CN107086483A - A kind of insulated type metal dampers plate and preparation method thereof - Google Patents
A kind of insulated type metal dampers plate and preparation method thereof Download PDFInfo
- Publication number
- CN107086483A CN107086483A CN201710443447.XA CN201710443447A CN107086483A CN 107086483 A CN107086483 A CN 107086483A CN 201710443447 A CN201710443447 A CN 201710443447A CN 107086483 A CN107086483 A CN 107086483A
- Authority
- CN
- China
- Prior art keywords
- plate
- type metal
- plate body
- metallic plate
- valve plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to a kind of insulated type metal dampers plate and preparation method thereof, belong to power supply or switching device for power distribution technical field.The insulated type metal dampers plate of the present invention, including the valve plate body being made up of insulating materials, the side of the valve plate body are provided with metallic plate, and bonding material layer is provided between the metallic plate and the valve plate body.The insulated type metal dampers plate of the present embodiment, valve plate body can make insulated type metal dampers have good electrical insulation capability, the mechanical strength of the metallic plate on valve plate body and energy reinforced insulation type metal dampers plate；The adhesion strength between metallic plate and valve plate body can be strengthened by being arranged on the layer of the bonding material between metallic plate and valve plate body, moreover it is possible to further enhance the electrical insulating property of insulated type metal dampers plate.
Description
Technical field
The present invention relates to a kind of insulated type metal dampers plate and preparation method thereof, belong to power supply or switching device for power distribution skill
Art field.
Background technology
Power distribution network is standardized to power supply reliability and the requirement more and more higher of security.Valve is AC metal closed switch
One of very important part in equipment, its reliability and security are to the stable operation of power network and the safety of plant maintenance personnel
Ensure extremely important.At present, the valve on ac metal closing switch gear is generally metal dampers or insulating materials valve, gold
Typically spraying epoxy powder is made category valve on a metal plate, because the volume of metallic plate is big, during dusty spray, gold
The deflection deformation for belonging to plate is big, covers epoxy powder uneven, the epoxy layer thickness dispersiveness after shaping is larger, and yield rate is not
Height, is not suitable for batch machining；Insulating materials valve is typically made up of single insulating materials (such as BMC plates), by insulating materials sheet
The limitation of body, insulating materials valve is easily deformed in use, mechanical strength and electrical strength existing defects, sternly
The reliability and security of insulating materials valve are have impact on again.
In the prior art, Authorization Notice No. discloses a kind of high insulation for CN204045943U Chinese utility model patent
Type valve arrangement, including upper valve and lower valve, upper valve and lower valve are made up of metal material, and surface is provided with and uses ring
The epoxy insulation layer for being used to isolate one-time contact of oxygen layer sulfuration process coating.The valve has a preferable mechanical strength, but
During use, coat, which is easily scratched, to come off to influence the insulating properties of valve.
The content of the invention
It is an object of the invention to provide the good insulated type metal dampers plate of a kind of high mechanical strength, electrical insulation capability.
Present invention also offers a kind of above-mentioned preparation method of insulated type metal dampers plate.
In order to realize the above object the technical scheme that the insulated type metal dampers plate of the present invention is used is：
A kind of insulated type metal dampers plate, including the valve plate body being made up of insulating materials, the valve plate body
Side is provided with metallic plate, and bonding material layer is provided between the metallic plate and the valve plate body.
The insulated type metal dampers plate of the present invention, metallic plate is arranged on the valve plate body being made up of insulating materials,
On the one hand the valve plate body being made up of insulating materials can make insulated type metal dampers have good electrical insulation capability, another
Aspect is arranged on the metallic plate on valve plate body and the mechanical strength of energy reinforced insulation type metal dampers plate；It is arranged on metallic plate
Bonding material layer between valve plate body can strengthen the adhesion strength between metallic plate and valve plate body, moreover it is possible to enter one
Walk the electrical insulating property of reinforced insulation type metal dampers plate.
