CN106988181A - A kind of luminous building block brick and preparation method thereof - Google Patents
A kind of luminous building block brick and preparation method thereof Download PDFInfo
- Publication number
- CN106988181A CN106988181A CN201611176241.7A CN201611176241A CN106988181A CN 106988181 A CN106988181 A CN 106988181A CN 201611176241 A CN201611176241 A CN 201611176241A CN 106988181 A CN106988181 A CN 106988181A
- Authority
- CN
- China
- Prior art keywords
- parts
- building block
- block brick
- glass
- brick
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of luminous building block brick and preparation method thereof, the luminous building block brick component is made up of cement, coarse-fine aggregate, sand, passivation glass, shape-fixing agent, appropriate amount of water；Passivation glass is to reflect the soft thin glass of light or is the bright coated glass of reflection light；Preparation method includes weighing component by weight, and mixer stirring pours into building blocks mould, obtains building block brick；Obtaining re-laying passivation glass after one layer of cement is smeared in building block brick upper surface, smearing shape-fixing agent after rolling, obtain luminous building block brick.The present invention is simple in construction, easy to use, only needs to just to complete to install by being mutually matched between splicing block and splicing groove between brick body, solves the single shortcoming of traditional brick body function, and making material energy-conserving and environment-protective.
Description
Technical field
The invention belongs to road pavement technical field, more particularly to a kind of luminous building block brick and preparation method thereof.
Background technology
At present, fragment of brick because its small volume, intensity is big the features such as, be widely used in building and road pavement, but
The function of traditional fragment of brick is more single, simply single to be used as construction material, its effectively effective area but not by
Sufficiently utilize.
In without the weaker environment of light source or light source, environment of the probability of happening much larger than light source abundance of accident, though
Right some areas are provided with the lighting apparatus such as street lamp, but these equipment are invariably costly, while space-consuming, in face of this feelings
How brick body, be effectively effectively combined, be urgent problem by condition with light source.
The common processing mode of cullet is buried for soil, but glass is not oxidizable, have impact on environmental protection；Cullet cannot be effective
Utilize；Traditional brick is in building structure is built by laying, and it is slower to build speed, and existing building block brick is at dim light or night
In, it is impossible to provide light, it is impossible to make driving safer.
The content of the invention
It is an object of the invention to provide a kind of luminous building block brick and preparation method thereof, it is intended to solves scrap glass now and obtains
Less than a kind of settling mode of effective recycling；Traditional brick is built in building structure is built by laying and speed of production is slower, and
And existing building block brick is in dim light or in night, it is impossible to provide light, it is impossible to make the problem of driving is safer.The present invention
Building block brick can be allowed under dim light or in night, and in the case of light can not being provided, using night spark remaining light or
Under the light-illuminating of vehicle, cullet can be allowed to allow road is clearer to show via the reflection of light, increase passerby
Driving and walking safety.
The present invention is achieved in that a kind of luminous building block brick, and luminous building block brick component by weight is by cement 75
Part~100 parts, 200 parts~240 parts of coarse-fine aggregate, 150 parts~188 parts of sand, 15 parts~30 parts of passivation glass, shape-fixing agent 3 parts~8
Part, appropriate amount of water composition.
Further, the passivation glass is to reflect the soft thin glass of light or is the bright coated glass of reflection light.
Further, coarse-fine aggregate particle diameter is less than 8mm；
The addition of water will ask for Optimum according to moulding process.
Another object of the present invention is to provide a kind of preparation method of luminous building block brick, the preparation method of the luminous building block brick
Comprise the following steps：
75 parts~100 parts of cement, 200 parts~240 parts of coarse-fine aggregate, 150 parts~188 parts of sand, passivation are weighed by weight
15 parts~30 parts of glass, 3 parts~8 parts of shape-fixing agent, it is standby；
After 200 parts~240 parts of coarse-fine aggregate, the advanced mixer stirring 1min~5min of 150 parts~188 parts of sand, then add
Enter 75 parts~100 parts of cement；Add suitable quantity of water stirring 5min~10min after dry stirring 1min~5min；Obtain mixture slurry；
Mixture slurry is poured into building blocks mould, pressurizeed, form removal obtains building block brick；
Obtaining re-laying 15 parts~30 parts of passivation glass after one layer of cement is smeared in building block brick upper surface, applied after rolling
3 parts~8 parts shape-fixing agents are spread, luminous building block brick is obtained.
