CN107057480A - A kind of solar street light protective paint and preparation method thereof - Google Patents
A kind of solar street light protective paint and preparation method thereof Download PDFInfo
- Publication number
- CN107057480A CN107057480A CN201710467149.4A CN201710467149A CN107057480A CN 107057480 A CN107057480 A CN 107057480A CN 201710467149 A CN201710467149 A CN 201710467149A CN 107057480 A CN107057480 A CN 107057480A
- Authority
- CN
- China
- Prior art keywords
- parts
- street light
- solar street
- protective paint
- light protective
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of solar street light protective paint, belong to solar street light technical field, include the raw material of following parts by weight：50 60 parts of styrene-acrylic emulsion, 15 18 parts of inositol hexaphosphate, 35 parts of aluminium powder, 13 parts of zinc oxide, 46 parts of sericite, 14 16 parts of iron oxide red, 10 12 parts of aluminium triphosphate, 0.1 0.8 parts of thickener, 0.2 0.5 parts of surfactant, 0.5 1 parts of levelling agent, 0.4 0.7 parts of defoamer, 12 parts of antirust agent, 12 parts of coalescents, 0.1 0.3 parts of mould inhibitor, 15 17 parts of water；The invention also discloses a kind of preparation method of solar street light protective paint；The present invention is environment friendly and pollution-free, and cementitiousness is strong, and with preferably antirust ability, service life is long.
Description
Technical field
The present invention relates to solar street light technical field, specifically, relate to a kind of solar street light protective paint and
Its preparation method.
Background technology
Solar street light is powered using crystal silicon solar energy battery, non-maintaining valve-control sealed accumulator（Colloid battery）
Electric energy is stored, ultra-bright LED light fixture is controlled as light source, and by intelligent charging-discharging controller, for replacing traditional public power
The street lamp of power illumination.Need not lay cable, without Alternating Current Power Supply, do not produce the electricity charge；Using direct current supply, control；With stable
Property good, long lifespan, luminous efficiency it is high, install easy maintenance, security performance height, energy-conserving and environment-protective, it is economical and practical the advantages of.Can be extensive
Applied to places such as city primary and secondary arterial highway, cell, factory, tourist attractions, parking lots.
Solar street light has generally comprised lamp stand, and the material of lamp stand is generally metal material, and lamp stand needs to be chronically exposed to
Outdoor, so being easy to get rusty, being corroded, so needing protective paint to protect it.
And current protective paint mainly has two kinds, one kind is the outdoor powdery paints of spraying, with adhesive force is good, hardness is high
Advantage, but there is the shortcomings of poor resistance to ag(e)ing, loss of gloss, easy efflorescence in outdoor powdery paints, and good outdoor powder can protect light, protect color 3
Year or so, it is poor to occur as soon as discoloration, loss of gloss less than one-year age, play powder phenomenon.Another is to paint, but paint is used
Organic solvent, these organic solvents are usually harmful, have pollution and incendive solvent to air, and can into
It is evaporate into when film in air, thus so-called dangers to health also just produce.And these harmful substances can't be
All volatilized in short time clean, for example formaldehyde, it is likely to require could volatilize totally for 5 to 10 years completely.
So needing a kind of solar street light with protective paint to solve the above problems.
The content of the invention
It is an object of the invention to overcoming above-mentioned the deficiencies in the prior art there is provided a kind of solar street light protective paint and
Its preparation method, environment friendly and pollution-free, cementitiousness is strong, and with preferably antirust ability, service life is long.
A kind of solar street light protective paint that the present invention is provided, includes the raw material of following parts by weight：
50-60 parts of styrene-acrylic emulsion, 15-18 parts of inositol hexaphosphate, 3-5 parts of aluminium powder, 1-3 parts of zinc oxide, 4-6 parts of sericite, oxygen
Change 14-16 parts of iron oxide red, 10-12 parts of aluminium triphosphate, 0.1-0.8 parts of thickener, 0.2-0.5 parts of surfactant, levelling agent
0.5-1 parts, 0.4-0.7 parts of defoamer, 1-2 parts of antirust agent, 1-2 parts of coalescents, 0.1-0.3 parts of mould inhibitor, 15-17 parts of water.
Preferably, the mesh number of aluminium powder, zinc oxide, sericite is 300-400 mesh, the mesh of iron oxide red and aluminium triphosphate
Number is 500-600 mesh.
Preferably, thickener is diatomite, attapulgite soil, guar gum, chitosan, one kind of gum arabic or two
The mixture of the above is planted, surfactant is alkyl glucoside.
