CN107042560A - Seamless spliced moisture-proof floor and its preparation technology - Google Patents
Seamless spliced moisture-proof floor and its preparation technology Download PDFInfo
- Publication number
- CN107042560A CN107042560A CN201710042617.3A CN201710042617A CN107042560A CN 107042560 A CN107042560 A CN 107042560A CN 201710042617 A CN201710042617 A CN 201710042617A CN 107042560 A CN107042560 A CN 107042560A
- Authority
- CN
- China
- Prior art keywords
- oil
- floor
- moisture
- proof
- seamless spliced
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of seamless spliced moisture-proof floor and its preparation technology, its back side is provided with intensive miniature wave channel；The surrounding of the seamless spliced moisture-proof floor scribbles moistureproof weather-proof vegetable oil, wherein the moistureproof weather-proof vegetable oil includes Chinese catalpa oil, refines linseed oil, refines tung oil, tea-seed oil and kuh-seng oil, and weight ratio is：Chinese catalpa oil：Refine linseed oil：Refine tung oil：Tea-seed oil：Kuh-seng oil=2:3:3:1:1.The piece on floor no longer retains a gap up and down after the seamless spliced moisture-proof floor splicing of the present invention, can effectively prevent back moisture/moisture, dust rubbish etc. from being invaded from the gap at side side or the back side, while moistureproof weather resistance is good, it is not easy to deform.
Description
Technical field
The present invention relates to a kind of seamless spliced moisture-proof floor and its preparation technology and utilize the seamless spliced moisture-proof floor system
The mattress and pillow obtained.
Background technology
The common solid wooden floor board surface treatment of in the market is divided into two major classes such as UV paints, PU paints, and the tongue and groove of timber floor mainly divides
Detained and two major classes of lock to be flat, but all timber floors have a common deadly defect, corner part and back are moistureproof
Poor ability, the problems such as easily being caused deformation, such as arch camber, tile, cracking, contracting seam by ambient temperature and humidity change, after-sales service
Or dispute takes place frequently, very big worry is brought to production and sales business and user.
The content of the invention
The present invention is in view of the above-mentioned problems, propose a kind of seamless spliced moisture-proof floor and its preparation technology, to solve now
The defect for having technology timber floor to be easily deformed, reaches that protection against the tide/weather resistance is good, seamless spliced, it is not easy to the purpose of deformation.
The technical scheme that the present invention takes is as follows：
The present invention provides a kind of seamless spliced moisture-proof floor, and its back side is provided with intensive miniature wave channel；The seamless spelling
The surrounding for connecing moisture-proof floor scribbles moistureproof weather-proof vegetable oil, wherein the moistureproof weather-proof vegetable oil includes Chinese catalpa oil, refines flax
Oil, refines tung oil, tea-seed oil and kuh-seng oil, and weight ratio is：Chinese catalpa oil：Refine linseed oil：Refine tung oil：Tea-seed oil：Kuh-seng oil=
2:3:3:1:1。
Further, tongue and groove is all opened in the surrounding side of the seamless spliced moisture-proof floor using rectangular shaped.
It is preferred that, the A/F 1.0-2.0mm of each groove of miniature wave channel.
It is preferred that, the depth 0.25-0.5mm of each groove of miniature wave channel.
The present invention also provides a kind of preparation technology of above-mentioned seamless spliced moisture-proof floor, comprises the following steps：
Step a, solid wood blank is stacked 60-90 days by groined type；
Step b, carries out four sides tongue and groove by the solid wood blank after stacking and scrapes, and surrounding side is all opened using rectangular shaped
Tongue and groove is opened, then transverse miniature wave channel is opened at the back of blank；
Step c, will hold the semi-finished floor of the miniature wave channel of tongue and groove and back successfully, be heated by automatic chain formula baking machine
To 37-45 DEG C；
Step d, 1 weather-proof vegetable oil of protection against the tide is uniformly sprayed by floor surrounding, and quantity for spray is 15-20g/ square meters；Place
Dried 12-18 hours in 25-35 DEG C of temperature, humidity 50-60% environment；
Step e, after the 1st spraying is dried, carries out the 2nd synthetic resin spraying, quantity for spray is 10-15g/ square meters；So
It is placed in 10-35 DEG C of temperature, humidity 50-60% environment and dries 4-8 hours afterwards；
Step f, by semi-finished floor of the surrounding after 2 times spray, is put into automatic chain baking machine, timber floor is carried on the back
Portion is warmed to 37-45 DEG C；
Step g, then in floor back 2 times weather-proof vegetable oil of protection against the tide of the continuous roller coat of flexible plastic roller, coating weight is 15-
20g/ square meters；
Step h, by the semi-finished floor of the good moistureproof weather-proof vegetable oil of back roller coat, lies in and dries on brandreth, be placed in temperature
Spend in 20-35 DEG C, wind speed 0.2-0.3 meter per seconds, humidity 50-60% environment and dry 12-18 hours；
Step i, by above-mentioned semi-finished floor, puts into full-automatic UV production lines, to back 2 epoxidized linseed oils third of roller coat again
Olefin(e) acid ester, drying is toasted through UV light；
Step j, then the acrylic acid modified system UV paints of face progress roller coat on floor, toast after drying through ultraviolet light, obtain
To seamless spliced moisture-proof floor of the invention；
The moistureproof weather-proof vegetable oil includes Chinese catalpa oil, refines linseed oil, refines tung oil, tea-seed oil and kuh-seng oil, weight ratio
For：Chinese catalpa oil：Refine linseed oil：Refine tung oil：Tea-seed oil：Kuh-seng oil=2:3:3:1:1.
