyethylene fibre.
Described plasticizer is phosphorus benzene bis-acid potassium two fat, and described stabilizer is triphenyl phosphite, and described firming agent is triethylene tetramine.
The preparation method of a kind of environmental protection power distribution cabinet glass reinforced plastic panel, comprises the steps:
S1, glass cleaning is clean, drying；
S2, will be polished at glass surface with electric polisher, reach mirror effect；Then uniform brushing releasing agent；
S3, weigh epoxy resin 35-55 part according to weight portion, fluororesin 20-25 part, reinforcing fiber 40-50 part, kieselguhr 15-25 part, polyvinyl butyral resin 8-15 part, naphthoic acid cobalt styrene 6-10 part, cyclohexanone peroxide 5-10 part, polyester resin 2-4 part, titanium dioxide 4-8 part, triethylamine 3-9 part, aluminium sesquioxide 4-8 part, dispersant 2-4 part, defoamer 1-5 part, plasticizer 3-6 part, stabilizer 1-5 part and firming agent 2-8 part add in stirring container, stir 10-20min at temperature is 30-55 DEG C；Obtain gumming solution；
S4, on the glass of step S2, the gumming solution of step S3 gained is uniformly brushed, the most at room temperature stand 10-15min, continue brushing gumming solution；
S5, finally by after step S4 gluing glass drying device dry after obtain surface should smooth, the glass reinforced plastic panel of flawless, uniform color.
A kind of environmental protection power distribution cabinet glass reinforced plastic panel, is prepared from including by the raw material of following weight portion: epoxy resin 36-50 part, fluororesin 21-24 part, reinforcing fiber 45-58 part, kieselguhr 18-20 part, polyvinyl butyral resin 9-14 part, naphthoic acid cobalt styrene 7-9 part, cyclohexanone peroxide 6-9 part, polyester resin 3-4 part, titanium dioxide 5-7 part, triethylamine 4-8 part, aluminium sesquioxide 5-7 part, dispersant 2-4 part, defoamer 2-4 part, plasticizer 4-6 part, stabilizer 2-5 part and firming agent 4-7 part.
Embodiment 1:
S1, glass cleaning is clean, drying；
S2, will be polished at glass surface with electric polisher, reach mirror effect；Then uniform brushing releasing agent；
S3, weigh epoxy resin 39 parts according to weight portion, fluororesin 23 parts, reinforcing fiber 48 parts, 19 parts of kieselguhr, polyvinyl butyral resin 11 parts, naphthoic acid cobalt styrene 8 parts, cyclohexanone peroxide 6 parts, 4 parts of polyester resin, titanium dioxide 6 parts, triethylamine 5 parts, aluminium sesquioxide 6 parts, dispersant 3 parts, defoamer 3 parts, plasticizer 5 parts, stabilizer 4 parts and 6 parts of firming agent add in stirring container, stir 15min at temperature is 44 DEG C；Obtain gumming solution；
S4, on the glass of step S2, the gumming solution of step S3 gained is uniformly brushed, the most at room temperature stand 12min, continue brushing gumming solution；
S5, finally by after step S4 gluing glass drying device dry after obtain surface should smooth, the glass reinforced plastic panel of flawless, uniform color.
Embodiment 2:
S1, glass cleaning is clean, drying；
S2, will be polished at glass surface with electric polisher, reach mirror effect；Then uniform brushing releasing agent；
S3, weigh epoxy resin 55 parts according to weight portion, fluororesin 25 parts, reinforcing fiber 50 parts, 25 parts of kieselguhr, polyvinyl butyral resin 15 parts, naphthoic acid cobalt styrene 10 parts, cyclohexanone peroxide 10 parts, 4 parts of polyester resin, titanium dioxide 8 parts, triethylamine 9 parts, aluminium sesquioxide 8 parts, dispersant 4 parts, defoamer 5 parts, plasticizer 6 parts, stabilizer 5 parts and 8 parts of firming agent add in stirring container, stir 20min at temperature is 55 DEG C；Obtain gumming solution；
S4, on the glass of step S2, the gumming solution of step S3 gained is uniformly brushed, the most at room temperature stand 15min, continue brushing gumming solution；
S5, finally by after step S4 gluing glass drying device dry after obtain surface should smooth, the glass reinforced plastic panel of flawless, uniform color.
Embodiment 3:
S1, glass cleaning is clean, drying；
S2, will be polished at glass surface with electric polisher, reach mirror effect；Then uniform brushing releasing agent；
S3, weigh epoxy resin 35 parts according to weight portion, fluororesin 20 parts, reinforcing fiber 40 parts, 15 parts of kieselguhr, polyvinyl butyral resin 8 parts, naphthoic acid cobalt styrene 6 parts, cyclohexanone peroxide 5 parts, 2 parts of polyester resin, titanium dioxide 4 parts, triethylamine 3 parts, aluminium sesquioxide 4 parts, dispersant 2 parts, defoamer 1 part, plasticizer 3 parts, stabilizer 1 part and 2 parts of firming agent add in stirring container, stir 10min at temperature is 30 DEG C；Obtain gumming solution；
S4, on the glass of step S2, the gumming solution of step S3 gained is uniformly brushed, the most at room temperature stand 10-15min, continue brushing gumming solution；
S5, finally by after step S4 gluing glass drying device dry after obtain surface should smooth, the glass reinforced plastic panel of flawless, uniform color.