Preferably, levelling agent be silicone oil, it is polyether polyester azo polyether polyeste, dimethyl silicone polymer, alkyl-modified
One or two or more kinds of mixtures of organosiloxane；Defoamer is polyoxyethylene polyoxypropylene pentaerythrite ether and polyoxy second
The mixture of alkene polyoxy propyl alcohol amidogen ether, weight ratio between the two is 1:1.
Preferably, antirust agent is natrium nitrosum, sodium carbonate, the mixture of triethanolamine, the weight ratio between three is
4:2:1。
Preferably, coalescents are alcohol ester 12, mould inhibitor is phenol, pentachlorophenol, one kind of sodium benzoate or two kinds
Mixture above.
Present invention also offers a kind of preparation method of solar street light protective paint, comprise the following steps：
（1）, by above-mentioned parts by weight weigh various raw materials；
（2）, by styrene-acrylic emulsion, inositol hexaphosphate, aluminium powder, zinc oxide, sericite, iron oxide red, aluminium triphosphate, water add
20-30min is stirred in reactor, control temperature stands 5-10min, obtain mixture at 50-60 DEG C；
（3）, again add into reactor thickener, it is surfactant, levelling agent, defoamer, antirust agent, coalescents, mould proof
Agent, rise temperature stirs 30-40min, is subsequently cooled to room temperature to 70-80 DEG C.
Wherein,
Step（2）In mixing speed be 300-400r/min.
Step（3）In mixing speed be 500-600r/min.
A kind of solar street light protective paint of the present invention and preparation method thereof, environment friendly and pollution-free, cementitiousness is strong, has
Preferably antirust ability, service life long, specifically has the beneficial effect that：
（1）, styrene-acrylic emulsion can improve the alkaline-resisting of protective paint, oil resistant, heat-resisting, ageing-resistant performance；Inositol hexaphosphate can be effectively
The cementitiousness of protective paint is improved, can rapidly be chelated with metal on surface, one layer of fine and close unimolecule complex compound diaphragm of formation,
Corrosion of metal can effectively be suppressed；Aluminium powder can improve the antirust ability of protective paint, and it has sclay texture, form paint film tight
It is close, there is the ability of stronger reflection ultraviolet, the anti-aging ability of paint film can be improved；
（2）, sericite can improve the wear resistence, wearability and high temperature insulation of protective paint；Iron oxide red, aluminium triphosphate can conducts
Pigment；Iron oxide red can be used as sun-screening agent；It is thickener, surfactant, levelling agent, defoamer, antirust agent, coalescents, anti-
Mould dose can effectively improve the performance of protective paint；
（3）, preparation method it is simple, can stably prepare protective paint；The present invention replaces the organic solvent in paint, ten using water
Divide environmental protection.
Embodiment
Invention is described in further detail below in conjunction with specific embodiment.
Embodiment 1
A kind of solar street light protective paint of the present embodiment, includes the raw material of following parts by weight：
50 parts of styrene-acrylic emulsion, 15 parts of inositol hexaphosphate, 3 parts of aluminium powder, 1 part of zinc oxide, 4 parts of sericite, 14 parts of iron oxide red, three
10 parts of poly aluminium phosphate, 0.1 part of thickener, 0.2 part of surfactant, 0.5 part of levelling agent, 0.4 part of defoamer, 1 part of antirust agent, into
1 part of film auxiliary agent, 0.1 part of mould inhibitor, 15 parts of water.
In the present embodiment, aluminium powder, zinc oxide, the mesh number that the mesh number of sericite is 300 mesh, iron oxide red and aluminium triphosphate
For 500 mesh.
In the present embodiment, thickener is diatomite, attapulgite soil, guar gum, chitosan, the mixing of gum arabic
Thing, surfactant is alkyl glucoside.
In the present embodiment, levelling agent is silicone oil, polyether polyester azo polyether polyeste, dimethyl silicone polymer, alkyl change
The mixture of property organosiloxane；Defoamer is polyoxyethylene polyoxypropylene pentaerythrite ether and polyoxyethylene polyoxy propyl alcohol amidogen ether
Mixture, weight ratio between the two is 1:1.
In the present embodiment, antirust agent is the weight ratio between natrium nitrosum, sodium carbonate, the mixture of triethanolamine, three
For 4:2:1.
In the present embodiment, coalescents are alcohol ester 12, and mould inhibitor is phenol, pentachlorophenol, the mixture of sodium benzoate.
