CN107043480A - Capacitor insulation shield material and preparation method thereof - Google Patents
Capacitor insulation shield material and preparation method thereof Download PDFInfo
- Publication number
- CN107043480A CN107043480A CN201611025140.XA CN201611025140A CN107043480A CN 107043480 A CN107043480 A CN 107043480A CN 201611025140 A CN201611025140 A CN 201611025140A CN 107043480 A CN107043480 A CN 107043480A
- Authority
- CN
- China
- Prior art keywords
- parts
- nano
- density polyethylene
- shield material
- insulation shield
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of capacitor insulation shield material, according to the mass fraction, its composition of raw materials is as follows:1000~1500 parts of diatomite, 1000~1300 parts of medium density polyethylene resin, 1000~1500 parts of di-n-octyl sebacate, 800~1200 parts of metallocene linear-low density polyethylene, 1200~1800 parts of nano-sized carbon, 35~50 parts of nano-calcium carbonate, 10~20 parts of polyvinyl chloride resin, 50~80 parts of zinc sulfate, 60~90 parts of bipentaerythrite, 30~60 parts of dibutyl ester.The present invention prepares capacitor insulation shield material using diatomite, polyvinyl chloride resin, nano-calcium carbonate and zinc sulfate, with no coupling product, strong operability, and effectively control production cost the advantages of, the present invention can both dissolve auxiliary resin very well, diatomite in formula can improve insulating shield material antiseptic property, while nano-calcium carbonate can also further solve bubble problem.
Description
Technical field
The present invention relates to a kind of capacitor insulation shield material and preparation method thereof.
Background technology
With developing rapidly for economic construction, the continuous improvement of people's standard of living, all kinds of infrastructure in town and country it is quick
Development, it is increasing to all kinds of capacitor demands, therefore the quality of continuous improvement capacitor seems particularly significant, and constantly carry
The performance of high capacitance shield material, improves the performance such as anti-corrosion, wear-resisting, anti-aging, it can be ensured that to the protecting effect of capacitor.
The content of the invention
The technical problem to be solved in the present invention is to overcome existing defect there is provided a kind of capacitor insulation shield material, by matter
Number meter is measured, its composition of raw materials is as follows:
1000~1500 parts of diatomite, 1000~1300 parts of medium density polyethylene resin, di-n-octyl sebacate 1000~
1500 parts, 800~1200 parts of metallocene linear-low density polyethylene, 1200~1800 parts of nano-sized carbon, nano-calcium carbonate 35~50
Part, 10~20 parts of polyvinyl chloride resin, 50~80 parts of zinc sulfate, 60~90 parts of bipentaerythrite, 30~60 parts of dibutyl ester.
Further, according to the mass fraction, its composition of raw materials is as follows for the capacitor insulation shield material:
1200 parts of diatomite, 1000 parts of medium density polyethylene resin, di-n-octyl sebacate 1200, metallocene linear low density
Polyethylene 1000,1500 parts of nano-sized carbon, 40~45 parts of nano-calcium carbonate, 15 parts of polyvinyl chloride resin, 60~70 parts of zinc sulfate, double seasons penta
70~85 parts of tetrol, 40~50 parts of dibutyl ester.
It is preferred that, according to the mass fraction, its composition of raw materials is as follows for the capacitor insulation shield material:
1000 parts of diatomite, 1000 parts of medium density polyethylene resin, 1000 parts of di-n-octyl sebacate, metallocene linear are low close
Spend 800 parts of polyethylene, 1200 parts of nano-sized carbon, 35 parts of nano-calcium carbonate, 10 parts of polyvinyl chloride resin, 50 parts of zinc sulfate, bipentaerythrite 60
Part, 30 parts of dibutyl ester.
It is preferred that, according to the mass fraction, its composition of raw materials is as follows for the capacitor insulation shield material:
1500 parts of diatomite, 1300 parts of medium density polyethylene resin, 1500 parts of di-n-octyl sebacate, metallocene linear are low close
Spend 1200 parts of polyethylene, 1800 parts of nano-sized carbon, 50 parts of nano-calcium carbonate, 20 parts of polyvinyl chloride resin, 80 parts of zinc sulfate, bipentaerythrite
90 parts, 60 parts of dibutyl ester.
Another aspect of the present invention discloses a kind of production method of capacitor insulation shield material, and it includes following step
Suddenly:
1), diatomite is crushed, nano-sized carbon, medium density polyethylene resin is then proportionally added into, di-n-octyl sebacate, receives
Rice calcium carbonate, metallocene linear-low density polyethylene, polyvinyl chloride resin, bipentaerythrite, obtain mixture;
2) add in other residual components, feeding high-speed kneading machine, 6-15min is mediated at 110-150 DEG C, wait to mediate material
After cooling, feeding double screw extruder granulation produces capacitor insulation shield material.
