CN106995662A - A kind of polishing powder polished used in ultra-thin glass eyeglass process and preparation method thereof - Google Patents
A kind of polishing powder polished used in ultra-thin glass eyeglass process and preparation method thereof Download PDFInfo
- Publication number
- CN106995662A CN106995662A CN201710286753.7A CN201710286753A CN106995662A CN 106995662 A CN106995662 A CN 106995662A CN 201710286753 A CN201710286753 A CN 201710286753A CN 106995662 A CN106995662 A CN 106995662A
- Authority
- CN
- China
- Prior art keywords
- parts
- polishing
- added
- ultra
- minutes
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of polishing powder polished used in ultra-thin glass eyeglass process and preparation method thereof, it is prepared from including following components, 50 100 parts of Brazil wax, 5 10 parts of beeswax, 35 parts of oxalic acid, 25 parts of oleic acid, 15 parts of surfactant, 8 10 parts of ammonium fluoride, 230 250 parts of mineral oil, 5 25 parts of oily organic siliconresin, 100 120 parts of neopelex, 57 parts of magnesium carbonate, 15 20 parts of 50% sodium hydrate aqueous solution, 40 50 parts of ammoniacal liquor, 30 40 parts of waterglass, 25 parts of sodium metasilicate, 23 parts of emulsifying agent, 56 parts of dispersant, 56 parts of cleaning agent.In polishing process, using the polishing agent of preparation, cut will not occur to camera lens surface, it can be incubated strong to simply being repaired at surface scratch, more importantly using the durability of polishing agent reinforcing glass simultaneously, strengthen light transmittance, while using polishing, glass surface is cleaned, the oil stain on surface is removed, is easy to overlay film, while strengthening intensity before overlay film, it is harmless without toxic effect, it is pollution-free, it is easy to use, repair and quick.
Description
Technical field:
The present invention relates to glass processing field, and in particular to a kind of polishing powder used in polishing ultra-thin glass eyeglass process and
Its preparation method.
Background technology:
Glass lens:It is the eyeglass being made using optical glass as raw material, the eyeglass with than other materials is more resistant to scraping, resistance to height
Temperature, eyeglass is relatively thin, it is not easy to scratching, and refractive index is high, and (ordinary tablet is 1.523, and superthin section is:More than 1.72, reach as high as 2.0)
The advantages of, but sheet glass is frangible, material is laid particular stress on.Do not have coloured glass lens to claim optics funeral broker (white tiles), coloured glass mirror
Pink in piece claims Kroc match eyeglass (red), and Kroc match eyeglass can absorb ultraviolet, to strong light slightly absorption.
The noun associated with glass lens has:Refractive index, A Erbei numbers, center of lens optics, light transmittance, spread glass eyeglass etc..
Glass polishing solution is directed to the novel polishing liquid of ultrahigh hardness Glass Design, and it is applied to all kinds of superhard glass, for example,
The characteristics of crystal works glass, high pbo glass, high boron glass, devitrified glass, optical quartz glass etc., this kind of glass being
Stability is good, and hardness is very high, is wasted time and energy when processing with common polishing fluid, and easily cause defect.
The content of the invention:
The technical problems to be solved by the invention are to overcome the defect of prior art to polish ultra-thin glass mirror there is provided one kind
Polishing powder used in piece process and preparation method thereof.
The technical problems to be solved by the invention are realized using following technical scheme.
A kind of polishing powder polished used in ultra-thin glass eyeglass process, it is characterised in that:It is prepared from including following components,
50-100 parts of Brazil wax, 5-10 parts of beeswax, 3-5 parts of oxalic acid, 2-5 parts of oleic acid, 1-5 parts of surfactant, fluorine
Change 8-10 parts of ammonium, 230-250 parts of mineral oil, 5-25 parts of oily organic siliconresin, 100-120 parts of neopelex, carbon
Sour magnesium 5-7 parts, 15-20 parts of 50% sodium hydrate aqueous solution, 40-50 parts of ammoniacal liquor, 30-40 parts of waterglass, 2-5 parts of sodium metasilicate, breast
2-3 parts of agent, 5-6 parts of dispersant, 5-6 parts of cleaning agent.
