CN107034680A - A kind of finishing technique of viscose glue interwoven fabric - Google Patents
A kind of finishing technique of viscose glue interwoven fabric Download PDFInfo
- Publication number
- CN107034680A CN107034680A CN201710440468.6A CN201710440468A CN107034680A CN 107034680 A CN107034680 A CN 107034680A CN 201710440468 A CN201710440468 A CN 201710440468A CN 107034680 A CN107034680 A CN 107034680A
- Authority
- CN
- China
- Prior art keywords
- fabric
- viscose glue
- finishing technique
- wet cloth
- type frame
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A kind of finishing technique of viscose glue interwoven fabric, belongs to viscose rayon processing technology field.Characterized in that, processing step is：1）The fabric fabric enters dye jigger in open width mode, is run in the water of 13 DEG C ~ 18 DEG C water temperatures to smooth, without holding side, folding line；2）In wet cloth last volume to A type frame after dyeing, and wet cloth yardage roll is kept with 18r/min ~ 22r/min rotating speed uniform rotation；3）After wet cloth debatching in A type frame, by being arranged on the water suction of the suction hose before groove with control fabric containing damp rate 53% ~ 60%；4）Fabric after water suction is 65% ~ 70% by padding machine chain of command material liquid carrying rate, soft finish liquid is configured in groove, then carrying out soft treatment and baking operation.The present invention realizes product quality and is obviously improved, and saves the consumption of steam, electric power, and auxiliary dosage is substantially reduced.
Description
Technical field
A kind of finishing technique of viscose glue interwoven fabric, belongs to viscose rayon processing technology field.
Background technology
Because the gloss appearance of viscose rayon is beautiful, soft, smooth, the fabric being made has superpower antistatic property,
The sensation being attached on body will not be produced, thus it is very smooth, it is particularly suitable for motion dress.Its moisture percentage best suits human body skin
The physiological requirement of skin, with good gas permeability and humidity conditioning function, is unanimously referred to as " fabric that can be breathed " by domestic and international media.
The fabric of it and other fiber blends or intertexture have the advantages that it is soft, smooth it is nice and cool, ventilative, antistatic, dye it is gorgeous,
With incomparable styles of fabric such as polyester-cotton blend, numb cotton, pure cottons, especially as advantage of the silk-like fabric in style and price
More aobvious protrusion, therefore viscose glue interweaving type fabric is in spin on and obtained increasing application.It is structural due to viscose rayon
Matter, wet modulus is larger, and violent expansion occurs in fiber after moisture absorption, and diameter and elongation can increase by 50% or so, then occur after drying
Rapid desufflation, the fiber wet modulus such as the terylene being interleaved with, cotton, silk is then much smaller, therefore such interwoven fabric is general with viscous
Glue fiber is used as parallel.Due to the larger difference of two kinds of fiber wet modulus, during dyeing and printing process arrangement, water moisture absorption is met
Can occur many places fine wrinkle in cloth cover because hygral expansion is inconsistent afterwards, bring greatly difficult to dyeing arrangement.In dyeing by jigger, after
Arrange after open width drying, then obvious fine wrinkle still occurs when upper softening agent or other finishing agents, cause fabric drop etc. can not
Use.There is following technical problem during printing and dyeing, arrangement in such fabric：
1st, such fabric grey cloth can not shape or tentering before dye jigger is entered, and the fabric after tentering meets water meeting on dye jigger
There are a large amount of folding lines, will be unable to recover after rolled, ply rolling.
2nd, after dye jigger last volume, fabric can cause yardage roll ectonexine moisture content to differ greatly in A type frame, adjust padding machine pressure
Power and speed speed all can not be controlled accurately.Fabric feel and the problem of inconsistent style around often occurring.
3rd, after drying from forming machine softening agent technique, wrinkle occurs after padding softening agent through groove in fabric before padding machine
Trace, fine wrinkle will be unable to recover after being padded through padding machine, even if increase expander, roller can not strut wrinkle print, be formed seriously
Grade product.
4th, the goods in A type frame is first dried through padding machine squezzing, then the secondary two one bath two-step methods through padding machine padding finishing agent are arranged
Technique, product quality is difficult to ensure, and causes the repeat consumption of steam, electric power.
The content of the invention
The technical problem to be solved in the present invention is：The deficiencies in the prior art are overcome to prevent viscose glue from interweaving there is provided one kind
Fabric production process produces the finishing technique of the viscose glue interwoven fabric of fine wrinkle.
