CN106986537A - A kind of production technology for the glass door of elevator that changes colour - Google Patents
A kind of production technology for the glass door of elevator that changes colour Download PDFInfo
- Publication number
- CN106986537A CN106986537A CN201710208160.9A CN201710208160A CN106986537A CN 106986537 A CN106986537 A CN 106986537A CN 201710208160 A CN201710208160 A CN 201710208160A CN 106986537 A CN106986537 A CN 106986537A
- Authority
- CN
- China
- Prior art keywords
- elevator
- glass door
- component
- agbr
- casio
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses one kind discoloration glass door of elevator, include each component of following mass fraction:SiO2:40~60;AlPO4:10~15;CaSiO3:5~15;B2O3:6~10;NaOH:5~8;KCl:4~6;Li2O:2~5;AgBr:4~7;CuO:5~7;La2O3:2~4;SnO2:3~6.The present invention can make glass door of elevator adjust the shade of glass door of elevator according to extraneous intensity of illumination, keep the soft of transmitted ray, lift appreciation effect, while having higher modulus of elasticity and higher hardness.
Description
【Technical field】
The present invention relates to the technical field of glass door of elevator manufacture, particularly a kind of production technology for the glass door of elevator that changes colour
Technical field.
【Background technology】
With the continuous improvement of people's living standard and developing rapidly for construction industry, elevator has increasingly becomed the modern times and built
Build essential vertical transportation instrument, the outward appearance for the elevator that the design of elevator door is directly affected and straight, therefore, technology in the industry
Personnel constantly undergo technological transformation, attractive in appearance to seek low cost, reliably elevator door.With the popularization of sightseeing elevator, people
To the security requirement more and more higher of elevator, in order to meet the sight of sightseeing elevator, sightseeing elevator often takes glass door knot
Structure.But glass door of elevator is faced with integral light-transmitting while sight is met again, during elevator motion, due to the external world
The Strength Changes of light, cause strong light direct beam to produce injury to eyes, influence appreciation effect.
【The content of the invention】
The purpose of the present invention is exactly to solve the problems of the prior art, proposes a kind of production work for the glass door of elevator that changes colour
Skill, can make glass door of elevator adjust the shade of glass door of elevator according to extraneous intensity of illumination, keep the soft of transmitted ray
With appreciation effect is lifted, while having higher modulus of elasticity and higher hardness.
To achieve the above object, the present invention proposes a kind of discoloration glass door of elevator, includes each group of following mass fraction
Point:
Preferably, the mass fraction of each component is:SiO2:40~50;AlPO4:10~12;CaSiO3:5~10;
B2O3:6~8;NaOH:5~6;KCl:4~5;Li2O:2~4;AgBr:4~7;CuO:5~6;La2O3:2~3;SnO2:3~5.
Preferably, the mass fraction of each component is:SiO2:40~55;AlPO4:10~14;CaSiO3:10~
15;B2O3:7~10;NaOH:5~7;KCl:5~6;Li2O:3~5;AgBr:6~7;CuO:5~7;La2O3:3~4;SnO2:5
~6.
Preferably, the mass fraction of each component is:SiO2:50~60;AlPO4:12~15;CaSiO3:8~15;
B2O3:8~10;NaOH:6~7;KCl:5~6;Li2O:2~3;AgBr:4~5;CuO:6~7;La2O3:2~4;SnO2:4~
6。
The present invention proposes a kind of production technology for the glass door of elevator that changes colour, and comprises the following steps successively:
Step one:Contain SiO according to the weighing accurate in scale given by component2、AlPO4、CaSiO3、B2O3、NaOH、KCl、
Li2O、AgBr、CuO、La2O3、SnO2Raw material and uniformly mix, be prepared into qualified batch;
Step 2:Batch prepared by step one carries out three-stage in glass-melting furnace and founded, and glass melting temperature is followed successively by
1000~1200 DEG C, 1300~1400 DEG C, 1500~1660 DEG C, every section found after be incubated 1 hour, be prepared into qualified melting
Material;
Step 3:Melting charge prepared by step 2 carries out shaping cooling, obtains finished product, censorship, qualified rear packaging and storage.
Compared with prior art, the present invention can make glass door of elevator adjust glass door of elevator according to extraneous intensity of illumination
Shade, keeps the soft of transmitted ray, lifts appreciation effect, while having higher modulus of elasticity and higher hardness.
