CN107053416A - A kind of bamboo chip softening agent and preparation method thereof - Google Patents
A kind of bamboo chip softening agent and preparation method thereof Download PDFInfo
- Publication number
- CN107053416A CN107053416A CN201710442420.9A CN201710442420A CN107053416A CN 107053416 A CN107053416 A CN 107053416A CN 201710442420 A CN201710442420 A CN 201710442420A CN 107053416 A CN107053416 A CN 107053416A
- Authority
- CN
- China
- Prior art keywords
- parts
- alcohol
- softening agent
- bamboo chip
- apeo
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of bamboo chip softening agent, it is made up of the component of following parts by weight：5 12 parts of dimethylaniline, 39 parts of alcohol ether glucoside, 5 15 parts of APEO, 6 12 parts of stearyl alcohol, 13 parts of lemon, 13 parts of dioctyl sodium sulfosuccinate, 13 parts of methyl hydroxybenzoate, 10 20 parts of chloromethyloxirane, 38 parts of cellulase, 6 12 parts of isoamyl alcohol, 16 parts of triethanolamine, 38 parts of neopelex, 25 parts of aluminum stearate, 29 parts of nickel stearate, 6 11 parts of petroleum ether, 16 parts of Sodium Polyacrylate, 28 parts of urea, 6 13 parts of wood pitch, 27 parts of cobalt naphthenate, 120 160 parts of deionized water.Compared with prior art, the bamboo chip softening agent has more preferable bating effect, and preparation method is simple.
Description
Technical field
The present invention relates to bamboo weaving technical field, and in particular to a kind of bamboo chip softening agent and preparation method thereof.
Background technology
Bamboo is perennial lignified plant, the tool aerial stem of plant (bamboo bar) and subterranean stem (bamboo whip).Bamboo bar is often cylindrical shape, seldom
For quadrangle, it is formed by connecting by internode and section, internode is often hollow, a small number of solid, section is made up of sheaths of bamboo shoots ring and burr.The volume of bamboo
Fabric is widely present in the life of people, and when weaving, because part bamboo chip is harder more crisp, bamboo chip breaks during causing braiding
Split, so as to cause inferior rate in bamboo braiding higher, therefore need to carry out sofening treatment bamboo before braiding, so as to comply with establishment
It is required that.Traditional bamboo chip softening is general all roasting using fire, and this softening mode is excessively simple, easily roasting disconnected bamboo cane, influence bamboo cane
Toughness and intensity.
The content of the invention
It is an object of the invention to provide a kind of bamboo chip softening agent and preparation method thereof, it can effectively solve background technology
In the technical problem that is previously mentioned.
To achieve the above object, the present invention provides following technical scheme：
A kind of bamboo chip softening agent, it is made up of the component of following parts by weight：5-12 parts of dimethylaniline, alcohol ether glucoside
3-9 parts, 5-15 parts of APEO, 6-12 parts of stearyl alcohol, 1-3 parts of lemon, 1-3 parts of dioctyl sodium sulfosuccinate, Buddhist nun
1-3 parts of tortoise beetle ester of pool, 10-20 parts of chloromethyloxirane, 3-8 parts of cellulase, 6-12 parts of isoamyl alcohol, 1-6 parts of triethanolamine,
3-8 parts of neopelex, 2-5 parts of aluminum stearate, 2-9 parts of nickel stearate, 6-11 parts of petroleum ether, Sodium Polyacrylate 1-6
Part, 2-8 parts of urea, 6-13 parts of wood pitch, 2-7 parts of cobalt naphthenate, 120-160 parts of deionized water.
Preferably, the bamboo chip softening agent is made up of the component of following parts by weight：8 parts of dimethylaniline, alcohol ether glucoside 5
Part, 10 parts of APEO, 9 parts of stearyl alcohol, 1.5 parts of lemon, 2 parts of dioctyl sodium sulfosuccinate, methyl hydroxybenzoate 1
Part, 12 parts of chloromethyloxirane, 6 parts of cellulase, 9 parts of isoamyl alcohol, 3 parts of triethanolamine, 4 parts of neopelex,
2.5 parts of aluminum stearate, 5 parts of nickel stearate, 10 parts of petroleum ether, 2 parts of Sodium Polyacrylate, 2 parts of urea, 8 parts of wood pitch, cobalt naphthenate
4 parts, 150 parts of deionized water.