The present invention uses above-mentioned raw materials to carry out the proportioning combination of science, the panel prepared, density is little, lightweight, and hardness is high, good toughness, electrical insulating property is good, has preferable fire resistance, corrosion resistance, wearability and anti-static ability, time saving and energy saving during installation, safe and reliable, extend the service life of electric power cabinet.
The above is only the preferred embodiment of the present invention; it should be pointed out that, for those skilled in the art, under the premise without departing from the principles of the invention; can also make some improvements and modifications, these improvements and modifications also should be regarded as protection scope of the present invention.
Claims (6)
1. an environmental protection power distribution cabinet glass reinforced plastic panel, it is characterized in that, be prepared from including by the raw material of following weight portion: epoxy resin 35-55 part, fluororesin 20-25 part, reinforcing fiber 40-50 part, kieselguhr 15-25 part, polyvinyl butyral resin 8-15 part, naphthoic acid cobalt styrene 6-10 part, cyclohexanone peroxide 5-10 part, polyester resin 2-4 part, titanium dioxide 4-8 part, triethylamine 3-9 part, aluminium sesquioxide 4-8 part, dispersant 2-4 part, defoamer 1-5 part, plasticizer 3-6 part, stabilizer 1-5 part and firming agent 2-8 part.
A kind of environmental protection power distribution cabinet glass reinforced plastic panel the most according to claim 1, it is characterised in that described reinforcing fiber is one or more in carbon fiber, glass fibre, polyethylene fibre.
A kind of environmental protection power distribution cabinet glass reinforced plastic panel the most according to claim 1, it is characterised in that described plasticizer is phosphorus benzene bis-acid potassium two fat, and described stabilizer is triphenyl phosphite, and described firming agent is triethylene tetramine.
The preparation method of a kind of environmental protection power distribution cabinet glass reinforced plastic panel the most according to claim 1, it is characterised in that comprise the steps:
S1, glass cleaning is clean, drying；
S2, will be polished at glass surface with electric polisher, reach mirror effect；Then uniform brushing releasing agent；
S3, weigh epoxy resin 35-55 part according to weight portion, fluororesin 20-25 part, reinforcing fiber 40-50 part, kieselguhr 15-25 part, polyvinyl butyral resin 8-15 part, naphthoic acid cobalt styrene 6-10 part, cyclohexanone peroxide 5-10 part, polyester resin 2-4 part, titanium dioxide 4-8 part, triethylamine 3-9 part, aluminium sesquioxide 4-8 part, dispersant 2-4 part, defoamer 1-5 part, plasticizer 3-6 part, stabilizer 1-5 part and firming agent 2-8 part add in stirring container, stir 10-20min at temperature is 30-55 DEG C；Obtain gumming solution；
S4, on the glass of step S2, the gumming solution of step S3 gained is uniformly brushed, the most at room temperature stand 10-15min, continue brushing gumming solution；
S5, finally by after step S4 gluing glass drying device dry after obtain surface should smooth, the glass reinforced plastic panel of flawless, uniform color.
A kind of environmental protection power distribution cabinet glass reinforced plastic panel the most according to claim 1, it is characterized in that, be prepared from including by the raw material of following weight portion: epoxy resin 36-50 part, fluororesin 21-24 part, reinforcing fiber 45-58 part, kieselguhr 18-20 part, polyvinyl butyral resin 9-14 part, naphthoic acid cobalt styrene 7-9 part, cyclohexanone peroxide 6-9 part, polyester resin 3-4 part, titanium dioxide 5-7 part, triethylamine 4-8 part, aluminium sesquioxide 5-7 part, dispersant 2-4 part, defoamer 2-4 part, plasticizer 4-6 part, stabilizer 2-5 part and firming agent 4-7 part.
A kind of environmental protection power distribution cabinet glass reinforced plastic panel the most according to claim 1, it is characterized in that, be prepared from including by the raw material of following weight portion: epoxy resin 39 parts, fluororesin 23 parts, reinforcing fiber 48 parts, 19 parts of kieselguhr, polyvinyl butyral resin 11 parts, naphthoic acid cobalt styrene 8 parts, cyclohexanone peroxide 6 parts, 4 parts of polyester resin, titanium dioxide 6 parts, triethylamine 5 parts, aluminium sesquioxide 6 parts, dispersant 3 parts, defoamer 3 parts, plasticizer 5 parts, stabilizer 4 parts and 6 parts of firming agent.