The beneficial effect that is reached of the present invention is:The present invention uses diatomite, polyvinyl chloride resin, nano-calcium carbonate and zinc sulfate
Capacitor insulation shield material is prepared, with no coupling product, strong operability, and the advantages of effectively control production cost, the present invention was both
The diatomite in auxiliary resin, formula can be dissolved very well can improve insulating shield material antiseptic property, while nano-calcium carbonate
Bubble problem can also further be solved.
Embodiment
The preferred embodiments of the present invention are illustrated below, it will be appreciated that preferred embodiment described herein is only used
In the description and interpretation present invention, it is not intended to limit the present invention.
Embodiment 1
A kind of capacitor insulation shield material, according to the mass fraction, its composition of raw materials is as follows:
1000 parts of diatomite, 1300 parts of medium density polyethylene resin, 1000 parts of di-n-octyl sebacate, metallocene linear are low close
Spend 1200 parts of polyethylene, 1200 parts of nano-sized carbon, 50 parts of nano-calcium carbonate, 10 parts of polyvinyl chloride resin, 80 parts of zinc sulfate.
The capacitor insulation shield material of the present invention, is prepared using following methods:
1), diatomite is crushed, nano-sized carbon, medium density polyethylene resin is then proportionally added into, di-n-octyl sebacate, receives
Rice calcium carbonate, metallocene linear-low density polyethylene, polyvinyl chloride resin, bipentaerythrite, obtain mixture;
2) add in other residual components, feeding high-speed kneading machine, 6-15min is mediated at 110-150 DEG C, wait to mediate material
After cooling, feeding double screw extruder granulation produces capacitor insulation shield material.
Embodiment 2
A kind of capacitor insulation shield material, according to the mass fraction, its composition of raw materials is as follows:
1500 parts of diatomite, 1000 parts of medium density polyethylene resin, 1500 parts of di-n-octyl sebacate, metallocene linear are low close
Spend 800 parts of polyethylene, 1800 parts of nano-sized carbon, 35 parts, 20 parts polyvinyl chloride resins of nano-calcium carbonate, 50 parts of zinc sulfate.
The capacitor insulation shield material of the present invention, is prepared using following methods:
1), diatomite is crushed, nano-sized carbon, medium density polyethylene resin is then proportionally added into, di-n-octyl sebacate, receives
Rice calcium carbonate, metallocene linear-low density polyethylene, polyvinyl chloride resin, bipentaerythrite, obtain mixture;
2) add in other residual components, feeding high-speed kneading machine, 6-15min is mediated at 110-150 DEG C, wait to mediate material
After cooling, feeding double screw extruder granulation produces capacitor insulation shield material.
Embodiment 3
A kind of capacitor insulation shield material, according to the mass fraction, its composition of raw materials is as follows:
1200 parts of diatomite, 1000 parts of medium density polyethylene resin, 1200 parts of di-n-octyl sebacate, metallocene linear are low close
Spend 1000 parts of polyethylene, 1500 parts of nano-sized carbon, nano-calcium carbonate Ca45 part, 15 parts of polyvinyl chloride resins, 60 parts of zinc sulfate.
The capacitor insulation shield material of the present invention, is prepared using following methods:
1), diatomite is crushed, nano-sized carbon, medium density polyethylene resin is then proportionally added into, di-n-octyl sebacate, receives
Rice calcium carbonate, metallocene linear-low density polyethylene, polyvinyl chloride resin, bipentaerythrite, obtain mixture;
2) add in other residual components, feeding high-speed kneading machine, 6-15min is mediated at 110-150 DEG C, wait to mediate material
After cooling, feeding double screw extruder granulation produces capacitor insulation shield material.
Embodiment 4
A kind of capacitor insulation shield material, according to the mass fraction, its composition of raw materials is as follows:
1200 parts of diatomite, 1100 parts of medium density polyethylene resin, 1200 parts of di-n-octyl sebacate, metallocene linear are low close
Spend 1000 parts of polyethylene, 1500 parts of nano-sized carbon, 40 parts of nano-calcium carbonate, 15 parts of polyvinyl chloride resins, 70 parts of zinc sulfate.
The capacitor insulation shield material of the present invention, is prepared using following methods:
1), diatomite is crushed, nano-sized carbon, medium density polyethylene resin is then proportionally added into, di-n-octyl sebacate, receives
Rice calcium carbonate, metallocene linear-low density polyethylene, polyvinyl chloride resin, bipentaerythrite, obtain mixture;
2) add in other residual components, feeding high-speed kneading machine, 6-15min is mediated at 110-150 DEG C, wait to mediate material
After cooling, feeding double screw extruder granulation produces capacitor insulation shield material.
