CN101407652A - Preparation of UV curing luminous paint - Google Patents
Preparation of UV curing luminous paint Download PDFInfo
- Publication number
- CN101407652A CN101407652A CNA2008101363365A CN200810136336A CN101407652A CN 101407652 A CN101407652 A CN 101407652A CN A2008101363365 A CNA2008101363365 A CN A2008101363365A CN 200810136336 A CN200810136336 A CN 200810136336A CN 101407652 A CN101407652 A CN 101407652A
- Authority
- CN
- China
- Prior art keywords
- percent
- luminescent material
- preparation
- rare earth
- luminous
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a preparation method of an ultraviolet curing luminous coating which is prepared by the following formula according to the weight percentage: 1 percent to 20 percent of rare earth superlong afterglow luminescent material which is carried out the surface modification by vinylsilane coupling agent, 40 percent to 70 percent film-forming substance, 1 percent to 10 percent photoinitiator, 5 percent to 25 percent pigment and filler, 0 percent to 5 percent organic solvent or water, 0.01 percent to 5 percent dispersant, 0.01 percent to 5 percent defoamer and 1 percent to 8 percent other auxiliary agents. The preparation method has the advantages that: 1. the surface modified rare earth superlong afterglow luminescent material has better compatibility and simultaneously improves the luminous intensity of the luminous coating and prolongs the luminescence time; 2. the ultraviolet curing luminous coating not only has the luminous performance as the ordinary luminous coating, but is also characterized by rapid curing, good coating performance, no greatly volatile solvent, and the like; and 3. the preparation method is beneficial to the elimination of the environmental pollution and the saving of the organic solvent.
Description
Technical field
The present invention relates to a kind of preparation method of coating, relate in particular to a kind of preparation method of UV curing luminous paint.
Background technology
Along with the development of modern science and technology and the enhancing day by day of people's environmental consciousness, more and more urgent to the demand that can produce tremendous economic and social benefit, environmental protection composite functional material attractive in appearance.The rare earth light-storing and emitting material as a kind of environmental protection, stable, " green " luminescent material has caused people's extensive concern efficiently.The luminous paint of ultraviolet light polymerization has fabulous light-accumulated luminous effect, life-span is long, can under outdoor sunlight, be exposed to the sun, round-the-clock use, nontoxic, safe and reliable, can be used for that round-the-clock outdoor various indicatrixs, billboard, Emergency Light, building decoration are decorateed and the fields such as direction board of motorway.
Luminous indication mechanism in the buildings is mainly the electroluminescence type Pointing sign board.Yet, because the electroluminescent label must rely on power supply, and must be ability works better under the situation that all components and parts do not damage, in case power failure, outage or components and parts damaged condition occur, promptly can not bring into play its sign, indicative function.And the long afterglow photoluminescence label is the energy of absorption sunlight and light and stores, and sends light in the dark again, does not need power supply, there is not damage of components and out of use problem, also do not need routine maintenance, the reliability height is optimal emergent Warning Mark.Long after glow luminous material is a class advanced luminescent material that grows up early 1990s, the luminosity height, time of persistence is long, "dead" pollution, and the kind of luminescent material is constantly increasing, and the scope of emission wavelength has also almost covered whole visible lights, this makes long-persistence luminous label not only obtain to use widely aspect the emergent indication, and also the application for other sign, sign provides wide prospect.
Summary of the invention
The object of the present invention is to provide a kind of preparation method of UV curing luminous paint, table and rare earth overlength afterglow luminescent material (SrAl after the modification
2O
4: Eu
2+, Dy
3+) have better consistency, improve the luminous intensity of luminous paint simultaneously and prolonged fluorescent lifetime.