The thickness of the metallic plate is 0.5~1.0mm.The thickness of the bonding material layer is 0.5~1.5mm.The work
The thickness of door-plate body is 6.0~9.0mm.
The bonding material layer is included away from the first silane coupling agent coating, the adhesive solidification arranged successively on metallic plate direction
Layer and the second primer layer.The thickness ratio of first primer layer, adhesive cured layer and the second primer layer be 0.05~
0.10:0.4~1.3:0.05~0.10.
The valve plate body is provided with groove, and the metallic plate is arranged in groove, and the bonding material layer is located at recessed
The bottom of groove.Metallic plate is arranged in groove, the thickness and weight of insulated type metal dampers plate can be reduced；Preparing simultaneously
During metal dampers plate, it is easy to the positioning to metallic plate and smears silane coupling agent and adhesive, and silane coupling agent can be prevented and gluing
Agent is flowed out.
The metallic plate is identical with the depth of groove with the thickness sum of bonding material layer.
The side of the remote metallic plate of the valve plate body is provided with reinforcement.Reinforcement is set on valve plate body
The mechanical strength of insulated type metal dampers plate can be further enhanced.
Pigtail splice is provided with the metallic plate.The pigtail splice is lead bolt.Set pigtail splice be easy to by
Metal plate earthing, it is to avoid leakage current and charge inducing cause damage to equipment and affected personnel, further enhancing insulated type
The security of metal dampers plate.
The valve plate body is SMC or BMC compacting is formed.The material of metallic plate can select carbon structural steels or
Stainless steel, such as Q195 carbon structural steels, 1Cr18Ni9Ti stainless steels.
The technical scheme that is used of preparation method of the insulated type metal dampers plate of the present invention for：
A kind of preparation method of above-mentioned insulated type metal dampers plate, comprises the following steps：
1) it will be used for setting the position progress polishing of metallic plate to form buffed surface on valve plate body, buffed surface is cleared up dry
Only；
It will be used for carrying out phosphorating treatment formation adhesive surface, Ran Houzai with the one side that valve plate body is bonded on metallic plate
Adhesive surface is cleaned, dried；
2) silane coupling agent is coated on the buffed surface of valve plate body and the adhesive surface of metallic plate respectively, solvent flashing is stood；
3) buffed surface and metallic plate that valve plate body is coated with into silane coupling agent coat the adhesive surface of silane coupling agent using gluing
Agent is bonded, and is produced.
The preparation method of the insulated type metal dampers plate of the present invention, process is simple to operate, and metal is lived
Door-plate is more smooth, operates safety and reliability, it is possible to increase electrically and mechanical strength.
The silane coupling agent can use the silane coupling agent of prior art.Such as, GBN-11 silane coupling agents or 1812 type bottoms can be used
Paint.GBN-11 silane coupling agents produce for Zhonglan Chenguang Chemical Institute Co., Ltd..1812 type silane coupling agents are that chemical industry is held high by Guangzhou state
Science and Technology Ltd. produces, and the silane coupling agent is divided to 1812A and two kinds of components of 1812B.By 1812A and 1812B according to mass ratio be 10:
Used after 1 ratio mixing.
The cleaning fluid used when being cleaned to the metallic plate after phosphatization for second alcohol and water mixed liquor.
The bonding is that silicone rubber adhesive is coated on the buffed surface for coating the valve plate body after silane coupling agent, then will
The adhesive surface of metallic plate coating silane coupling agent is placed on buffed surface towards valve plate body, is solidified.
The adhesive is silicone rubber adhesive.
The silicone rubber adhesive is double component room temperature vulcanization silicon rubber.The host and vulcanizing agent of bi-component sulphurated siliastic
Mass ratio be 18~24:1.Using in first 30 minutes, the host is well mixed with vulcanizing agent, then is coated.Mixing
Carried out by the way of stirring.The rotating speed of stirring is 120~280r/min, and the time is 3~8min.
The double component room temperature vulcanization silicon rubber is GMX-6117 silicon rubber.GMX-6117 silicon rubber is middle blue morning twilight chemical industry
Co., Ltd of research institute produces.
