CN106987147A - 一种彩色沥青及其制备方法 - Google Patents

一种彩色沥青及其制备方法 Download PDF

Info

Publication number
CN106987147A
CN106987147A CN201710357430.2A CN201710357430A CN106987147A CN 106987147 A CN106987147 A CN 106987147A CN 201710357430 A CN201710357430 A CN 201710357430A CN 106987147 A CN106987147 A CN 106987147A
Authority
CN
China
Prior art keywords
parts
clay
color
preparation
color asphalt
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710357430.2A
Other languages
English (en)
Inventor
王筱天
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201710357430.2A priority Critical patent/CN106987147A/zh
Publication of CN106987147A publication Critical patent/CN106987147A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种彩色沥青及其制备方法，以质量份数计，由以下组分组成：无机颜料10‑20份，浅色乳化沥青30‑60份，陶土10‑20份，橡胶粉10‑14份。本发明一种彩色沥青及其制备方法的有益效果是，陶土与颜料加入浅色乳化沥青，可以制成其他彩色的沥青，从而生产出各种颜色的沥青，对于公路应用来说色彩丰富，避免单一深色路面导致司机出现视觉疲劳。陶土具有优异的抗冻融特性和耐高温特性，使得彩色沥青的低温抗冻性能得到提升，在温度低时，防止出现裂纹，影响公路使用寿命，在高温时则可以防止变软。

Description

一种彩色沥青及其制备方法
技术领域
本发明属于材料制备技术领域，涉及一种彩色沥青，本发明还涉及上述沥青的制备方法。
背景技术
沥青是一种对温度很敏感的材料，随着温度升高，沥青会变软，粘结力下降，温度下降时会变稠、变脆，丧失粘结力。在夏季高温地区，沥青受温度影响性能变软，大型车辆通过时会形成压痕。冬天寒冷地区时，沥青则低温下变硬容易出现颜色衰减、脱色、裂纹。这些影响了公路的使用寿命，并且黑色沥青路面长久让司机会视觉疲劳，容易引发交通意外。
发明内容
本发明的目的是提供一种彩色沥青，解决了现有技术中沥青受温度影响容易产生压痕或裂纹、色彩单一容易引发视觉疲劳的问题。
本发明还提供了一种上述沥青的制备方法。
本发明所采用的技术方案是，一种彩色沥青，以质量份数计，由以下组分组成：无机颜料10-20份，浅色乳化沥青30-60份，陶土10-20份，橡胶粉10-14份。
本发明的特征还在于，
所述陶土大小为15-20目。
本发明另一种技术方案，一种彩色沥青的制备方法，按照以下步骤进行：
步骤一，
在搅拌罐中倒入自来水，将搅拌罐放入分散机下进行分散，分散机转速1000r/min，时间为3-5分钟；
步骤二，
以质量份数计，称取无机颜料10-20份，浅色乳化沥青30-60份，陶土10-20份，橡胶粉10-14份，将以上组分依次加入搅拌罐内，并放入分散机下进行分散，分散机转速800r/min，时间为5-10分钟，即得。
本发明的有益效果是，陶土与颜料加入浅色乳化沥青，可以制成其他彩色的沥青，从而生产出各种颜色的沥青，对于公路应用来说色彩丰富，避免单一深色路面导致司机出现视觉疲劳。陶土具有优异的抗冻融特性和耐高温特性，使得彩色沥青的低温抗冻性能得到提升，在温度低时，防止出现裂纹，影响公路使用寿命，在高温时则可以防止变软。
具体实施方式
下面结合具体实施方式对本发明进行详细说明。
本发明一种彩色沥青，以质量份数计，由以下组分组成：无机颜料10-20份，浅色乳化沥青30-60份，陶土10-20份，橡胶粉10-14份。
所述陶土大小为15-20目。
本发明一种彩色沥青的制备方法，按照以下步骤进行：
步骤一，
在搅拌罐中倒入自来水，将搅拌罐放入分散机下进行分散，分散机转速1000r/min，时间为3-5分钟；
步骤二，
以质量份数计，称取无机颜料10-20份，浅色乳化沥青30-60份，陶土10-20份，橡胶粉10-14份，将以上组分依次加入搅拌罐内，并放入分散机下进行分散，分散机转速800r/min，时间为5-10分钟，即得。
本发明一种彩色沥青及其制备方法，陶土与颜料加入浅色乳化沥青，可以制成其他彩色的沥青，从而生产出各种颜色的沥青，对于公路应用来说色彩丰富，避免单一深色路面导致司机出现视觉疲劳。陶土具有优异的抗冻融特性和耐高温特性，使得彩色沥青的低温抗冻性能得到提升，在温度低时，防止出现裂纹，影响公路使用寿命，在高温时则可以防止变软。
实施例1
在搅拌罐中倒入自来水，将搅拌罐放入分散机下进行分散，分散机转速1000r/min，时间为3分钟；以质量份数计，称取无机颜料10份，浅色乳化沥青30份，陶土10份，橡胶粉10份，将以上组分依次加入搅拌罐内，并放入分散机下进行分散，分散机转速800r/min，时间为5分钟，即得。
实施例2
在搅拌罐中倒入自来水，将搅拌罐放入分散机下进行分散，分散机转速1000r/min，时间为4分钟；以质量份数计，称取无机颜料15份，浅色乳化沥青45份，陶土15份，橡胶粉12份，将以上组分依次加入搅拌罐内，并放入分散机下进行分散，分散机转速800r/min，时间为7分钟，即得。
实施例3
在搅拌罐中倒入自来水，将搅拌罐放入分散机下进行分散，分散机转速1000r/min，时间为5分钟；以质量份数计，称取无机颜料20份，浅色乳化沥青60份，陶土20份，橡胶粉14份，将以上组分依次加入搅拌罐内，并放入分散机下进行分散，分散机转速800r/min，时间为10分钟，即得。

Claims (3)

1.一种彩色沥青，其特征在于，以质量份数计，由以下组分组成：无机颜料10-20份，浅色乳化沥青30-60份，陶土10-20份，橡胶粉10-14份。
2.根据权利要求1所述的一种彩色沥青及其制备方法，其特征在于，所述陶土大小为15-20目。
3.一种如权利要求1所述的彩色沥青制备方法，其特征在于，按照以下步骤进行：
步骤一，
在搅拌罐中倒入自来水，将搅拌罐放入分散机下进行分散，分散机转速1000r/min，时间为3-5分钟；
步骤二，
以质量份数计，称取无机颜料10-20份，浅色乳化沥青30-60份，陶土10-20份，橡胶粉10-14份，将以上组分依次加入搅拌罐内，并放入分散机下进行分散，分散机转速800r/min，时间为5-10分钟，即得。
CN201710357430.2A 2017-05-19 2017-05-19 一种彩色沥青及其制备方法 Pending CN106987147A (zh)