CN107200531A - A kind of ecological permeable pavement brick and preparation method thereof - Google Patents
A kind of ecological permeable pavement brick and preparation method thereof Download PDFInfo
- Publication number
- CN107200531A CN107200531A CN201710410552.3A CN201710410552A CN107200531A CN 107200531 A CN107200531 A CN 107200531A CN 201710410552 A CN201710410552 A CN 201710410552A CN 107200531 A CN107200531 A CN 107200531A
- Authority
- CN
- China
- Prior art keywords
- parts
- raw material
- basic unit
- cement
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention provides a kind of ecological permeable pavement brick and preparation method thereof, is related to pavior brick production technical field, and ecological permeable pavement brick includes surface layer and basic unit, and surface layer includes the raw material of following parts by weight：13 parts of 20 30 parts of cement, 25 30 parts of sand, 5 10 parts of rubble, 46 parts of building waste residue coarse aggregate, 36 parts of volcanic ash, 6 10 parts of glass dust, 5 10 parts of flyash, 3 10 parts of clay, 0.4 0.6 parts of water reducer, 0.3 0.5 parts of pigment powder and water；Basic unit includes the raw material of following parts by weight：23 parts of 22 30 parts of cement, 18 32 parts of sand, 17 23 parts of rubble and water；Preparation method comprises the following steps：(1) surface layer preparation of batch；(2) basic unit's preparation of batch；(3) shaping, the demoulding, pile and maintenance；The present invention solves existing pavior brick and exists that to be unable to refuse reclamation, bad hydraulic permeability, compression strength low and the problem of wear no resistance.
Description
Technical field
The invention belongs to pavior brick production technical field, and in particular to a kind of ecological permeable pavement brick and preparation method thereof.
Background technology
Pavior brick is a kind of pavement, by mainly by cement, stone and sand be raw material, it is processed, vibration pressurization or
Other moulding process are made, for lay the concrete road surface of urban road pavement, city square etc. and the block of ground surface works,
Plate etc., its application is very wide, and the consumption of daily material is very big, in the urgent need to increasing income and decreasing expenditure.
Building waste residue and industrial residue have some corner that city is greatly deposited in as municipal refuse, not only not
The value of recycling can be realized, occupancy urban land, pollution environment, the development in serious restriction city is there is also.
Pavior brick is big except materials demand, and there is also bad hydraulic permeability, compression strength are low and asking of wearing no resistance for its own
Topic.
The content of the invention
Exist that to be unable to refuse reclamation, bad hydraulic permeability, compression strength low and wear no resistance to solve existing pavior brick
The problem of, it is an object of the invention to provide a kind of ecological permeable pavement brick and preparation method thereof, the ecological permeable pavement brick of preparation
Have the advantages that good water permeability, compression strength be high, wearability is good and energy-conserving and environment-protective.
The invention provides following technical scheme：
A kind of ecological permeable pavement brick, including surface layer and basic unit：
The surface layer includes the raw material of following parts by weight：20-30 parts of cement, 25-30 parts of sand, 5-10 parts of rubble, building are useless
4-6 parts of slag coarse aggregate, 3-6 parts of volcanic ash, 6-10 parts of glass dust, 5-10 parts of flyash, 3-10 parts of clay, water reducer 0.4-0.6
1-3 parts of part, 0.3-0.5 parts of pigment powder and water；
The basic unit includes the raw material of following parts by weight：22-30 parts of cement, 18-32 parts of sand, 17-23 parts of rubble and water 2-3
Part.
Building waste residue coarse aggregate, volcanic ash, glass dust and flyash are added in raw material, making for pavior brick former material is reduced
With having reached the purpose of refuse reclamation.
Preferably,
The surface layer includes the raw material of following parts by weight：25 parts of cement, 27.5 parts of sand, 7.5 parts of rubble, the thick bone of building waste residue
5 parts of material, 4.5 parts of volcanic ash, 8 parts of glass dust, 7.5 parts of flyash, 6.5 parts of clay, 0.5 part of water reducer, 0.4 part of pigment powder and water
2 parts；
The basic unit includes the raw material of following parts by weight：2.5 parts of 26 parts of cement, 25 parts of sand, 20 parts of rubble and water.
Preferably, the cement in the surface layer and basic unit's raw material is that strength grade is 52.5 grades of Portland cements,
So that the pavior brick compression strength produced is high.
Preferably, the particle diameter of the surface layer and the rubble in basic unit's raw material is 6-8mm.
Preferably, the water reducer in basic unit's raw material is lignin sulfonate water reducer, it is possible to reduce water consumption
More than 10-15%, improves concrete workability and inhibition of slump-loss.
