CN107057443A - It is a kind of for mixed solvent component of PVC special coatings and preparation method thereof - Google Patents
It is a kind of for mixed solvent component of PVC special coatings and preparation method thereof Download PDFInfo
- Publication number
- CN107057443A CN107057443A CN201611216761.6A CN201611216761A CN107057443A CN 107057443 A CN107057443 A CN 107057443A CN 201611216761 A CN201611216761 A CN 201611216761A CN 107057443 A CN107057443 A CN 107057443A
- Authority
- CN
- China
- Prior art keywords
- parts
- mixed solvent
- pvc
- preparation
- component
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to technical field of coatings, it is specifically related to a kind of for mixed solvent component of PVC special coatings and preparation method thereof.It is made up of the component of following parts by weight：15 parts of dimethylbenzene, 3.5 parts of cyclohexanone, 2.5 parts of dibutyl phthalates, 1.5 parts of propyl alcohol, 3.5 parts of linoleic acid, 5 parts of water, 5 parts of solvent naphthas and 3 parts of motherwort glucosides.The present invention for mixed solvent component of PVC special coatings and preparation method thereof, by adding the component rationally designed, particularly motherwort glucoside, the solubility property of mixed solvent can be lifted, coating perfection is further set to be coated on PVC, both the aesthetics of product can be promoted, the service life of PVC product can be made to lift more than 50% again.
Description
Technical field
The present invention relates to technical field of coatings, be specifically related to a kind of mixed solvent component for PVC special coatings and
Its preparation method.
Background technology
PVC was once the general-purpose plastics of yield maximum in the world, using widely.In construction material, industrial product, daily
In terms of product, flooring laminate, floor tile, artificial leather, tubing, electric wire, packaging film, bottle, expanded material, encapsulant, fiber
It is widely used.But, because the color of PVC products is ugly, mattness, it is therefore desirable to which a kind of coating is by its surface
" covering ".
The content of the invention
It is an object of the invention to provide a kind of PVC special coatings and preparation method thereof, the mixing for PVC special coatings
Solvent composition and preparation method thereof, to achieve the above object, present invention employs following technical scheme：
A kind of mixed solvent component for PVC special coatings, is made up of the component of following parts by weight：
15 parts of dimethylbenzene, 3.5 parts of cyclohexanone, 2.5 parts of dibutyl phthalates, 1.5 parts of propyl alcohol, 3.5 parts of linoleic acid, 5 parts of water,
5 parts of solvent naphthas and 3 parts of motherwort glucosides.
A kind of preparation method of mixed solvent component for PVC special coatings, step is as follows：
15 parts of dimethylbenzene, 3.5 parts of cyclohexanone and 2.5 parts of dibutyl phthalates, stirring 2 are added first into stirring container
h；Then 1.5 parts of propyl alcohol, 3.5 parts of linoleic acid, 5 parts of water and 5 parts of solvent naphthas are added, 2 h are stirred；3 parts of motherwort glucosides are eventually adding,
Stir 0.5 h.
A kind of PVC special coatings, are made up of the component of following parts by weight：
15 parts of mixed solvent components, 2.5 parts of precipitated calcium carbonates, 3.5 parts of triethanolamines, 5 parts of hydroxypropyl methyl celluloses, 4.5 parts
Active masterbatch, 6.5 parts of dispersants, 6 parts of wetting agents, 5.5 parts of polyurethane levelling agents.
A kind of preparation method of PVC special coatings, step is as follows：
15 parts of mixed solvent components are added first into stirring container, it is 1000 r/min to control rotating speed, adds 2.5 parts of lightweight carbon
Sour calcium, 3.5 parts of triethanolamines and 5 parts of hydroxypropyl methyl celluloses, it is 1500 r/min to control rotating speed, stirs 1 h；It is eventually adding
4.5 parts of active masterbatch and 6.5 parts of dispersants, it is 1500 r/min to control rotating speed, stirs 1 h；It is eventually adding 6 parts of wetting agents, 5.5
Part polyurethane levelling agent, it is 800 r/min to control rotating speed, stirs 2 h, obtains PVC special coatings.