The present invention is achieved like this, and is made up of following prescription quality per-cent: vinyl silicane coupling agent (KH-570) carries out the rare earth overlength afterglow luminescent material (SrAl of surface modification
2O
4: Eu
2+, Dy
3+) 1%-20%, filmogen (epoxy acrylate (EA)) 40%-70%, light trigger 1%-10%, color stuffing 1%-10%, solvent (organic solvent or water) 0%-5%, dispersion agent (Sodium hexametaphosphate 99) 0.01%-5%, defoamer (tributyl phosphate) 0.01%-5%,, other auxiliary agents 1%-8%;
It is characterized in that the processing method step is:
1, use vinyl silicane coupling agent (KH-570) to rare earth overlength afterglow luminescent material (SrAl
2O
4: Eu
2+, Dy
3+) carry out the preparation of surface modification, with the rare earth overlength afterglow luminescent material (SrAl of 5%-15%
2O
4: Eu
2+, Dy
3+) and the dehydrated alcohol of 60%-90% mix, ultrasonic dispersing 20min adds the silane coupling agent (KH-570) of 1%-5%, stirs and transfers pH=1, stirred 4 hours down at 30 ℃-50 ℃, suction filtration, standby;
2, surface treated luminous pigment, light trigger mixed type triaryl hexafluorophosphate, epoxy acrylate (EA), color stuffing, solvent (organic solvent or water), dispersion agent, other auxiliary agents are mixed middling speed dispersed with stirring 50-80 minute;
3, add other coatings additive(s)s commonly used, middling speed dispersed with stirring 10-30 minute again;
4, brushing is on the plank of a dried and clean, and brushing thickness 0.2-1.0mm after solidifying 10-20 minute under the 300W ultraviolet lamp, promptly makes finished product coating after the cooling.
Advantage of the present invention is: 1, the rare earth overlength afterglow luminescent material (SrAl of surface modification
2O
4: Eu
2+, Dy
3+) have better consistency, improve the luminous intensity of luminous paint simultaneously and prolonged fluorescent lifetime; 2, use UV curing luminous paint, have the luminescent properties of common luminous paint, have fast setting, film performance simultaneously and well, do not contain the big characteristics such as solvent of volatility; 3, help eliminating pollution to environment, saved organic solvent again, the luminescent properties that has remedied luminous paint simultaneously is the deficiency of forfeiture easily.
Embodiment
Embodiment one
Carry out the rare earth overlength afterglow luminescent material (SrAl of surface modification by vinyl silicane coupling agent (KH-570)
2O
4: Eu
2+, Dy
3+) 10%, filmogen (epoxy acrylate (EA)) 45%, light trigger 4%, color stuffing (titanium dioxide, zinc sulfide white, talcum powder, light calcium carbonate etc.) 25%, solvent (organic solvent or water) 5%, dispersion agent (Sodium hexametaphosphate 99) 2%, defoamer (tributyl phosphate) 2%, other auxiliary agents 7% form;
With vinyl silicane coupling agent (KH-570) to rare earth overlength afterglow luminescent material (SrAl
2O
4: Eu
2+, Dy
3+) carry out the preparation of surface modification, rare earth overlength afterglow luminescent material (SrAl with 5%
2O
4: Eu
2+, Dy
3+) and 60% dehydrated alcohol mix, ultrasonic dispersing 20min adds the silane coupling agent (KH-570) of 1%-5%, stirs and transfers pH=1, stirred 4 hours down at 30 ℃, suction filtration, standby; Surface treated luminescent material, light trigger mixed type triaryl hexafluorophosphate, epoxy acrylate (EA), color stuffing, solvent (organic solvent or water), dispersion agent, defoamer, other auxiliary agents are mixed middling speed dispersed with stirring 50 minutes; Add other coatings additive(s)s commonly used, the middling speed dispersed with stirring is 10 minutes again; Brushing is on the plank of a dried and clean, and brushing thickness 0.2mm after solidifying 15 minutes under the 300W ultraviolet lamp, promptly makes finished product coating after the cooling.