Preferred scheme one:It is prepared from including following components,
50 parts of Brazil wax, 5 parts of beeswax, 3 parts of oxalic acid, 2 parts of oleic acid, 1 part of surfactant, 8 parts of ammonium fluoride, mineral oil
230 parts, 5 parts of oily organic siliconresin, 100 parts of neopelex, 5 parts of magnesium carbonate, 50% sodium hydrate aqueous solution 15
Part, 40 parts of ammoniacal liquor, 30 parts of waterglass, 2 parts of sodium metasilicate, 2 parts of emulsifying agent, 5 parts of dispersant, 5 parts of cleaning agent.
Preferred scheme two:It is prepared from including following components,
100 parts of Brazil wax, 10 parts of beeswax, 5 parts of oxalic acid, 5 parts of oleic acid, 5 parts of surfactant, 10 parts of ammonium fluoride, ore deposit
250 parts of thing oil, 25 parts of oily organic siliconresin, 120 parts of neopelex, 7 parts of magnesium carbonate, 50% sodium hydroxide are water-soluble
20 parts of liquid, 50 parts of ammoniacal liquor, 40 parts of waterglass, 5 parts of sodium metasilicate, 3 parts of emulsifying agent, 6 parts of dispersant, 6 parts of cleaning agent.
A kind of polishing powder, preparation method thereof polished used in ultra-thin glass eyeglass process, it is characterised in that:Comprise the following steps
Step 1:Brazil wax is heated, with waterglass after thawing, stirring, 5-9 minutes;
Step 2:160 DEG C -170 DEG C are warming up to again, add emulsifying agent, 50% sodium hydrate aqueous solution, heating stirring, duration
10 minutes;
Step 3:Mineral oil is added, is stirred, 5-9 minutes, is lighted, neopelex is added in combustion process,
After burning 10-15 minutes, ammoniacal liquor covering is added;
Step 4:It is put into refrigerating chamber, carries out -15 DEG C of freezings;
Step 5:Freezing is formed after block, takes out, magnesium carbonate is poured on ice cube, lighted, in combustion process, adds beeswax;
Step 6:After 1 minute, cleaning agent is sprayed, 1 day is stood, extruded, filtering takes solid;
Step 7:Oxalic acid and oleic acid are mixed;
Step 8:Mixed solvent and surfactant are added in bottle, stirred, 2-3 minutes;
Step 9:Heating bottle, to 81-86 DEG C, adds oily organic siliconresin, continues to stir 1 hour;
Step 10:Sodium metasilicate is added, continues to react stirring 10 minutes;
Step 11:110 DEG C are warming up to again, solid is added, is stirred, and are incorporated wherein to solid, are eventually adding dispersant
Terminating reaction, cooling;
Step 12:Place in the sun, stand 2 days, extruding takes solid, pulverized.
Beneficial effect is to realize the ultra-thin camera eyeglass of small size in mobile phone by the technique, flat board, on computer should
With so that product can accomplish exquisiter, attractive in appearance, more importantly, in polishing process, will not using the polishing agent of preparation
There is cut to camera lens surface, while polishing agent reinforcing glass can more importantly be utilized to simply being repaired at surface scratch
Durability, insulation is strong, strengthens light transmittance, while using polishing, glass surface is cleaned, the oil stain on removal surface,
It is easy to overlay film, while strengthening intensity before overlay film, no toxic effect is harmless, pollution-free, easy to use, repairs and quick.
Embodiment:
In order that the technical means, the inventive features, the objects and the advantages of the present invention are easy to understand, tie below
Specific embodiment is closed, the present invention is expanded on further.
