CN107031149A - A kind of super flexible fever tablet based on graphene - Google Patents
A kind of super flexible fever tablet based on graphene Download PDFInfo
- Publication number
- CN107031149A CN107031149A CN201710292425.8A CN201710292425A CN107031149A CN 107031149 A CN107031149 A CN 107031149A CN 201710292425 A CN201710292425 A CN 201710292425A CN 107031149 A CN107031149 A CN 107031149A
- Authority
- CN
- China
- Prior art keywords
- pur
- graphene
- layer
- fever tablet
- super flexible
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of super flexible fever tablet based on graphene, including textile layer, substrate layer PUR, graphene film layer, electrode and encapsulated layer PUR, substrate layer PUR is above textile layer, graphene film layer is above substrate layer PUR, two electrodes are respectively arranged on above graphene film layer and are located at two ends respectively, and encapsulated layer PUR is located above two electrodes and covers two electrodes and graphene film layer comprehensively.The present invention regard this elastomer of PUR as the attachment substrate of graphene film and the encapsulation on whole fever tablet surface, and substrate layer PUR is attached to textile surface, reduce significantly planar stretch, make fever tablet that there is very excellent flex capability, suitable for the wearable product such as clothes, and washing machine cleaning can be placed directly in, significantly improve the ease of use of user.
Description
Technical field
The present invention relates to a kind of flexible fever tablet, more particularly to a kind of super flexible fever tablet based on graphene.
Background technology
Wearable electronic product industry is in booming period, and fever tablet has also gradually been applied to the products such as clothes
On, it is possible to achieve low-voltage long-time heating, some body illnesses of auxiliary treatment or for warming.
Existing fever tablet is heated usually using conductive metal material, is also had using novel conductive material such as graphene, nanometer
Silver wire etc. is used as exothermic material, and these materials are generally required for being attached to harder substrate such as PET (poly terephthalic acid second two
Alcohol ester) on sheet material, in order to avoid forming bending in use, cause conductive material damaged, the reliability of product is influenceed, so very
Difficulty realizes excellent flex capability.
And for wearable application product such as clothes, the flexibility of fever tablet is important, and clothes are when changing clothes,
Traditional fever tablet can only use specific cleaning way, or need to clean again after dismantling, to user using making troubles.
The content of the invention
The purpose of the present invention is that that a kind of flex capability is provided to solve the above problems is excellent and can be directly clear
The super flexible fever tablet based on graphene washed.
The present invention is achieved through the following technical solutions above-mentioned purpose：
A kind of super flexible fever tablet based on graphene, including textile layer, substrate layer PUR, graphene film layer,
Electrode and encapsulated layer PUR, the substrate layer PUR is above the textile layer, and the graphene film layer is set
Above the substrate layer PUR, two electrodes are respectively arranged on above the graphene film layer and are located at respectively
Two ends, the encapsulated layer PUR is located above two electrodes and covers two electrodes and the graphene comprehensively
Film layer.
Specifically, the textile layer is terylene, polyamide fibre, pure cotton, viscose rayon, blending, spandex, fiber crops, Modal fibre
It is one or more compound in dimension, composite filament, soybean fiber；Further, the textile layer is preferably woven fabric fabric,
Its institutional framework is one or more compound in plain, twill, satin weave, jacquard weave, rib weave.
Specifically, the substrate layer PUR and encapsulated layer PUR be ethene and its copolymer analog, polyurethanes,
It is one or more compound in polyamide-based, polyesters, amorphous state alpha-olefin copolymer species, TPO, phenylethylene；Institute
The softening point temperature for stating encapsulated layer PUR is higher than the softening point temperature of the substrate layer PUR.
Preferably, the thickness of the substrate layer PUR and the encapsulated layer PUR is 1 μm of -2 ㎜；Further, institute
The thickness for stating substrate layer PUR is more preferably 30 μm -200 μm, and the thickness of the encapsulated layer PUR is more preferably 10 μm -500
μm。
Preferably, the electrode is metal electrode or carbon electrode, the thickness of the electrode is 0.1 μm of -1mm；Further,
The electrode is more preferably silver electrode, and the thickness of the electrode is more preferably 1 μm -50 μm.
The beneficial effects of the present invention are：
The present invention regard this elastomer of PUR as the attachment substrate of graphene film and the envelope on whole fever tablet surface
Dress, and substrate layer PUR is attached to textile surface, significantly planar stretch is reduced, there is fever tablet very excellent
Different flex capability, it is adaptable to the wearable product such as clothes, and washing machine cleaning can be placed directly in, significantly improve user
Ease of use；Super flexible fever tablet of the present invention based on graphene can be made using ripe equipment and technique,
It is easy to large-scale production and application.
Brief description of the drawings
Fig. 1 is the cross section structure diagram of the super flexible fever tablet of the present invention based on graphene.