Further, the amount of one layer of cement is smeared according to can be completely by 15 parts~30 parts of passivation obtaining building block brick upper surface
Glass adhesion will ask for Optimum on building block brick；
Mixture slurry is poured into building blocks mould moulding pressure for 150kgf/cm2~300kgf/cm2。
Further, during coarse-fine aggregate level is matched somebody with somebody, 20%~30% is accounted for more than 2mm hole sizers；Glue bone ratio 1: 5.
Another object of the present invention is to provide a kind of flower nursery fence for being equipped with above-mentioned luminous building block brick.
The passivation glass for the luminous building block brick that the present invention is provided is cementing on brick surface, by the refraction of light, so as to reach hair
The effect of light, can be according to the type of brick, purposes, intensity etc., to change type of glass, meets the purposes used.For glass
It is required that, to ensure security standpoint, the glass one after crushing is obtuse angle, it is to avoid pedestrian scratches after falling down, from the refraction of light,
Glass can use thin, transparent glass, and the ratio of refraction with such glass light is milder, or with the glass after plated film, instead
The bright light shot out.
After the shaping of high pressure brick, a thin layer of glass and appropriate cement is sprinkled, after rolling, is finally smeared
Upper shape-fixing agent；Brick on pavement, can use lightweight aggregate, convenient to carry.
To handling glass acute angle using cyclone in the processing of glass obtuse angle, broken after waste and old glass is reclaimed
Broken, the glass broken off has sharp acute angle, and life security can be influenceed in the later stage uses and applies, so also having after broken
One procedure, is exactly the broken rear sharp glass of polishing, and the glass after crushing puts into cyclone, utilizes the blowout of machine
Wind makes between glass and glass phase mutual friction remove acute angle, it is out of service after, glass will carry out sub-sieve again, take the specification of needs to enter
Exercise and use, this just can guarantee that the security using the product.When under darkness, the good results are evident embodies for luminous brick
Come, at dusk, dim light, setting sun light is irradiated to road surface, and people are come over from distant place it can be found that having a sudden strain of a muscle on road surface
One light dodged, but these luminous points will not be dazzling, very soft, when night came, in road up train, car light irradiation exists
On road surface, there are many place's bright spots on a road.Under no lamp condition, one of light irradiation past, it is found that these
In the range of luminous point is restrained on one point, make driving safer.Cullet is set to be utilized effectively.
Compared with prior art, the beneficial effects of the invention are as follows：The luminous building block brick structure of the present invention is simple, installation side
Just, only need to by splicing block and splicing groove between being mutually matched just can complete install, save substantial amounts of manpower, saved into
This.
Luminous building block brick prepared by the preparation method of the present invention can be used for crossing or flower nursery fence, living area road,
Square road surface, municipal works road surfacing.By improving, luminous building block brick intensity can reach more than 40Mp.
Brief description of the drawings
Fig. 1 is luminous building block brick preparation method flow chart provided in an embodiment of the present invention.
Embodiment
In order to make the purpose , technical scheme and advantage of the present invention be clearer, with reference to embodiments, to the present invention
It is further elaborated.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, it is not used to
Limit the present invention.
The application principle of the present invention is explained in detail below in conjunction with the accompanying drawings.
As shown in figure 1, the embodiment of the present invention provides a kind of preparation method of luminous building block brick, comprise the following steps：
S101：Weigh by weight 75 parts~100 parts of cement, 200 parts~240 parts of coarse-fine aggregate, 150 parts~188 parts of sand,
15 parts~30 parts of passivation glass, 3 parts~8 parts of shape-fixing agent, it is standby；
S102：After 200 parts~240 parts of coarse-fine aggregate, the advanced mixer stirring 1min~5min of 150 parts~188 parts of sand,
Add 75 parts~100 parts of cement；Add suitable quantity of water stirring 5min~10min after dry stirring 1min~5min；Obtain mixture slurry；
S103：Mixture slurry is poured into building blocks mould, pressurizeed, form removal obtains building block brick；
S104：Obtaining re-laying 15 parts~30 parts of passivation glass after one layer of cement is smeared in building block brick upper surface, rolling
Apply afterwards and spread 3 parts~8 parts shape-fixing agents, obtain luminous building block brick.