Further, in step a, the solid wood blank moisture content after balance is stacked for before 10.5-13.5%, and every blank
In after the difference of three sections of moisture content and upper, middle and lower three layers of moisture content be no more than 3%.
Further, in step b each groove of miniature wave channel A/F 1.0-2.0mm；Depth 0.25-0.5mm.
Further, the synthetic resin in step e is polyurethane.
Further, in step h, brandreth horizontal interval spacing 5-10cm is dried, between the upper and lower every 20-25cm.
It is preferred that, in step i, the viscosity of epoxidized linseed oil acrylate is 100-150Pa.s；Acrylic acid modified system UV
The viscosity of paint is 100-150Pa.s.
Compared with prior art, the beneficial effects of the invention are as follows：
Traditional timber floor bottom and edge do not carry out damp-proof treatment, easily absorb ground moisture after mating formation and expand
Acuter angles wide at the top and narrow at the bottom are set at arch camber, floor splicing, expanded its purpose is to vacating space by floor bottoms.And this
The surrounding side of the seamless spliced timber floor of invention, has broken traditional acuter angles wide at the top and narrow at the bottom, uses wide up and down
The consistent right-angle structure of degree, the piece on floor no longer retains a gap up and down after splicing, can effectively prevent back moisture/tide
Gas, dust rubbish etc. are invaded from the gap at side side or the back side.
In order to which the floor back and side of preventing right-angle structure make moist expansion, this is on the one hand employed in side and back specially
The special formula of profit --- " moistureproof weather-proof vegetable oil " depth of penetration processing, it is ensured that side and back will not water swellings；Two sides
Face is to open to have intensive transverse miniature wave channel at floor back, dredges permeation functions with moisture, therefore need not reserve expansion
Space is gap.
The moistureproof weather-proof vegetable oil of the present invention includes Multiple components, wherein Chinese catalpa oil, refining linseed oil, refining tung oil etc., this
Three vegetable oils are coated on wood surface, are by weather-proof vegetable oil with very strong waterproof, moisture-proof role, and present invention process
It is heated up to carry out roller coat again at 55-70 DEG C, vegetable oil understands the wood internal that infiltrates into of fast deep under high temperature action, protection against the tide is anti-
It is aqueous to become apparent from persistently.And special natural plant insecticide sterilization component --- tea-seed oil and hardship is added in the formula
Ginseng oil.Tea-seed oil has the effect such as desinsection, sterilization, anti-inflammatory；Kuh-seng oil also there is very strong desinsection, antibacterial bacteriostatic, anti-inflammatory etc. to make
With, therefore, through the coated timber floor of the moistureproof weather-proof vegetable oil high temperature of the present invention, not only with moistureproof and waterproof function, but also have
There is the effect such as desinsection, antibacterial and bacteriostatic, anti-mildew, no matter what environment is timber floor is arranged under, all without having to worry about arch camber of making moist, hair
The problems such as mould, infested, stain fungus infringement, really make seamless spliced floor accomplish 360 degree of stereoscopic protective.
Further, the back side of timber floor is laterally provided with miniature wave channel, the width 1.0-2.0mm of wave channel, depth
0.25-0.5mm.The advantage of the transverse groove is：The position energy ventilation of timber floor rear-face contact rough ground, and horizontal wave
Groove destroys and has interrupted the rift grain wood fiber structure of timber, can effectively reduce timber floor back and make moist caused deformation.
