CN106995974A - A kind of crystal cotton is tried to stop people from fighting each other wire side material and its production technology - Google Patents
A kind of crystal cotton is tried to stop people from fighting each other wire side material and its production technology Download PDFInfo
- Publication number
- CN106995974A CN106995974A CN201610050629.6A CN201610050629A CN106995974A CN 106995974 A CN106995974 A CN 106995974A CN 201610050629 A CN201610050629 A CN 201610050629A CN 106995974 A CN106995974 A CN 106995974A
- Authority
- CN
- China
- Prior art keywords
- cotton
- combs
- fabric
- yarn
- fighting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses crystal cotton and tried to stop people from fighting each other wire side material, the fabric is formed by polyamide fibre, spandex and cotton yarn warp knit, the mass percent of the polyamide fibre, spandex and cotton yarn is respectively 51 63%, 18 28% and 19 21%, the fineness of polyamide fibre, spandex and cotton yarn is respectively 44 dtex, 310 470 dtex and 80 S, the breadth of the fabric is 210 220 cm, and the grammes per square metre of fabric is 160 210 g/m2The horizontal density of fabric is 16 18 w/cm, the vertical density of fabric is 60 86 c/cm, in warping and weaving process, the GB1 combs of single comb structure organization use raw material for chinlon filament, GB2 combs use raw material for chinlon filament, and GB3 uses raw material for cotton ammonia wrap yarn, and GB4 combs use raw material for cotton ammonia wrap yarn.The present invention provides a kind of meshed new body shaping underwear fabric of tool for numerous women, meets women to aesthetic feeling and the demand of comfort level, it is ensured that female pathology health.
Description
Technical field
The invention belongs to cloth textile process and clothes technical field, tried to stop people from fighting each other wire side in particular to a kind of crystal cotton
Material and its production technology.
Background technology
Take care of health and keep good figure with the improvement of living standards, people increasingly pay close attention to.Body shaping underwear turn into women pursue,
The clothes that heat is held in both hands, body shaping underwear can be rebuild, remold body curvature, leave the fine figure expression nothing of women.Research shows, moulds
Body underwear is often difficult ventilative and excessively fetters body, easily causes and gynaecology's disease is induced after dermatitis and bacterial reproduction, retrograde infection
Disease.
Traditional body shaping underwear is the mesh or lycra cloth of polyamide fibre and thicker spandex warp knit, the gas permeability of the fabric and is led
It is moist poor；Quality Pure Cotton Yarn Production or cotton blended yarn and thinner spandex containing weft can also be formed stretch fabric, the fabric mutability, to human body
The pressure at position is larger.
Cotton yarn is because of its fiber soft-touch, to the stingless excitation of skin, and hygroscopicity is high, good heat preservation performance and many without electrostatic etc.
Advantage, producer is used as body shaping underwear raw material, reaches moisturizing, absorbing sweat, ventilative and other effects.Cotton yarn is because more than its filoplume and being broken
It is strongly poor, it can not be woven on high machine tricot machine；Meanwhile, the fabric structure being made on weft machine is unstable, bullet
Property and response rate are poor.
China Patent Publication No. CN102560863A, publication date is on 07 11st, 2012, entitled《Warp knit cotton is tried to stop people from fighting each other face
Material and its preparation technology》, it is of the invention to disclose a kind of warp knitted cotton lycra fabric and its preparation technology of fabric, it is desirable to provide Yi Zhongjie
Structure is stable, and the good warp knitted cotton lycra fabric of elasticity, the fabric is made up of the component of following mass percents：12-28% cotton yarns,
18-36% spandexs and 50-70% chinlon filaments, its preparation technology include single comb group when warping, weaving, dyeing and finishing, warping and weaving
The GB1 combs for knitting structure are chinlon filament, and GB2 combs are spandex, and GB3 combs are spandex, and GB4 combs are the bright and beautiful wrap yarn of cotton.The present invention is combined
Cotton yarn, polyamide fibre and spandex advantage make the good lycra fabric of Stability Analysis of Structures, elasticity, but the fabric does not have mesh, as
Permeability is limited when body shaping underwear, it is impossible to preferably meet women to comfort level and the demand of health.
The content of the invention
Wire side material and its production technology the present invention is intended to provide a kind of crystal cotton is tried to stop people from fighting each other, by changing production technology to solving
Certainly the loosely organized of body shaping underwear fabric, moisturizing and absorbing sweat poor performance, elasticity capacity be weak and the not excellent problem of air permeable effect, be
Numerous women provide a kind of meshed new body shaping underwear fabric of tool, meet women to aesthetic feeling and the demand of comfort level, it is ensured that
Female pathology health.
