CN107021709A - Permeable pavement brick that a kind of pitch is recycled and preparation method thereof - Google Patents
Permeable pavement brick that a kind of pitch is recycled and preparation method thereof Download PDFInfo
- Publication number
- CN107021709A CN107021709A CN201710410557.6A CN201710410557A CN107021709A CN 107021709 A CN107021709 A CN 107021709A CN 201710410557 A CN201710410557 A CN 201710410557A CN 107021709 A CN107021709 A CN 107021709A
- Authority
- CN
- China
- Prior art keywords
- parts
- raw material
- basic unit
- discarded
- cement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention provides permeable pavement brick that a kind of pitch is recycled and preparation method thereof, is related to pavior brick production technical field, and the pavior brick includes surface layer and basic unit, and surface layer includes the raw material of following parts by weight：Discarded 13 parts of 30 40 parts of bituminous concrete, 20 28 parts of cement, 25 33 parts of sand, 5 10 parts of rubble, 46 parts of emulsified asphalt, 36 parts of miberal powder, 6 10 parts of glass fibre, 1.2 2.4 parts of venamul, 3 10 parts of clay, 0.8 1.6 parts of rubber powder, 5 10 parts of air-entrainment, 0.4 0.6 parts of water reducer, 0.3 0.5 parts of pigment powder and water；Basic unit includes the raw material of following parts by weight：Discarded 23 parts of 30 35 parts of bituminous concrete, 22 24 parts of cement, 18 32 parts of sand, 17 23 parts of rubble and water；Preparation method comprises the following steps：（1）Surface layer preparation of batch；（2）Basic unit's preparation of batch；（3）Shaping, the demoulding, pile and maintenance；The present invention solve existing pavior brick exist be unable to that refuse reclamation, bad hydraulic permeability, unit weight are big, non-skid property is poor, compression strength is low, corrosion-resistant and the problem of poor shock resistance.
Description
Technical field
The invention belongs to pavior brick production technical field, and in particular to permeable pavement brick and its system that a kind of pitch is recycled
Preparation Method.
Background technology
Pavior brick is a kind of pavement, by mainly by cement, stone and sand be raw material, it is processed, vibration pressurization or
Other moulding process are made, for lay the concrete road surface of urban road pavement, city square etc. and the block of ground surface works,
Plate etc., its application is very wide, and the consumption of daily material is very big, in the urgent need to increasing income and decreasing expenditure.
China it is annual because Asphalt Concrete Pavement Maintenance, maintenance and rebuilding produce dig, milling asphaltic road-mix surface course
Material has millions of tons, and is also increased with about annual 15% speed.The generation of this substantial amounts of ground surface material, a side
Serious environmental pollution is caused in face, is on the other hand a kind of resource for the country of this high-quality asphalt of China extremely scarcity
Significant wastage, it is dirty to improve resource utilization and reduction environment if these waste asphalt pavement material regenerations can be utilized
Dye, and several hundred million first expenses can be saved；Therefore, waste asphalt pavement material how is made full use of to turn into the field urgently to be resolved hurrily
Technical problem.
Pavior brick is big except materials demand, and its own is there is also bad hydraulic permeability, non-skid property is poor, compression strength is low, resistance to
Corrosivity is poor, shock resistance is poor and the problem of big unit weight.
The content of the invention
Exist to solve existing pavior brick and be unable to that refuse reclamation, bad hydraulic permeability, unit weight are big, non-skid property is poor, anti-
The problem of Compressive Strength is low, corrosion-resistant and shock resistance are poor, it is an object of the invention to provide a kind of pitch recycle it is saturating
Water route face brick and preparation method thereof, the permeable pavement brick that the pitch of preparation is recycled has that good water permeability, unit weight be small, compression strength
Height, good non-skid property, good corrosion resistance, good and energy-conserving and environment-protective the advantage of shock resistance.