Embodiment
The invention will be further described below in conjunction with the accompanying drawings：
Heated as shown in figure 1, the super flexible fever tablet of the present invention based on graphene includes textile layer 5, substrate layer
Glue 4, graphene film layer 3, electrode 1 and encapsulated layer PUR 2, substrate layer PUR 4 is above textile layer 5, graphite
Alkene film layer 3 is above substrate layer PUR 4, and two electrodes 1 are respectively arranged on above graphene film layer 3 and difference position
In two ends, encapsulated layer PUR 2 is located above two electrodes 1 and covers two electrodes 1 and graphene film layer 3 comprehensively；Tool
For body, textile layer 5 is terylene, polyamide fibre, pure cotton, viscose rayon, blending, spandex, fiber crops, Modal fibre, composite filament, soybean
One or more compound in fiber, preferably woven fabric fabric, its institutional framework is plain, twill, satin weave, carried
It is flower, one or more compound in rib weave；Substrate layer PUR 4 and encapsulated layer PUR 2 are ethene and its copolymerization
One kind in species, polyurethanes, polyamide-based, polyesters, amorphous state alpha-olefin copolymer species, TPO, phenylethylene
Or it is a variety of compound；The softening point temperature of encapsulated layer PUR 2 is higher than the softening point temperature of substrate layer PUR 4；Substrate layer heat
The thickness of melten gel 4 and encapsulated layer PUR 2 is 1 μm of -2 ㎜；The thickness of substrate layer PUR 4 is more preferably 30 μm -200 μm, envelope
The thickness of dress layer PUR 2 is more preferably 10 μm -500 μm；Electrode 1 is metal electrode or carbon electrode, preferably silver electrode, electrode
Thickness be 0.1 μm of -1mm, preferably 1 μm -50 μm.
In order to illustrate the manufacturability of the super flexible fever tablet of the present invention based on graphene, its system is exemplified below
Process is made, but following methods are conventional methods, are not the protection objects of the present invention.
With reference to Fig. 1, first pass through the mode of hot pressing, substrate layer PUR 4 is brought into close contact with textile layer 5 together with, so
Afterwards substrate layer PUR 4 surface transfer graphene film layer 3, specifically, can using hot visbreaking glue as transfer medium,
Graphene film layer 3 is shifted to the surface of substrate layer PUR 4 by corroding growth substrates method, it is thin in graphene after the completion of transfer
The upper surface printing photocuring ag paste electrode of film layer 3, specifically, print thickness is 10 microns, and by ultraviolet light irradiation, is made
Silver paste solidifies, and silver electrode 1 is formed after solidification；Then the side of hot pressing is passed through above electrode 1 and graphene film layer 3
Formula, laminating encapsulated layer PUR 2, hot pressing temperature now is higher than the softening temperature of encapsulated layer PUR 2, while being less than substrate layer
The softening temperature of PUR 4, the super flexible fever tablet of the present invention based on graphene is obtained after laminating.
Above-described embodiment is presently preferred embodiments of the present invention, is not the limitation to technical solution of the present invention, as long as
The technical scheme that can be realized without creative work on the basis of above-described embodiment, is regarded as falling into patent of the present invention
Rights protection scope in.
Claims (8)
1. a kind of super flexible fever tablet based on graphene, it is characterised in that：Including textile layer, substrate layer PUR, graphite
Alkene film layer, electrode and encapsulated layer PUR, the substrate layer PUR is above the textile layer, the graphene
Film layer is above the substrate layer PUR, and two electrodes are respectively arranged on above the graphene film layer simultaneously
It is located at two ends respectively, the encapsulated layer PUR is located above two electrodes and covers two electrodes and institute comprehensively
State graphene film layer.
2. the super flexible fever tablet according to claim 1 based on graphene, it is characterised in that：The textile layer is to wash
It is one or more in synthetic fibre, polyamide fibre, pure cotton, viscose rayon, blending, spandex, fiber crops, Modal fibre, composite filament, soybean fiber
It is compound.
3. the super flexible fever tablet according to claim 2 based on graphene, it is characterised in that：The textile layer is machine
Woven fabric fabric, its institutional framework is one or more compound in plain, twill, satin weave, jacquard weave, rib weave.
4. the super flexible fever tablet according to claim 1 based on graphene, it is characterised in that：The substrate layer PUR
It is ethene and its copolymer analog, polyurethanes, polyamide-based, polyesters, amorphous state alpha-olefin copolymer with encapsulated layer PUR
It is one or more compound in species, TPO, phenylethylene；The softening point temperature of the encapsulated layer PUR is higher than institute
State the softening point temperature of substrate layer PUR.
5. the super flexible fever tablet according to claim 4 based on graphene, it is characterised in that：The substrate layer PUR
Thickness with the encapsulated layer PUR is 1 μm of -2 ㎜.
6. the super flexible fever tablet according to claim 5 based on graphene, it is characterised in that：The substrate layer PUR
Thickness be 30 μm -200 μm, the thickness of the encapsulated layer PUR is 10 μm -500 μm.
7. the super flexible fever tablet according to claim 1 based on graphene, it is characterised in that：The electrode is metal electricity
Pole or carbon electrode, the thickness of the electrode is 0.1 μm of -1mm.
8. the super flexible fever tablet according to claim 7 based on graphene, it is characterised in that：The electrode is silver electricity
Pole, the thickness of the electrode is 1 μm -50 μm.