CN107043566A - A kind of putty powder and preparation method thereof - Google Patents
A kind of putty powder and preparation method thereof Download PDFInfo
- Publication number
- CN107043566A CN107043566A CN201710446168.9A CN201710446168A CN107043566A CN 107043566 A CN107043566 A CN 107043566A CN 201710446168 A CN201710446168 A CN 201710446168A CN 107043566 A CN107043566 A CN 107043566A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- polished rice
- white
- attapulgite clay
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of putty powder, include the raw material of following parts by weight：10~30 parts of white portland cement, 15~45 parts of magnetite powder, 8~20 parts of modified attapulgite clay, 5~12 parts of desulfurated plaster, 18~48 parts of humidity-controlling functional material, 10~30 parts of White Bentonite, 7~18 parts of polished rice, 2~8 parts of hydroxymethyl cellulose, 3~6 parts of tourmaline powder anionic additive, 2~5 parts of nanometer porous silica, 1.2~2.6 parts of mould inhibitor, 1~2 part of neopelex, 1~3 part of nano inorganic antimicrobial agent.The putty powder environmental protection, with damping, antibacterial and mouldproof, the function of purifying air, service life is long, is adapted to promote.
Description
Technical field
The invention belongs to decoration material field, and in particular to a kind of putty powder and preparation method thereof.
Background technology
Increasingly raising with people to ornament materials quality and Functional Requirement, matched putty also gradually causes
The concern of people.Traditional putty has that low intensity, water absorption rate are big, quality is loose, containing formaldehyde etc. fatal defects, it is impossible to meet day
The use requirement that benefit is improved；On the other hand, existing humidity adjusting material is directly added into powder of lacquer putty for use on the damping effect that can not play, and
Need to be allocated from the suitability of whole components, therefore, high-quality environmental protection in the market, the putty production with humidity conditioning function
Product still belong to blank.
The content of the invention
The invention provides a kind of putty powder and preparation method thereof, the deficiency in above-mentioned background technology is solved, it is described
Putty powder environmental protection, with damping, antibacterial and mouldproof, the function of purifying air, service life is long, is adapted to promote.
In order to solve the problem of prior art is present, adopt the following technical scheme that：
A kind of putty powder, includes the raw material of following parts by weight：10~30 parts of white portland cement, magnetite powder 15~45
Part, 8~20 parts of modified attapulgite clay, 5~12 parts of desulfurated plaster, 18~48 parts of humidity-controlling functional material, White Bentonite 10~
30 parts, 7~18 parts of polished rice, 2~8 parts of hydroxymethyl cellulose, 3~6 parts of tourmaline powder anionic additive, nanometer porous dioxy
2~5 parts of SiClx, 1.2~2.6 parts of mould inhibitor, 1~2 part of neopelex, 1~3 part of nano inorganic antimicrobial agent.
It is preferred that, the putty powder includes the raw material of following parts by weight：13~27 parts of white portland cement, magnetic
It is 21~38 parts of Iron Ore Powder, 9~16 parts of modified attapulgite clay, 8~10 parts of desulfurated plaster, 22~43 parts of humidity-controlling functional material, white
17~23 parts of color bentonite, 9~14 parts of polished rice, 4~6 parts of hydroxymethyl cellulose, 4~5 parts of tourmaline powder anionic additive, receive
2.5~3.5 parts of meter level porous silica, 1.7~2.2 parts of mould inhibitor, neopelex 1.2~1.7 part, nanometer nothing
1.4~2.5 parts of machine antiseptic.
It is preferred that, the putty powder includes the raw material of following parts by weight：18 parts of white portland cement, magnetic iron ore
26 parts of powder, 13 parts of modified attapulgite clay, 9 parts of desulfurated plaster, 27 parts of humidity-controlling functional material, 22 parts of White Bentonite, polished rice 11
Part, 5 parts of hydroxymethyl cellulose, 4.4 parts of tourmaline powder anionic additive, 3 parts of nanometer porous silica, mould inhibitor 1.9
Part, 1.6 parts of neopelex, 1.8 parts of nano inorganic antimicrobial agent.