A kind of crystal cotton is tried to stop people from fighting each other wire side material, and the fabric is formed by polyamide fibre, spandex and cotton yarn warp knit, polyamide fibre, spandex and cotton
The mass percent of yarn is respectively 51-63%, 18-28% and 19-21%, and the fineness of the polyamide fibre, spandex and cotton yarn is respectively 44
Dtex, 310-470 dtex and 80 S.
Further, the breadth of the fabric is 210-220 cm, and the grammes per square metre of fabric is 175-180g/m2, the horizontal stroke of fabric
Density is 16 w/cm, and the vertical density of fabric is 63-78 c/cm.
Further, the step of production technology includes warping, weaving, dyeing, the warping and woven single comb group successively
Knitting structure is：
GB1 is combed：2-0,2-4,4-2,4-6,4-2,2-4//
GB2 is combed：4-6,4-2,2-4,2-0,2-4,4-2//
GB3 is combed：0-0,2-2//
GB4 is combed：2-2,0-0//
Further, the GB1 combs use raw material for chinlon filament, and the GB2 combs use raw material for chinlon filament, the GB3
Raw material is used for cotton ammonia wrap yarn, the GB4 combs use raw material for cotton ammonia wrap yarn.
Further, the cotton ammonia coating cotton thread is using 310-470 dtex spandexs that 80 S cotton yarns are opposite with its twist direction
Direction be wrapped.
Further, GB1 combs and GB2 combs are respectively arranged with separating needle in the warping and weaving process, and GB3 combs and GB4 are combed and needed
Remove separating needle.
Further, in the weaving process four combs take entry to yarn mode and be successively：GB1 combs wear 1 empty, GB2 for 1
Comb and worn for 1 sky 1, GB3 combs wear 1 sky for 1, GB4 combs are worn for 1 sky 1.
Further, two selvedges of fabric take 1 to wear 3 empty to entry to yarn mode, totally 6 groups in the weaving process.
The advantage of the invention is that：This production technology is raw material by using cotton ammonia wrap yarn and chinlon filament, overcomes modeling
The loosely organized of body underwear fabric, moisturizing and absorbing sweat poor performance, elasticity capacity be weak and the not excellent problem of air permeable effect, are vast
Women provides a kind of meshed new body shaping underwear fabric of tool, meets women to aesthetic feeling and the demand of comfort level, it is ensured that women
Physiological health.
Embodiment
In order to improve the loosely organized of body underwear fabric, moisturizing and absorbing sweat poor performance, elasticity capacity be weak and air permeable effect
Not excellent problem, a kind of meshed new body shaping underwear fabric of tool is provided for numerous women, meets women to aesthetic feeling and comfortable
The demand of degree, it is ensured that female pathology health, the present invention provides a kind of crystal cotton and tried to stop people from fighting each other wire side material and its production technology.
In embodiment 1, a kind of crystal cotton is tried to stop people from fighting each other wire side material, is made up of following mass percent components：19% cotton, 18% ammonia
Synthetic fibre and 63% polyamide fibre, the positive key component of the fabric are polyamide fibre, and the main component of reverse side is cotton ammonia wrap yarn.
In embodiment 2, a kind of crystal cotton is tried to stop people from fighting each other wire side material, is made up of following mass percent components：21% cotton, 28% ammonia
Synthetic fibre and 51% polyamide fibre, the positive key component of the fabric are polyamide fibre, and the main component of reverse side is cotton ammonia wrap yarn.
The technological process of production of the fabric is as follows：
Ingredient inspection → upper yarn（Constant temperature is placed）→ warping → upper axle → entrys → weaves → and cropping, weigh → fabric puts in storage → water
Wash → pre-setting → dyeing → end sizing（Arrange）→ product inspection → clot, weigh, packaging → finished product storage
During upper yarn, to reduce bobbin draw distance and yarn bends degree difference, it is ensured that yarn road is short, advantageously ensures that
Whole yarn tension is highly consistent.On polyamide fibre during yarn, shaking out will manage after creel according to the careful ground of unreeling direction, favorably
In avoiding artificial damage spool, it is ensured that instrument is used safely.
During warping, the raw material that single comb institutional framework is used for：
GB1：44 dtex chinlon filaments
GB2：44 dtex chinlon filaments
GB3：80 S/310-470 dtex cotton ammonia wrap yarns
GB4：80 S/310-470 dtex cotton ammonia wrap yarns
The cotton ammonia wrap yarn is to twist with the fingers 80 S cotton yarns with it using 310-470 dtex spandexs to be wrapped in the opposite direction,
The untwisting of cotton yarn is so not only prevent, the strength of yarn is also add, the Yarn break under high-speed production is reduced, solved
The problems such as young pilose antler that cotton yarn occurs tangles broken yarn and weaving flyings is weaved on the high machine number.The weight range of cotton ammonia wrap yarn is
0.5-0.8 kg/.