The technical solution adopted for the present invention to solve the technical problems is：The finishing technique of the viscose glue interwoven fabric, it is special
Levy and be, processing step is：
1）The fabric fabric enters dye jigger in open width mode, is run in the water of 13 DEG C ~ 18 DEG C water temperatures to smooth, without holding side,
Folding line；
2）In wet cloth last volume to A type frame after dyeing, and keep wet cloth yardage roll with 18r/min ~ 22r/min rotating speed at the uniform velocity
Rotate；
3）After wet cloth debatching in A type frame, by being arranged on the water suction of the suction hose before groove with control fabric containing damp rate 53%
~60%；
4）Fabric after water suction is 65% ~ 70% by padding machine chain of command material liquid carrying rate, configures soft finish liquid in groove, then
Carry out soft treatment and baking operation.
Machine on the dry cloth of grey cloth of the present invention, it is smooth without subsequent processing of being allowed for access after folding line to silk fabric face.Wet cloth in A type frame
After debatching, the rate containing tide of fabric is controlled by being arranged on the water suction of the suction hose before groove；Using water suction -- upper softening agent+drying
The method of " two steps of bath " is dried and soft treatment.Traditional material treatment is first in multiple-roll dryer using the first step
Upper first to be dried through padding machine squezzing, the technique of padding finishing liquid on the collator for have groove realizes the soft whole of fabric to second step again
Reason, and present invention process before multiple-roll dryer groove then by installing suction hose additional using the suction of pulsating pump in advance by face
Expect the moisture removal of surface and fibrous outer, enter back into groove padding finishing liquid, one time is that can be achieved originally to roll on dryer
The effect of water drying-one bath two-step of padding finishing agent two.Wet cloth in the A type frame first step after debatching passes through what is installed additional before roll
Suction hose removes 30% or so moisture, and the wet cloth of second step moisture percentage 50% or so is directly entered groove and pads softening agent mixing
Liquid, by going out cloth after being dried to the rate 10% containing tide.
It is preferred that, step 3）Described in be 57% ~ 58% containing damp rate.The realization of the present invention needs to roll in multiple-roll dryer
Install suction hose one before groove additional, connect pulsating pump, double water sucking mouth is fully contacted with cloth cover, and soaking effect is reached by cornerite
Most preferably, after the wet cloth debatching in A type frame, by fabric guide roll-suction hose-expander-groove-padding machine-fabric guide roll-tension force
Frame-expander-multiple-roll dry-controls frame-goes out cloth.
It is preferred that, step 4）Described in soft finish liquid constituent mass concentration include polyether polyester chain block silicone oil
13 g/L ~ 17g/L, 4 g/L of epoxidized polyether silicone oil ~ 6g/L, 600 15 g/L of crosslinking agent ~ 2.5g/L, the g/L of glacial acetic acid 0.35
~ 0.56g/L.The adjustment that the present invention passes through production technology so that this " dressing " process auxiliaries consumption 15g/l or so is i.e. reachable
To traditional handicraft auxiliary dosage 30g/l effect.After being arranged through this technique, fabric is rolled up to A types through 160 DEG C of spray vapour tenterings of stenter
On frame, examined through radial direction checking machine：Silk fabric face is smooth, and gloss is soft, no folding line, and wrinkle print, quality reaches national standard high-class product.
It is preferred that, step 4）Described in soft finish liquid constituent mass concentration include polyether polyester chain block silicone oil
14 g/L ~ 15g/L, epoxidized polyether silicone oil 5g/L ~ 5.5g/L, 600 1.75 g/L of crosslinking agent ~ 2.15g/L, glacial acetic acid
0.42g/L ~ 0.51g/L。
It is preferred that, step 4）Described in baking operation using multiple-roll collator dry, cloth cover contains during cropping after drying
Damp rate is 10% ~ 15%.Overly moist then air-dries print to be formed, and overdrying can then cause to produce retraction, fabric breadth after later process tentering
Not enough.
It is preferred that, step 3）Described in water temperature be 16 DEG C ~ 17 DEG C.
It is preferred that, step 3）Described in A type frame on wet cloth yardage roll rotating speed be 20r/min.Dye gigging engine dyeing in the present invention
Color is finished, on fabric last volume to A type frame, and multiple-roll dryer is directly entered if timely drying；It can not such as dry in time, then
The motor in A type frame is started, yardage roll uniform speed slow is rotated, gravity balance is kept, it is therefore prevented that drying debatching makes center of gravity unbalance, makes
Into cloth surface damage.