Preferably, the surface thickness is 4-6mm, improves the compression strength of pavior brick.
Preferably, the building waste residue coarse aggregate in the face stock be particle diameter in 5-8mm waste ceramic particle, can
Preferably bear the effect of skeleton.
A kind of preparation method of ecological permeable pavement brick, comprises the following steps：
(1) raw material is weighed according to the parts by weight of face stock, by face stock cement, sand, rubble, the thick bone of building waste residue
Ball mill mixing and ball milling 18-22min is delivered in material, volcanic ash, glass dust, flyash, clay, water reducer, pigment powder and water transport；
(2) raw material is weighed according to the parts by weight of basic unit's raw material, wheel is delivered into basic unit's raw material cement, sand, rubble and water transport
Mill stirs 20-28min；
(3) first the face stock after ball milling is added in the mould of block machine, then again toward the mould of block machine
The basic unit's raw material added in tool after stirring, by block machine high pressure composite molding, the demoulding, pile, maintenance.
The beneficial effects of the invention are as follows：
1st, the present invention is solved existing pavior brick and deposited by the adjustment and control of satisfy the need face brick composition of raw materials and preparation method
Being unable to, refuse reclamation, bad hydraulic permeability, compression strength are low and the problem of wear no resistance；
2nd, the cement in heretofore described surface layer and basic unit's raw material is that strength grade is 52.5 grades of normal silicate water
Mud so that the pavior brick compression strength produced is high；
3rd, the water reducer in heretofore described basic unit's raw material is lignin sulfonate water reducer, it is possible to reduce water consumption
More than 10-15%, improve concrete workability and inhibition of slump-loss；
4th, the building waste residue coarse aggregate in heretofore described face stock is waste ceramic particle of the particle diameter in 5-8mm,
The effect of skeleton can preferably be born.
5th, building waste residue coarse aggregate, volcanic ash, glass dust and flyash are added in the present invention in raw material, pavior brick is reduced
The use of former material, has reached the purpose of refuse reclamation.
Embodiment
Embodiment 1
A kind of ecological permeable pavement brick, including surface layer and basic unit：
Surface layer includes the raw material of following parts by weight：25 parts of cement, 27.5 parts of sand, 7.5 parts of rubble, building waste residue coarse aggregate 5
Part, 4.5 parts of volcanic ash, 8 parts of glass dust, 7.5 parts of flyash, 6.5 parts of clay, 0.5 part of water reducer, 0.4 part of pigment powder and water 2
Part；
Basic unit includes the raw material of following parts by weight：2.5 parts of 26 parts of cement, 25 parts of sand, 20 parts of rubble and water.
Building waste residue coarse aggregate, volcanic ash, glass dust and flyash are added in raw material, making for pavior brick former material is reduced
With having reached the purpose of refuse reclamation.
Cement in surface layer and basic unit's raw material is that strength grade is 52.5 grades of Portland cements so that produced
Pavior brick compression strength is high.
The particle diameter of surface layer and the rubble in basic unit's raw material is 6-8mm.
Water reducer in basic unit's raw material is lignin sulfonate water reducer, it is possible to reduce more than the 10-15% of water consumption,
Improve concrete workability and inhibition of slump-loss.
Surface thickness is 4-6mm, improves the compression strength of pavior brick.
Building waste residue coarse aggregate in face stock is particle diameter in 5-8mm waste ceramic particle, can preferably be undertaken
Play skeleton.
A kind of preparation method of ecological permeable pavement brick, comprises the following steps：
(1) raw material is weighed according to the parts by weight of face stock, by face stock cement, sand, rubble, the thick bone of building waste residue
Ball mill mixing and ball milling 22min is delivered in material, volcanic ash, glass dust, flyash, clay, water reducer, pigment powder and water transport；
(2) raw material is weighed according to the parts by weight of basic unit's raw material, wheel is delivered into basic unit's raw material cement, sand, rubble and water transport
Mill stirs 28min；
(3) first the face stock after ball milling is added in the mould of block machine, then again toward the mould of block machine
The basic unit's raw material added in tool after stirring, by block machine high pressure composite molding, the demoulding, pile, maintenance.
Embodiment 2
A kind of ecological permeable pavement brick, including surface layer and basic unit：
Surface layer includes the raw material of following parts by weight：20 parts of cement, 25 parts of sand, 5 parts of rubble, 4 parts of building waste residue coarse aggregate, fire
1 part of 3 parts of mountain ash, 6 parts of glass dust, 5 parts of flyash, 3 parts of clay, 0.4 part of water reducer, 0.3 part of pigment powder and water；
Basic unit includes the raw material of following parts by weight：2 parts of 22 parts of cement, 18 parts of sand, 17 parts of rubble and water.
