CN107052929A - Composite ceramics turning blank and preparation method thereof - Google Patents
Composite ceramics turning blank and preparation method thereof Download PDFInfo
- Publication number
- CN107052929A CN107052929A CN201710350631.XA CN201710350631A CN107052929A CN 107052929 A CN107052929 A CN 107052929A CN 201710350631 A CN201710350631 A CN 201710350631A CN 107052929 A CN107052929 A CN 107052929A
- Authority
- CN
- China
- Prior art keywords
- ceramic form
- composite ceramics
- turning blank
- die cavity
- packed layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to field of ceramic processing, it is intended to solve Ceramic manufacturing in the prior art efficiency it is very low the problem of there is provided a kind of composite ceramics turning blank and preparation method thereof.Composite ceramics turning blank includes ceramic form, packed layer.Packed layer includes being bonded in the work surface of ceramic form and fills the first filling part of the pit on work surface.The preparation method of composite ceramics turning blank includes filling step:The inserts of melting is added into the die cavity for the mould for being placed with ceramic form, the packed layer for the pit for being bonded in the work surface of ceramic form and filling work surface is formed after inserts cooling.The beneficial effects of the invention are as follows Ceramic manufacturing efficiency high and excellent surface can be obtained.
Description
Technical field
The present invention relates to field of ceramic processing, in particular to composite ceramics turning blank and preparation method thereof.
Background technology
Engineering ceramics has widely because of its good hardness and wear resistance, good heat endurance and chemical stability
Application scenarios.However, because engineering ceramics high rigidity and high brittle material character, in process, due to its hard fragility,
Easily there are the situations such as processing crackle, surface damage, overall fragmentation, be a kind of difficult-to-machine material.
At present, in the industrial production, ceramic main machining method is grinding, but the efficiency of grinding is very
Lowly.
The content of the invention
The present invention is intended to provide composite ceramics turning blank, to solve, Ceramic manufacturing efficiency of the prior art is low to ask
Topic.
Another object of the present invention is to provide a kind of composite ceramics turning base for possessing above-mentioned composite ceramics turning blank
The preparation method of part.
What embodiments of the invention were realized in:
The embodiment of the present invention provides a kind of composite ceramics turning blank, and it includes ceramic form, packed layer.Packed layer includes
It is bonded in the work surface of ceramic form and fills the first filling part of the pit on work surface.
By filling packed layer, the first filling part filling of packed layer in the work surface of ceramic form in the present embodiment
Pit on work surface, in the turnery processing using larger cutting data, turning cutting tool puts on ceramic form surface
Horizontal force supported jointly by the laterally supporting power of ceramic form and the first filling part, the ceramic form of pit can equally be received
To good lateral support, ceramic form cutting lay is therefore substantially zeroed and parallel with joint efforts everywhere by of substantially equal load
In the work surface of ceramic form, ceramic form is not easy the crackle for depth direction occur or occurs collapsing broken phenomenon, so as to
Smooth finished surface is obtained under larger cutting data.Thus, the composite ceramics turning blank in the present embodiment can allow for
The machining of larger cutting data, with high in machining efficiency and result in the beneficial effect of smooth finished surface.
In one embodiment of the invention:
Packed layer also includes the second filling part for surrounding the side face of ceramic form.
In one embodiment of the invention:
Ceramic form is to have clamping between plate-like structure, and the outer peripheral face of the second filling part and the side face of ceramic form
Portion.
In one embodiment of the invention:
Heat molten type material of the packed layer by fusing point less than ceramic form is constituted.
The embodiment of the present invention also provides a kind of preparation method of composite ceramics turning blank, and it is used to prepare foregoing be combined
Ceramic turning blank.The preparation method of composite ceramics turning blank comprises the following steps:
Filling step:The inserts of melting is added into the die cavity for the mould for being placed with ceramic form, after inserts cooling
Form the packed layer for the pit for being bonded in the work surface of ceramic form and filling work surface.
In one embodiment of the invention:
The preparation method of composite ceramics turning blank is additionally included in the bonding step before filling step.Bonding step is will
Ceramic form is adhered to the bottom surface of mould.