The feature and advantage of the present invention will be described in detail by embodiment.
【Embodiment】
A kind of discoloration glass door of elevator of the invention, includes each component of following mass fraction:
Embodiment one, the mass fraction of each component is:SiO2:40~50;AlPO4:10~12;CaSiO3:5~10;
B2O3:6~8;NaOH:5~6;KCl:4~5;Li2O:2~4;AgBr:4~7;CuO:5~6;La2O3:2~3;SnO2:3~5.
Embodiment two, the mass fraction of each component is:SiO2:40~55;AlPO4:10~14;CaSiO3:10~
15;B2O3:7~10;NaOH:5~7;KCl:5~6;Li2O:3~5;AgBr:6~7;CuO:5~7;La2O3:3~4;SnO2:5
~6.
Embodiment three, the mass fraction of each component is:SiO2:50~60;AlPO4:12~15;CaSiO3:8~15;
B2O3:8~10;NaOH:6~7;KCl:5~6;Li2O:2~3;AgBr:4~5;CuO:6~7;La2O3:2~4;SnO2:4~
6。
The present invention proposes a kind of production technology for the glass door of elevator that changes colour, and comprises the following steps successively:
Step one:Contain SiO according to the weighing accurate in scale given by component2、AlPO4、CaSiO3、B2O3、NaOH、KCl、
Li2O、AgBr、CuO、La2O3、SnO2Raw material and uniformly mix, be prepared into qualified batch;
Step 2:Batch prepared by step one carries out three-stage in glass-melting furnace and founded, and glass melting temperature is followed successively by
1000~1200 DEG C, 1300~1400 DEG C, 1500~1660 DEG C, every section found after be incubated 1 hour, be prepared into qualified melting
Material;
Step 3:Melting charge prepared by step 2 carries out shaping cooling, obtains finished product, censorship, qualified rear packaging and storage.
Compared with prior art, the present invention can make glass door of elevator adjust glass door of elevator according to extraneous intensity of illumination
Shade, keeps the soft of transmitted ray, lifts appreciation effect, while having higher modulus of elasticity and higher hardness.
Above-described embodiment is the description of the invention, is not limitation of the invention, it is any to simple transformation of the present invention after
Scheme belong to protection scope of the present invention.
Claims (5)
1. one kind discoloration glass door of elevator, it is characterised in that:Include each component of following mass fraction:
2. a kind of discoloration glass door of elevator as claimed in claim 1, it is characterised in that:The mass fraction of each component is:
SiO2:40~50;AlPO4:10~12;CaSiO3:5~10;B2O3:6~8;NaOH:5~6;KCl:4~5;Li2O:2~4;
AgBr:4~7;CuO:5~6;La2O3:2~3;SnO2:3~5.
3. a kind of discoloration glass door of elevator as claimed in claim 1, it is characterised in that:The mass fraction of each component is:
SiO2:40~55;AlPO4:10~14;CaSiO3:10~15;B2O3:7~10;NaOH:5~7;KCl:5~6;Li2O:3~5;
AgBr:6~7;CuO:5~7;La2O3:3~4;SnO2:5~6.
4. a kind of discoloration glass door of elevator as claimed in claim 1, it is characterised in that:The mass fraction of each component is:
SiO2:50~60;AlPO4:12~15;CaSiO3:8~15;B2O3:8~10;NaOH:6~7;KCl:5~6;Li2O:2~3;
AgBr:4~5;CuO:6~7;La2O3:2~4;SnO2:4~6.
5. a kind of production technology for the glass door of elevator that changes colour, it is characterised in that:Comprise the following steps successively:
Step one:Contain SiO according to the weighing accurate in scale given by component2、AlPO4、CaSiO3、B2O3、NaOH、KCl、Li2O、
AgBr、CuO、La2O3、SnO2Raw material and uniformly mix, be prepared into qualified batch;
Step 2:Batch prepared by step one carries out three-stage in glass-melting furnace and founded, and glass melting temperature is followed successively by 1000
~1200 DEG C, 1300~1400 DEG C, 1500~1660 DEG C, every section found after be incubated 1 hour, be prepared into qualified melting charge;
Step 3:Melting charge prepared by step 2 carries out shaping cooling, obtains finished product, censorship, qualified rear packaging and storage.