Further, during traditional timber floor processing, processed under the conditions of normal temperature (0-25 DEG C), paint infiltration is compared
Shallow, adhesive force is very low.And the present invention is weather-proof vegetable oil (four sides for being just coated with timber floor after 37-45 DEG C of processing of excess temperature
Spraying, back side roller coat) because pore is opened timber at high temperature, wood internal is penetrated into beneficial to vegetable oil depth, can be provided
Good moistureproof and waterproof performance, and adhesive force is strong.Key be the present invention weather-proof vegetable oil in tea-seed oil, kuh-seng oil into
Point, permeate deeper, can more prevent corrosion bacterium, stain fungus mycelia of wood internal etc. to encroach on timber floor.
The present invention first carries out special equilibrium processing by the moisture content to timber floor first, and then opposite side carries out right angle knot
Structure processing, makes it not stay a gap after splicing, and back side unlatching has miniature ripple glaze to cut off length to grain design, floor heat
Pore is opened after processing, is coated with moistureproof weather-proof vegetable oil to the timber bottom and surrounding side of exploitation, is allowed its depth to be absorbed to
Wood internal.Thus the product made, " preset slot " gap, humidity resistance and weatherability pole can not be stayed when installing splicing
By force；Avoid traditional solid sawn floor install that reserved piece operation is constant, shelter evil people and countenance evil practices be not easily cleaned, effect of mating formation unsightly etc. lacks
Point, and key is that stabilization is unlikely to deform after product is installed, and is adapted to the South and the North different zones varying environment and installs and use, is lifted
The use value of solid wooden floor board and use scope and decorative effect.
Brief description of the drawings
Fig. 1 be in the embodiment of the present invention 2 the miniature wave channel of back structural representation.
Embodiment：
With reference to specific embodiment, the present invention is described in detail.
Embodiment 1
Moistureproof weather-proof plant oil formula
By weight ratio
Chinese catalpa oil：Refine linseed oil：Refine tung oil：Tea-seed oil：Kuh-seng oil=2:3:3:1:1
Wherein:Chinese catalpa oil：Relative density (25/25 DEG C) 0.936~0.944, refractive index (25 DEG C) 1.481~1.484, iodine number
169~190.
Refine linseed oil：Relative density 0.92-0.98, iodine number 165-200gl2/100g, free acid content 2.1-2.6%,
Viscosity 8-10pas, refraction index 1.480-1.485.
Refine tung oil：Relative density 0.940-0.943, iodine number 163-200gl2/100g, free acid content 5.5-8%, folding
Optical index 1.510-1.520.
Tea-seed oil：Relative density 0.912-0.917, iodine number 80-90g/100g, free fatty acid content 0.15-0.2%.
Kuh-seng oil：Relative density 0.90-0.912, refraction index 1.45-1.58.
Embodiment 2
The preparation technology of seamless spliced moisture-proof floor, comprises the following steps：
The first step：
By the solid wood blank that moisture content is 9-14%, air humidity is placed on for 55-65%, and wind speed is 0.1-0.2m/ seconds
Environment in stack balance health-preserving 60-90 days by groined type, make the moisture control after its balance in 10.5-13.5%, and often
The difference of three layers of moisture content of three sections of moisture content and upper, middle and lower is no more than 3% after in before piece blank.
The present invention uses the balance health-preserving of 60-90 days so that the participation stress of wood internal thoroughly discharges.
The present invention is handled by 3% moisture content difference, is reduced floor moisture absorption inequality and is deformed.
Second step：
Above-mentioned blank is subjected to four sides tongue and groove and scraped, tongue and groove is all opened in surrounding side using rectangular shaped；Again in base
Material is that the back unlatching transverse miniature wave channel on floor is as shown in Figure 1.The depth 0.2-0.5mm of the miniature each groove of wave channel, it is wide
1.5-3mm is spent, is covered with entirely back.
Such a intensive miniature wave channel is opened up in the present invention so that the position of floor rear-face contact rough ground can ventilate logical
Wind, permeation functions are dredged with moisture, and horizontal wave channel destroys and interrupted the rift grain wood fiber structure of timber, can be effective
Timber floor back is reduced to make moist caused deformation.
3rd step：
The semi-finished floor of the miniature wave of surrounding tongue and groove and back will be held successfully, be warmed to by automatic chain formula baking machine
37-45 DEG C, open to the outside world after making its timber pore/hair on the neck hole heated, beneficial to vegetable oil depth of penetration, is convenient at next step protection against the tide
Reason.