It is preferred that, the preparation method of the modified attapulgite clay is as follows：Take common concave-convex rod clay plus acetic acid fully anti-
Should, separation, dry, grinding can obtain the modified attapulgite clay.
It is preferred that, the adjustment functional material is that diatomite, zeolite powder and sepiolite are 2 in mass ratio:1:1 mixing it is mixed
Compound.
It is preferred that, the electrodeless antiseptic of nanometer is silver ion antimicrobial agent.
A kind of method for preparing the putty powder, comprises the following steps：
（1）White portland cement, magnetite powder, modified attapulgite clay, desulfurated plaster, humidity conditioning function are weighed by above-mentioned formula
It is material, White Bentonite, polished rice, hydroxymethyl cellulose, tourmaline powder anionic additive, nanometer porous silica, anti-
Mould dose, neopelex, nano inorganic antimicrobial agent, it is standby；
（2）The water of 3~8 times of polished rice own wt, boiling to pulpous state, filtering are added into polished rice unless slurry, cools down, does
Dry, grind into powder, obtains polished rice gel powder；
（3）By the first acidizing pretreatment of humidity-controlling functional material, then calcining 1~2 hour in hot environment is placed in, cooling is subsequently placed in
Powder is ground into pulverizer, pretreated humidity-controlling functional material is obtained；
（4）By white portland cement, magnetite powder, modified attapulgite clay, desulfurated plaster, step（3）Obtained damping work(
Can material, White Bentonite, step（2）Obtained polished rice gel powder, neopelex is mixed and is put into ball mill
Ball milling 2~3 hours, obtains mixed material；
（5）By step（4）Obtained mixed material is mixed with remaining raw material, is put into superfine mill and is milled, after milling
Grain fineness be less than 0.025 millimeter, packaging, you can obtain the putty powder.
It is preferred that, the step（3）The temperature of high temperature environment is 500~800 DEG C.
Compared with prior art, it has the advantages that the present invention：
Putty powder environmental protection of the present invention, with damping, antibacterial and mouldproof, the function of purifying air, service life is long,
It is adapted to promote, it is specific as follows：
（1）Humidity-controlling functional material and attapulgite clay are with the addition of in putty powder raw material of the present invention, function material is adjusted
Expect that for the mixture of diatomite, zeolite powder and sepiolite, diatomite, zeolite powder, sepiolite and attapulgite clay are porous nothing
Machine mineral matter, porous, inorganic mineral matter mixes with other raw materials and is applied to metope, can effectively adjust indoor air humidity, is allowed to control
In the range of health is beneficial to, while pollution-free, Diamond Search release, environmental protection；
（2）Mould inhibitor and inorganic nano antiseptic are with the addition of in putty powder of the present invention, there is the powder of lacquer putty for use on
The function of antimildew and antibacterial；
（3）It is of the present invention and tourmaline anion additive is with the addition of in putty powder, born so air can be produced
Ion, can cleaning ambient air, be conducive to health.
Embodiment
With reference to specific embodiment, the present invention is expanded on further.These embodiments be merely to illustrate the present invention and without
In limitation the scope of the present invention.
Embodiment 1
The present embodiment is related to a kind of putty powder, includes the raw material of following parts by weight：10 parts of white portland cement, magnetic iron ore
15 parts of powder, 8 parts of modified attapulgite clay, 5 parts of desulfurated plaster, 18 parts of humidity-controlling functional material, 10 parts of White Bentonite, 7 parts of polished rice,
2 parts of hydroxymethyl cellulose, 3 parts of tourmaline powder anionic additive, 2 parts of nanometer porous silica, 1.2 parts of mould inhibitor, ten
1 part of dialkyl benzene sulfonic acids sodium, 1 part of nano inorganic antimicrobial agent.
Wherein, the preparation method of the modified attapulgite clay is as follows：Common concave-convex rod clay plus acetic acid is taken fully to react,
Separation, dry, grinding can obtain the modified attapulgite clay.