During warping, warping machine temperature control is at 25 DEG C, and humidity maintains 70-80% and is advisable, relatively high and stable temperature
Degree and humidity contribute to the stabilization of cotton yarn turn and the reduction of filoplume.
Chinlon filament and cotton ammonia wrap yarn warping technology parameter：
| Raw material thread | Unit type | Linear velocity | Warping radical | Tension in Warping | Draw ratio |
| Chinlon filament | DS21/30NC-S | 600 m/min | 600 | 7-9 g/dN | —— |
| 80S/310 dtex | DSE-H-21/30 | 170 m/min | 598 | —— | 120% |
| 80S/470 dtex | DSE-H-21/30 | 170 m/min | 598 | —— | 120% |
During warp knit weaving, tricot machine parameter is as follows：
Type：RSE4N-1
Machine number：The mm of 28 pins/25.4
Door width：330.2 mm（130 cun）
Warp-knit list combs institutional framework：
GB1：2-0,2-4,4-2,4-6,4-2,2-4//
GB2：4-6,4-2,2-4,2-0,2-4,4-2//
GB3：0-0,2-2//
GB4：2-2,0-0//
Warp-knit raw material is：
GB1：44 dtex chinlon filaments
GB2：44 dtex chinlon filaments
GB3：80 S/310-470 dtex cotton ammonia wrap yarns
GB4：80 S/310-470 dtex cotton ammonia wrap yarns
, it is necessary to by raschel machine in weaving process（Raschel)）Drawing angle to be set as 170 °.In view of cotton ammonia
The fracture strength demand of wrap yarn, 1800 revs/min are adjusted to by the rotating speed of tricot machine from 2000 revs/min, for start optimized rotating speed.Brocade
Synthetic fibre long filament is in warping and weaving process, and warping machine and tricot machine GB1 combs and GB2 combs are respectively arranged with separating needle；In view of cotton ammonia bag
The easier generation of filoplume flyings of yarn is covered, the GB3 combs of warping machine and tricot machine and GB4 comb separating needles are removed, reduce cotton ammonia
The line resistance of cotton yarn yarn route in wrap yarn.
Tricot machine is using above-mentioned single comb institutional framework, and chinlon filament and cotton ammonia cover yarn all using 1 wear that 1 is empty or 1 sky 1 is worn
Entry to yarn method, both R. concomitans makes adjacent windings out of touch in the part of stringer, so that on warp knit fabric
Form the eyed structure of definite shape.In weaving process, two selvedges of fabric wear 3 totally 6 groups of skies using 1, can so subtract
The tension force of small selvedge yarn, the number of times for reducing bad pin and broken yarn improves Homes Using TV.
After warping machine and tricot machine are used 8 hours, to arrange to do a board cleaning, cotton ammonia can be so removed in time
The accumulation filoplume that cotton yarn is formed on board in wrap yarn, it is to avoid form flyings on comb section separating needle and tangle, it is to avoid fabric occurs
Fault and broken yarn.
Complete after weaving, 600 meters of Cropping Length is weighed, pack, blank storage.In dyeing, be firstly added in auxiliary agent and
Caustic soda, is warming up to 90 DEG C of 60 min of holding with 2.5 DEG C/min speed, cools to 60 DEG C of overflows, draining, water inlet.Add HAC,
15 min are kept at 50 DEG C, after draining, water inlet, auxiliary agent and H are added2O2, it is warming up to 95 DEG C with 2.5 DEG C/min and keeps 120
Min, cools to 60 DEG C of overflows.15 min are kept at 45 DEG C, hot wash adds anti-creasing agent and water purification agent, dye is added successively afterwards twice
Material, first time Nacl, second Nacl, first time soda ash, second of soda ash, 60 DEG C are warming up to 1 DEG C/min.At 60 DEG C
Keep adding soda ash soaping agent after 40 min, overflow, cold water acidity, the min of draining 10.20 min, 60 DEG C of drainings are kept at 95 DEG C
Clean, add anti-creasing agent, levelling agent dyestuff, (NH2) 2SO2And HAC.It is warming up to 1 DEG C/min after 70 DEG C and keeps 10 min, then
Be warming up to after 95 DEG C and keep 30 min, 60 DEG C of overflows, 45 DEG C keep 15 min after hot wash twice, i.e., dyeing terminate.
Finally, the specification of finished product fabric is as follows：
Breadth is 210-220 cm, and grammes per square metre is 175-180 g/m2, close horizontal stroke is 16 w/cm, and it is 63-78 c/cm to indulge close.
