CN106987217A - Waterproof foam double-faced adhesive band - Google Patents
Waterproof foam double-faced adhesive band Download PDFInfo
- Publication number
- CN106987217A CN106987217A CN201710233170.8A CN201710233170A CN106987217A CN 106987217 A CN106987217 A CN 106987217A CN 201710233170 A CN201710233170 A CN 201710233170A CN 106987217 A CN106987217 A CN 106987217A
- Authority
- CN
- China
- Prior art keywords
- pressure
- sensitive adhesive
- layer
- solvent
- line
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Present invention is disclosed a kind of waterproof foam double-faced adhesive band, successively including release layer, the first pressure-sensitive adhesive layer, the first enhancement layer, the first flexible pressure-sensitive glue-line, foamed cotton layer, the second flexible pressure-sensitive glue-line, the second enhancement layer, the second pressure-sensitive adhesive layer.The invention provides a kind of waterproof foam double-faced adhesive band, water resistance is good, and adhesion strength is high, while high temperature resistant and cryogenic property are good, and cost of manufacture is cheap, can be with steady production.
Description
Technical field
The invention belongs to tape technology field, more particularly to a kind of waterproof foam double-faced adhesive band.
Background technology
With making rapid progress for electronic product, to the performance requirement more and more higher of double-faced adhesive tape, especially height is bonded
Intensity, high and low temperature resistance, water resistance etc..High and low temperature resistance generally refers to ensure quilt under high temperature or low temperature environment
Viscous thing does not fall off and has certain peel strength.Water resistance is primarily referred to as preventing water from bonding gusset from double faced adhesive tape and penetrating into,
Performance impact is caused to product.This high-low temperature resistant Waterproof double sticky tape is widely used, available for engineering machinery, automobile instrument panel
Seal foaming pad, washing machine sealing gasket etc., also in the various production technologies of digital product electronic component, engraving plate or face
The stickup of plate and part, especially because its heat resistance, available for interim fixed, the masking, film part in heating process
Deng the purposes such as protection, conveying, be also applied to high-temperature insulation protection, reinforcement protection of the industries such as electronic apparatus, instrument etc..
At present, two-sided tape is more based on normal temperature double-faced adhesive tape on the market, and without water resistance, part high temperature resistant is double
Most of face adhesive tape uses Kapton to be carrier, and organic silicon pressure-sensitive adhesive is the double-faced adhesive tape of main body,
It is high without water proofing property and price although it can be short of with resistance to more than 150 DEG C of high temperature on bonding force and contaminative
It is expensive;Also there is part high temperature resistant double-faced adhesive tape to use PET film for carrier, two sided coatings Modified Acrylic Ester Pressure Sensitive Adhesive or
Rubber pressure-sensitive adhesive sticks agent, although adhesion strength is than larger, and resistance to elevated temperatures is also preferable, but does not have water resistance equally.
In the market water-resistant type two-sided tape, it is common that using PE foams as carry base, two sided coatings rubber-type adhesive, silica gel or
Acrylic pressure sensitive adhesive.As shown in figure 1, being conventional double-faced adhesive tape structure schematic diagram, in the both sides of PE/PET foamed cotton layers 12
Coated with acrylic pressure sensitive glue-line 11 and 13, the side of acrylic pressure sensitive glue-line 13 is fitted with off-style paper layer 14.Water resistance all compares
Well, adhesion strength is high, and adhesive high and low temperature resistance is also good, but because foam is foaming structure, inside is containing many micro-
Hole, causes foam intensity decreases itself, especially in the case of a high temperature, foam intensity decreases itself it is more serious, have impact on bubble
The overall adhesion strength of cotton two-sided tape.3M production Waterproof double sticky tape --- VHB adhesive tapes, whole glue-line be it is integral, no
Containing any load base, there are many hole-closing structures inside colloid, adhesion strength is high, and resistance to elevated temperatures is good, and water resistance is excellent, but price is high
It is expensive.
The content of the invention
In view of the defect that above-mentioned prior art is present, the purpose of the present invention is to propose to a kind of adhesion strength height, high-low temperature resistant
Performance it is good and again have water resistance the two-sided foam tape of reinforced type, it is cheap, can as electronic applications double faced adhesive tape
Adhesive tape is used.