4th step：
37-45 DEG C of floor surrounding is uniformly sprayed to the moistureproof weather-proof vegetable oil in 1 embodiment 1, quantity for spray is 15-
20g/ square meters, viscosity is 20Pa.s.It is then placed within 25-35 DEG C of temperature, humidity 50-60% environment and dries 12-18 hours.
The present invention sprays moistureproof weather-proof vegetable oil at 37-45 DEG C, and due to timber, pore is opened at high temperature, beneficial to plant
Oily depth penetrates into wood internal, can provide good moistureproof and waterproof performance, and adhesive force is strong.More key is the present invention
Weather-proof vegetable oil in tea-seed oil, kuh-seng oil component, permeate it is deeper, get over can prevent corrosion bacterium, the stain fungus of wood internal
Mycelia etc. encroaches on timber floor.
6th step：
After the 1st spraying is dried, the 2nd polyurethane coating is carried out.Quantity for spray be 10-15g/ square meters, plus ketone dilute
Viscosity is 20Pa.s after agent, is then placed within 10-35 DEG C of temperature, humidity 50-60% environment and dries 4-8 hours.
7th step：
By semi-finished floor of the surrounding after 2 times spray, the automatic chain baking machine of heating chain-type 1.5-2 meters long is put into
It is interior, timber floor back is warmed to 37-45 DEG C, open to the outside world after making the timber pore at its floor back heated, then open
The floor back moistureproof weather-proof vegetable oil of flexible plastic roller 2 times embodiments 1 of continuous roller coat, coating weight is 15-20g/ square meters.
Because there is miniature wave channel at the back on floor, therefore should be using the moistureproof weather-proof of the rubber tire roller coat back of soft material
Oil, can the moistureproof weather-proof vegetable oil of even spread with the groove inwall and bottom land that ensure miniature wave channel.
8th step：
By the semi-finished floor of the good moistureproof weather-proof vegetable oil of back roller coat, lie in compartment away from 5-10cm, between the upper and lower every
20-25cm's dries on brandreth, is placed in 20-35 DEG C of temperature, wind speed 0.2-0.3 meter per seconds, humidity 50-60% environment and dries
12-18 hours, after its fully dry (tack-free) afterwards enter next process.
9th step：
By above-mentioned semi-finished floor, full-automatic UV production lines are put into, 2 viscosity of roller coat are 100-150Pa.s again to back
Epoxidized linseed oil acrylate, through UV light toast dry after i.e. back PROCESS FOR TREATMENT finish.
Tenth step：
The floor finished through above-mentioned PROCESS FOR TREATMENT, then the viscosity in the face of 6 bottom of face progress roller coat 3 on floor is 100-150s
Acrylic acid modified system UV paint, through ultraviolet light toast dry after, get product timber floor --- seamless spliced moistureproof weather-proof wood
Floor, just can sell after packing and use.
Wherein, 6 bottom：After floor surface is first using the abrasive band sanding of 80-100 mesh, continuous 2 times acrylic acid modified bodies of roller coat
It is UV priming paint, is dried through ultraviolet light；Again with continuous 2 times acrylic acid modified system UV priming paint of roller coat again after the abrasive band sanding of 120 mesh,
Dried through ultraviolet light；Finally with continuous 2 times acrylic acid modified system UV priming paint of roller coat again after the abrasive band sanding of 180 mesh, through ultraviolet
Light is dried.Each roller coat amount of priming paint is 20-25g/ square meters.
3 faces：After prime treatment is got well, wood floor surface is with after the abrasive band sanding of 200 mesh, and roller coat 1 time is acrylic acid modified
System UV finish paints, are dried through ultraviolet light；Again with 1 time acrylic acid modified system UV finish paint of roller coat again after the abrasive band sanding of 240 mesh, warp
Ultraviolet light is dried；Finally with 1 time acrylic acid modified system UV finish paint of roller coat again after the abrasive band sanding of 400 mesh, dried through ultraviolet light.
Each roller coat amount of finish paint is 15-20g/ square meters.
The preferred embodiments of the present invention are the foregoing is only, the scope of patent protection of the present invention is not thereby limited, it is all
It is the equivalent structure transformation made with description of the invention and accompanying drawing content, is directly or indirectly used in other related technologies
Field, similarly includes within the scope of the present invention.