Preferably, the bamboo chip softening agent is made up of the component of following parts by weight：12 parts of dimethylaniline, alcohol ether glucoside
6 parts, 6 parts of APEO, 8 parts of stearyl alcohol, 2 parts of lemon, 2 parts of dioctyl sodium sulfosuccinate, 2 parts of methyl hydroxybenzoate,
14 parts of chloromethyloxirane, 6 parts of cellulase, 10 parts of isoamyl alcohol, 3 parts of triethanolamine, 6 parts of neopelex, firmly
3 parts of resin acid aluminium, 5 parts of nickel stearate, 7 parts of petroleum ether, 4 parts of Sodium Polyacrylate, 4 parts of urea, 8 parts of wood pitch, 5 parts of cobalt naphthenate,
130 parts of deionized water.
Preferably, the bamboo chip softening agent is made up of the component of following parts by weight：6 parts of dimethylaniline, alcohol ether glucoside 9
Part, 10 parts of APEO, 7 parts of stearyl alcohol, 3 parts of lemon, 3 parts of dioctyl sodium sulfosuccinate, 1 part of methyl hydroxybenzoate,
12 parts of chloromethyloxirane, 4 parts of cellulase, 8 parts of isoamyl alcohol, 3 parts of triethanolamine, 5 parts of neopelex is stearic
Sour 5 parts of aluminium, 8 parts of nickel stearate, 11 parts of petroleum ether, 2 parts of Sodium Polyacrylate, 6 parts of urea, 10 parts of wood pitch, 5 parts of cobalt naphthenate,
120 parts of deionized water.
The preparation method of described bamboo chip softening agent, its step is as follows：
(1) each raw material components are weighed according to ratio of weight and number；
(2) stearyl alcohol, isoamyl alcohol, alcohol ether glucoside, APEO and petroleum ether are taken, is put into agitator tank, 25-35 is stirred
Minute, whipping temp is 60-70 DEG C, obtains mixed solution A：
(3) dimethylaniline, dioctyl sodium sulfosuccinate, Ni Bo are added into the mixed solution A obtained by step (2)
Tortoise beetle ester, chloromethyloxirane, cellulase, isoamyl alcohol, triethanolamine, neopelex, aluminum stearate and hard
Resin acid nickel, 115-125 DEG C of whipping temp, quick stirring 5-8 minutes obtains mixed solution B：
(4) lemon, Sodium Polyacrylate, urea, wood pitch, ring are added into the mixed solution B obtained by step (3)
Alkanoic acid cobalt and deionized water, 80-90 DEG C of whipping temp after stirring 30-45 minutes, stand 1-2 hours, continue to stir 15-20 points
Clock, normal temperature cooling.
Compared with prior art, the beneficial effects of the invention are as follows：
Bamboo chip softening agent in the present invention mainly added with dimethylaniline, alcohol ether glucoside, APEO, stearyl alcohol,
Chloromethyloxirane, nickel stearate, petroleum ether and wood pitch, and formed with the collocation of remaining advantages of reasonable raw material components, it has system
It is standby simple, the advantages of bating effect is good, and the bamboo chip softening agent will not shadow in whole preparation process and later stage use
Ring health.
Embodiment
Technical scheme is described in detail with reference to embodiment, but protection domain is not limited thereto.