The Main physical performance indications of finished product fabric are as follows：
Elastic extension is 110-180%（The kg of testing standard FZ/T 70006,3.5）, elastic recovery rate is >=85%（Test mark
The quasi- kg of FZ/T 70006,3.5）, bursting strength is 160-220 N.
The data area gone out given in above-mentioned each technological parameter is the data area as obtained by concrete practice, is respectively provided with
Certain feasibility, below by way of specific embodiment, the invention will be further described.
Warp knit production technology is single（On）
Warp knit production technology is single（Under）
Warp knit production technology list two（On）
Through warp knit production technology list two（Under）
By described above, the advantage of the invention is that：This production technology is by using 310-470 dtex spandexs by 80 S cottons
Yarn twists with the fingers looping in the opposite direction with it and weaves cotton ammonia wrap yarn, overcomes cotton yarn hairiness many and the shortcomings of ultimate strength is poor, guarantor
The advantages of staying cotton yarn moisturizing, absorbing sweat and excellent air permeable effect；Relative to being that raw material is passed through with chinlon filament, the bright and beautiful wrap yarn of spandex and cotton
For the lycra fabric compiled, present invention chinlon filament and cotton ammonia wrap yarn are adopted in warping and weaving process as raw material
With four comb institutional frameworks, 1 is chosen in weaving process and wears that 1 is empty and 1 sky 1 is worn entrys to yarn mode, two selvedges of fabric use 1
3 short side formulas are worn, chinlon filament and cotton ammonia wrap yarn are woven into the lycra fabric with mesh, the face of trying to stop people from fighting each other without mesh is overcome
Expect the problems such as permeability is not good and elastic weak, increase the fabric permeability, while ensureing the elasticity and response rate of the fabric.
Above content is to combine specific preferred embodiment further description made for the present invention, it is impossible to assert
The specific implementation of the present invention is confined to these explanations.For general technical staff of the technical field of the invention,
On the premise of not departing from present inventive concept, some simple deduction or replace can also be made, the guarantor of the present invention should be considered as belonging to
Protect scope.
Claims (8)
- The wire side material 1. crystal cotton is tried to stop people from fighting each other, it is characterised in that the fabric is formed by polyamide fibre, spandex and cotton yarn warp knit, the polyamide fibre, The mass percent of spandex and cotton yarn is respectively 51-63%, 18-28% and 19-21%, the fineness point of the polyamide fibre, spandex and cotton yarn Wei not 44 dtex, 310-470 dtex and 80 S.
- The wire side material 2. crystal cotton according to claim 1 is tried to stop people from fighting each other, the breadth of the fabric is 210-220 cm, gram of fabric Weight is 175-180 g/m2, the horizontal density of fabric is 16 w/cm, and the vertical density of fabric is 63-78 c/cm.
- The step of production technology of wire side material 3. crystal cotton according to claim 1 is tried to stop people from fighting each other, production technology, wraps successively Include warping, weaving, dyeing, it is characterised in that the warping and woven single comb institutional framework are：GB1 is combed：2-0,2-4,4-2,4-6,4-2,2-4//GB2 is combed：4-6,4-2,2-4,2-0,2-4,4-2//GB3 is combed：0-0,2-2//GB4 is combed：2-2,0-0//.
- The production technology of wire side material 4. crystal cotton according to claim 3 is tried to stop people from fighting each other, it is characterised in that the GB1 combs are used Raw material is chinlon filament, and the GB2 combs use raw material for chinlon filament, and the GB3 uses raw material for cotton ammonia wrap yarn, described GB4 combs use raw material for cotton ammonia wrap yarn.
- The production technology of wire side material 5. crystal cotton according to claim 4 is tried to stop people from fighting each other, it is characterised in that the cotton ammonia wrap yarn Line is to twist with the fingers 80 S cotton yarns with it using 310-470 dtex spandexs to be wrapped in the opposite direction.
- The production technology of wire side material 6. crystal cotton according to claim 3 is tried to stop people from fighting each other, it is characterised in that the warping and weaving During GB1 combs and GB2 combs be respectively arranged with separating needle, GB3 combs and GB4 combs need to remove separating needle.
- The production technology of wire side material 7. crystal cotton according to claim 3 is tried to stop people from fighting each other, it is characterised in that in the weaving process What four combs were taken, which entrys to yarn mode, is successively：GB1 combs wear 1 sky for 1, and GB2 combs are worn for 1 sky 1, and GB3 combs wear 1 sky, GB4 combs for 1 Worn for 1 sky 1.
- The production technology of wire side material 8. crystal cotton according to claim 3 is tried to stop people from fighting each other, it is characterised in that in the weaving process Two selvedges of fabric are taken 1 to wear 3 and empty entried to yarn mode, totally 6 groups.