The purpose of the present invention will be achieved by the following technical programs:
A kind of waterproof foam double-faced adhesive band, successively including release layer, the first pressure-sensitive adhesive layer, the first enhancement layer, first is flexible
Pressure-sensitive adhesive layer, foamed cotton layer, the second flexible pressure-sensitive glue-line, the second enhancement layer, the second pressure-sensitive adhesive layer.
Further, first pressure-sensitive adhesive layer and second pressure-sensitive adhesive layer are by solvent-borne type polyacrylic pressure sensitive adhesive
Constitute;The solvent that the solvent-borne type polyacrylic pressure sensitive adhesive is used is organic solvent butyl oxide, methylisobutylketone, propane diols first
Ether, propylene glycol methyl ether acetate, propylene-glycol ethyl ether acetate, ethyl acetate, butyl acetate, ethyl lactate, methyl acetoacetate,
One or more in methyl acetoacetate;The thickness of first pressure-sensitive adhesive layer and second pressure-sensitive adhesive layer is respectively 25 μm
~60 μm.Solvent-borne type polyacrylic pressure sensitive adhesive, cohesive force is strong, and resistance to elevated temperatures is good, and thickness is 25 μm~60 μm, and thickness is less than
25 μm then bond the fastness of affixed object not enough, and thickness is also easy to produce larger compacted during glue-line stress if relatively slow higher than solidifying if 70 μm
Become and cause to bond failure, and cost is higher.
Further, first enhancement layer and second enhancement layer are constituted by PET film, and its thickness is 10 μm~25
μm.The thickness of PET film is in 10 μm~25 μ ms, and being primarily due to thickness can cause base material excessively thin less than 10 μm, existing life
Production. art is difficult reply, and thickness can then cause foam double-faced adhesive band resistance to warpage to be deteriorated more than 25 μm, meanwhile, because base material is thick
Degree is thickening to cause rise in price.
Further, the PET film is two-sided corona base material, and surface tension is more than or equal to 50 dynes.
Further, the first flexible pressure-sensitive glue-line and the second flexible pressure-sensitive glue-line are by solvent-borne type acrylic pressure
Quick glue is constituted;The solvent that the solvent-borne type acrylic pressure sensitive adhesive is used is organic solvent butyl oxide, methylisobutylketone, propane diols first
Ether, propylene glycol methyl ether acetate, propylene-glycol ethyl ether acetate, ethyl acetate, butyl acetate, toluene, one kind in dimethylbenzene or
It is a variety of;The first flexible pressure-sensitive glue-line and the second flexible pressure-sensitive bondline thickness are respectively 5 μm~25 μm, and thickness is less than 5 μ
M then the first enhancement layer, the second enhancement layer and foamed cotton layer adhesive fastness not enough, thickness be more than 25 μm then strain relief layer because
Stress meeting overrelaxation, causes bonding defect and cost is higher.
Further, the foamed cotton layer is made up of PE foams, and the coefficient of foaming of the PE foams is 3~5, and its thickness is
150 μm~250 μm.The foamed cotton layer is made up of PE foams, and it is closed-cell foam structure, and abscess is fine and close, and tensile strength is big, makes
During, stress can be effectively discharged, the adhesion strength of foam tape is improved.PE foamed cotton layers are closed-cell foam structure, foaming
Multiple is 3~5, and less than 3 buffering effects are weak, and sound absorption qualities and heat-proof quality are deteriorated, and higher than 5 cohesive strengths are poor, are being made
The tear of PE foams is easily caused during foam double-faced adhesive band use;Its thickness is 150 μm~250 μ ms, because thickness is less than
150 μm possibly can not effectively discharge the stress produced by external forces, and base material or glue-line can be caused to destroy, and thickness exceedes
250 μm can cause PE foamed cotton layers caused by high temperature or external forces are excessive creep and be permanently deformed.PE foams are not limited to routine
Color such as white, black, all kinds of color schemes can be debugged according to demand.
The present invention protrusion effect be:The invention provides a kind of waterproof foam double-faced adhesive band, water resistance is good, bonds strong
Degree is high, while high temperature resistant and cryogenic property are good, and cost of manufacture is cheap, can be with steady production.
Just accompanying drawing in conjunction with the embodiments below, the embodiment to the present invention is described in further detail, so that of the invention
Technical scheme is more readily understood, grasped.