Building waste residue coarse aggregate, volcanic ash, glass dust and flyash are added in raw material, making for pavior brick former material is reduced
With having reached the purpose of refuse reclamation.
Cement in surface layer and basic unit's raw material is that strength grade is 52.5 grades of Portland cements so that produced
Pavior brick compression strength is high.
The particle diameter of surface layer and the rubble in basic unit's raw material is 6-8mm.
Water reducer in basic unit's raw material is lignin sulfonate water reducer, it is possible to reduce more than the 10-15% of water consumption,
Improve concrete workability and inhibition of slump-loss.
Surface thickness is 4-6mm, improves the compression strength of pavior brick.
Building waste residue coarse aggregate in face stock is particle diameter in 5-8mm waste ceramic particle, can preferably be undertaken
Play skeleton.
A kind of preparation method of ecological permeable pavement brick, comprises the following steps：
(1) raw material is weighed according to the parts by weight of face stock, by face stock cement, sand, rubble, the thick bone of building waste residue
Ball mill mixing and ball milling 22min is delivered in material, volcanic ash, glass dust, flyash, clay, water reducer, pigment powder and water transport；
(2) raw material is weighed according to the parts by weight of basic unit's raw material, wheel is delivered into basic unit's raw material cement, sand, rubble and water transport
Mill stirs 28min；
(3) first the face stock after ball milling is added in the mould of block machine, then again toward the mould of block machine
The basic unit's raw material added in tool after stirring, by block machine high pressure composite molding, the demoulding, pile, maintenance.
Embodiment 3
A kind of ecological permeable pavement brick, including surface layer and basic unit：
Surface layer includes the raw material of following parts by weight：30 parts of cement, 30 parts of sand, 10 parts of rubble, 6 parts of building waste residue coarse aggregate,
3 parts of 6 parts of volcanic ash, 10 parts of glass dust, 10 parts of flyash, 10 parts of clay, 0.6 part of water reducer, 0.5 part of pigment powder and water；
Basic unit includes the raw material of following parts by weight：3 parts of 30 parts of cement, 32 parts of sand, 23 parts of rubble and water.
Building waste residue coarse aggregate, volcanic ash, glass dust and flyash are added in raw material, making for pavior brick former material is reduced
With having reached the purpose of refuse reclamation.
Cement in surface layer and basic unit's raw material is that strength grade is 52.5 grades of Portland cements so that produced
Pavior brick compression strength is high.
The particle diameter of surface layer and the rubble in basic unit's raw material is 6-8mm.
Water reducer in basic unit's raw material is lignin sulfonate water reducer, it is possible to reduce more than the 10-15% of water consumption,
Improve concrete workability and inhibition of slump-loss.
Surface thickness is 4-6mm, improves the compression strength of pavior brick.
Building waste residue coarse aggregate in face stock is particle diameter in 5-8mm waste ceramic particle, can preferably be undertaken
Play skeleton.
A kind of preparation method of ecological permeable pavement brick, comprises the following steps：
(1) raw material is weighed according to the parts by weight of face stock, by face stock cement, sand, rubble, the thick bone of building waste residue
Ball mill mixing and ball milling 18min is delivered in material, volcanic ash, glass dust, flyash, clay, water reducer, pigment powder and water transport；
(2) raw material is weighed according to the parts by weight of basic unit's raw material, wheel is delivered into basic unit's raw material cement, sand, rubble and water transport
Mill stirs 20min；
(3) first the face stock after ball milling is added in the mould of block machine, then again toward the mould of block machine
The basic unit's raw material added in tool after stirring, by block machine high pressure composite molding, the demoulding, pile, maintenance.
Comparative example
A kind of pavior brick, including surface layer and basic unit：
Surface layer includes the raw material of following parts by weight：1 part of 20 parts of cement, 25 parts of sand, 5 parts of rubble, 0.3 part of pigment powder and water；
Basic unit includes the raw material of following parts by weight：2 parts of 22 parts of cement, 18 parts of sand, 17 parts of rubble and water.
A kind of preparation method of pavior brick, comprises the following steps：
(1) raw material is weighed according to the parts by weight of face stock, by face stock cement, sand, rubble, pigment powder and water transport
Deliver to ball mill mixing and ball milling 22min；
(2) raw material is weighed according to the parts by weight of basic unit's raw material, wheel is delivered into basic unit's raw material cement, sand, rubble and water transport
Mill stirs 28min；
(3) first the face stock after ball milling is added in the mould of block machine, then again toward the mould of block machine
The basic unit's raw material added in tool after stirring, by block machine high pressure composite molding, the demoulding, pile, maintenance.