The embodiment of the present invention also provides a kind of composite ceramics turning blank, and it includes also serving as mould and the base with die cavity
Plate, the ceramic form being arranged in die cavity.Ceramic form is bonded in the bottom surface of die cavity by tack coat.Ceramic blank is removed in die cavity
Space outside part takes up space is filled with packed layer.Packed layer include be filled in ceramic form side face and die cavity side face it
Between the first filling part and covering ceramic form work surface outwardly and fill second of the pit on work surface
Filling part.
In one embodiment of the invention:
The heat molten type material of the same race of tack coat and packed layer by fusing point less than ceramic form is constituted.
In one embodiment of the invention:
The material of packed layer is the metal or alloy that high molecular polymer or fusing point are less than ceramic form.
The embodiment of the present invention also provides a kind of preparation method of composite ceramics turning blank, and it is used to prepare foregoing be combined
Ceramic turning blank.The preparation method of composite ceramics turning blank comprises the following steps:
The underrun hot melt of ceramic form is bonded in the bottom surface of die cavity, and keeps the side face and die cavity of ceramic form
Side face separately, the upper surface of ceramic form be located at the opening of die cavity where within plane;
Add the inserts as melted into die cavity, inserts is filled between the side face of ceramic form and the side face of die cavity
Gap and the upper surface of covering ceramic form, form packed layer.
In summary, in the embodiment of the present invention composite ceramics turning blank and the preparation method of composite ceramics turning blank
With beneficial effect high in machining efficiency.
Brief description of the drawings
In order to illustrate the technical solution of the embodiments of the present invention more clearly, below will be attached to what is used required in embodiment
Figure is briefly described, it will be appreciated that the following drawings illustrate only certain embodiments of the present invention, therefore is not construed as pair
The restriction of scope, for those of ordinary skill in the art, on the premise of not paying creative work, can also be according to this
A little accompanying drawings obtain other related accompanying drawings.
Fig. 1 is the structural representation of the composite ceramics turning blank in the embodiment of the present invention one;
Fig. 2 is sectional views of the Fig. 1 along line B-B;
Fig. 3 is zoomed-in view at Fig. 1 A;
Structural representation when Fig. 4 is prepared for the composite ceramics turning blank in the embodiment of the present invention two;
Fig. 5 is the structural representation of the composite ceramics turning blank in the embodiment of the present invention three;
Fig. 6 is sectional views of the Fig. 5 along line D-D;
Fig. 7 is zoomed-in view at Fig. 5 C;
Fig. 8 be Fig. 5 in substrate topology view.
Icon:100- composite ceramics turning blanks;200- composite ceramics turning blanks;10- ceramic forms;20- packed layers;
The filling parts of 21- first;The filling parts of 22- second;22a- clamping parts;30- substrates;40- tack coats;90- moulds;C1- pits;P1-
Work surface;Q1- die cavitys.
Embodiment
To make the purpose, technical scheme and advantage of the embodiment of the present invention clearer, below in conjunction with the embodiment of the present invention
In accompanying drawing, the technical scheme in the embodiment of the present invention is clearly and completely described, it is clear that described embodiment is
A part of embodiment of the present invention, rather than whole embodiments.The present invention implementation being generally described and illustrated herein in the accompanying drawings
The component of example can be arranged and designed with a variety of configurations.
Therefore, the detailed description of embodiments of the invention below to providing in the accompanying drawings is not intended to limit claimed
The scope of the present invention, but be merely representative of the present invention selected embodiment.Based on the embodiment in the present invention, this area is common
The every other embodiment that technical staff is obtained under the premise of creative work is not made, belongs to the model that the present invention is protected
Enclose.
It should be noted that:Similar label and letter represents similar terms in following accompanying drawing, therefore, once a certain Xiang Yi
It is defined in individual accompanying drawing, then it further need not be defined and explained in subsequent accompanying drawing.
In the description of the invention, it is necessary to explanation, if occur term " " center ", " on ", " under ", "left", "right",
The orientation or position relationship of the instruction such as " vertical ", " level ", " interior ", " outer " be based on orientation shown in the drawings or position relationship,
The orientation or position relationship usually put when either the invention product is used, are for only for ease of the description present invention and simplification is retouched
State, rather than indicate or imply that the device or element of meaning there must be specific orientation, with specific azimuth configuration and operation,
Therefore it is not considered as limiting the invention.If only being used in addition, occurring term " first ", " second " etc. in description of the invention
Described in distinguishing, and it is not intended that indicating or implying relative importance.