Embodiment one：
A kind of bamboo chip softening agent, it is made up of the component of following parts by weight：8 parts of dimethylaniline, alcohol ether glucoside 5
Part, 10 parts of APEO, 9 parts of stearyl alcohol, 1.5 parts of lemon, 2 parts of dioctyl sodium sulfosuccinate, methyl hydroxybenzoate 1
Part, 12 parts of chloromethyloxirane, 6 parts of cellulase, 9 parts of isoamyl alcohol, 3 parts of triethanolamine, 4 parts of neopelex,
2.5 parts of aluminum stearate, 5 parts of nickel stearate, 10 parts of petroleum ether, 2 parts of Sodium Polyacrylate, 2 parts of urea, 8 parts of wood pitch, cobalt naphthenate
4 parts, 150 parts of deionized water.
The preparation method of described bamboo chip softening agent, its step is as follows：
(1) each raw material components are weighed according to ratio of weight and number；
(2) stearyl alcohol, isoamyl alcohol, alcohol ether glucoside, APEO and petroleum ether are taken, is put into agitator tank, 30 points are stirred
Clock, whipping temp is 60 DEG C, obtains mixed solution A：
(3) dimethylaniline, dioctyl sodium sulfosuccinate, Ni Bo are added into the mixed solution A obtained by step (2)
Tortoise beetle ester, chloromethyloxirane, cellulase, isoamyl alcohol, triethanolamine, neopelex, aluminum stearate and hard
Resin acid nickel, 120 DEG C of whipping temp, quick stirring 6 minutes obtains mixed solution B：
(4) lemon, Sodium Polyacrylate, urea, wood pitch, ring are added into the mixed solution B obtained by step (3)
Alkanoic acid cobalt and deionized water, 80 DEG C of whipping temp after stirring 36 minutes, stand 1 hour, continue to stir 20 minutes, normal temperature cooling
.
Embodiment two：
A kind of bamboo chip softening agent, it is made up of the component of following parts by weight：12 parts of dimethylaniline, alcohol ether glucoside 6
Part, 6 parts of APEO, 8 parts of stearyl alcohol, 2 parts of lemon, 2 parts of dioctyl sodium sulfosuccinate, 2 parts of methyl hydroxybenzoate, chlorine
14 parts of methyl oxirane, 6 parts of cellulase, 10 parts of isoamyl alcohol, 3 parts of triethanolamine, 6 parts of neopelex is stearic
Sour 3 parts of aluminium, 5 parts of nickel stearate, 7 parts of petroleum ether, 4 parts of Sodium Polyacrylate, 4 parts of urea, 8 parts of wood pitch, 5 parts of cobalt naphthenate is gone
130 parts of ionized water.
The preparation method of described bamboo chip softening agent, its step is as follows：
(1) each raw material components are weighed according to ratio of weight and number；
(2) stearyl alcohol, isoamyl alcohol, alcohol ether glucoside, APEO and petroleum ether are taken, is put into agitator tank, 30-35 is stirred
Minute, whipping temp is 65-70 DEG C, obtains mixed solution A：
(3) dimethylaniline, dioctyl sodium sulfosuccinate, Ni Bo are added into the mixed solution A obtained by step (2)
Tortoise beetle ester, chloromethyloxirane, cellulase, isoamyl alcohol, triethanolamine, neopelex, aluminum stearate and hard
Resin acid nickel, 115-125 DEG C of whipping temp, quick stirring 5-10 minutes obtains mixed solution B：
(4) lemon, Sodium Polyacrylate, urea, wood pitch, ring are added into the mixed solution B obtained by step (3)
Alkanoic acid cobalt and deionized water, 82-86 DEG C of whipping temp after stirring 30 minutes, stand 2 hours, continue to stir 20 minutes, normal temperature is cold
But.
Embodiment three：
A kind of bamboo chip softening agent, it is made up of the component of following parts by weight：6 parts of dimethylaniline, alcohol ether glucoside 9
Part, 10 parts of APEO, 7 parts of stearyl alcohol, 3 parts of lemon, 3 parts of dioctyl sodium sulfosuccinate, 1 part of methyl hydroxybenzoate,
12 parts of chloromethyloxirane, 4 parts of cellulase, 8 parts of isoamyl alcohol, 3 parts of triethanolamine, 5 parts of neopelex is stearic
Sour 5 parts of aluminium, 8 parts of nickel stearate, 11 parts of petroleum ether, 2 parts of Sodium Polyacrylate, 6 parts of urea, 10 parts of wood pitch, 5 parts of cobalt naphthenate,
120 parts of deionized water.