Embodiment 4
Embodiment 1, embodiment 2, embodiment 3 and comparative example are subjected to the property on water penetration, compression strength and wearability
It can test, test result is as shown in table 1.
Table 1 is embodiment 1, embodiment 2, embodiment 3 and comparative example performance test data.
From the data of table 1 compare as can be seen that it is an advantage of the invention that：
1st, a kind of ecological permeable pavement brick and preparation method thereof, implementation is can be seen that from the pavior brick coefficient of permeability measured
Example 1-3 coefficient of permeability value is above comparative example, illustrates that the pavior brick has good water permeability.
2nd, a kind of ecological permeable pavement brick and preparation method thereof, reality is can be seen that from the pavior brick compression strength value measured
The compression strength value for applying a 1-3 is above comparative example, illustrates that the pavior brick compression strength is high.
3rd, a kind of ecological permeable pavement brick and preparation method thereof, from the pavior brick abrasion resistance measured as can be seen that embodiment
1-3 abrasion resistance is above comparative example, illustrates that the anti-wear performance of the pavior brick is good.
4th, a kind of ecological permeable pavement brick and preparation method thereof, can in the data of each index from the pavior brick measured
Go out, embodiment 1 is superior to embodiment 2, embodiment 3 and comparative example, and embodiment 2 and embodiment 3 are superior to comparative example, illustrate this
The composition of raw materials of pavior brick and the reasonability of preparation method.
The preferred embodiments of the present invention are the foregoing is only, are not intended to limit the invention, although with reference to foregoing reality
Apply example the present invention is described in detail, for those skilled in the art, it still can be to foregoing each implementation
Technical scheme described in example is modified, or equivalent substitution, all essences in the present invention are carried out to which part technical characteristic
God is with principle, and any modification, equivalent substitution and improvements made etc. should be included in the scope of the protection.
Claims (8)
1. a kind of ecological permeable pavement brick, including surface layer and basic unit, it is characterised in that：
The surface layer includes the raw material of following parts by weight：20-30 parts of cement, 25-30 parts of sand, 5-10 parts of rubble, building waste residue are thick
4-6 parts of aggregate, 3-6 parts of volcanic ash, 6-10 parts of glass dust, 5-10 parts of flyash, 3-10 parts of clay, 0.4-0.6 parts of water reducer, face
1-3 parts of 0.3-0.5 parts of feed powder and water；
The basic unit includes the raw material of following parts by weight：2-3 parts of 22-30 parts of cement, 18-32 parts of sand, 17-23 parts of rubble and water.
2. ecological permeable pavement brick according to claim 1, including surface layer and basic unit, it is characterised in that：
The surface layer includes the raw material of following parts by weight：25 parts of cement, 27.5 parts of sand, 7.5 parts of rubble, building waste residue coarse aggregate 5
Part, 4.5 parts of volcanic ash, 8 parts of glass dust, 7.5 parts of flyash, 6.5 parts of clay, 0.5 part of water reducer, 0.4 part of pigment powder and water 2
Part；
The basic unit includes the raw material of following parts by weight：2.5 parts of 26 parts of cement, 25 parts of sand, 20 parts of rubble and water.
3. ecological permeable pavement brick according to claim 1, it is characterised in that：Cement in the surface layer and basic unit's raw material
It is that strength grade is 52.5 grades of Portland cements.
4. ecological permeable pavement brick according to claim 1, it is characterised in that：Rubble in the surface layer and basic unit's raw material
Particle diameter be 6-8mm.
5. ecological permeable pavement brick according to claim 1, it is characterised in that：Water reducer in basic unit's raw material is wood
Mahogany sulfonate class water reducer.
6. ecological permeable pavement brick according to claim 1, it is characterised in that：The surface thickness is 4-6mm.
7. ecological permeable pavement brick according to claim 1, it is characterised in that：Building waste residue in the face stock is thick
Aggregate is waste ceramic particle of the particle diameter in 5-8mm.
8. a kind of preparation method of ecological permeable pavement brick as described in one of claim 1 to 7, it is characterised in that including with
Lower step：
(1) weigh raw material according to the parts by weight of face stock, by face stock cement, sand, rubble, building waste residue coarse aggregate,
Ball mill mixing and ball milling 18-22min is delivered in volcanic ash, glass dust, flyash, clay, water reducer, pigment powder and water transport；
(2) raw material is weighed according to the parts by weight of basic unit's raw material, edge runner is delivered into basic unit's raw material cement, sand, rubble and water transport
Stir 20-28min；
(3) first the face stock after ball milling is added in the mould of block machine, then again toward in the mould of block machine
The basic unit's raw material added after stirring, by block machine high pressure composite molding, the demoulding, pile, maintenance.