If being not offered as requiring that part is absolute in addition, occurring the term such as term " level ", " vertical " in description of the invention
Level or pendency, but can be slightly tilted.As " level " only refers to its direction with respect to more level for " vertical ", not
It is to represent that the structure must be fully horizontal, but can be slightly tilted.
In the description of the invention, in addition it is also necessary to explanation, unless otherwise clearly defined and limited, if there is term
" setting ", " installation ", " connected ", " connection " should be interpreted broadly, for example, it may be being fixedly connected or detachably connecting
Connect, or be integrally connected;Can be mechanical connection or electrical connection;Can be joined directly together, middle matchmaker can also be passed through
Jie is indirectly connected to, and can be the connection of two element internals.For the ordinary skill in the art, can be with concrete condition
Understand the concrete meaning of above-mentioned term in the present invention.
Embodiment one
Fig. 1 is the structural representation of the composite ceramics turning blank 100 in the embodiment of the present invention one;Fig. 2 is Fig. 1 along B-B
The sectional view of line;Fig. 3 is zoomed-in view at Fig. 1 A.It refer to the composite ceramics turning base in Fig. 1, Fig. 2, Fig. 3, the present embodiment
Part 100 includes ceramic form 10 and packed layer 20.Packed layer 20 includes being bonded in the work surface P1 of ceramic form 10 and filled out
The pit C1 filled on work surface P1 the first filling part 21.
In process, process tool will apply horizontal force perpendicular to pit C1 depth directions to ceramic form 10.
Inventor's research finds that one of the reason for existing Machining of Ceramics method generally uses grinding is ceramic batch to be processed
Surface be the out-of-flatness with many pit C1 surface, this makes ceramic form 10 in the horizontal force by cutter, and not
The resistivity that can be provided with depth layer is different, is mainly reflected in the top layer with pit C1 due to pit C1 presence, and
The feature of certain cantilever design is presented, lateral support ability is lost at pit C1, so that top layer cutter active force and lateral
Making a concerted effort between support force is not zero, and making a concerted effort more than lower floor, so that ceramic surface is acted on ceramics by one on the whole
The top layer of blank 10, and using pit C1 hole bottom as the torque of application point, the torque causes, in the presence of the horizontal force of cutter,
Easily crack tangential direction of the ceramic form 10 along pit C1 lower ends, serious will appear to collapsing that depth direction extends
Fragment, so that smooth finished surface can not be obtained by the method for turning processing of big cutting data, limits the processing of ceramics
Efficiency.
Packed layer 20, the first of packed layer 20 are filled by the work surface P1 in ceramic form 10 in the present embodiment
Pit C1 on the filling work surface of filling part 21 P1, in the turnery processing using larger cutting data, turning cutting tool is applied
The horizontal force for being added on the surface of ceramic form 10 is supported jointly by the laterally supporting power of the filling part 21 of ceramic form 10 and first, pit
Ceramic form 10 at C1 can equally receive good lateral support, and the cutting lay of ceramic form 10 is everywhere by of substantially equal
Load, therefore work surface P1 substantially zeroed with joint efforts and parallel to ceramic form 10, ceramic form 10 are not easy to occur deeply
Spend the crackle in direction or occur collapsing broken phenomenon, so as to obtain smooth finished surface under larger cutting data.Thus, this reality
The machining that the composite ceramics turning blank 100 in example can allow for larger cutting data is applied, with high in machining efficiency and energy
Enough obtain the beneficial effect of smooth finished surface.
For the side face of further protection ceramic form 10, packed layer 20 also includes surrounding the second of the side face of ceramic form 10
Filling part 22.The setting of second filling part 22 causes when needing to carry out rounding processing to the seamed edge of ceramic form 10, can
Ensure seamed edge uniform force in process, be less prone to and collapse broken phenomenon.And the outer peripheral face and ceramic blank of the second filling part 22
Can also have clamping part 22a between the side face of part 10, to facilitate the clamping of the ceramic form 10 of plate-like structure before processing, keep away
Exempting from directly clamping ceramic form 10 influences the processing of ceramic form 10.