It is preferred that, step 4）Described in fabric liquid carrying rate be 67% ~ 68%.
Due to also needing soft or other functional treatments after the drying of such fabric, therefore the present invention is using water suction -- dressing
The method of+drying " two steps of bath ", makes fabric complete the processing of finishing agent under wet condition, is risen after solving viscose rayon water suction
The problem of wrinkle.
It is preferred that, softening agent used is the softening agent 3165 that Suzhou Liansheng Chemicals Co., Ltd. produces（Amino silicone is soft
Agent）With smooth agent 6820（Block ternary polymerization silicone oil softener）.Crosslinking agent is the friendship that Zibo Ha Gen Textile Co., Ltd. produces
Join agent 600.Glacial acetic acid is the nertralizer NAC that Jiangsu Suo Pu chemical inc is produced.
Compared with prior art, a kind of finishing technique of viscose glue interwoven fabric of the invention is had an advantageous effect in that：
1st, silk fabric face is smooth before the present invention ensures fabric from upper dye jigger to dyeing, no folding line；
2nd, because fabric can not be dried in time in A type frame, due to time or length or evening, yardage roll ectonexine contains damp rate and there is larger difference
Different, to ensure that finishing effect is consistent before and after yardage roll, the first step of the present invention first passes through suction hose the containing cloth cover installed additional before groove
Water rate is down to 50% or so by 80%, accomplishes that into before padding machine fabric-surface water content is consistent, and second step is by padding machine by the liquid carrying rate of fabric
Adjust to 65%-70%, groove finishing agent is continued into cylinder at any time, accomplishes that the arrangement agent concentration in groove is consistent；
3rd, because fabric enters higher containing damp rate before groove under the technique of this dressing, therefore compared with the technique of dry finishing pair
The consumption that the consumption of finishing agent has soft finishing agent in larger difference, the present invention can reduce 30% or so；
4th, the present invention realizes drying, and upper finishing agent two-step process is united two into one, and product quality is obviously improved, and saves one
The consumption of the steam, electric power of step process, auxiliary dosage also saves half, great popularization.Examined through radial direction checking machine：Silk fabric face
Smooth, gloss is soft, no folding line, and wrinkle print, quality reaches national standard high-class product.
Embodiment
With reference to specific embodiment, the present invention is further illustrated.
Embodiment 1
This technical face gauge lattice DTY75D × R120D 173 × 120
1）Machine on dry cloth, add water 800L, 16 DEG C of 4 roads of operating, discharge opeing；
2）Refining, dyeing course are omited；
3）In wet cloth last volume to A type frame after dyeing, and wet cloth yardage roll is kept with 20 r/min rotating speed uniform rotation；
4）Multiple-roll dryer absorbs water（The rate containing tide of fabric is controlled 58%）-- pad soft finish liquid（Chain of command material liquid carrying rate
For 67%）+ drying（130 DEG C of drying temperature, baking operation is dried using multiple-roll collator, moisture content of cloth surface during cropping after drying
13%；The composition of soft finish liquid includes：The g/L of polyether polyester chain block silicone oil 15, epoxidized polyether silicone oil 5g/L, crosslinking agent
600 2.0 g/L, glacial acetic acid 0.45g/L；
5）160 DEG C of tenter-frames, Pen Qi Give wet 5% go out yardage roll to A type frame, to be tested.
Embodiment 2
This technical face gauge lattice DTY75D × R120D 173 × 120
1）The humidified Qi Give wet 60% of fabric after tentering, debatching enters member hired car and carried out fully " wet pretreatment "；
2）Machine on wet cloth, add water 500L, 16 DEG C of 2 roads of operating, discharge opeing；
3）Refining, dyeing course are omited；
4）In wet cloth last volume to A type frame after dyeing, and wet cloth yardage roll is kept with 19 r/min rotating speed uniform rotation:；
5）Multiple-roll dryer absorbs water（The rate containing tide of fabric is controlled 58%）-- pad soft finish liquid（Chain of command material liquid carrying rate
For 67%）+ drying（130 DEG C of drying temperature, baking operation is dried using multiple-roll collator, moisture content of cloth surface during cropping after drying
14%；
The composition of soft finish liquid includes：Polyether polyester chain block silicone oil 15g/L, epoxidized polyether silicone oil 5.5g/L, crosslinking agent
600 2.15g/L, glacial acetic acid 0.51g/L；
6）160 DEG C of tenter-frames, Pen Qi Give wet 5% go out yardage roll to A type frame, to be tested.