Wherein, the adjustment functional material is that diatomite, zeolite powder and sepiolite are 2 in mass ratio:1:The mixing of 1 mixing
Thing.
Wherein, the electrodeless antiseptic of the nanometer is silver ion antimicrobial agent.
A kind of method for preparing the putty powder, comprises the following steps：
（1）White portland cement, magnetite powder, modified attapulgite clay, desulfurated plaster, humidity conditioning function are weighed by above-mentioned formula
It is material, White Bentonite, polished rice, hydroxymethyl cellulose, tourmaline powder anionic additive, nanometer porous silica, anti-
Mould dose, neopelex, nano inorganic antimicrobial agent, it is standby；
（2）The water of 3 times of polished rice own wt, boiling to pulpous state, filtering are added into polished rice unless slurry, cools down, dry, grind
Clay into power, obtain polished rice gel powder；
（3）By the first acidizing pretreatment of humidity-controlling functional material, then calcining 1 hour in hot environment is placed in, cooling is subsequently placed in crushing
Powder is ground into machine, pretreated humidity-controlling functional material is obtained；
（4）By white portland cement, magnetite powder, modified attapulgite clay, desulfurated plaster, step（3）Obtained damping work(
Can material, White Bentonite, step（2）Obtained polished rice gel powder, neopelex is mixed and is put into ball mill
Ball milling 2 hours, obtains mixed material；
（5）By step（4）Obtained mixed material is mixed with remaining raw material, is put into superfine mill and is milled, after milling
Grain fineness be less than 0.025 millimeter, packaging, you can obtain the putty powder.
Wherein, the step（3）The temperature of high temperature environment is 500 DEG C.
Embodiment 2
The present embodiment is related to a kind of putty powder, includes the raw material of following parts by weight：30 parts of white portland cement, magnetic iron ore
45 parts of powder, 20 parts of modified attapulgite clay, 12 parts of desulfurated plaster, 48 parts of humidity-controlling functional material, 30 parts of White Bentonite, polished rice 18
Part, 8 parts of hydroxymethyl cellulose, 6 parts of tourmaline powder anionic additive, 5 parts of nanometer porous silica, 2.6 parts of mould inhibitor,
2 parts of neopelex, 3 parts of nano inorganic antimicrobial agent.
Wherein, the preparation method of the modified attapulgite clay is as follows：Common concave-convex rod clay plus acetic acid is taken fully to react,
Separation, dry, grinding can obtain the modified attapulgite clay.
Wherein, the adjustment functional material is that diatomite, zeolite powder and sepiolite are 2 in mass ratio:1:The mixing of 1 mixing
Thing.
Wherein, the electrodeless antiseptic of the nanometer is silver ion antimicrobial agent.
A kind of method for preparing the putty powder, comprises the following steps：
（1）White portland cement, magnetite powder, modified attapulgite clay, desulfurated plaster, humidity conditioning function are weighed by above-mentioned formula
It is material, White Bentonite, polished rice, hydroxymethyl cellulose, tourmaline powder anionic additive, nanometer porous silica, anti-
Mould dose, neopelex, nano inorganic antimicrobial agent, it is standby；
（2）The water of 8 times of polished rice own wt, boiling to pulpous state, filtering are added into polished rice unless slurry, cools down, dry, grind
Clay into power, obtain polished rice gel powder；
（3）By the first acidizing pretreatment of humidity-controlling functional material, then calcining 2 hours in hot environment are placed in, cooling is subsequently placed in crushing
Powder is ground into machine, pretreated humidity-controlling functional material is obtained；
（4）By white portland cement, magnetite powder, modified attapulgite clay, desulfurated plaster, step（3）Obtained damping work(
Can material, White Bentonite, step（2）Obtained polished rice gel powder, neopelex is mixed and is put into ball mill
Ball milling 3 hours, obtains mixed material；
（5）By step（4）Obtained mixed material is mixed with remaining raw material, is put into superfine mill and is milled, after milling
Grain fineness be less than 0.025 millimeter, packaging, you can obtain the putty powder.