A kind of polishing powder polished used in ultra-thin glass eyeglass process,
Preferred scheme one:It is prepared from including following components,
50 parts of Brazil wax, 5 parts of beeswax, 3 parts of oxalic acid, 2 parts of oleic acid, 1 part of surfactant, 8 parts of ammonium fluoride, mineral oil
230 parts, 5 parts of oily organic siliconresin, 100 parts of neopelex, 5 parts of magnesium carbonate, 50% sodium hydrate aqueous solution 15
Part, 40 parts of ammoniacal liquor, 30 parts of waterglass, 2 parts of sodium metasilicate, 2 parts of emulsifying agent, 5 parts of dispersant, 5 parts of cleaning agent.
A kind of polishing powder, preparation method thereof polished used in ultra-thin glass eyeglass process, it is characterised in that:Comprise the following steps
Step 1:Brazil wax is heated, with waterglass after thawing, stirring, 5-9 minutes;
Step 2:160 DEG C -170 DEG C are warming up to again, add emulsifying agent, 50% sodium hydrate aqueous solution, heating stirring, duration
10 minutes;
Step 3:Mineral oil is added, is stirred, 5-9 minutes, is lighted, neopelex is added in combustion process,
After burning 10-15 minutes, ammoniacal liquor covering is added;
Step 4:It is put into refrigerating chamber, carries out -15 DEG C of freezings;
Step 5:Freezing is formed after block, takes out, magnesium carbonate is poured on ice cube, lighted, in combustion process, adds beeswax;
Step 6:After 1 minute, cleaning agent is sprayed, 1 day is stood, extruded, filtering takes solid;
Step 7:Oxalic acid and oleic acid are mixed;
Step 8:Mixed solvent and surfactant are added in bottle, stirred, 2-3 minutes;
Step 9:Heating bottle, to 81-86 DEG C, adds oily organic siliconresin, continues to stir 1 hour;
Step 10:Sodium metasilicate is added, continues to react stirring 10 minutes;
Step 11:110 DEG C are warming up to again, solid is added, is stirred, and are incorporated wherein to solid, are eventually adding dispersant
Terminating reaction, cooling;
Step 12:Place in the sun, stand 2 days, extruding takes solid, pulverized.
Preferred scheme two:It is prepared from including following components,
100 parts of Brazil wax, 10 parts of beeswax, 5 parts of oxalic acid, 5 parts of oleic acid, 5 parts of surfactant, 10 parts of ammonium fluoride, ore deposit
250 parts of thing oil, 25 parts of oily organic siliconresin, 120 parts of neopelex, 7 parts of magnesium carbonate, 50% sodium hydroxide are water-soluble
20 parts of liquid, 50 parts of ammoniacal liquor, 40 parts of waterglass, 5 parts of sodium metasilicate, 3 parts of emulsifying agent, 6 parts of dispersant, 6 parts of cleaning agent.
A kind of polishing powder, preparation method thereof polished used in ultra-thin glass eyeglass process, it is characterised in that:Comprise the following steps
Step 1:Brazil wax is heated, with waterglass after thawing, stirring, 5-9 minutes;
Step 2:160 DEG C -170 DEG C are warming up to again, add emulsifying agent, 50% sodium hydrate aqueous solution, heating stirring, duration
10 minutes;
Step 3:Mineral oil is added, is stirred, 5-9 minutes, is lighted, neopelex is added in combustion process,
After burning 10-15 minutes, ammoniacal liquor covering is added;
Step 4:It is put into refrigerating chamber, carries out -15 DEG C of freezings;
Step 5:Freezing is formed after block, takes out, magnesium carbonate is poured on ice cube, lighted, in combustion process, adds beeswax;
Step 6:After 1 minute, cleaning agent is sprayed, 1 day is stood, extruded, filtering takes solid;
Step 7:Oxalic acid and oleic acid are mixed;
Step 8:Mixed solvent and surfactant are added in bottle, stirred, 2-3 minutes;
Step 9:Heating bottle, to 81-86 DEG C, adds oily organic siliconresin, continues to stir 1 hour;
Step 10:Sodium metasilicate is added, continues to react stirring 10 minutes;
Step 11:110 DEG C are warming up to again, solid is added, is stirred, and are incorporated wherein to solid, are eventually adding dispersant
Terminating reaction, cooling;
Step 12:Place in the sun, stand 2 days, extruding takes solid, pulverized.