The invention provides following technical scheme：
The permeable pavement brick that a kind of pitch is recycled, including surface layer and basic unit：
The surface layer includes the raw material of following parts by weight：Discarded 30-40 parts of bituminous concrete, 20-28 parts of cement, 25-33 parts of sand,
5-10 parts of rubble, 4-6 parts of emulsified asphalt, 3-6 parts of miberal powder, 6-10 parts of glass fibre, 1.2-2.4 parts of venamul,
3-10 parts of clay, 0.8-1.6 parts of rubber powder, 5-10 parts of air-entrainment, 0.4-0.6 parts of water reducer, 0.3-0.5 parts of pigment powder and water 1-
3 parts；
The basic unit includes the raw material of following parts by weight：Discarded 30-35 parts of bituminous concrete, 22-24 parts of cement, 18-32 parts of sand,
2-3 parts of 17-23 parts of rubble and water.
Discarded bituminous concrete is with the addition of in raw material, existing pavior brick former material consumption is solved big, it is impossible to which waste is sharp again
With the problem of, then because discarded bituminous concrete itself has the advantages that compression strength is high, skid resistance is good and shock resistance is good.
Preferably,
The surface layer includes the raw material of following parts by weight：Discarded 35 parts of bituminous concrete, 24 parts of cement, 29 parts of sand, rubble 7.5
Part, 5 parts of emulsified asphalt, 4.5 parts of miberal powder, 8 parts of glass fibre, 1.8 parts of venamul, 6.5 parts of clay, rubber powder
2 parts of 1.2 parts, 7.5 parts of air-entrainment, 0.5 part of water reducer, 0.4 part of pigment powder and water；
The basic unit includes the raw material of following parts by weight：Discarded 32.5 parts of bituminous concrete, 23 parts of cement, 25 parts of sand, rubble 20
2.5 parts of part and water.
According to pavior brick made from above-mentioned composition of raw materials, with good water permeability, unit weight is small, compression strength is high, skid resistance
Can good, good corrosion resistance, good and energy-conserving and environment-protective the advantage of shock resistance.
Preferably, the cement in the surface layer and basic unit's raw material is that strength grade is 62.5 grades of portland cements so that
The pavior brick compression strength produced is high.
Preferably, the particle diameter of the surface layer and the rubble in basic unit's raw material is 8-10mm, can preferably bear skeleton
Effect.
Preferably, the water reducer in basic unit's raw material is naphthalene sulfonate water reducer, and water-reducing rate is up to 25%.
Preferably, the surface thickness is 6-8mm, improves the compression strength of pavior brick.
Preferably, the air-entrainment in the face stock is aluminium powder, improves mobility during mixed material stirring, obtained
Pavior brick has the advantages that unit weight is small.
A kind of preparation method for the permeable pavement brick that pitch is recycled, comprises the following steps：
（1）Parts by weight according to face stock weigh raw material, and the discarded bituminous concrete in face stock first is transported into first
Pulverizer is crushed, then by the discarded bituminous concrete of crushing, cement, sand, rubble, emulsified asphalt, miberal powder, glass fibre, poly- second
Ball mill mixing and ball milling 15- is delivered in vinyl acetate emulsion, clay, rubber powder, air-entrainment, water reducer, pigment powder and water transport
20min；
（2）Parts by weight according to basic unit's raw material weigh raw material, and the discarded bituminous concrete in basic unit's raw material first is transported into second
Pulverizer is crushed, and basic unit's raw material cement, sand, rubble and water transport are delivered into edge runner stirring 20-28min；
（3）First the face stock after ball milling is added in the mould of block machine, then again toward in the mould of block machine
The basic unit's raw material added after stirring, by block machine high pressure composite molding, the demoulding, pile, maintenance.
The beneficial effects of the invention are as follows：
1st, the present invention is by the adjustment and control of satisfy the need face brick composition of raw materials and preparation method, and solving that pavior brick exists can not
Refuse reclamation, bad hydraulic permeability, unit weight are big, non-skid property is poor, compression strength is low, corrosion-resistant and shock resistance difference ask
Topic；
2nd, the cement in heretofore described surface layer and basic unit's raw material is that strength grade is 62.5 grades of portland cements so that system
The pavior brick compression strength produced is high；
3rd, the particle diameter of heretofore described surface layer and the rubble in basic unit's raw material is 8-10mm, can preferably bear skeleton
Effect；
4th, the water reducer in heretofore described basic unit's raw material is naphthalene sulfonate water reducer, and water-reducing rate is up to 25%；
5th, heretofore described surface thickness is 6-8mm, improves the compression strength of pavior brick；
6th, the air-entrainment in heretofore described face stock is aluminium powder, improves mobility during mixed material stirring, obtained
Pavior brick has the advantages that unit weight is small.