The preparation method of described bamboo chip softening agent, its step is as follows：
(1) each raw material components are weighed according to ratio of weight and number；
(2) stearyl alcohol, isoamyl alcohol, alcohol ether glucoside, APEO and petroleum ether are taken, is put into agitator tank, 30-32 is stirred
Minute, whipping temp is 62-65 DEG C, obtains mixed solution A：
(3) dimethylaniline, dioctyl sodium sulfosuccinate, Ni Bo are added into the mixed solution A obtained by step (2)
Tortoise beetle ester, chloromethyloxirane, cellulase, isoamyl alcohol, triethanolamine, neopelex, aluminum stearate and hard
Resin acid nickel, 120-122 DEG C of whipping temp, quick stirring 3-12 minutes obtains mixed solution B：
(4) lemon, Sodium Polyacrylate, urea, wood pitch, ring are added into the mixed solution B obtained by step (3)
Alkanoic acid cobalt and deionized water, 80-90 DEG C of whipping temp after stirring 42-45 minutes, stand 1-2 hours, continue to stir 16-18 points
Clock, normal temperature cooling.
Example IV：
A kind of bamboo chip softening agent, it is made up of the component of following parts by weight：8 parts of dimethylaniline, alcohol ether glucoside 8
Part, 13 parts of APEO, 7 parts of stearyl alcohol, 1 part of lemon, 2 parts of dioctyl sodium sulfosuccinate, 3 parts of methyl hydroxybenzoate,
15 parts of chloromethyloxirane, 6 parts of cellulase, 12 parts of isoamyl alcohol, 3 parts of triethanolamine, 8 parts of neopelex, firmly
3 parts of resin acid aluminium, 3 parts of nickel stearate, 7 parts of petroleum ether, 5 parts of Sodium Polyacrylate, 5 parts of urea, 10 parts of wood pitch, cobalt naphthenate 4.5
Part, 150 parts of deionized water.
The preparation method of described bamboo chip softening agent, its step is as follows：
(1) each raw material components are weighed according to ratio of weight and number；
(2) stearyl alcohol, isoamyl alcohol, alcohol ether glucoside, APEO and petroleum ether are taken, is put into agitator tank, 25-35 is stirred
Minute, whipping temp is 60-70 DEG C, obtains mixed solution A：
(3) dimethylaniline, dioctyl sodium sulfosuccinate, Ni Bo are added into the mixed solution A obtained by step (2)
Tortoise beetle ester, chloromethyloxirane, cellulase, isoamyl alcohol, triethanolamine, neopelex, aluminum stearate and hard
Resin acid nickel, 115-125 DEG C of whipping temp, quick stirring 5-8 minutes obtains mixed solution B：
(4) lemon, Sodium Polyacrylate, urea, wood pitch, ring are added into the mixed solution B obtained by step (3)
Alkanoic acid cobalt and deionized water, 80-90 DEG C of whipping temp after stirring 30-45 minutes, stand 1-2 hours, continue to stir 15-20 points
Clock, normal temperature cooling.
Embodiment five：
A kind of bamboo chip softening agent, it is made up of the component of following parts by weight：5 parts of dimethylaniline, alcohol ether glucoside 3
Part, 5 parts of APEO, 6 parts of stearyl alcohol, 1 part of lemon, 1 part of dioctyl sodium sulfosuccinate, 1 part of methyl hydroxybenzoate, chlorine
10 parts of methyl oxirane, 3 parts of cellulase, 6 parts of isoamyl alcohol, 1 part of triethanolamine, 3 parts of neopelex, stearic acid
2 parts of aluminium, 2 parts of nickel stearate, 6 parts of petroleum ether, 1 part of Sodium Polyacrylate, 2 parts of urea, 6 parts of wood pitch, 2 parts of cobalt naphthenate, go from
Sub- 120 parts of water.