The thickness that the adhesive is coated on valve plate body is 0.5~1.5mm.
The time of the solidification is 3~5h.
While solidification, pressure is applied to metallic plate and valve plate body.Stressed size is applied for 5.0~15.0MPa.
Set fluted on the valve plate body, be used for setting the position of metallic plate on valve plate body positioned at described recessed
Trench bottom.Metallic plate is arranged in groove, is easy to the positioning to metallic plate and smears silane coupling agent and adhesive, and can prevent
Only silane coupling agent and adhesive outflow；The thickness and quality of insulated type metal dampers plate can also be reduced simultaneously.
The preparation method of above-mentioned insulated type metal dampers plate, which is additionally included in, welds a number of bolt on metallic plate.In gold
The bolt welded on category plate can be for lead.
Brief description of the drawings
Fig. 1 is the structural representation of the insulated type metal dampers plate of embodiment 1；
Fig. 2 sets the structural representation of the side of groove for the valve plate body of the insulated type metal dampers plate of embodiment 1；
Fig. 3 sets the structural representation of the side of reinforcement for the valve plate body of the insulated type metal dampers plate of embodiment 1
Figure；
Fig. 4 is the front view of the metallic plate of the insulated type metal dampers plate of embodiment 1；
Fig. 5 is the left view of the metallic plate of the insulated type metal dampers plate of embodiment 1；
Fig. 6 is Fig. 1 A-A sectional views；
Fig. 7 is the structural representation of the insulated type metal dampers plate of embodiment 4.
Embodiment
Technical scheme is further described below in conjunction with embodiment.
The material of metallic plate employed in embodiment is Q195 carbon structural steels；The valve plate body used
For BMC plates.
Embodiment 1
The insulated type metal dampers plate of the present embodiment, as shown in figs. 1 to 6, including the valve plate sheet being made up of insulating materials
Body 1, the side of valve plate body 1, which is set in fluted 5, the groove 5, is provided with metallic plate 2, metallic plate 2 and the bottom of groove 5
Between be provided with bonding material layer 7, the side wall of metallic plate 2 is brought into close contact with the cell wall 3 of groove 5, sets leaded on metallic plate 2
Bolt 4；The first primer layer (not shown), gluing that bonding material layer 7 is arranged successively on the direction away from metallic plate 2
Agent cured layer (not shown) and the second primer layer (not shown) composition；The thickness of metallic plate 2 and bonding material layer 7
Sum is identical with the depth of groove 5；The side of the remote metallic plate 2 of valve plate body 1 is provided with reinforcement 6, and reinforcement 6 is by indulging
The wrong cross reinforcing of traversed by and waling composition.
The thickness of valve plate body 1 is 6.0mm, and the thickness of metallic plate 2 is 0.5mm, and the thickness of bonding material layer 7 is
0.5mm；The thickness ratio of first primer layer, bonding material layer and the second primer layer is 0.05：0.40：0.05.
The preparation method of the insulated type metal dampers plate of the present embodiment, comprises the following steps：
1) side is set into reeded valve plate body for setting the position of metallic plate to polish coarse with sand paper, formation is beaten
Flour milling, buffed surface is clean with alcohol washes, place 5min；For setting the position of metallic plate to be located at valve plate body side
Bottom portion of groove；
It will be used for carrying out phosphorating treatment formation adhesive surface with the one side that valve plate body is bonded on metallic plate, then will
Adhesive surface is clean with alcohol washes, places 5min；
2) silane coupling agent is coated on the buffed surface of valve plate body and the adhesive surface of metallic plate respectively, 3min volatilizations are stood molten
Agent；The GBN-11 type silane coupling agents that the silane coupling agent used produces for Co., Ltd of Zhong Lan morning twilight research institute；
3) by the host and vulcanizing agent of GMX-6117 silicon rubber according to 20:After 1 mass ratio mixing, with turning for 120r/min
Speed stirring 8min, is well mixed, and thickness is formed on the buffed surface that valve plate body coating silane coupling agent is coated onto in 30min
It is placed on for 0.5mm coat, then the adhesive surface that metallic plate is coated into silane coupling agent towards the buffed surface on valve plate body,
Increase places with the pressure for reforming 5.0MPa, solidifies 3h at normal temperatures on a metal plate；The GMX-6117 silicon rubber used
Produced for Zhonglan Chenguang Chemical Institute Co., Ltd.；
4) welding lead bolt, is produced and then on a metal plate.