Embodiment
Embodiment 1
The permeable pavement brick that a kind of pitch is recycled, including surface layer and basic unit：
Surface layer includes the raw material of following parts by weight：Discarded 35 parts of bituminous concrete, 24 parts of cement, 29 parts of sand, 7.5 parts of rubble, breast
Change 5 parts of pitch, 4.5 parts of miberal powder, 8 parts of glass fibre, 1.8 parts of venamul, 6.5 parts of clay, 1.2 parts of rubber powder,
2 parts of 7.5 parts of air-entrainment, 0.5 part of water reducer, 0.4 part of pigment powder and water；
Basic unit includes the raw material of following parts by weight：Discarded 32.5 parts of bituminous concrete, 23 parts of cement, 25 parts of sand, 20 parts of rubble and
2.5 parts of water.
According to pavior brick made from above-mentioned composition of raw materials, with good water permeability, unit weight is small, compression strength is high, skid resistance
Can good, good corrosion resistance, good and energy-conserving and environment-protective the advantage of shock resistance.
Discarded bituminous concrete is with the addition of in raw material, existing pavior brick former material consumption is solved big, it is impossible to which waste is sharp again
With the problem of, then because discarded bituminous concrete itself has the advantages that compression strength is high, skid resistance is good and shock resistance is good.
Cement in surface layer and basic unit's raw material is that strength grade is 62.5 grades of portland cements so that the road surface produced
Brick compression strength is high.
The particle diameter of surface layer and the rubble in basic unit's raw material is 8-10mm, can preferably bear the effect of skeleton.
Water reducer in basic unit's raw material is naphthalene sulfonate water reducer, and water-reducing rate is up to 25%.
Surface thickness is 6-8mm, improves the compression strength of pavior brick.
Air-entrainment in face stock is aluminium powder, improves mobility during mixed material stirring, and obtained pavior brick has
The small advantage of unit weight.
A kind of preparation method for the permeable pavement brick that pitch is recycled, comprises the following steps：
（1）Parts by weight according to face stock weigh raw material, and the discarded bituminous concrete in face stock first is transported into first
Pulverizer is crushed, then by the discarded bituminous concrete of crushing, cement, sand, rubble, emulsified asphalt, miberal powder, glass fibre, poly- second
Ball mill mixing and ball milling 20min is delivered in vinyl acetate emulsion, clay, rubber powder, air-entrainment, water reducer, pigment powder and water transport；
（2）Parts by weight according to basic unit's raw material weigh raw material, and the discarded bituminous concrete in basic unit's raw material first is transported into second
Pulverizer is crushed, and basic unit's raw material cement, sand, rubble and water transport are delivered into edge runner stirring 28min；
（3）First the face stock after ball milling is added in the mould of block machine, then again toward in the mould of block machine
The basic unit's raw material added after stirring, by block machine high pressure composite molding, the demoulding, pile, maintenance.
Embodiment 2
The permeable pavement brick that a kind of pitch is recycled, including surface layer and basic unit：
Surface layer includes the raw material of following parts by weight：Discarded 30 parts of bituminous concrete, 20 parts of cement, 25 parts of sand, 5- parts of rubble, emulsification
4 parts of pitch, 3 parts of miberal powder, 6 parts of glass fibre, 1.2 parts of venamul, 3 parts of clay, 0.8 part of rubber powder, air-entrainment 5
Part, 0.4 part of water reducer, 0.3 part of pigment powder and 1 part of water；
Basic unit includes the raw material of following parts by weight：Discarded 30 parts of bituminous concrete, 22 parts of cement, 18 parts of sand, 17 parts of rubble and water 2
Part.
Discarded bituminous concrete is with the addition of in raw material, existing pavior brick former material consumption is solved big, it is impossible to which waste is sharp again
With the problem of, then because discarded bituminous concrete itself has the advantages that compression strength is high, skid resistance is good and shock resistance is good.