Embodiment 3
This technical face gauge lattice DTY75D × R120D 173 × 120
1）The humidified Qi Give wet 60% of fabric after tentering, debatching enters member hired car and carried out fully " wet pretreatment "；
2）Machine on wet cloth, add water 500L, 17 DEG C of 2 roads of operating, discharge opeing；
3）Refining, dyeing course are omited；
4）In wet cloth last volume to A type frame after dyeing, and wet cloth yardage roll is kept with 21 r/min rotating speed uniform rotation:；
5）Multiple-roll dryer absorbs water（The rate containing tide of fabric is controlled 57%）-- pad soft finish liquid（Chain of command material liquid carrying rate
For 68%）+ drying（130 DEG C of drying temperature, baking operation is dried using multiple-roll collator, moisture content of cloth surface during cropping after drying
12%；
The composition of soft finish liquid includes：The g/L of polyether polyester chain block silicone oil 14, epoxidized polyether silicone oil 5g/L, crosslinking agent
600 1.75 g/L, glacial acetic acid 0.42g/L；
6）160 DEG C of tenter-frames, Pen Qi Give wet 5% go out yardage roll to A type frame, to be tested.
Embodiment 4
This technical face gauge lattice DTY75D × R120D 173 × 120
1）The humidified Qi Give wet 60% of fabric after tentering, debatching enters member hired car and carried out fully " wet pretreatment "；
2）Machine on wet cloth, add water 500L, 13 DEG C of 2 roads of operating, discharge opeing；
3）Refining, dyeing course are omited；
4）In wet cloth last volume to A type frame after dyeing, and wet cloth yardage roll is kept with 18 r/min rotating speed uniform rotation:；
5）Multiple-roll dryer absorbs water（The rate containing tide of fabric is controlled 53%）-- pad soft finish liquid（Chain of command material liquid carrying rate
For 65%）+ drying（130 DEG C of drying temperature, baking operation is dried using multiple-roll collator, moisture content of cloth surface during cropping after drying
15%；
The composition of soft finish liquid includes：The g/L of polyether polyester chain block silicone oil 13, epoxidized polyether silicone oil 6g/L, crosslinking agent
600 15 g/L, glacial acetic acid 0.56g/L；
6）160 DEG C of tenter-frames, Pen Qi Give wet 5% go out yardage roll to A type frame, to be tested.
Embodiment 5
This technical face gauge lattice DTY75D × R120D 173 × 120
1）The humidified Qi Give wet 60% of fabric after tentering, debatching enters member hired car and carried out fully " wet pretreatment "；
2）Machine on wet cloth, add water 500L, 18 DEG C of 2 roads of operating, discharge opeing；
3）Refining, dyeing course are omited；
4）In wet cloth last volume to A type frame after dyeing, and wet cloth yardage roll is kept with 18 r/min rotating speed uniform rotation:；
5）Multiple-roll dryer absorbs water（The rate containing tide of fabric is controlled 60%）-- pad soft finish liquid（Chain of command material liquid carrying rate
For 70%）+ drying（130 DEG C of drying temperature, baking operation is dried using multiple-roll collator, moisture content of cloth surface during cropping after drying
10%；
The composition of soft finish liquid includes：Polyether polyester chain block silicone oil 17g/L, the g/L of epoxidized polyether silicone oil 4, crosslinking agent
600 2.5g/L, the g/L of glacial acetic acid 0.35；
6）160 DEG C of tenter-frames, Pen Qi Give wet 5% go out yardage roll to A type frame, to be tested.
Comparative example 1
This technical face gauge lattice DTY75D × R120D 173 × 120
1）Machine on dry cloth, add water 800L, 20 DEG C of 4 roads of operating, discharge opeing；
2）Refining, dyeing course are omited；
3）In wet cloth last volume to A type frame after dyeing, and wet cloth yardage roll is kept with 20 r/min rotating speed uniform rotation:；
4）The squezzing of multiple-roll dryer is dried（130℃）, 45 ms/min of speed；
5）Multiple-roll collator pads softening agent+drying（130℃）, 45 ms/min of speed；
The auxiliary agent technique of soft finish：
The 30g/l of softening agent 3165, the 10g/l of smooth agent 6820
The 2.5g/l of crosslinking agent 600, acetic acid 0.5g/l
6）160 DEG C of tenter-frames, Pen Qi Give wet 5% go out yardage roll to A type frame, to be tested.