Brief description of the drawings
Fig. 1 is the double-faced adhesive tape structure schematic diagram of prior art;
Fig. 2 is the structural representation of the embodiment of the present invention.
Embodiment
Embodiment 1
As shown in Fig. 2 a kind of waterproof foam double-faced adhesive band of the present embodiment, successively including release layer 1, the first pressure-sensitive adhesive layer
2, the first enhancement layer 3, the first flexible pressure-sensitive glue-line 4, foamed cotton layer 5, the second flexible pressure-sensitive glue-line 6, the second enhancement layer 7, the second pressure
Quick glue-line 8.
Release layer 1 is two-sided release liners, and the thickness of release layer 1 is 100 μm, and off-type force is 10g/inch.
First pressure-sensitive adhesive layer 2 and the second pressure-sensitive adhesive layer 8 are constituted by solvent-borne type polyacrylic pressure sensitive adhesive, and Tg points are less than-
40 DEG C, solid content is 25%;The solvent that solvent-borne type polyacrylic pressure sensitive adhesive is used is organic solvent ethyl acetate;First is pressure-sensitive
The thickness of the pressure-sensitive adhesive layer 8 of glue-line 2 and second is respectively 25 μm.
First enhancement layer 3 and the second enhancement layer 7 are constituted by PET film, and its thickness is 10 μm.PET film is two-sided corona base
Material, surface tension is more than or equal to 50 dynes.
First flexible pressure-sensitive glue-line 4 and the second flexible pressure-sensitive glue-line 6 are constituted by solvent-borne type acrylic pressure sensitive adhesive, solvent-borne type
Acrylic pressure sensitive adhesive solid content is 30%;The solvent that solvent-borne type acrylic pressure sensitive adhesive is used is ethyl acetate;First flexible pressure-sensitive
The thickness of 4 and second flexible pressure-sensitive glue-line of glue-line 6 is respectively 5 μm.
Foamed cotton layer 5 is made up of PE foams, and the coefficient of foaming of PE foams is 3, and its thickness is 150 μm.
The preparation method of the present embodiment is as follows:
1st, by the solvent-borne type acrylic pressure sensitive adhesive (scientific and technological (Changzhou) Co., Ltd of new synthetic fibre provides) of 50 parts by weight by blade coating
Device is coated on the PET film that thickness is 10 μm, is placed in baking oven and the glue-line of 5 μ m-thicks is formed after 80 DEG C of dry 2min, with 150 μ m-thicks
Spend the tow sides laminating of black PE foams, you can obtain by the first enhancement layer 3, the first flexible pressure-sensitive glue-line 4, foamed cotton layer 5, the
Two flexible pressure-sensitive glue-lines 6, the stress release buffer structure layer that the second enhancement layer 7 is constituted;
2nd, the solvent-borne type polyacrylic pressure sensitive adhesive (scientific and technological (Changzhou) Co., Ltd of new synthetic fibre provides) of 50 parts by weight is used into second
It is 25% that acetoacetic ester, which is diluted to solid content, and the isocyanate curing agent L-45 (Bayer offer) of 1.5 parts by weight of addition is simultaneously sufficient
Stir, the masking liquid is coated on release layer 1, be placed in baking oven after 90 DEG C of dry 4min, 25 μ m thicks of gained will be dried
The outside of glue-line and the first enhancement layer 3 fit, and same step is also fitted the pressure-sensitive adhesives of 25 μ m thicks on the outside of the second enhancement layer 7
Oxidant layer, is placed in (40 DEG C) of curing chamber and cures 3 days, produce waterproof foam double-faced adhesive band.
During using the present embodiment, the enhancement layer 3 of foamed cotton layer 5 and first and the second enhancement layer 7 together constitute stress release and delayed
Rush structure sheaf.When waterproof foam double-faced adhesive band bond the object such as product and during by external forces, can be effectively whole
The scattered stress of stress release buffer structure layer, prevents the foam tape tear caused by the stress concentration that the external world is produced.
Embodiment 2
As shown in Fig. 2 a kind of waterproof foam double-faced adhesive band of the present embodiment, successively including release layer 1, the first pressure-sensitive adhesive layer
2, the first enhancement layer 3, the first flexible pressure-sensitive glue-line 4, foamed cotton layer 5, the second flexible pressure-sensitive glue-line 6, the second enhancement layer 7, the second pressure
Quick glue-line 8.