Heat molten type material of the foregoing packed layer 20 by fusing point less than ceramic form 10 is constituted, and for example packed layer 20 is by high score
Sub- polymer or fusing point are constituted less than the metal or alloy of ceramic form 10, and such as aluminium and its alloy or titanium and its alloy are constituted.
Embodiment two
The preparation method of composite ceramics turning blank 100 in the present embodiment is used to prepare the composite ceramics in embodiment one
Turning blank 100.Fig. 4 (coordinating referring to Fig. 1, Fig. 2, Fig. 3) is referred to, the preparation method of composite ceramics turning blank 100 includes
Filling step, i.e., add the inserts of melting, after inserts cooling into the die cavity Q1 for the mould 90 for being placed with ceramic form 10
Form the packed layer 20 for the pit C1 for being bonded in the work surface P1 of ceramic form 10 and filling work surface P1.It is optional
Ground, spaced between the side face of ceramic form 10 and die cavity Q1 side face, packed layer 20 includes being bonded in ceramic form 10
Work surface P1 and the first filling part 21 and the side face of encirclement ceramic form 10 for filling the pit C1 on work surface P1
The second filling part 22.Composite ceramics turning blank 100 after the completion of shaping can be used for turnery processing, and can be cut in larger
Cut and preferably surface effect is obtained under consumption.Alternatively, bonding step is may also include before filling step.Bonding step is will
Ceramic form 10 is adhered to the bottom surface of mould 90.Bonding agent for bonded ceramics blank 10 and mould 90 can be silicates
Bonding agent, phosphoric acid salt bonding agent, aluminate class bonding agent.
After composite ceramics turning blank 100 is machined, by heating make it is remaining be bonded on ceramic form 10 fill out
Charge fusing is separated with ceramic batch, so as to obtain desired ceramic workpiece.
Embodiment three
Fig. 5 is the structural representation of the composite ceramics turning blank 200 in the embodiment of the present invention three;Fig. 6 is Fig. 5 along D-D
The sectional view of line;Fig. 7 is enlarged drawing at Fig. 5 C.It refer to the composite ceramics turning blank in Fig. 5, Fig. 6, Fig. 7, the present embodiment
200 include also serving as mould and have die cavity Q1 substrate 30, the ceramic form 10 being arranged in die cavity Q1.Fig. 8 shows substrate
30 structure.Ceramic form 10 is bonded in die cavity Q1 bottom surface by tack coat 40.Alternatively, tack coat 40 and packed layer 20 by
Fusing point is constituted less than the heat molten type material of the same race of ceramic form 10.The sky outside ceramic form 10 is taken up space is removed in die cavity Q1
Between be filled with packed layer 20.Alternatively, the material of packed layer 20 is the gold that high molecular polymer or fusing point are less than ceramic form 10
Category or alloy, such as aluminium alloy.Packed layer 20 includes the work surface P1 outwardly of covering ceramic form 10 and fills to be added
The first filling part 21 of pit C1 on the P1 of work surface and it is filled between the side face of ceramic form 10 and die cavity Q1 side face
Second filling part 22.
The composite ceramics turning blank 100 in composite ceramics turning blank 200 and embodiment one in the present embodiment is basic
Identical, its difference is, in addition to also serves as mould and the substrate 30 with die cavity Q1.On the one hand substrate 30 can further carry
The holistic resistant behavior of high composite ceramics turning blank 200 so that the active force that ceramic form 10 is subject in processing can be very
It is distributed on composite ceramics turning blank 200 well, further ceramic form 10 collapses broken or produces crack during reduction processing, another
The composite ceramics turning blank 100 that aspect instead of in embodiment one mould 90 required when being molded.
Therefore, the composite ceramics turning blank 200 in the present embodiment can allow for the machining of larger cutting data, tool
There are beneficial effect that is high in machining efficiency and resulting in smooth finished surface, and the shaping of composite ceramics turning blank 200
Journey does not need additional mold.