2 technical face gauge lattice DTY75D × R120D 173 × 120 of comparative example
1）Machine on the dry cloth of fabric after tentering, add water 800L, 20 DEG C of 4 roads of operating, discharge opeing；
2）Refining, dyeing course are omited；
3）In wet cloth last volume to A type frame after dyeing, and wet cloth yardage roll is kept with 20 r/min rotating speed uniform rotation:；
4）The squezzing of multiple-roll dryer is dried（130℃）, 45 ms/min of speed；
5）Multiple-roll collator pads softening agent+drying（130℃）, 45 ms/min of speed；
The auxiliary agent technique of soft finish：
The 15g/l of softening agent 3165, the 5g/l of smooth agent 6820
The 2g/l of crosslinking agent 600, acetic acid 0.5g/l
6）160 DEG C of tenter-frames, Pen Qi Give wet 5% go out yardage roll to A type frame, to be tested.
Examine；Because the art inventions mainly solve time problem of appearance of class fabric, therefore the inherent quality index of product
It is not described, according to FZ/T 62007-2003《Sheet》Standard appearance requirement, the fabric silk fabric face of embodiment is smooth, and gloss is soft
With soft smooth, no folding line, wrinkle, the defect such as colourless willow；There is irregular folding line in comparative example 1, the silk fabric face of comparative example 2,
Goods of inferior quality drops in comparative example 1, and the especially folding line of comparative example 2, color willow is serious, and feel is also slightly poor, serious drop etc., it is impossible to use.
The above described is only a preferred embodiment of the present invention, being not the limitation for making other forms to the present invention, appoint
What those skilled in the art changed or be modified as possibly also with the technology contents of the disclosure above equivalent variations etc.
Imitate embodiment.But it is every without departing from technical solution of the present invention content, the technical spirit according to the present invention is to above example institute
Any simple modification, equivalent variations and the remodeling made, still fall within the protection domain of technical solution of the present invention.
Claims (8)
1. a kind of finishing technique of viscose glue interwoven fabric, it is characterised in that processing step is：
1）The fabric fabric enters dye jigger in open width mode, is run in the water of 13 DEG C ~ 18 DEG C water temperatures to smooth, without holding side,
Folding line；
2）In wet cloth last volume to A type frame after dyeing, and keep wet cloth yardage roll with 18r/min ~ 22r/min rotating speed at the uniform velocity
Rotate；
3）After wet cloth debatching in A type frame, by being arranged on the water suction of the suction hose before groove with control fabric containing damp rate 53%
~60%；
4）Fabric after water suction is 65% ~ 70% by padding machine chain of command material liquid carrying rate, configures soft finish liquid in groove, then
Carry out soft treatment and baking operation.
2. a kind of finishing technique of viscose glue interwoven fabric according to claim 1, it is characterised in that：Step 3）Described in
It is 57% ~ 58% containing damp rate.
3. a kind of finishing technique of viscose glue interwoven fabric according to claim 1, it is characterised in that：Step 4）Described in
The constituent mass concentration of soft finish liquid includes 13 g/L of polyether polyester chain block silicone oil ~ 17g/L, epoxidized polyether silicone oil 4
G/L ~ 6g/L, 600 15 g/L of crosslinking agent ~ 2.5g/L, 0.35 g/L of glacial acetic acid ~ 0.56g/L.
4. a kind of finishing technique of viscose glue interwoven fabric according to claim 1, it is characterised in that：Step 4）Described in
The constituent mass concentration of soft finish liquid includes 14 g/L of polyether polyester chain block silicone oil ~ 15g/L, epoxidized polyether silicone oil 5g/
L ~ 5.5g/L, 600 1.75 g/L of crosslinking agent ~ 2.15g/L, glacial acetic acid 0.42g/L ~ 0.51g/L.
5. a kind of finishing technique of viscose glue interwoven fabric according to claim 1, it is characterised in that：Step 4）Described in
Baking operation using multiple-roll collator dry, after drying during cropping moisture content of cloth surface 10% ~ 15%.
6. a kind of finishing technique of viscose glue interwoven fabric according to claim 1, it is characterised in that：Step 1）Described in
Water temperature is 16 DEG C ~ 17 DEG C.
7. a kind of finishing technique of viscose glue interwoven fabric according to claim 1, it is characterised in that：Step 3）Described in
The rotating speed of wet cloth yardage roll is 20r/min in A type frame.
8. a kind of finishing technique of viscose glue interwoven fabric according to claim 1, it is characterised in that：Step 4）Described in
Fabric liquid carrying rate is 67% ~ 68%.