Release layer 1 is two-sided release liners, and the thickness of release layer 1 is 100 μm, and off-type force is 10g/inch.
First pressure-sensitive adhesive layer 2 and the second pressure-sensitive adhesive layer 8 are constituted by solvent-borne type polyacrylic pressure sensitive adhesive, and Tg points are less than-
40 DEG C, solid content is 30%;The solvent that solvent-borne type polyacrylic pressure sensitive adhesive is used is ethyl acetate;The He of first pressure-sensitive adhesive layer 2
The thickness of second pressure-sensitive adhesive layer 8 is respectively 60 μm.
First enhancement layer 3 and the second enhancement layer 7 are constituted by PET film, and its thickness is 25 μm.PET film is two-sided corona base
Material, surface tension is more than or equal to 50 dynes.
First flexible pressure-sensitive glue-line 4 and the second flexible pressure-sensitive glue-line 6 are constituted by solvent-borne type acrylic pressure sensitive adhesive, solvent-borne type
Acrylic pressure sensitive adhesive solid content is 25%;The solvent that solvent-borne type acrylic pressure sensitive adhesive is used is ethyl acetate;First flexible pressure-sensitive
The thickness of 4 and second flexible pressure-sensitive glue-line of glue-line 6 is respectively 25 μm.
Foamed cotton layer 5 is made up of PE foams, and the coefficient of foaming of PE foams is 5, and its thickness is 250 μm.
The preparation method of the present embodiment is same as Example 1.
Embodiment 3
As shown in Fig. 2 a kind of waterproof foam double-faced adhesive band of the present embodiment, successively including release layer 1, the first pressure-sensitive adhesive layer
2, the first enhancement layer 3, the first flexible pressure-sensitive glue-line 4, foamed cotton layer 5, the second flexible pressure-sensitive glue-line 6, the second enhancement layer 7, the second pressure
Quick glue-line 8.
Release layer 1 is the two-sided mould release membrances of PET, and the thickness of release layer 1 is 100 μm, and off-type force is 10g/inch.
First pressure-sensitive adhesive layer 2 and the second pressure-sensitive adhesive layer 8 are constituted by solvent-borne type polyacrylic pressure sensitive adhesive, and Tg points are less than-
40 DEG C, solid content is 30%;The solvent that solvent-borne type polyacrylic pressure sensitive adhesive is used is ethyl acetate;The He of first pressure-sensitive adhesive layer 2
The thickness of second pressure-sensitive adhesive layer 8 is respectively 35 μm.
First enhancement layer 3 and the second enhancement layer 7 are constituted by PET film, and its thickness is 10 μm.PET film is two-sided corona base
Material, surface tension is more than or equal to 50 dynes.
First flexible pressure-sensitive glue-line 4 and the second flexible pressure-sensitive glue-line 6 are constituted by solvent-borne type acrylic pressure sensitive adhesive, solvent-borne type
Acrylic pressure sensitive adhesive solid content is 25%;The solvent that solvent-borne type acrylic pressure sensitive adhesive is used is ethyl acetate;First flexible pressure-sensitive
The thickness of 4 and second flexible pressure-sensitive glue-line of glue-line 6 is respectively 10 μm.
Foamed cotton layer 5 is made up of PE foams, and the coefficient of foaming of PE foams is 4, and its thickness is 200 μm.
The preparation method of the present embodiment is same as Example 1.
Embodiment 4
As shown in Fig. 2 a kind of waterproof foam double-faced adhesive band of the present embodiment, successively including release layer 1, the first pressure-sensitive adhesive layer
2, the first enhancement layer 3, the first flexible pressure-sensitive glue-line 4, foamed cotton layer 5, the second flexible pressure-sensitive glue-line 6, the second enhancement layer 7, the second pressure
Quick glue-line 8.
Release layer 1 is the two-sided mould release membrances of PET, and the thickness of release layer 1 is 100 μm, and off-type force is 10g/inch.
First pressure-sensitive adhesive layer 2 and the second pressure-sensitive adhesive layer 8 are constituted by solvent-borne type polyacrylic pressure sensitive adhesive, and Tg points are less than-
40 DEG C, solid content is 30%;The solvent that solvent-borne type polyacrylic pressure sensitive adhesive is used is butyl acetate;The He of first pressure-sensitive adhesive layer 2
The thickness of second pressure-sensitive adhesive layer 8 is respectively 45 μm.