Adhesive strength between the metallic plate and valve plate body of the insulated type metal dampers plate of the present embodiment is 900N/m,
Industrial frequency withstand voltage 42kV, without flashover is punctured, electrical insulation properties are good.
Embodiment 2
The insulated type valve plate of the present embodiment, including the valve plate body being made up of insulating materials, the one of valve plate body
Side set it is fluted, metallic plate is provided with groove, be provided between metallic plate and bottom portion of groove bonding material layer, metallic plate and
The cell wall of groove is brought into close contact, and leaded bolt is set on metallic plate；Bonding material layer by away from metallic plate direction on successively
The first primer layer, adhesive cured layer and the second primer layer composition of arrangement；The thickness of metallic plate and bonding material layer it
It is identical with the depth of groove；The side of the remote metallic plate of lead bolt valve plate body is provided with reinforcement, reinforcement by
Crisscross cross reinforcing and waling composition.
The thickness of valve plate body is 7.0mm, and the thickness of metallic plate is 0.8mm, and the thickness of bonding material layer is 1.0mm；
The thickness ratio of first primer layer, bonding material layer and the second primer layer is 0.10：0.80：0.10.
The preparation method of the insulated type metal dampers plate of the present embodiment, comprises the following steps：
1) side is set into reeded valve plate body for setting the position of metallic plate to polish coarse with sand paper, formation is beaten
Flour milling, buffed surface is clean with alcohol washes, place 4min；For setting the position of metallic plate to be located at valve plate body side
Bottom portion of groove；
It will be used for carrying out phosphorating treatment formation adhesive surface with the one side that valve plate body is bonded on metallic plate, then will
Adhesive surface is clean with alcohol washes, places 4min；
2) silane coupling agent is coated on the buffed surface of valve plate body and the adhesive surface of metallic plate respectively, 5min volatilizations are stood molten
Agent；The GBN-11 type silane coupling agents that the silane coupling agent used produces for Co., Ltd of Zhong Lan morning twilight research institute；
3) by the host and vulcanizing agent of GMX-6117 silicon rubber according to 20:After 1 mass ratio mixing, with turning for 200r/min
Speed stirring 5min, is well mixed, and thickness is formed on the buffed surface that valve plate body coating silane coupling agent is coated onto in 30min
It is placed on for 1mm coat, then the adhesive surface that metallic plate is coated into silane coupling agent towards the buffed surface on valve plate body,
Increase places with the pressure for reforming 8.0MPa, solidifies 5h at normal temperatures on metallic plate；The GMX-6117 silicon rubber used for
Zhonglan Chenguang Chemical Institute Co., Ltd. produces；
4) welding lead bolt, is produced and then on a metal plate.
Adhesive strength between the metallic plate and valve plate body of the insulated type metal dampers plate of the present embodiment is 950N/m,
Industrial frequency withstand voltage 42kV, without flashover is punctured, electrical insulation properties are good.
Embodiment 3
The insulated type valve plate of the present embodiment, including the valve plate body being made up of insulating materials, the one of valve plate body
Side set it is fluted, metallic plate is provided with groove, be provided between metallic plate and bottom portion of groove bonding material layer, metallic plate and
The cell wall of groove is brought into close contact, and leaded bolt is set on metallic plate；Bonding material layer by away from metallic plate direction on successively
The first primer layer, adhesive cured layer and the second primer layer composition of arrangement；The thickness of metallic plate and bonding material layer it
It is identical with the depth of groove；The side of the remote metallic plate of lead bolt valve plate body is provided with reinforcement, reinforcement by
Crisscross cross reinforcing and waling composition.