The present invention prepares capacitor insulation shield material using diatomite, polyvinyl chloride resin, nano-calcium carbonate and zinc sulfate, has
No coupling product, strong operability, and effectively control production cost the advantages of, the present invention can both dissolve auxiliary resin very well, be formulated
In diatomite can improve insulating shield material antiseptic property, asked while nano-calcium carbonate can also further solve foaming
Topic.
Finally it should be noted that:The preferred embodiments of the present invention are the foregoing is only, are not intended to limit the invention,
Although the present invention is described in detail with reference to the foregoing embodiments, for those skilled in the art, it still may be used
To be modified to the technical scheme described in foregoing embodiments, or equivalent substitution is carried out to which part technical characteristic.
Within the spirit and principles of the invention, any modification, equivalent substitution and improvements made etc., should be included in the present invention's
Within protection domain.
Claims (7)
1. a kind of capacitor insulation shield material, it is characterised in that according to the mass fraction, its composition of raw materials is as follows:
1000~1500 parts of diatomite, 1000~1300 parts of medium density polyethylene resin, 1000~1500 parts of di-n-octyl sebacate,
800~1200 parts of metallocene linear-low density polyethylene, 1200~1800 parts of nano-sized carbon, 35~50 parts of nano-calcium carbonate, PVC trees
10~20 parts of fat, 50~80 parts of zinc sulfate, 60~90 parts of bipentaerythrite, 30~60 parts of dibutyl ester.
2. a kind of capacitor insulation shield material as claimed in claim 1, it is characterised in that according to the mass fraction, its raw material is matched somebody with somebody
Side is as follows:
1200 parts of diatomite, 1000 parts of medium density polyethylene resin, 1200 parts of di-n-octyl sebacate, metallocene linear low density gather
1000 parts of ethene, 1500 parts of nano-sized carbon, 40~45 parts of nano-calcium carbonate, 15 parts of polyvinyl chloride resin, 60~70 parts of zinc sulfate, double seasons penta
70~85 parts of tetrol, 40~50 parts of dibutyl ester.
3. a kind of capacitor insulation shield material as claimed in claim 1, it is characterised in that according to the mass fraction, its raw material is matched somebody with somebody
Side is as follows:
1000 parts of diatomite, 1000 parts of medium density polyethylene resin, 1000 parts of di-n-octyl sebacate, metallocene linear low density gather
800 parts of ethene, 1200 parts of nano-sized carbon, 35 parts of nano-calcium carbonate, 10 parts of polyvinyl chloride resin, 50 parts of zinc sulfate, 60 parts of bipentaerythrite,
30 parts of dibutyl ester.
4. a kind of capacitor insulation shield material as claimed in claim 1, it is characterised in that according to the mass fraction, its raw material is matched somebody with somebody
Side is as follows:
1500 parts of diatomite, 1300 parts of medium density polyethylene resin, 1500 parts of di-n-octyl sebacate, metallocene linear low density gather
1200 parts of ethene, 1800 parts of nano-sized carbon, 50 parts of nano-calcium carbonate, 20 parts of polyvinyl chloride resin, 80 parts of zinc sulfate, 90 parts of bipentaerythrite,
60 parts of dibutyl ester.
5. the production method of capacitor insulation shield material described in a kind of claim 1, it is characterised in that comprise the following steps:
1), diatomite is crushed, nano-sized carbon, medium density polyethylene resin, di-n-octyl sebacate, nano-sized carbon is then proportionally added into
Sour calcium, metallocene linear-low density polyethylene, polyvinyl chloride resin, bipentaerythrite, obtain mixture;
2) add and mediated in other residual components, feeding high-speed kneading machine, after material cooling is mediated, feeding double screw extruder is made
Grain, produces capacitor insulation shield material.
6. the production method of capacitor insulation shield material according to claim 5, it is characterised in that the ratio of each material presses matter
Amount number is calculated as:
1000~1500 parts of diatomite, 1000~1300 parts of medium density polyethylene resin, 1000~1500 parts of di-n-octyl sebacate,
800~1200 parts of metallocene linear-low density polyethylene, 1200~1800 parts of nano-sized carbon, 35~50 parts of nano-calcium carbonate, PVC trees
10~20 parts of fat, 50~80 parts of zinc sulfate, 60~90 parts of bipentaerythrite, 30~60 parts of dibutyl ester.
7. the production method of capacitor insulation shield material according to claim 5, it is characterised in that step 2) in, Jiang Geyuan
In material feeding high-speed kneading machine, 6-15min is mediated at 110-150 DEG C.