Cement in surface layer and basic unit's raw material is that strength grade is 62.5 grades of portland cements so that the road surface produced
Brick compression strength is high.
The particle diameter of surface layer and the rubble in basic unit's raw material is 8-10mm, can preferably bear the effect of skeleton.
Water reducer in basic unit's raw material is naphthalene sulfonate water reducer, and water-reducing rate is up to 25%.
Surface thickness is 6-8mm, improves the compression strength of pavior brick.
Air-entrainment in face stock is aluminium powder, improves mobility during mixed material stirring, and obtained pavior brick has
The small advantage of unit weight.
A kind of preparation method for the permeable pavement brick that pitch is recycled, comprises the following steps：
（1）Parts by weight according to face stock weigh raw material, and the discarded bituminous concrete in face stock first is transported into first
Pulverizer is crushed, then by the discarded bituminous concrete of crushing, cement, sand, rubble, emulsified asphalt, miberal powder, glass fibre, poly- second
Ball mill mixing and ball milling 20min is delivered in vinyl acetate emulsion, clay, rubber powder, air-entrainment, water reducer, pigment powder and water transport；
（2）Parts by weight according to basic unit's raw material weigh raw material, and the discarded bituminous concrete in basic unit's raw material first is transported into second
Pulverizer is crushed, and basic unit's raw material cement, sand, rubble and water transport are delivered into edge runner stirring 28min；
（3）First the face stock after ball milling is added in the mould of block machine, then again toward in the mould of block machine
The basic unit's raw material added after stirring, by block machine high pressure composite molding, the demoulding, pile, maintenance.
Embodiment 3
The permeable pavement brick that a kind of pitch is recycled, including surface layer and basic unit：
Surface layer includes the raw material of following parts by weight：Discarded 40 parts of bituminous concrete, 28 parts of cement, 33 parts of sand, 10 parts of rubble, emulsification
6 parts of pitch, 6 parts of miberal powder, 10 parts of glass fibre, 2.4 parts of venamul, 10 parts of clay, 1.6 parts of rubber powder, aerating
3 parts of 10 parts of agent, 0.6 part of water reducer, 0.5 part of pigment powder and water；
Basic unit includes the raw material of following parts by weight：Discarded 35 parts of bituminous concrete, 24 parts of cement, 32 parts of sand, 23 parts of rubble and water 3
Part.
Discarded bituminous concrete is with the addition of in raw material, existing pavior brick former material consumption is solved big, it is impossible to which waste is sharp again
With the problem of, then because discarded bituminous concrete itself has the advantages that compression strength is high, skid resistance is good and shock resistance is good.
Cement in surface layer and basic unit's raw material is that strength grade is 62.5 grades of portland cements so that the road surface produced
Brick compression strength is high.
The particle diameter of surface layer and the rubble in basic unit's raw material is 8-10mm, can preferably bear the effect of skeleton.
Water reducer in basic unit's raw material is naphthalene sulfonate water reducer, and water-reducing rate is up to 25%.
Surface thickness is 6-8mm, improves the compression strength of pavior brick.
Air-entrainment in face stock is aluminium powder, improves mobility during mixed material stirring, and obtained pavior brick has
The small advantage of unit weight.
A kind of preparation method for the permeable pavement brick that pitch is recycled, comprises the following steps：
（1）Parts by weight according to face stock weigh raw material, and the discarded bituminous concrete in face stock first is transported into first
Pulverizer is crushed, then by the discarded bituminous concrete of crushing, cement, sand, rubble, emulsified asphalt, miberal powder, glass fibre, poly- second
Ball mill mixing and ball milling 15min is delivered in vinyl acetate emulsion, clay, rubber powder, air-entrainment, water reducer, pigment powder and water transport；
（2）Parts by weight according to basic unit's raw material weigh raw material, and the discarded bituminous concrete in basic unit's raw material first is transported into second
Pulverizer is crushed, and basic unit's raw material cement, sand, rubble and water transport are delivered into edge runner stirring 20min；
（3）First the face stock after ball milling is added in the mould of block machine, then again toward in the mould of block machine
The basic unit's raw material added after stirring, by block machine high pressure composite molding, the demoulding, pile, maintenance.