The thickness of valve plate body is 9.0mm, and the thickness of metallic plate is 1.0mm, and the thickness of bonding material layer is 1.5mm；
The thickness ratio of first primer layer, bonding material layer and the second primer layer is 0.10：1.30：0.10.
The preparation method of the insulated type metal dampers plate of the present embodiment, comprises the following steps：
1) side is set into reeded valve plate body for setting the position of metallic plate to polish coarse with sand paper, formation is beaten
Flour milling, buffed surface is clean with alcohol washes, place 4min；For setting the position of metallic plate to be located at valve plate body side
Bottom portion of groove；
It will be used for carrying out phosphorating treatment formation adhesive surface with the one side that valve plate body is bonded on metallic plate, then will
Adhesive surface is clean with alcohol washes, places 4min；
2) silane coupling agent is coated on the buffed surface of valve plate body and the adhesive surface of metallic plate respectively, 3min volatilizations are stood molten
Agent；The GBN-11 type silane coupling agents that the silane coupling agent used produces for Co., Ltd of Zhong Lan morning twilight research institute；
3) by the host and vulcanizing agent of GMX-6117 silicon rubber according to 20:After 1 mass ratio mixing, with turning for 280r/min
Speed stirring 3min, is well mixed, and thickness is formed on the buffed surface that valve plate body coating silane coupling agent is coated onto in 30min
It is placed on for 1.5mm coat, then the adhesive surface that metallic plate is coated into silane coupling agent towards the buffed surface on valve plate body,
Increase places with the pressure for reforming 15MPa, solidifies 5h at normal temperatures on a metal plate；The GMX-6117 silicon rubber used
Produced for Zhonglan Chenguang Chemical Institute Co., Ltd.；
4) welding lead bolt, is produced and then on a metal plate.
Adhesive strength between the metallic plate and valve plate body of the insulated type metal dampers plate of the present embodiment is 950N/m,
Industrial frequency withstand voltage 42kV, without flashover is punctured, electrical insulation properties are good.
Embodiment 4
The insulated type metal dampers plate of the present embodiment, as shown in fig. 7, comprises the valve plate body 1 being made up of insulating materials,
The side of valve plate body 1 sets and sets leaded bolt 4 on metallic plate 2, metallic plate 2；Metallic plate 2 and valve plate body 1 it
Between be provided with bonding material layer 7, bonding material layer 7 by away from metallic plate 2 direction on arrange successively the first primer layer (figure
In do not show), adhesive cured layer (not shown) and the second primer layer (not shown) composition；Valve plate body 1
The side of remote metallic plate 2 be provided with reinforcement 6, reinforcement 6 is by crisscross cross reinforcing and waling group
Into.
The thickness of valve plate body 1 is 6.0mm, and the thickness of metallic plate 2 is 1.0mm, and the thickness of bonding material layer 7 is
1.5mm；The thickness ratio of first primer layer, bonding material layer and the second primer layer is 0.10：1.30：0.10.
The preparation method of the insulated type metal dampers plate of the present embodiment, comprises the following steps：
1) valve plate body is used for setting to the position coarse formation buffed surface of sand paper polishing of metallic plate, buffed surface is used
Alcohol washes are clean, place 4min；
It will be used for carrying out phosphorating treatment formation adhesive surface with the one side that valve plate body is bonded on metallic plate, then will
Adhesive surface is clean with alcohol washes, places 4min；
2) silane coupling agent is coated on the buffed surface of valve plate body and the adhesive surface of metallic plate respectively, 3min volatilizations are stood molten
Agent；The GBN-11 type silane coupling agents that the silane coupling agent used produces for Co., Ltd of Zhong Lan morning twilight research institute；
3) by the host and vulcanizing agent of GMX-6117 silicon rubber according to 24:After 1 mass ratio mixing, with turning for 240r/min
Speed stirring 5min, is well mixed, and thickness is formed on the buffed surface that valve plate body coating silane coupling agent is coated onto in 30min
It is placed on for 1.5mm coat, then the adhesive surface that metallic plate is coated into silane coupling agent towards the buffed surface on valve plate body,
Increase places with the pressure for reforming 10MPa, solidifies 3h at normal temperatures on a metal plate；The GMX-6117 silicon rubber used
Produced for Zhonglan Chenguang Chemical Institute Co., Ltd.；
4) welding lead bolt, is produced and then on a metal plate.