Further, the amount of one layer of cement is smeared according to can be completely by 15 parts~30 parts of passivation obtaining building block brick upper surface
Glass adhesion will ask for Optimum on building block brick；
Mixture slurry is poured into building blocks mould moulding pressure for 150kgf/cm2~300kgf/cm2。
Further, during coarse-fine aggregate level is matched somebody with somebody, 20%~30% is accounted for more than 2mm hole sizers；Glue bone ratio 1: 5.
A kind of luminous building block brick provided in an embodiment of the present invention, luminous building block brick component by weight is by 75 parts of cement
~100 parts, 200 parts~240 parts of coarse-fine aggregate, 150 parts~188 parts of sand, 15 parts~30 parts of passivation glass, shape-fixing agent 3 parts~8
Part, appropriate amount of water composition.
Further, the passivation glass is to reflect the soft thin glass of light or is the bright coated glass of reflection light.
Further, coarse-fine aggregate particle diameter is less than 8mm；
The addition of water will ask for Optimum according to moulding process.
The application principle of the present invention is described further with reference to specific embodiment.
The passivation glass for the luminous building block brick that the present invention is provided is cementing on brick surface, by the refraction of light, so as to reach hair
The effect of light, can be according to the type of brick, purposes, intensity etc., to change type of glass, meets the purposes used.For glass
It is required that, to ensure security standpoint, the glass one after crushing is obtuse angle, it is to avoid pedestrian scratches after falling down, from the refraction of light,
Glass can use thin, transparent glass, and the ratio of refraction with such glass light is milder, or with the glass after plated film, instead
The bright light shot out.
After the shaping of high pressure brick, a thin layer of glass and appropriate cement is sprinkled, after rolling, is finally smeared
Upper shape-fixing agent；Brick on pavement, can use lightweight aggregate, convenient to carry.
To handling glass acute angle using cyclone in the processing of glass obtuse angle, broken after waste and old glass is reclaimed
Broken, the glass broken off has sharp acute angle, and life security can be influenceed in the later stage uses and applies, so also having after broken
One procedure, is exactly the broken rear sharp glass of polishing, and the glass after crushing puts into cyclone, utilizes the blowout of machine
Wind makes between glass and glass phase mutual friction remove acute angle, it is out of service after, glass will carry out sub-sieve again, take the specification of needs to enter
Exercise and use, this just can guarantee that the security using the product.When under darkness, the good results are evident embodies for luminous brick
Come, at dusk, dim light, setting sun light is irradiated to road surface, and people are come over from distant place it can be found that having a sudden strain of a muscle on road surface
One light dodged, but these luminous points will not be dazzling, very soft, when night came, in road up train, car light irradiation exists
On road surface, there are many place's bright spots on a road.Under no lamp condition, one of light irradiation past, it is found that these
In the range of luminous point is restrained on one point, make driving safer.Cullet is set to be utilized effectively.
The luminous building block brick structure of the present invention is simple, easy for installation, only need to be by mutual between splicing block and splicing groove
Matching just can complete to install, and save substantial amounts of manpower, saved cost.
Luminous building block brick prepared by the preparation method of the present invention can be used for crossing or flower nursery fence, living area road,
Square road surface, municipal works road surfacing.By improving, luminous building block brick intensity can reach more than 40Mp.
In preparation method provided in an embodiment of the present invention,
1) selection of raw material：Luminous building block brick produced by the invention, need to typically select high-mark cement, preferably select
More than No. 42.5 cement, such as No. 52.5 portland cements.Early high, the 28d labels by force of cement will foot.
The rubble of 10mm particle diameters can not be had more than on aggregate selection principle, stone matter should be that (crush values index should not for hard stone
More than 12%), the preferred broken rubble of reaction type, grain shape is good, corner angle are small, sheet is few.Clay content is less than 1.5% for most
It is good.
The level of sand is with wanting reasonable, and sand in preferably selecting can fill 10% or so fine sand, to improve the compactness of product.
2) match ratio：Luminous building block brick produced by the invention and thickness bone used in concrete road pavement brick (30MPa~35MPa)
It is different that the level of material, which is matched somebody with somebody,.Concrete materials level be with can use a parameter --- " fineness modulus " is represented, it be one greatly
Cause the parameter being directly proportional to the mean size of particle in given aggregate.Computational methods are by one group of sieve aperture 10mm~0.15mm sieve
Son, with the screen over-size of each sieve (not including plate), is converted to the result obtained by cumulative percent addition, divided by 100 gained
Numerical value.