The preferred embodiments of the present invention are the foregoing is only, are not intended to limit the invention, although with reference to foregoing reality
Apply example the present invention is described in detail, for those skilled in the art, it still can be to foregoing each implementation
Technical scheme described in example is modified, or equivalent substitution, all essences in the present invention are carried out to which part technical characteristic
God is with principle, and any modification, equivalent substitution and improvements made etc. should be included in the scope of the protection.
Claims (8)
1. the permeable pavement brick that a kind of pitch is recycled, including surface layer and basic unit, it is characterised in that：
The surface layer includes the raw material of following parts by weight：Discarded 30-40 parts of bituminous concrete, 20-28 parts of cement, 25-33 parts of sand,
5-10 parts of rubble, 4-6 parts of emulsified asphalt, 3-6 parts of miberal powder, 6-10 parts of glass fibre, 1.2-2.4 parts of venamul,
3-10 parts of clay, 0.8-1.6 parts of rubber powder, 5-10 parts of air-entrainment, 0.4-0.6 parts of water reducer, 0.3-0.5 parts of pigment powder and water 1-
3 parts；
The basic unit includes the raw material of following parts by weight：Discarded 30-35 parts of bituminous concrete, 22-24 parts of cement, 18-32 parts of sand,
2-3 parts of 17-23 parts of rubble and water.
2. the permeable pavement brick that pitch according to claim 1 is recycled, it is characterised in that：
The surface layer includes the raw material of following parts by weight：Discarded 35 parts of bituminous concrete, 24 parts of cement, 29 parts of sand, rubble 7.5
Part, 5 parts of emulsified asphalt, 4.5 parts of miberal powder, 8 parts of glass fibre, 1.8 parts of venamul, 6.5 parts of clay, rubber powder
2 parts of 1.2 parts, 7.5 parts of air-entrainment, 0.5 part of water reducer, 0.4 part of pigment powder and water；
The basic unit includes the raw material of following parts by weight：Discarded 32.5 parts of bituminous concrete, 23 parts of cement, 25 parts of sand, rubble 20
2.5 parts of part and water.
3. the permeable pavement brick that pitch according to claim 1 is recycled, it is characterised in that：The surface layer and basic unit's raw material
In cement be strength grade for 62.5 grades of portland cements.
4. the permeable pavement brick that pitch according to claim 1 is recycled, it is characterised in that：The surface layer and basic unit's raw material
In rubble particle diameter be 8-10mm.
5. the permeable pavement brick that pitch according to claim 1 is recycled, it is characterised in that：Subtracting in basic unit's raw material
Aqua is naphthalene sulfonate water reducer.
6. the permeable pavement brick that pitch according to claim 1 is recycled, it is characterised in that：The surface thickness is 6-
8mm。
7. the permeable pavement brick that pitch according to claim 1 is recycled, it is characterised in that：Adding in the face stock
Gas agent is aluminium powder.
8. a kind of preparation method for the permeable pavement brick that pitch as described in one of claim 1 to 7 is recycled, its feature exists
In comprising the following steps：
（1）Parts by weight according to face stock weigh raw material, and the discarded bituminous concrete in face stock first is transported into first
Pulverizer is crushed, then by the discarded bituminous concrete of crushing, cement, sand, rubble, emulsified asphalt, miberal powder, glass fibre, poly- second
Ball mill mixing and ball milling 15- is delivered in vinyl acetate emulsion, clay, rubber powder, air-entrainment, water reducer, pigment powder and water transport
20min；
（2）Parts by weight according to basic unit's raw material weigh raw material, and the discarded bituminous concrete in basic unit's raw material first is transported into second
Pulverizer is crushed, and basic unit's raw material cement, sand, rubble and water transport are delivered into edge runner stirring 20-28min；
（3）First the face stock after ball milling is added in the mould of block machine, then again toward in the mould of block machine
The basic unit's raw material added after stirring, by block machine high pressure composite molding, the demoulding, pile, maintenance.