The preparation method of described bamboo chip softening agent, its step is as follows：
(1) each raw material components are weighed according to ratio of weight and number；
(2) stearyl alcohol, isoamyl alcohol, alcohol ether glucoside, APEO and petroleum ether are taken, is put into agitator tank, 25-35 is stirred
Minute, whipping temp is 60-70 DEG C, obtains mixed solution A：
(3) dimethylaniline, dioctyl sodium sulfosuccinate, Ni Bo are added into the mixed solution A obtained by step (2)
Tortoise beetle ester, chloromethyloxirane, cellulase, isoamyl alcohol, triethanolamine, neopelex, aluminum stearate and hard
Resin acid nickel, 115-125 DEG C of whipping temp, quick stirring 5-8 minutes obtains mixed solution B：
(4) lemon, Sodium Polyacrylate, urea, wood pitch, ring are added into the mixed solution B obtained by step (3)
Alkanoic acid cobalt and deionized water, 80-90 DEG C of whipping temp after stirring 30-45 minutes, stand 1-2 hours, continue to stir 15-20 points
Clock, normal temperature cooling.
Embodiment six：
A kind of bamboo chip softening agent, it is made up of the component of following parts by weight：12 parts of dimethylaniline, alcohol ether glucoside 9
Part, 15 parts of APEO, 12 parts of stearyl alcohol, 3 parts of lemon, 3 parts of dioctyl sodium sulfosuccinate, 3 parts of methyl hydroxybenzoate,
20 parts of chloromethyloxirane, 3 parts of cellulase, 12 parts of isoamyl alcohol, 6 parts of triethanolamine, 8 parts of neopelex, firmly
5 parts of resin acid aluminium, 9 parts of nickel stearate, 11 parts of petroleum ether, 6 parts of Sodium Polyacrylate, 8 parts of urea, 13 parts of wood pitch, cobalt naphthenate 7
Part, 160 parts of deionized water.
The preparation method of described bamboo chip softening agent, its step is as follows：
(1) each raw material components are weighed according to ratio of weight and number；
(2) stearyl alcohol, isoamyl alcohol, alcohol ether glucoside, APEO and petroleum ether are taken, is put into agitator tank, 25-35 is stirred
Minute, whipping temp is 60-70 DEG C, obtains mixed solution A：
(3) dimethylaniline, dioctyl sodium sulfosuccinate, Ni Bo are added into the mixed solution A obtained by step (2)
Tortoise beetle ester, chloromethyloxirane, cellulase, isoamyl alcohol, triethanolamine, neopelex, aluminum stearate and hard
Resin acid nickel, 115-125 DEG C of whipping temp, quick stirring 5-8 minutes obtains mixed solution B：
(4) lemon, Sodium Polyacrylate, urea, wood pitch, ring are added into the mixed solution B obtained by step (3)
Alkanoic acid cobalt and deionized water, 80-90 DEG C of whipping temp after stirring 30-45 minutes, stand 1-2 hours, continue to stir 15-20 points
Clock, normal temperature cooling
Finally illustrate, the above embodiments are merely illustrative of the technical solutions of the present invention and it is unrestricted, although with reference to compared with
The present invention is described in detail good embodiment, it will be understood by those within the art that, can be to skill of the invention
Art scheme is modified or equivalent substitution, and without departing from the objective and scope of the technical program, it all should cover in the present invention
Right among.
Claims (5)
1. a kind of bamboo chip softening agent, it is characterised in that it is made up of the component of following parts by weight：Dimethylaniline 5-12
Part, 3-9 parts of alcohol ether glucoside, 5-15 parts of APEO, 6-12 parts of stearyl alcohol, 1-3 parts of lemon, dioctyl succinate sulfonic acid
1-3 parts of sodium, 1-3 parts of methyl hydroxybenzoate, 10-20 parts of chloromethyloxirane, 3-8 parts of cellulase, 6-12 parts of isoamyl alcohol, three second
1-6 parts of hydramine, 3-8 parts of neopelex, 2-5 parts of aluminum stearate, 2-9 parts of nickel stearate, 6-11 parts of petroleum ether, poly- third
1-6 parts of olefin(e) acid sodium, 2-8 parts of urea, 6-13 parts of wood pitch, 2-7 parts of cobalt naphthenate, 120-160 parts of deionized water.