Embodiment 5
The insulated type metal dampers plate of the present embodiment, including the valve plate body being made up of insulating materials, valve plate body
Side set it is fluted, metallic plate is provided with groove, be provided between metallic plate and bottom portion of groove bonding material layer, metal
The cell wall of plate and groove is brought into close contact, and leaded bolt is set on metallic plate；Bonding material layer is adhesive cured layer；Metallic plate
It is identical with the depth of groove with the thickness sum of bonding material layer；The side of the remote metallic plate of lead bolt valve plate body is set
Reinforcement is equipped with, reinforcement is made up of crisscross cross reinforcing and waling.
The thickness of valve plate body is 9.0mm, and the thickness of metallic plate is 1.0mm, and the thickness of bonding material layer is 1.5mm.
The preparation method of the insulated type metal dampers plate of the present embodiment, comprises the following steps：
1) side is set into reeded valve plate body for setting the position of metallic plate to polish coarse with sand paper, formation is beaten
Flour milling, buffed surface is clean with alcohol washes, place 4min；For setting the position of metallic plate to be located at valve plate body side
Bottom portion of groove；
It will be used for carrying out phosphorating treatment formation adhesive surface with the one side that valve plate body is bonded on metallic plate, then will
Adhesive surface is clean with alcohol washes, places 4min；
2) by the host and vulcanizing agent of GMX-6117 silicon rubber according to 20:After 1 mass ratio mixing, with turning for 280r/min
Speed stirring 3min, is well mixed, and it is 1.5mm's to be coated onto in 30min on the buffed surface of valve plate body and form thickness
Coat, then the adhesive surface that metallic plate is coated into silane coupling agent are placed on valve plate body towards the buffed surface, in metallic plate
Upper increase places with the pressure for reforming 10MPa, solidifies 5h at normal temperatures；The GMX-6117 silicon rubber used is middle blue morning
Co., Ltd of photoinitiator chemical research institute produces；
3) welding lead bolt, is produced and then on a metal plate.
The insulated type metal dampers plate of the present embodiment in the preparation, not using silane coupling agent, compared to other embodiment
Insulated type metal dampers plate, simply adhesion strength be slightly below other embodiment, other are functional.
Embodiment 6
The insulated type metal dampers plate of the present embodiment, including the valve plate body being made up of insulating materials, valve plate body
Side set it is fluted, metallic plate is provided with groove, be provided between metallic plate and bottom portion of groove bonding material layer, metal
The cell wall of plate and groove is brought into close contact, and leaded bolt is set on metallic plate；Bonding material layer is on the direction away from metallic plate
The first primer layer, adhesive cured layer and the second primer layer composition arranged successively；The thickness of metallic plate and bonding material layer
Spend sum identical with the depth of groove；The side of the remote metallic plate of lead bolt valve plate body is provided with reinforcement, strengthens
Muscle is made up of crisscross cross reinforcing and waling.
The thickness of valve plate body is 9.0mm, and the thickness of metallic plate is 1.0mm, and the thickness of bonding material layer is 1.5mm；
The thickness ratio of first primer layer, bonding material layer and the second primer layer is 0.10：1.30：0.10.