First enhancement layer 3 and the second enhancement layer 7 are constituted by PET film, and its thickness is 15 μm.PET film is two-sided corona base
Material, surface tension is more than or equal to 50 dynes.
First flexible pressure-sensitive glue-line 4 and the second flexible pressure-sensitive glue-line 6 are constituted by solvent-borne type acrylic pressure sensitive adhesive, solvent-borne type
Acrylic pressure sensitive adhesive solid content is 25%;The solvent that solvent-borne type acrylic pressure sensitive adhesive is used is toluene and dimethylbenzene;First is flexible
The thickness of 4 and second flexible pressure-sensitive glue-line of pressure-sensitive adhesive layer 6 is respectively 15 μm.
Foamed cotton layer 5 is made up of PE foams, and the coefficient of foaming of PE foams is 4, and its thickness is 200 μm.
The preparation method of the present embodiment is same as Example 1.
Comparative example
By 50 parts by weight can high-low temperature resistant polyacrylate pressure-sensitive stick agent coating fluid be diluted to ethyl acetate it is solid
Content is 30%, adds the isocyanate curing agent L-45 (Bayer offer) of 1.5 parts by weight and sufficiently stirs, this is applied
Liquid is coated on mould release membrance or paper, is placed in baking oven after 90 DEG C of dry 4min, will dry the glue-line and 200 μ m-thicks of 48 μ m thicks of gained
The laminating of PE foamed cotton layers, same step also fits the pressure-sensitive adhesive oxidant layer of 48 μ m thicks in the opposite side of PE foams, is placed in ripe
Change (40 DEG C) of room to cure 3 days, produce waterproof foam double-faced adhesive band.
Embodiment 1-4 and comparative example are subjected to performance test experiments, test result is as follows:
Wherein, specific test experiments method is as follows:
1. release experiment
Sample is first cut into 43mm × 33mm sheets, inner rectangular hole is cut then at the four inside 2mm in side edge, four sides are straight
Severing is unable at angle, the sample cut one side is peeled off and is first pasted on 304 stainless steel plates after release material, then peels off another side
Release material be pasted on the rectangle frame positions of 304 stainless steels, it is desirable to paste smooth, bonding area is 288mm2, then
Room temperature after 5s is pressed to place 20min, the good cylindrical counterweight of clamping, by model stainless steel plate with 10Kg counterweights the test specimens prepared
Face down and by the rectangle frame of stainless steel puller system upper grip downward vertical direction every sky place, make release element center pair
Quasi-cylindrical counterweight, it is 10mm/min to set puller system downward velocity, then the release performance of test sample and records release most
Great force value, unit is N.
2. shrinkage test
First foam tape view picture is attached in light release liners, it is 70mm (longitudinal direction) × 50mm's (transverse direction) to cut into specification
Print 3, then the first engineering peeling paper of sample is peeled off, be positioned over normal temperature environment 4 hours, sample is measured using ruler
Longitudinal foam length (sample be from volume first open the beginning peel off more than 2 layers after be sampled), use precision for 0.001mm chi
Very little measuring instrument is tested, and records length L2 after former long L1 and 4h, finally utilizes formula " shrinkage factor=(L1-L2)/L1*
100% " shrinkage from mold dimensions;Shrinkage factor≤0.5 is OK, otherwise NG.
3. waterproofing tests
Sample is first cut into 30mm × 30mm sheets, inner rectangular hole, four sides are cut then at the four inside 1.5mm in side edge
Right angle is unable to severing, and the sample cut one side is peeled off and is first pasted on after release material on one block of PC plate material, then is peeled off another
The release material in face is pasted on another block of PC plate material, it is desirable to paste smooth, bonding area is 171mm2, then will be prepared
Test specimens with 10Kg counterweights press 5s after room temperature at least place 1min, the single-pass glass tube or plastic tube for reusing a length of 1m are filled with
Whether water, test model is put into pipe, take out and intake inside observation sealing area after 30min.
4. resistance to warping property test
First sample is cut in 25mm × 150mm strips, attached on a diameter of 5cm steel pipe, 24h is placed, seen
Examine whether sample tilts.