The present embodiment additionally provides a kind of preparation method of solar street light protective paint, comprises the following steps：
（1）, by above-mentioned parts by weight weigh various raw materials；
（2）, by styrene-acrylic emulsion, inositol hexaphosphate, aluminium powder, zinc oxide, sericite, iron oxide red, aluminium triphosphate, water add
20min is stirred in reactor, control temperature stands 5min, obtain mixture at 50 DEG C；
（3）, again add into reactor thickener, it is surfactant, levelling agent, defoamer, antirust agent, coalescents, mould proof
Agent, rise temperature stirs 30min, is subsequently cooled to room temperature to 70 DEG C.
Wherein,
Step（2）In mixing speed be 300r/min.
Step（3）In mixing speed be 500r/min.
Embodiment 2
A kind of solar street light protective paint of the present embodiment, includes the raw material of following parts by weight：
55 parts of styrene-acrylic emulsion, 16 parts of inositol hexaphosphate, 4 parts of aluminium powder, 2 parts of zinc oxide, 5 parts of sericite, 15 parts of iron oxide red, three
11 parts of poly aluminium phosphate, 0.5 part of thickener, 0.4 part of surfactant, 0.8 part of levelling agent, 0.5 part of defoamer, 1.5 parts of antirust agent,
1.5 parts of coalescents, 0.2 part of mould inhibitor, 16 parts of water.
In the present embodiment, aluminium powder, zinc oxide, the mesh number that the mesh number of sericite is 400 mesh, iron oxide red and aluminium triphosphate
For 500 mesh.
In the present embodiment, thickener is diatomite, attapulgite soil, guar gum, chitosan, the mixing of gum arabic
Thing, surfactant is alkyl glucoside.
In the present embodiment, levelling agent is silicone oil, polyether polyester azo polyether polyeste, dimethyl silicone polymer, alkyl change
The mixture of property organosiloxane；Defoamer is polyoxyethylene polyoxypropylene pentaerythrite ether and polyoxyethylene polyoxy propyl alcohol amidogen ether
Mixture, weight ratio between the two is 1:1.
In the present embodiment, antirust agent is the weight ratio between natrium nitrosum, sodium carbonate, the mixture of triethanolamine, three
For 4:2:1.
In the present embodiment, coalescents are alcohol ester 12, and mould inhibitor is phenol, pentachlorophenol, the mixture of sodium benzoate.
The present embodiment additionally provides a kind of preparation method of solar street light protective paint, comprises the following steps：
（1）, by above-mentioned parts by weight weigh various raw materials；
（2）, by styrene-acrylic emulsion, inositol hexaphosphate, aluminium powder, zinc oxide, sericite, iron oxide red, aluminium triphosphate, water add
25min is stirred in reactor, control temperature stands 8min, obtain mixture at 55 DEG C；
（3）, again add into reactor thickener, it is surfactant, levelling agent, defoamer, antirust agent, coalescents, mould proof
Agent, rise temperature stirs 35min, is subsequently cooled to room temperature to 75 DEG C.
Wherein,
Step（2）In mixing speed be 350r/min.
Step（3）In mixing speed be 550r/min.
Embodiment 3
A kind of solar street light protective paint of the present embodiment, includes the raw material of following parts by weight：
60 parts of styrene-acrylic emulsion, 18 parts of inositol hexaphosphate, 5 parts of aluminium powder, 3 parts of zinc oxide, 6 parts of sericite, 16 parts of iron oxide red, three
12 parts of poly aluminium phosphate, 0.8 part of thickener, 0.5 part of surfactant, 1 part of levelling agent, 0.7 part of defoamer, 2 parts of antirust agent, film forming
2 parts of auxiliary agent, 0.3 part of mould inhibitor, 17 parts of water.
In the present embodiment, aluminium powder, zinc oxide, the mesh number that the mesh number of sericite is 400 mesh, iron oxide red and aluminium triphosphate
For 600 mesh.
In the present embodiment, thickener is diatomite, attapulgite soil, guar gum, chitosan, the mixing of gum arabic
Thing, surfactant is alkyl glucoside.
In the present embodiment, levelling agent is silicone oil, polyether polyester azo polyether polyeste, dimethyl silicone polymer, alkyl change
The mixture of property organosiloxane；Defoamer is polyoxyethylene polyoxypropylene pentaerythrite ether and polyoxyethylene polyoxy propyl alcohol amidogen ether
Mixture, weight ratio between the two is 1:1.
In the present embodiment, antirust agent is the weight ratio between natrium nitrosum, sodium carbonate, the mixture of triethanolamine, three
For 4:2:1.
In the present embodiment, coalescents are alcohol ester 12, and mould inhibitor is phenol, pentachlorophenol, the mixture of sodium benzoate.