Wherein, the step（3）The temperature of high temperature environment is 800 DEG C.
Embodiment 3
The present embodiment is related to a kind of putty powder, includes the raw material of following parts by weight：13 parts of white portland cement, magnetic iron ore
21 parts of powder, 9 parts of modified attapulgite clay, 8 parts of desulfurated plaster, 22 parts of humidity-controlling functional material, 17 parts of White Bentonite, 9 parts of polished rice,
4 parts of hydroxymethyl cellulose, 4 parts of tourmaline powder anionic additive, 2.5 parts of nanometer porous silica, 1.7 parts of mould inhibitor,
1.2 parts of neopelex, 1.4 parts of nano inorganic antimicrobial agent.
Wherein, the preparation method of the modified attapulgite clay is as follows：Common concave-convex rod clay plus acetic acid is taken fully to react,
Separation, dry, grinding can obtain the modified attapulgite clay.
Wherein, the adjustment functional material is that diatomite, zeolite powder and sepiolite are 2 in mass ratio:1:The mixing of 1 mixing
Thing.
Wherein, the electrodeless antiseptic of the nanometer is silver ion antimicrobial agent.
A kind of method for preparing the putty powder, comprises the following steps：
（1）White portland cement, magnetite powder, modified attapulgite clay, desulfurated plaster, humidity conditioning function are weighed by above-mentioned formula
It is material, White Bentonite, polished rice, hydroxymethyl cellulose, tourmaline powder anionic additive, nanometer porous silica, anti-
Mould dose, neopelex, nano inorganic antimicrobial agent, it is standby；
（2）The water of 4 times of polished rice own wt, boiling to pulpous state, filtering are added into polished rice unless slurry, cools down, dry, grind
Clay into power, obtain polished rice gel powder；
（3）By the first acidizing pretreatment of humidity-controlling functional material, then calcining 1.5 hours in hot environment are placed in, cooling is subsequently placed in powder
Powder is ground into broken machine, pretreated humidity-controlling functional material is obtained；
（4）By white portland cement, magnetite powder, modified attapulgite clay, desulfurated plaster, step（3）Obtained damping work(
Can material, White Bentonite, step（2）Obtained polished rice gel powder, neopelex is mixed and is put into ball mill
Ball milling 2.5 hours, obtains mixed material；
（5）By step（4）Obtained mixed material is mixed with remaining raw material, is put into superfine mill and is milled, after milling
Grain fineness be less than 0.025 millimeter, packaging, you can obtain the putty powder.
Wherein, the step（3）The temperature of high temperature environment is 600 DEG C.
Embodiment 4
The present embodiment is related to a kind of putty powder, includes the raw material of following parts by weight：27 parts of white portland cement, magnetic iron ore
38 parts of powder, 16 parts of modified attapulgite clay, 10 parts of desulfurated plaster, 43 parts of humidity-controlling functional material, 23 parts of White Bentonite, polished rice 14
Part, 6 parts of hydroxymethyl cellulose, 5 parts of tourmaline powder anionic additive, 3.5 parts of nanometer porous silica, mould inhibitor 2.2
Part, 1.7 parts of neopelex, 2.5 parts of nano inorganic antimicrobial agent.
Wherein, the preparation method of the modified attapulgite clay is as follows：Common concave-convex rod clay plus acetic acid is taken fully to react,
Separation, dry, grinding can obtain the modified attapulgite clay.
Wherein, the adjustment functional material is that diatomite, zeolite powder and sepiolite are 2 in mass ratio:1:The mixing of 1 mixing
Thing.
Wherein, the electrodeless antiseptic of the nanometer is silver ion antimicrobial agent.