The preparation method of the insulated type metal dampers plate of the present embodiment, comprises the following steps：
1) side is set into reeded valve plate body for setting the position of metallic plate to polish coarse with sand paper, formation is beaten
Flour milling, buffed surface is clean with alcohol washes, place 4min；For setting the position of metallic plate to be located at valve plate body side
Bottom portion of groove；
It will be used for carrying out phosphorating treatment formation adhesive surface with the one side that valve plate body is bonded on metallic plate, then will
Adhesive surface is clean with alcohol washes, places 4min；
2) silane coupling agent is coated on the buffed surface of valve plate body and the adhesive surface of metallic plate respectively, 3min volatilizations are stood molten
Agent；The silane coupling agent used is AC78 silane coupling agent；
3) by the host and vulcanizing agent of GMX-6117 silicon rubber according to 20:After 1 mass ratio mixing, with turning for 280r/min
Speed stirring 3min, is well mixed, and thickness is formed on the buffed surface that valve plate body coating silane coupling agent is coated onto in 30min
It is placed on for 1.5mm coat, then the adhesive surface that metallic plate is coated into silane coupling agent towards the buffed surface on valve plate body,
Increase places with the pressure for reforming 10MPa, solidifies 5h at normal temperatures on a metal plate；The GMX-6117 silicon rubber used
Produced for Zhonglan Chenguang Chemical Institute Co., Ltd.；
4) welding lead bolt, is produced and then on a metal plate.
Adhesive strength between the metallic plate and valve plate body of the insulated type metal dampers plate of the present embodiment is 850N/M
More than, industrial frequency withstand voltage 42kV, without flashover is punctured, electrical insulation properties are good.
The embodiment 7 of the insulated type metal dampers plate of the present invention, does not have with differing only in for embodiment 1 on valve plate body
There is setting reinforcement.
The embodiment 8 of the insulated type metal dampers plate of the present invention, does not have with the top surface for differing only in metallic plate of embodiment 1
There is the cell wall beyond groove.
Claims (10)
1. a kind of insulated type metal dampers plate, including the valve plate body being made up of insulating materials, it is characterised in that：The valve
The side of plate body is provided with metallic plate, and bonding material layer is provided between the metallic plate and the valve plate body.
2. insulated type metal dampers plate according to claim 1, it is characterised in that：The valve plate body is provided with recessed
Groove, the metallic plate is arranged in groove, and the bonding material layer is located at the bottom of groove.
3. insulated type metal dampers plate according to claim 2, it is characterised in that：The metallic plate and bonding material layer
Thickness sum is identical with the depth of groove.
4. the insulated type metal dampers plate according to any one in claims 1 to 3, it is characterised in that：The valve plate
The side of the remote metallic plate of body is provided with reinforcement.
5. insulated type metal dampers plate according to claim 1, it is characterised in that：Leaded connect is set on the metallic plate
Head.
6. a kind of preparation method of insulated type metal dampers plate as claimed in claim 1, it is characterised in that：Including following step
Suddenly：
1) it will be used for setting the position progress polishing of metallic plate to form buffed surface on valve plate body, buffed surface will be cleaned out；
It will be used for carrying out phosphorating treatment formation adhesive surface with the one side that valve plate body is bonded on metallic plate, then will bond
Cleaned, dried in face；
2) silane coupling agent is coated on the buffed surface of valve plate body and the adhesive surface of metallic plate respectively, solvent flashing is stood；
3) adhesive surface for the buffed surface and metallic plate coating silane coupling agent that valve plate body is coated with into silane coupling agent is entered using adhesive
Row bonding, is produced.
7. the preparation method of insulated type metal dampers plate according to claim 6, it is characterised in that：The bonding is by glue
Stick be coated in coating silane coupling agent after valve plate body buffed surface on, then by metallic plate coat silane coupling agent adhesive surface direction
Valve plate body is placed on buffed surface, solidification.
8. the preparation method of insulated type metal dampers plate according to claim 6, it is characterised in that：The adhesive is silicon
Rubber based adhesives.
9. the preparation method of insulated type metal dampers plate according to claim 7, it is characterised in that：The adhesive is double
Component room temperature vulcanization silicon rubber, the host of double component room temperature vulcanization silicon rubber and the mass ratio of vulcanizing agent are 18~24:1.
10. the preparation method of insulated type metal dampers plate according to claim 7, it is characterised in that：It is right while solidification
Metallic plate and valve plate body apply pressure.