Claims (10)
1. seamless spliced moisture-proof floor, it is characterised in that the back side of the seamless spliced moisture-proof floor is provided with intensive miniature ripple
Unrestrained groove；The surrounding of the seamless spliced moisture-proof floor scribbles moistureproof weather-proof vegetable oil, wherein the moistureproof weather-proof vegetable oil bag
Chinese catalpa oil is included, linseed oil is refined, tung oil, tea-seed oil and kuh-seng oil is refined, weight ratio is：Chinese catalpa oil：Refine linseed oil：Refine tung oil：
Tea-seed oil：Kuh-seng oil=2:3:3:1:1.
2. seamless spliced moisture-proof floor as claimed in claim 1, it is characterised in that the surrounding of the seamless spliced moisture-proof floor
Tongue and groove is all opened using rectangular shaped in side.
3. seamless spliced moisture-proof floor as claimed in claim 1, it is characterised in that the opening of each groove of miniature wave channel is wide
Spend 1.0-2.0mm.
4. seamless spliced moisture-proof floor as claimed in claim 1, it is characterised in that the depth of each groove of miniature wave channel
0.25-0.5mm。
5. a kind of preparation technology of seamless spliced moisture-proof floor as claimed in claim 1, it is characterised in that the preparation technology
Comprise the following steps：
Step a, solid wood blank is stacked 60-90 days by groined type；
Step b, carries out four sides tongue and groove by the solid wood blank after stacking and scrapes, and surrounding side is all opened using rectangular shaped and looked forward to
Mouthful, then open transverse miniature wave channel at the back of blank；
Step c, will hold the semi-finished floor of the miniature wave channel of tongue and groove and back successfully, is warmed to by automatic chain formula baking machine
37-45℃；
Step d, 1 weather-proof vegetable oil of protection against the tide is uniformly sprayed by floor surrounding, and quantity for spray is 15-20g/ square meters；It is placed on temperature
Dried 12-18 hours in 25-35 DEG C of degree, humidity 50-60% environment；
Step e, after the 1st spraying is dried, carries out the 2nd synthetic resin spraying, quantity for spray is 10-15g/ square meters；Then put
Put and dried 4-8 hours in 10-35 DEG C of temperature, humidity 50-60% environment；
Step f, by semi-finished floor of the surrounding after 2 times spray, is put into automatic chain baking machine, timber floor back is added
Temperature arrives 37-45 DEG C；
Step g, then in floor back 2 times weather-proof vegetable oil of protection against the tide of the continuous roller coat of flexible plastic roller, coating weight is 15-20g/
Square meter；
Step h, by the semi-finished floor of the good moistureproof weather-proof vegetable oil of back roller coat, lies in and dries on brandreth, be placed in temperature 20-
Dried 12-18 hours in 35 DEG C, wind speed 0.2-0.3 meter per seconds, humidity 50-60% environment；
Step i, by above-mentioned semi-finished floor, puts into full-automatic UV production lines, to back 2 epoxidized linseed oil acrylic acid of roller coat again
Ester, drying is toasted through UV light；
Step j, then the acrylic acid modified system UV paints of face progress roller coat on floor, toast after drying through ultraviolet light, obtain this
Invent seamless spliced moisture-proof floor；
The moistureproof weather-proof vegetable oil includes Chinese catalpa oil, refines linseed oil, refines tung oil, tea-seed oil and kuh-seng oil, and weight ratio is：Chinese catalpa
Oil：Refine linseed oil：Refine tung oil：Tea-seed oil：Kuh-seng oil=2:3:3:1:1.
6. the preparation technology of seamless spliced moisture-proof floor as claimed in claim 5, it is characterised in that in step a, stacks balance
Solid wood blank moisture content afterwards be 10.5-13.5%, and every blank before in after three sections of moisture content and three layers of upper, middle and lower it is aqueous
The difference of rate is no more than 3%.
7. the preparation technology of seamless spliced moisture-proof floor as claimed in claim 5, it is characterised in that miniature wave in step b
The A/F 1.0-2.0mm of each groove of groove；Depth 0.25-0.5mm.
8. the preparation technology of seamless spliced moisture-proof floor as claimed in claim 5, it is characterised in that the synthesis tree in step e
Fat is polyurethane.
9. the preparation technology of seamless spliced moisture-proof floor as claimed in claim 5, it is characterised in that in step h, dry brandreth
Horizontal interval spacing 5-10cm, between the upper and lower every 20-25cm.
10. the preparation technology of seamless spliced moisture-proof floor as claimed in claim 5, it is characterised in that in step i, epoxy is sub-
The viscosity of sesame oil acrylate is 100-150Pa.s；The viscosity of acrylic acid modified system UV paints is 100-150Pa.s.