A kind of method for preparing the putty powder, comprises the following steps：
（1）White portland cement, magnetite powder, modified attapulgite clay, desulfurated plaster, humidity conditioning function are weighed by above-mentioned formula
It is material, White Bentonite, polished rice, hydroxymethyl cellulose, tourmaline powder anionic additive, nanometer porous silica, anti-
Mould dose, neopelex, nano inorganic antimicrobial agent, it is standby；
（2）The water of 5 times of polished rice own wt, boiling to pulpous state, filtering are added into polished rice unless slurry, cools down, dry, grind
Clay into power, obtain polished rice gel powder；
（3）By the first acidizing pretreatment of humidity-controlling functional material, then calcining 1.3 hours in hot environment are placed in, cooling is subsequently placed in powder
Powder is ground into broken machine, pretreated humidity-controlling functional material is obtained；
（4）By white portland cement, magnetite powder, modified attapulgite clay, desulfurated plaster, step（3）Obtained damping work(
Can material, White Bentonite, step（2）Obtained polished rice gel powder, neopelex is mixed and is put into ball mill
Ball milling 2.8 hours, obtains mixed material；
（5）By step（4）Obtained mixed material is mixed with remaining raw material, is put into superfine mill and is milled, after milling
Grain fineness be less than 0.025 millimeter, packaging, you can obtain the putty powder.
Wherein, the step（3）The temperature of high temperature environment is 700 DEG C.
Embodiment 5
The present embodiment is related to a kind of putty powder, includes the raw material of following parts by weight：18 parts of white portland cement, magnetic iron ore
26 parts of powder, 13 parts of modified attapulgite clay, 9 parts of desulfurated plaster, 27 parts of humidity-controlling functional material, 22 parts of White Bentonite, polished rice 11
Part, 5 parts of hydroxymethyl cellulose, 4.4 parts of tourmaline powder anionic additive, 3 parts of nanometer porous silica, mould inhibitor 1.9
Part, 1.6 parts of neopelex, 1.8 parts of nano inorganic antimicrobial agent.
Wherein, the preparation method of the modified attapulgite clay is as follows：Common concave-convex rod clay plus acetic acid is taken fully to react,
Separation, dry, grinding can obtain the modified attapulgite clay.
Wherein, the adjustment functional material is that diatomite, zeolite powder and sepiolite are 2 in mass ratio:1:The mixing of 1 mixing
Thing.
Wherein, the electrodeless antiseptic of the nanometer is silver ion antimicrobial agent.
A kind of method for preparing the putty powder, comprises the following steps：
（1）White portland cement, magnetite powder, modified attapulgite clay, desulfurated plaster, humidity conditioning function are weighed by above-mentioned formula
It is material, White Bentonite, polished rice, hydroxymethyl cellulose, tourmaline powder anionic additive, nanometer porous silica, anti-
Mould dose, neopelex, nano inorganic antimicrobial agent, it is standby；
（2）The water of 7 times of polished rice own wt, boiling to pulpous state, filtering are added into polished rice unless slurry, cools down, dry, grind
Clay into power, obtain polished rice gel powder；
（3）By the first acidizing pretreatment of humidity-controlling functional material, then calcining 1.8 hours in hot environment are placed in, cooling is subsequently placed in powder
Powder is ground into broken machine, pretreated humidity-controlling functional material is obtained；
（4）By white portland cement, magnetite powder, modified attapulgite clay, desulfurated plaster, step（3）Obtained damping work(
Can material, White Bentonite, step（2）Obtained polished rice gel powder, neopelex is mixed and is put into ball mill
Ball milling 2.3 hours, obtains mixed material；
（5）By step（4）Obtained mixed material is mixed with remaining raw material, is put into superfine mill and is milled, after milling
Grain fineness be less than 0.025 millimeter, packaging, you can obtain the putty powder.
Wherein, the step（3）The temperature of high temperature environment is 550 DEG C.
The specific embodiment of the present invention is described above.It is to be appreciated that the invention is not limited in above-mentioned
Particular implementation, those skilled in the art can make various deformations or amendments within the scope of the claims, this not shadow
Ring the substantive content of the present invention.
