CN107056153A - A kind of environment-friendlyantiqued antiqued black bricks formula - Google Patents
A kind of environment-friendlyantiqued antiqued black bricks formula Download PDFInfo
- Publication number
- CN107056153A CN107056153A CN201710225356.9A CN201710225356A CN107056153A CN 107056153 A CN107056153 A CN 107056153A CN 201710225356 A CN201710225356 A CN 201710225356A CN 107056153 A CN107056153 A CN 107056153A
- Authority
- CN
- China
- Prior art keywords
- parts
- environment
- friendlyantiqued
- antiqued
- black
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of environment-friendlyantiqued antiqued black bricks formula, count, be made up of following raw material by weight：55 parts of cement paste, 7 parts of clinker, 7 parts of aluminum nitride powder, steel gray 5 parts, 8 parts of iron oxide black, 6 parts of tealeaf residue powder, grey 3 parts of gravel, 6 parts of mud, 8 parts of ceramic polished waste residue, 4 parts of yellow sand, 0.2 part of water reducer, 3 parts of fiber.Compared with the prior art, the present invention is using cement as main material, and composition is simple, and cost of manufacture is far smaller than the blue bricks of clay firing, effectively reduces cost, reduces the consumption of clay in refractory brick；Solid pollutant is recycled, the purpose turned waste into wealth is reached, while greatly reducing pollution on the environment in manufacturing process.
Description
Technical field
The present invention relates to a kind of environment-friendlyantiqued antiqued black bricks formula.
Background technology
The reparation and protection of ancient building are due to by factors such as itself historical values and humanity history environment of protection building
Difference, thus during the pseudo-classic building of repairing should restoring the old as the old, i.e., recover to be protected original style of building as much as possible, and current
The blue bricks for being used to repair can only imitate the size of blue bricks mostly, it is impossible to the texture of former ancient building is carried out imitative as former state
System, conventional imitative blue bricks is concrete structure, i.e., the mixing compacting that added water with cement, sand, black powder is formed, and antidetonation anti-pressure ability is poor.
The content of the invention
It is an object of the invention to provide a kind of environment-friendlyantiqued antiqued black bricks formula.
The technical scheme that the present invention solves above-mentioned technical problem is as follows：A kind of environment-friendlyantiqued antiqued black bricks formula, by weight
Meter, is made up of following raw material：55 parts of cement paste, 7 parts of clinker, 7 parts of aluminum nitride powder, steel gray 5 parts, 8 parts of iron oxide black, tealeaf residue
6 parts of powder, grey 3 parts of gravel, 6 parts of mud, 8 parts of ceramic polished waste residue, 4 parts of yellow sand, 0.2 part of water reducer, 3 parts of fiber.
The beneficial effects of the invention are as follows：Using cement as main material, composition is simple, and cost of manufacture is far smaller than clay
The blue bricks of firing, effectively reduces cost, reduces the consumption of clay in refractory brick；Solid pollutant is recycled, reached
The purpose turned waste into wealth, while greatly reducing pollution on the environment in manufacturing process.
Embodiment
The principles and features of the present invention are described below, and the given examples are served only to explain the present invention, is not intended to limit
Determine the scope of the present invention.
A kind of environment-friendlyantiqued antiqued black bricks formula, is counted by weight, is made up of following raw material：55 parts of cement paste, clinker 7
Part, 7 parts of aluminum nitride powder, steel gray 5 parts, it is 8 parts of iron oxide black, 6 parts of tealeaf residue powder, grey 3 parts of gravel, 6 parts of mud, ceramic polished useless
8 parts of slag, 4 parts of yellow sand, 0.2 part of water reducer, 3 parts of fiber.
The present invention is using cement as main material, and composition is simple, and cost of manufacture is far smaller than the blue bricks of clay firing, has
What is imitated reduces cost, reduces the consumption of clay in refractory brick；Solid pollutant is recycled, the mesh turned waste into wealth is reached
, while greatly reducing pollution on the environment in manufacturing process.
The foregoing is only presently preferred embodiments of the present invention, be not intended to limit the invention, it is all the present invention spirit and
Within principle, any modification, equivalent substitution and improvements made etc. should be included in the scope of the protection.
Claims (1)
1. a kind of environment-friendlyantiqued antiqued black bricks formula, it is characterised in that count by weight, is made up of following raw material：Cement paste 55
Part, 7 parts of clinker, 7 parts of aluminum nitride powder, steel gray 5 parts, 8 parts of iron oxide black, 6 parts of tealeaf residue powder, grey 3 parts of gravel, 6 parts of mud, pottery
8 parts of porcelain polishing slag, 4 parts of yellow sand, 0.2 part of water reducer, 3 parts of fiber.