2. a kind of bamboo chip softening agent according to claim 1, it is characterised in that：The bamboo chip softening agent is by following parts by weight
Several components are made：8 parts of dimethylaniline, 5 parts of alcohol ether glucoside, 10 parts of APEO, 9 parts of stearyl alcohol, lemon 1.5
Part, 2 parts of dioctyl sodium sulfosuccinate, 1 part of methyl hydroxybenzoate, 12 parts of chloromethyloxirane, 6 parts of cellulase, isoamyl alcohol 9
Part, 3 parts of triethanolamine, 4 parts of neopelex, 2.5 parts of aluminum stearate, 5 parts of nickel stearate, 10 parts of petroleum ether, poly- third
2 parts of olefin(e) acid sodium, 2 parts of urea, 8 parts of wood pitch, 4 parts of cobalt naphthenate, 150 parts of deionized water.
3. a kind of bamboo chip softening agent according to claim 1, it is characterised in that：The bamboo chip softening agent is by following parts by weight
Several components are made：12 parts of dimethylaniline, 6 parts of alcohol ether glucoside, 6 parts of APEO, 8 parts of stearyl alcohol, 2 parts of lemon,
2 parts of dioctyl sodium sulfosuccinate, 2 parts of methyl hydroxybenzoate, 14 parts of chloromethyloxirane, 6 parts of cellulase, isoamyl alcohol 10
Part, 3 parts of triethanolamine, 6 parts of neopelex, 3 parts of aluminum stearate, 5 parts of nickel stearate, 7 parts of petroleum ether, polyacrylic acid
4 parts of sodium, 4 parts of urea, 8 parts of wood pitch, 5 parts of cobalt naphthenate, 130 parts of deionized water.
4. a kind of bamboo chip softening agent according to claim 1, it is characterised in that：The bamboo chip softening agent is by following parts by weight
Several components are made：6 parts of dimethylaniline, 9 parts of alcohol ether glucoside, 10 parts of APEO, 7 parts of stearyl alcohol, 3 parts of lemon,
3 parts of dioctyl sodium sulfosuccinate, 1 part of methyl hydroxybenzoate, 12 parts of chloromethyloxirane, 4 parts of cellulase, 8 parts of isoamyl alcohol,
3 parts of triethanolamine, 5 parts of neopelex, 5 parts of aluminum stearate, 8 parts of nickel stearate, 11 parts of petroleum ether, Sodium Polyacrylate
2 parts, 6 parts of urea, 10 parts of wood pitch, 5 parts of cobalt naphthenate, 120 parts of deionized water.
5. the preparation method of the bamboo chip softening agent according to any one of claim 1-4, it is characterised in that step is as follows：
(1) each raw material components are weighed according to ratio of weight and number；
(2) stearyl alcohol, isoamyl alcohol, alcohol ether glucoside, APEO and petroleum ether are taken, is put into agitator tank, 25-35 points of stirring
Clock, whipping temp is 60-70 DEG C, obtains mixed solution A：
(3) dimethylaniline, dioctyl sodium sulfosuccinate, Metagin are added into the mixed solution A obtained by step (2)
Ester, chloromethyloxirane, cellulase, isoamyl alcohol, triethanolamine, neopelex, aluminum stearate and stearic acid
Nickel, 115-125 DEG C of whipping temp, quick stirring 5-8 minutes obtains mixed solution B：
(4) lemon, Sodium Polyacrylate, urea, wood pitch, aphthenic acids are added into the mixed solution B obtained by step (3)
Cobalt and deionized water, 80-90 DEG C of whipping temp after stirring 30-45 minutes, stand 1-2 hours, continue stirring 15-20 minutes, often
Temperature cooling.