Claims (8)
1. a kind of putty powder, it is characterised in that include the raw material of following parts by weight：10~30 parts of white portland cement,
15~45 parts of magnetite powder, 8~20 parts of modified attapulgite clay, 5~12 parts of desulfurated plaster, 18~48 parts of humidity-controlling functional material,
10~30 parts of White Bentonite, 7~18 parts of polished rice, 2~8 parts of hydroxymethyl cellulose, 3~6 parts of tourmaline powder anionic additive,
Nanometer porous 2~5 parts of silica, 1.2~2.6 parts of mould inhibitor, 1~2 part of neopelex, nano inorganic antibacterial
1~3 part of agent.
2. putty powder according to claim 1, it is characterised in that include the raw material of following parts by weight：White silicic acid
13~27 parts of salt cement, 21~38 parts of magnetite powder, 9~16 parts of modified attapulgite clay, 8~10 parts of desulfurated plaster, damping work(
Can 22~43 parts of material, 17~23 parts of White Bentonite, 9~14 parts of polished rice, 4~6 parts of hydroxymethyl cellulose, tourmaline powder bear from
Sub- 4~5 parts of additive, 2.5~3.5 parts of nanometer porous silica, 1.7~2.2 parts of mould inhibitor, neopelex
1.2~1.7 parts, 1.4~2.5 parts of nano inorganic antimicrobial agent.
3. putty powder according to claim 1, it is characterised in that include the raw material of following parts by weight：White silicic acid
18 parts of salt cement, 26 parts of magnetite powder, 13 parts of modified attapulgite clay, 9 parts of desulfurated plaster, 27 parts of humidity-controlling functional material, white
22 parts of bentonite, 11 parts of polished rice, 5 parts of hydroxymethyl cellulose, 4.4 parts of tourmaline powder anionic additive, nanometer porous dioxy
3 parts of SiClx, 1.9 parts of mould inhibitor, 1.6 parts of neopelex, 1.8 parts of nano inorganic antimicrobial agent.
4. putty powder according to claim 1, it is characterised in that the preparation method of the modified attapulgite clay is such as
Under：Take common concave-convex rod clay plus acetic acid fully to react, separate, dry, grinding and can obtain the modified attapulgite clay.
5. putty powder according to claim 1, it is characterised in that the adjustment functional material is diatomite, zeolite
Powder and sepiolite are 2 in mass ratio:1:The mixture of 1 mixing.
6. putty powder according to claim 1, it is characterised in that the electrodeless antiseptic of nanometer is silver-ion antibiotic
Agent.
7. a kind of method for preparing any one of claim 1~6 putty powder, it is characterised in that comprise the following steps：
（1）White portland cement, magnetite powder, modified attapulgite clay, desulfurated plaster, humidity conditioning function are weighed by above-mentioned formula
It is material, White Bentonite, polished rice, hydroxymethyl cellulose, tourmaline powder anionic additive, nanometer porous silica, anti-
Mould dose, neopelex, nano inorganic antimicrobial agent, it is standby；
（2）The water of 3~8 times of polished rice own wt, boiling to pulpous state, filtering are added into polished rice unless slurry, cools down, does
Dry, grind into powder, obtains polished rice gel powder；
（3）By the first acidizing pretreatment of humidity-controlling functional material, then calcining 1~2 hour in hot environment is placed in, cooling is subsequently placed in
Powder is ground into pulverizer, pretreated humidity-controlling functional material is obtained；
（4）By white portland cement, magnetite powder, modified attapulgite clay, desulfurated plaster, step（3）Obtained damping work(
Can material, White Bentonite, step（2）Obtained polished rice gel powder, neopelex is mixed and is put into ball mill
Ball milling 2~3 hours, obtains mixed material；
（5）By step（4）Obtained mixed material is mixed with remaining raw material, is put into superfine mill and is milled, after milling
Grain fineness be less than 0.025 millimeter, packaging, you can obtain the putty powder.
8. preparation method according to claim 7, it is characterised in that the step（3）The temperature of high temperature environment is 500
~800 DEG C.