The present embodiment additionally provides a kind of preparation method of solar street light protective paint, comprises the following steps：
（1）, by above-mentioned parts by weight weigh various raw materials；
（2）, by styrene-acrylic emulsion, inositol hexaphosphate, aluminium powder, zinc oxide, sericite, iron oxide red, aluminium triphosphate, water add
30min is stirred in reactor, control temperature stands 10min, obtain mixture at 60 DEG C；
（3）, again add into reactor thickener, it is surfactant, levelling agent, defoamer, antirust agent, coalescents, mould proof
Agent, rise temperature stirs 40min, is subsequently cooled to room temperature to 80 DEG C.
Wherein,
Step（2）In mixing speed be 400r/min.
Step（3）In mixing speed be 600r/min.
According to GB/T 0001-2008 examination criteria and detection method, the testing result of the protective paint in embodiment 1-3
It is as follows：
Drying time（Surface drying）≤1h；Drying time（Do solid work）≤24h；It is resistant to smog；1 month non-foaming non-corrosive of natural exposure
Do not ftracture and do not peel off；Low-temperature stability：Never degenerate.
So embodiment 1-3 has preferably antirust, resistance to acids and bases, cementitiousness is strong.
As can be seen from the above table, embodiment 1-3 has preferably mechanical performance, it may have preferably high-temperature flame-proof ability.
Described above is only the preferred embodiment of the present invention, and protection scope of the present invention is not limited merely to above-mentioned implementation
Example, all technical schemes belonged under thinking of the present invention belong to protection scope of the present invention.It should be pointed out that for the art
Those of ordinary skill for, some improvements and modifications without departing from the principles of the present invention, these improvements and modifications
It should be regarded as protection scope of the present invention.
Claims (9)
1. a kind of solar street light protective paint, it is characterised in that：Include the raw material of following parts by weight：
50-60 parts of styrene-acrylic emulsion, 15-18 parts of inositol hexaphosphate, 3-5 parts of aluminium powder, 1-3 parts of zinc oxide, 4-6 parts of sericite, oxygen
Change 14-16 parts of iron oxide red, 10-12 parts of aluminium triphosphate, 0.1-0.8 parts of thickener, 0.2-0.5 parts of surfactant, levelling agent
0.5-1 parts, 0.4-0.7 parts of defoamer, 1-2 parts of antirust agent, 1-2 parts of coalescents, 0.1-0.3 parts of mould inhibitor, 15-17 parts of water.
2. solar street light protective paint according to claim 1, it is characterised in that：Aluminium powder, zinc oxide, the mesh of sericite
It is 300-400 mesh to count, and the mesh number of iron oxide red and aluminium triphosphate is 500-600 mesh.
3. solar street light protective paint according to claim 1, it is characterised in that：Thickener is diatomite, concave convex rod
Stone soil, guar gum, chitosan, one or two or more kinds of mixtures of gum arabic, surfactant is alkyl glucoside.
4. solar street light protective paint according to claim 1, it is characterised in that：Levelling agent is silicone oil, polyether polyester
Azo polyether polyeste, dimethyl silicone polymer, one or two or more kinds of mixtures of alkyl-modified organosiloxane；Froth breaking
Agent is the mixture of polyoxyethylene polyoxypropylene pentaerythrite ether and polyoxyethylene polyoxy propyl alcohol amidogen ether, weight ratio between the two
For 1:1.
5. solar street light protective paint according to claim 1, it is characterised in that：Antirust agent is natrium nitrosum, carbonic acid
Weight ratio between the mixture of sodium, triethanolamine, three is 4:2:1.
6. solar street light protective paint according to claim 1, it is characterised in that：Coalescents are alcohol ester 12, are prevented
Mould dose is phenol, pentachlorophenol, one or two or more kinds of mixtures of sodium benzoate.
7. a kind of preparation method of solar street light protective paint according to claim 1-6 any one, its feature exists
In：Comprise the following steps：
（1）, by above-mentioned parts by weight weigh various raw materials；
（2）, by styrene-acrylic emulsion, inositol hexaphosphate, aluminium powder, zinc oxide, sericite, iron oxide red, aluminium triphosphate, water add
20-30min is stirred in reactor, control temperature stands 5-10min, obtain mixture at 50-60 DEG C；
（3）, again add into reactor thickener, it is surfactant, levelling agent, defoamer, antirust agent, coalescents, mould proof
Agent, rise temperature stirs 30-40min, is subsequently cooled to room temperature to 70-80 DEG C.
8. the preparation method of solar street light protective paint according to claim 7, it is characterised in that：Step（2）In
Mixing speed is 300-400r/min.
9. the preparation method of solar street light protective paint according to claim 7, it is characterised in that：Step（3）In
Mixing speed is 500-600r/min.