For concrete road pavement brick, greatly, then the surface texture of brick is coarse for " fineness modulus " of concrete materials；
" fineness modulus " is small, and the surface texture of brick will be more carefully.For lay port and pier road or municipal works luminous building block brick,
Both high intensity has been required, has required there is good-looking outward appearance again, therefore surface texture should not be too coarse.Generally 30MPa
Prevailing roadway brick concrete materials " fineness modulus " control be advisable (except secondary material distributing surface layer) 2.8 or so, and 40MPa with
The material " fineness modulus " of upper high-strength bricks for road surface need to be controlled 3.2 or so.
In the grading of aggregates of high-strength concrete pavior brick, 20%~30% should be accounted for more than 2mm hole sizers；Glue bone ratio general control exists
1: 5 or so.
The ratio of mud control for producing high-strength luminous building block brick is quite important, and amount of water is too low, then the hydration reaction of cement is not
Completely, cement gel growing amount is reduced, and the gelling power to aggregate around weakens, and produces pore, making the compactness of brick reduces, and inhales
Water rate is raised, and intensity declines；Amount of water is excessive, and luminous building block brick is through extruding in forming process, and cement mortar is largely extruded, meeting
The amount of gum material inside brick is reduced, and brick easily forms waist drum, and there is mold sticking, can equally influence the matter of brick in brick surface
Amount.
It may determine that whether the ratio of mud is suitable using intuitively method, the ratio of mud of the invention is controlled 0.1~0.6.Just
It is whether the side for observing the brick after shaping has clearly cement mortar appearance.If occurred without cement mortar, illustrate that the ratio of mud is relatively low；
If the cement mortar of large area occurs, then illustrate that the ratio of mud is higher.Best situation is that the side of brick has clearly cement mortar
Line, and it is apparent away from 1/3rd position suitable for reading.
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, all essences in the present invention
Any modifications, equivalent substitutions and improvements made within refreshing and principle etc., should be included in the scope of the protection.
Claims (7)
1. a kind of luminous building block brick, it is characterised in that luminous building block brick component by weight by 75 parts~100 parts of cement,
200 parts~240 parts of coarse-fine aggregate, 150 parts~188 parts of sand, 15 parts~30 parts of passivation glass, 3 parts~8 parts of shape-fixing agent, appropriate amount of water
Composition.
2. luminous building block brick as claimed in claim 1, it is characterised in that the passivation glass is the soft thin glass of refraction light
Or the coated glass become clear for reflection light.
3. luminous building block brick as claimed in claim 1, it is characterised in that coarse-fine aggregate particle diameter is less than 8mm；
The addition of water will ask for Optimum according to moulding process.
4. a kind of preparation method of luminous building block brick as claimed in claim 1, it is characterised in that the preparation of the luminous building block brick
Method comprises the following steps：
75 parts~100 parts of cement, 200 parts~240 parts of coarse-fine aggregate, 150 parts~188 parts of sand, passivation glass are weighed by weight
15 parts~30 parts, 3 parts~8 parts of shape-fixing agent, it is standby；
After 200 parts~240 parts of coarse-fine aggregate, the advanced mixer stirring 1min~5min of 150 parts~188 parts of sand, water is added
75 parts~100 parts of mud；Add suitable quantity of water stirring 5min~10min after dry stirring 1min~5min；Obtain mixture slurry；
Mixture slurry is poured into building blocks mould, pressurizeed, form removal obtains building block brick；
Obtaining re-laying 15 parts~30 parts of passivation glass after one layer of cement is smeared in building block brick upper surface, applying and spread after rolling
3 parts~8 parts shape-fixing agents, obtain luminous building block brick.
5. the preparation method of luminous building block brick as claimed in claim 4, it is characterised in that smeared obtaining building block brick upper surface
The amount of one layer of cement will ask for Optimum according to completely sticking to 15 parts~30 parts of passivation glass on building block brick；
Mixture slurry is poured into building blocks mould moulding pressure for 150kgf/cm2~300kgf/cm2。
6. the preparation method of luminous building block brick as claimed in claim 4, it is characterised in that during coarse-fine aggregate level is matched somebody with somebody, 2mm hole sizers
It is remaining to account for 20%~30%；Glue bone ratio 1: 5.
7. a kind of flower nursery fence for being equipped with luminous building block brick described in claim 1.