CN104960052A - Wicker softening method - Google Patents

Abstract

The invention relates to a wicker softening method. The method comprises the following steps: 1, preparing a treatment fluid A; 2, immersing wickers in the treatment fluid A at 42DEG C for 18h, taking out the wickers, and braiding; and 3, processing by using a treatment fluid B. The wicker softening method is simple, and can soften wickers before braiding to reduce the braiding difficulty and prevent the cracking or fracture of the wickers in the braiding process.

Description

A kind of wicker softening method

Technical field

The invention belongs to treating of wood field, be specifically related to a kind of wicker softening method.

Background technology

Wicker, be a kind of important wicker plaiting article raw material, wicker is more crisp, carry out sofening treatment to be then difficult to weave if do not added, not only easily cause wicker to ftracture even to fracture, the outward appearance causing goods unsightly, easily causes and causes the quality of handicraft to reduce because wicker fractures in braiding process.

Summary of the invention

The object of this invention is to provide a kind of wicker softening method, improve the bating effect of wicker, and complete laggard row relax in braiding, the intensity of wicker can be recovered.

The present invention is achieved through the following technical solutions:

A kind of wicker softening method, comprises the following steps:

(1), preparation treatment fluid A, by weight, by 160 parts, water, glycerine 8.6 parts, tributyl phosphate 0.8 part is heated to 35 DEG C makes it fully mix, and then adds 8.2 parts, urea, 5.2 parts, potassium nitrate, makes its abundant mixed dissolution, obtain treatment fluid A;

(2), by wicker use treatment fluid immersion treatment 18h at 42 DEG C, then wicker is pulled out, weave;

(3), treatment fluid B process, 68 parts, water, sodium salicylate 2.4 parts are stirred at 42-45 DEG C, it is made fully to dissolve, then woven wicker work is put into and wherein soak, immersion treatment 2h, then add sodium acid carbonate 4.6 parts and make it dissolve, continue to soak 3h, pull out, use clear water to rinse well.

Beneficial effect of the present invention: wicker softening method provided by the invention is simple, wicker can be softened before braiding, reduces the difficulty of braiding, prevents wicker cracking or fracture in braiding process, improves quality of item; And liquid A and medical liquid B are processed respectively, after liquid A process, wicker flexibility can be made to increase, and when preventing from weaving, wicker fractures or ftractures, the quality of goods is caused to decline, after braiding completes, use medical liquid B to carry out immersion treatment, the intensity of wicker can be made to recover, strengthen its serviceability, and goods stability is high in use procedure, indeformable, and in use procedure, the corrosion resistance of goods is enhanced.Prepared by the present invention can reach more than 10 years rear service time, and can not be out of shape in use procedure.

Detailed description of the invention

A kind of wicker softening method, comprises the following steps:

(1), preparation treatment fluid A, by weight, by 160 parts, water, glycerine 8.6 parts, tributyl phosphate 0.8 part is heated to 35 DEG C makes it fully mix, and then adds 8.2 parts, urea, 5.2 parts, potassium nitrate, makes its abundant mixed dissolution, obtain treatment fluid A;

(2), by the twigs of the chaste tree use treatment fluid immersion treatment 18h at 42 DEG C, then the twigs of the chaste tree are pulled out, weave;

(3), treatment fluid B process, 68 parts, water, sodium salicylate 2.4 parts are stirred at 42-45 DEG C, it is made fully to dissolve, then woven twigs of the chaste tree goods are put into and wherein soak, immersion treatment 2h, then add sodium acid carbonate 4.6 parts and make it dissolve, continue to soak 3h, pull out, use clear water to rinse well.

Use treatment fluid A of the present invention process, use 700 wickers of same batch to process, arrange control group, the softening reagent of each group all enters immersion treatment 5h to wicker, and result is as following table:

Softening reagent	Experiment quantity	Ftracture after braiding quantity	Number of breaks after braiding	Damaged ratio (%)
					Softening agent of the present invention	100	2	0	2
Water	100	6	4	10
					Glycerine	100	8	0	8
79% water+20% glycerine+1% tributyl phosphate	100	9	2	11
					65% water+35% glycerine	100	10	2	12

Table 1

As shown in Table 1, treatment fluid A of the present invention obviously can promote bating effect relative to conventional softening agent, reduces the damaged ratio of wicker in braiding process, improves the quality of finished product.

Claims (1)

1. a wicker softening method, is characterized in that, comprises the following steps:

(1), preparation treatment fluid A, by weight, by 160 parts, water, glycerine 8.6 parts, tributyl phosphate 0.8 part is heated to 35 DEG C makes it fully mix, and then adds 8.2 parts, urea, 5.2 parts, potassium nitrate, makes its abundant mixed dissolution, obtain treatment fluid A;

(2), by wicker use treatment fluid immersion treatment 18h at 42 DEG C, then wicker is pulled out, weave;

(3), treatment fluid B process, 68 parts, water, sodium salicylate 2.4 parts are stirred at 42-45 DEG C, it is made fully to dissolve, then woven wicker work is put into and wherein soak, immersion treatment 2h, then add sodium acid carbonate 4.6 parts and make it dissolve, continue to soak 3h, pull out, use clear water to rinse well.