5. freeze impact property test
Sample is first cut into 25mm × 15mm sheets, PC is first pasted on after peeling the sample cut one side off release material
On sheet material, then peel off the release material of another side and be pasted in ABS plate, it is desirable to paste smooth, bonding area is
375mm2, the test specimens prepared are pressed with 10Kg counterweights low temperature baking oven are sent into after 5s, according to actual needs Selection experiment temperature
For 0 DEG C, -10 DEG C or -20 DEG C, taken out after 24h, sample is positioned over the high metopes of 1.2m, allows it to freely fall to ground, observed
Whether test specimens ftracture, generally higher than 5 times, and frequency is 2 times in 10s, if test model does not ftracture, to illustrate foam rubber
With qualified.
6. falling sphere is tested
Sample is first cut into 33mm × 33mm sheet, inner rectangular hole, four sides are cut then at the four inside 3mm in side edge
Right angle is unable to severing, and the sample cut one side is peeled off and is first pasted on PMMA sheet materials after release material, then peels off another side
Release material be pasted on the rectangle frame position of ABS plate, it is desirable to paste smooth, bonding area is 360mm2, will prepare
Good test model presses room temperature after 5s to place 24h with 10Kg counterweights, then test model is obtained into PMMA sheet materials one down and will be surveyed
Position is tried on the ground every sky placement, and a length of 125cm bilateral tubing one end is disposed vertically in test model test position
Surface, then allows No. 25 steel balls from bilateral tubing upper end center position free-falling shock-testing position, according to shock-testing
As a result falling ball impact test for several times is carried out, 15 Secondary Shocks experiments are at most carried out.If in 15 times test model be rushed to open if record falling sphere
Number of times, if after 15 times test model be not rushed to open if need to only record falling sphere number of times.
The present invention still has numerous embodiments, all technical sides formed by all use equivalents or equivalent transformation
Case, is within the scope of the present invention.
Claims (6)
1. a kind of waterproof foam double-faced adhesive band, it is characterised in that:Successively including release layer, the first pressure-sensitive adhesive layer, the first enhancement layer,
First flexible pressure-sensitive glue-line, foamed cotton layer, the second flexible pressure-sensitive glue-line, the second enhancement layer, the second pressure-sensitive adhesive layer.
2. waterproof foam double-faced adhesive band according to claim 1, it is characterised in that:First pressure-sensitive adhesive layer and described
Two pressure-sensitive adhesive layers are constituted by solvent-borne type polyacrylic pressure sensitive adhesive;The solvent that the solvent-borne type polyacrylic pressure sensitive adhesive is used
For organic solvent butyl oxide, methylisobutylketone, propylene glycol monomethyl ether, propylene glycol methyl ether acetate, propylene-glycol ethyl ether acetate, acetic acid
One or more in ethyl ester, butyl acetate, ethyl lactate, methyl acetoacetate, methyl acetoacetate;First pressure sensitive adhesive
The thickness of layer and second pressure-sensitive adhesive layer is respectively 25 μm~60 μm.
3. waterproof foam double-faced adhesive band according to claim 1, it is characterised in that:First enhancement layer and described second
Enhancement layer is constituted by PET film, and its thickness is 10 μm~25 μm.
4. waterproof foam double-faced adhesive band according to claim 3, it is characterised in that:The PET film is two-sided corona base material,
Surface tension is more than or equal to 50 dynes.
5. waterproof foam double-faced adhesive band according to claim 1, it is characterised in that:The first flexible pressure-sensitive glue-line and institute
The second flexible pressure-sensitive glue-line is stated to constitute by solvent-borne type acrylic pressure sensitive adhesive;The solvent that the solvent-borne type acrylic pressure sensitive adhesive is used
For organic solvent butyl oxide, methylisobutylketone, propylene glycol monomethyl ether, propylene glycol methyl ether acetate, propylene-glycol ethyl ether acetate, acetic acid
One or more in ethyl ester, butyl acetate, toluene, dimethylbenzene;The first flexible pressure-sensitive glue-line and the second flexible pressure
Quick bondline thickness is respectively 5 μm~25 μm.
6. waterproof foam double-faced adhesive band according to claim 1, it is characterised in that:The foamed cotton layer is made up of PE foams,
The coefficient of foaming of the PE foams is 3~5, and its thickness is 150 μm~250 μm.