Example IV
The preparation method of composite ceramics turning blank 200 in the present embodiment is used to prepare the composite ceramics in embodiment three
Turning blank 200.The preparation method of composite ceramics turning blank 200 comprises the following steps:
The underrun hot melt of ceramic form 10 is bonded in die cavity Q1 bottom surface, and keeps the side face of ceramic form 10
With die cavity Q1 side face separately, the upper surface of ceramic form 10 be located at die cavity Q1 opening where within plane;
Add the inserts as melted into die cavity Q1, inserts is filled the side face of ceramic form 10 and die cavity Q1 side face
Between gap and covering ceramic form 10 upper surface, formed packed layer 20.
The material of packed layer 20 in the present embodiment can be aluminium alloy.Bond the tack coat of ceramic form 10 and substrate 30
40 can be used silicates bonding agent, phosphoric acid salt bonding agent, aluminate class bonding agent.Substrate 30 can be made up of ceramics.
After ceramic form 10 is machined, heating causes tack coat 40 and the fusing of packed layer 20 to depart from ceramic form 10, pottery
Porcelain blank 10 and the taking-up from die cavity Q1, substrate 30 can be reused.
The preferred embodiments of the present invention are the foregoing is only, are not intended to limit the invention, for the skill of this area
For art personnel, the present invention can have various modifications and variations.Within the spirit and principles of the invention, that is made any repaiies
Change, equivalent substitution, improvement etc., should be included in the scope of the protection.
Claims (10)
1. a kind of composite ceramics turning blank, it is characterised in that:
The composite ceramics turning blank includes ceramic form, packed layer;
The packed layer includes being bonded in the work surface of the ceramic form and fills the pit on the work surface
The first filling part.
2. composite ceramics turning blank according to claim 1, it is characterised in that:
The packed layer also includes the second filling part for surrounding the side face of the ceramic form.
3. composite ceramics turning blank according to claim 2, it is characterised in that:
The ceramic form is between plate-like structure, and the outer peripheral face of second filling part and the side face of the ceramic form
With clamping part.
4. the composite ceramics turning blank according to claim any one of 1-3, it is characterised in that:
Heat molten type material of the packed layer by fusing point less than the ceramic form is constituted.
5. a kind of preparation method of composite ceramics turning blank, it is characterised in that:
The preparation method of the composite ceramics turning blank is used to prepare the composite ceramics car as described in claim any one of 1-4
Cut blank;The preparation method of the composite ceramics turning blank comprises the following steps:
Filling step:The inserts of melting is added into the die cavity for the mould for being placed with ceramic form, is formed after inserts cooling
It is bonded in the work surface of the ceramic form and fills the packed layer of the pit of the work surface.
6. the preparation method of composite ceramics turning blank according to claim 5, it is characterised in that the composite ceramics car
The preparation method for cutting blank is additionally included in bonding step before the filling step;
The bonding step is the bottom surface that the ceramic form is adhered to the mould.
7. a kind of composite ceramics turning blank, it is characterised in that the composite ceramics turning blank includes:
Also serve as mould and the substrate with die cavity;
The ceramic form in the die cavity is arranged at, the ceramic form is bonded in the bottom surface of the die cavity by tack coat;
The space outside the ceramic form takes up space is removed in the die cavity and is filled with packed layer;The packed layer includes filling out
The first filling part filled between the side face of the ceramic form and the side face of the die cavity and the court of the covering ceramic form
Outer work surface and the second filling part for filling the pit on the work surface.
8. composite ceramics turning blank according to claim 7, it is characterised in that:
The heat molten type material of the same race of the tack coat and the packed layer by fusing point less than the ceramic form is constituted.
9. composite ceramics turning blank according to claim 8, it is characterised in that:
The material of the packed layer is the metal or alloy that high molecular polymer or fusing point are less than the ceramic form.
10. a kind of preparation method of composite ceramics turning blank, it is characterised in that:
The preparation method of the composite ceramics turning blank is used to prepare the composite ceramics car as described in claim any one of 7-9
Cut blank;The preparation method of the composite ceramics turning blank comprises the following steps:
The underrun hot melt of ceramic form is bonded in the bottom surface of die cavity, and keeps the side face of the ceramic form and described
The side face of die cavity separately, the upper surface of the ceramic form be located at the opening of the die cavity where within plane;
Add the inserts as melted into the die cavity, inserts is filled the side face of the ceramic form and the week of the die cavity
The upper surface in gap and the covering ceramic form between face, forms the packed layer.