Beneficial effects of the present invention are shown：
The present invention can lift the solubility property of mixed solvent, enter by adding the component rationally designed, particularly motherwort glucoside
One step enables coating perfection to be coated on PVC, can both promote the aesthetics of product, and the use of PVC product can be made again
Life-span upgrading more than 50%.
Embodiment
Below with reference to embodiment, the present invention is described in detail.But, embodiment content is only to this hair
Bright example and explanation, affiliated those skilled in the art do various repair to described specific embodiment
Change or supplement or substituted using similar mode, design without departing from invention or surmount defined in the claims
Scope, all should belong to protection scope of the present invention.
Embodiment 1
A kind of mixed solvent component for PVC special coatings, is made up of the component of following parts by weight：
15 parts of dimethylbenzene, 3.5 parts of cyclohexanone, 2.5 parts of dibutyl phthalates, 1.5 parts of propyl alcohol, 3.5 parts of linoleic acid, 5 parts of water,
5 parts of solvent naphthas and 3 parts of motherwort glucosides.
A kind of preparation method of mixed solvent component for PVC special coatings, step is as follows：
15 parts of dimethylbenzene, 3.5 parts of cyclohexanone and 2.5 parts of dibutyl phthalates, stirring 2 are added first into stirring container
h；Then 1.5 parts of propyl alcohol, 3.5 parts of linoleic acid, 5 parts of water and 5 parts of solvent naphthas are added, 2 h are stirred；3 parts of motherwort glucosides are eventually adding,
Stir 0.5 h.
Embodiment 2
A kind of PVC special coatings, are made up of the component of following parts by weight：
15 parts of mixed solvent components（It is prepared by embodiment 1）, 2.5 parts of precipitated calcium carbonate, 3.5 parts of triethanolamines, 5 parts of hydroxypropyl methyls
Cellulose, 4.5 parts of active masterbatch, 6.5 parts of dispersants, 6 parts of wetting agents, 5.5 parts of polyurethane levelling agents.
A kind of preparation method of PVC special coatings, step is as follows：
15 parts of mixed solvent components are added first into stirring container, it is 1000 r/min to control rotating speed, adds 2.5 parts of lightweight carbon
Sour calcium, 3.5 parts of triethanolamines and 5 parts of hydroxypropyl methyl celluloses, it is 1500 r/min to control rotating speed, stirs 1 h；It is eventually adding
4.5 parts of active masterbatch and 6.5 parts of dispersants, it is 1500 r/min to control rotating speed, stirs 1 h；It is eventually adding 6 parts of wetting agents, 5.5
Part polyurethane levelling agent, it is 800 r/min to control rotating speed, stirs 2 h, obtains PVC special coatings.
Claims (2)
1. a kind of mixed solvent component for PVC special coatings, it is characterised in that：It is made up of the component of following parts by weight：
15 parts of dimethylbenzene, 3.5 parts of cyclohexanone, 2.5 parts of dibutyl phthalates, 1.5 parts of propyl alcohol, 3.5 parts of linoleic acid, 5 parts of water,
5 parts of solvent naphthas and 3 parts of motherwort glucosides.
2. a kind of preparation method for the mixed solvent component for being used for PVC special coatings as claimed in claim 1, step is as follows：
15 parts of dimethylbenzene, 3.5 parts of cyclohexanone and 2.5 parts of dibutyl phthalates, stirring 2 are added first into stirring container
h；Then 1.5 parts of propyl alcohol, 3.5 parts of linoleic acid, 5 parts of water and 5 parts of solvent naphthas are added, 2 h are stirred；3 parts of motherwort glucosides are eventually adding,
Stir 0.5 h.