Embodiment two
Carry out the rare earth overlength afterglow luminescent material (SrAl of surface modification by vinyl silicane coupling agent (KH-570)
2O
4: Eu
2+, Dy
3+) 15%, filmogen (epoxy acrylate (EA)) 55%, light trigger 4%, color stuffing (titanium dioxide, zinc sulfide white, talcum powder, light calcium carbonate etc.) 15%, solvent (organic solvent or water) 5%, dispersion agent (Sodium hexametaphosphate 99) 1%, defoamer (tributyl phosphate) 2%, other auxiliary agents 3% form;
With vinyl silicane coupling agent (KH-570) to rare earth overlength afterglow luminescent material (SrAl
2O
4: Eu
2+, Dy
3+) carry out the preparation of surface modification, rare earth overlength afterglow luminescent material (SrAl with 15%
2O
4: Eu
2+, Dy
3+) and 90% dehydrated alcohol mix, ultrasonic dispersing 20min adds 5% silane coupling agent (KH-570), stirs and transfers pH=1, stirred 4 hours down at 50 ℃, suction filtration, standby; Surface treated luminescent material, light trigger mixed type triaryl hexafluorophosphate, epoxy acrylate (EA), color stuffing, solvent (organic solvent or water), dispersion agent, defoamer, other auxiliary agents are mixed middling speed dispersed with stirring 80 minutes; Add other coatings additive(s)s commonly used, the middling speed dispersed with stirring is 30 minutes again; Brushing is on the plank of a dried and clean, and brushing thickness 1.0mm after solidifying 20 minutes under the 300W ultraviolet lamp, promptly makes finished product coating after the cooling.
Embodiment three
Carry out the rare earth overlength afterglow luminescent material (SrAl of surface modification by vinyl silicane coupling agent (KH-570)
2O
4: Eu
2+, Dy
3+) 20%, filmogen (epoxy acrylate (EA)) 65%, light trigger 4%, color stuffing (titanium dioxide, zinc sulfide white, talcum powder, light calcium carbonate etc.) 5%, solvent (organic solvent or water) 3%, dispersion agent (Sodium hexametaphosphate 99) 1%, defoamer (tributyl phosphate) 1%, other auxiliary agents 1% form;
With vinyl silicane coupling agent (KH-570) to rare earth overlength afterglow luminescent material (SrAl
2O
4: Eu
2+, Dy
3+) carry out the preparation of surface modification, rare earth overlength afterglow luminescent material (SrAl with 8%
2O
4: Eu
2+, Dy
3+) and 70% dehydrated alcohol mix, ultrasonic dispersing 20min adds 3% silane coupling agent (KH-570), stirs and transfers pH=1, stirred 4 hours down at 40 ℃, suction filtration, standby; Surface treated luminescent material, light trigger mixed type triaryl hexafluorophosphate, epoxy acrylate (EA), color stuffing, solvent (organic solvent or water), dispersion agent, defoamer, other auxiliary agents are mixed middling speed dispersed with stirring 65 minutes; Add other coatings additive(s)s commonly used, the middling speed dispersed with stirring is 20 minutes again; Brushing is on the plank of a dried and clean, and brushing thickness 1.0mm after solidifying 20 minutes under the 300W ultraviolet lamp, promptly makes finished product coating after the cooling.
Claims (1)
1, a kind of preparation method of UV curing luminous paint, be made up of following prescription quality per-cent: vinyl silicane coupling agent carries out rare earth overlength afterglow luminescent material 1%-20%, epoxy acrylate 40%-70%, light trigger 1%-10%, color stuffing 5%-25%, organic solvent or water 0%-5%, dispersion agent 0.01%-5%, defoamer 0.01%-5%, other auxiliary agents 1%-8% of surface modification;
It is characterized in that the processing method step is:
(1) with vinyl silicane coupling agent rare earth overlength afterglow luminescent material is carried out the preparation of surface modification, the rare earth overlength afterglow luminescent material of 5%-15% and the dehydrated alcohol of 60%-90% are mixed, ultrasonic dispersing 20min adds the silane coupling agent of 1%-5%, stir and transfer pH=1, stirred 4 hours down at 30 ℃-50 ℃, suction filtration, standby;
(2) surface treated luminescent material, light trigger mixed type triaryl hexafluorophosphate, epoxy acrylate, color stuffing, organic solvent or water, dispersion agent, other auxiliary agents are mixed middling speed dispersed with stirring 50-80 minute;
(3) add other coatings additive(s)s commonly used, middling speed dispersed with stirring 10-30 minute again;
(4) brushing is on the plank of a dried and clean, and brushing thickness 0.2-1.0mm after solidifying 10-20 minute under the 300W ultraviolet lamp, promptly makes finished product coating after the cooling.