General principle, principal character and the advantages of the present invention of the present invention has been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the simply explanation described in above-described embodiment and specification is originally
The principle of invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (4)
1. a kind of polishing powder polished used in ultra-thin glass eyeglass process, it is characterised in that:It is prepared from including following components,
50-100 parts of Brazil wax, 5-10 parts of beeswax, 3-5 parts of oxalic acid, 2-5 parts of oleic acid, 1-5 parts of surfactant, ammonium fluoride
8-10 parts, 230-250 parts of mineral oil, 5-25 parts of oily organic siliconresin, 100-120 parts of neopelex, magnesium carbonate
5-7 parts, 15-20 parts of 50% sodium hydrate aqueous solution, 40-50 parts of ammoniacal liquor, 30-40 parts of waterglass, 2-5 parts of sodium metasilicate, emulsifying agent
2-3 parts, 5-6 parts of dispersant, 5-6 parts of cleaning agent.
2. the polishing powder used in a kind of polishing ultra-thin glass eyeglass process according to claim 1, it is characterised in that:Bag
Following components is included to be prepared from,
50 parts of Brazil wax, 5 parts of beeswax, 3 parts of oxalic acid, 2 parts of oleic acid, 1 part of surfactant, 8 parts of ammonium fluoride, mineral oil 230
Part, 5 parts of oily organic siliconresin, 100 parts of neopelex, 5 parts of magnesium carbonate, 15 parts of 50% sodium hydrate aqueous solution,
40 parts of ammoniacal liquor, 30 parts of waterglass, 2 parts of sodium metasilicate, 2 parts of emulsifying agent, 5 parts of dispersant, 5 parts of cleaning agent.
3. the polishing powder used in a kind of polishing ultra-thin glass eyeglass process according to claim 1, it is characterised in that:Bag
Following components is included to be prepared from,
100 parts of Brazil wax, 10 parts of beeswax, 5 parts of oxalic acid, 5 parts of oleic acid, 5 parts of surfactant, 10 parts of ammonium fluoride, mineral oil
250 parts, 25 parts of oily organic siliconresin, 120 parts of neopelex, 7 parts of magnesium carbonate, 50% sodium hydrate aqueous solution 20
Part, 50 parts of ammoniacal liquor, 40 parts of waterglass, 5 parts of sodium metasilicate, 3 parts of emulsifying agent, 6 parts of dispersant, 6 parts of cleaning agent.
4. a kind of polishing powder, preparation method thereof polished used in ultra-thin glass eyeglass process, it is characterised in that:Comprise the following steps
Step 1:Brazil wax is heated, with waterglass after thawing, stirring, 5-9 minutes;
Step 2:160 DEG C -170 DEG C are warming up to again, add emulsifying agent, 50% sodium hydrate aqueous solution, heating stirring, 10 points of duration
Clock;
Step 3:Mineral oil is added, is stirred, 5-9 minutes, is lighted, neopelex is added in combustion process, is burnt
After 10-15 minutes, ammoniacal liquor covering is added;
Step 4:It is put into refrigerating chamber, carries out -15 DEG C of freezings;
Step 5:Freezing is formed after block, takes out, magnesium carbonate is poured on ice cube, lighted, in combustion process, adds beeswax;
Step 6:After 1 minute, cleaning agent is sprayed, 1 day is stood, extruded, filtering takes solid;
Step 7:Oxalic acid and oleic acid are mixed;
Step 8:Mixed solvent and surfactant are added in bottle, stirred, 2-3 minutes;
Step 9:Heating bottle, to 81-86 DEG C, adds oily organic siliconresin, continues to stir 1 hour;
Step 10:Sodium metasilicate is added, continues to react stirring 10 minutes;
Step 11:110 DEG C are warming up to again, solid is added, is stirred, is incorporated wherein to solid, are eventually adding dispersant termination
Reaction, cooling;
Step 12:Place in the sun, stand 2 days, extruding takes solid, pulverized.