CN106978667A - A kind of screen cloth preparation method - Google Patents
A kind of screen cloth preparation method Download PDFInfo
- Publication number
- CN106978667A CN106978667A CN201710269593.5A CN201710269593A CN106978667A CN 106978667 A CN106978667 A CN 106978667A CN 201710269593 A CN201710269593 A CN 201710269593A CN 106978667 A CN106978667 A CN 106978667A
- Authority
- CN
- China
- Prior art keywords
- screen cloth
- monofilament
- pur
- tpee
- masterbatch
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to screen cloth manufacture technology field, more particularly, to a kind of screen cloth preparation method, the screen cloth is woven by monofilament and yarn by Computerized flat knitting machine before this, and monofilament is the elastic thread that surface has PUR；Then arranged using stenter of shaping, make cloth cover smooth, and during tentering is heated, the PUR of monofilament surface melts and by monofilament together with warp binds, forms screen cloth.Monofilament extrudes wire-drawing shape, PUR cladding TPEE plastic cement and color masterbatch using TPEE particles, Masterbatch and hot melt adhesive tablet by twin-screw extrusion equipment, and forming surface has the elastic thread of PUR.Openwork jacquard of the present invention is various, during tentering is heated, the PUR of monofilament surface melt and by monofilament together with warp binds, screen cloth is formed, the tissue of cloth cover is reinforced, does not result in the check crack phenomenon of cloth, service life is long, and process velocity is fast, and cost is low.
Description
Technical field
The present invention relates to screen cloth manufacture technology field, made more particularly, to elasticated net cloth.
Background technology
Existing elastic force screen cloth, most of to be made using rubber or synthetic rubber, braiding makes inconvenience, and pattern is limited.
It is all good using early stage elastic force, but using can cause elastic force to fail afterwards to a certain extent, cause the deformation of whole product, use the longevity
Life is short.
The content of the invention
It is an object of the invention to provide a kind of screen cloth preparation method, braiding makes easy, and gained screen cloth pattern is more, elastic force
It is good, it is unlikely to deform.
To reach above-mentioned purpose, the present invention is adopted the following technical scheme that：
A kind of screen cloth preparation method, the screen cloth is woven by monofilament and yarn by Computerized flat knitting machine before this, and monofilament is that surface has heat
The elastic thread of melten gel；Then arranged using stenter of shaping, make cloth cover smooth, and during tentering is heated, monofilament
The PUR on surface melts and by monofilament together with warp binds, forms screen cloth.
Such scheme is further：The monofilament is squeezed using TPEE particles, Masterbatch and hot melt adhesive tablet by twin-screw
Go out equipment extrusion wire-drawing shape, wherein, TPEE particles and Masterbatch are mixed into the first screw rod and melt extrusion, hot melt adhesive tablet injection
Melt extrusion in second screw rod, the material of two screw rods sprays wire drawing by same spinneret, and PUR is coated TPEE modelings
Glue and color masterbatch, forming surface has the elastic thread of PUR.
Such scheme is further：The TPEE particles, Masterbatch and hot melt adhesive tablet enter twin-screw extrusion equipment it
Preceding drying 4 ~ 6 hours, makes its moisture control below 0.5%.
Such scheme is further：TPEE plastic cement and color masterbatch content by weight on the monofilament is 60 ~ 90%, hot melt
Glue is 10 ~ 40% by weight content.
Such scheme is further：The housekeeping temperature of the sizing stenter is 110 ~ 160 degrees Celsius, during sizing
Between be 20 ~ 60 seconds.
Such scheme is further：The screen cloth of gained is used for the elastic force ribbon for making chair, sofa, bed.
It is compared with the prior art, the present invention has the advantages that：
1st, woven using Computerized flat knitting machine, openwork jacquard is various, during tentering is heated, the PUR of monofilament surface melt and
By monofilament together with warp binds, screen cloth is formed, the tissue of cloth cover is reinforced, does not result in the check crack phenomenon of cloth.
2nd, TPEE plastic cement has the elasticity of rubber and the intensity of engineering plastics；Soft segment assigns its elasticity, makes it as rubber；Firmly
Section assigns its processing characteristics, makes it as plastics；Compared with rubber, it has more preferable processing characteristics and longer service life；
Compared with engineering material, equally there is the characteristics of intensity is high, and pliability and dynamic mechanical are more preferably, elasticity is good；Utilize TPEE
The self character of material is combined with PUR, the textile is had an indeformable advantage of good stretching, and screen cloth can be with
It will not deform for a long time, service life is long.
3rd, monofilament is made together with warp binds using temperature during sizing, so as to play the work for tying up yarn fixation
With without the sizing of upper resin liquid, reduction textile passes through chemically treated process, makes product more environmentally-friendly；And process velocity is fast,
Cost is low.
Embodiment：
The present invention provides a kind of screen cloth preparation method, specifically, and the screen cloth is woven by monofilament and yarn by Computerized flat knitting machine before this,
Monofilament is the elastic thread that surface has PUR；Then arranged using stenter of shaping, make cloth cover smooth, and drawn in heating
During width, the PUR of monofilament surface melts and by monofilament together with warp binds, forms screen cloth.What this method made
Screen cloth, openwork jacquard is various, obtains more multi-configuration item, and lifting uses face, and screen cloth can be made as individual layer or double-decker, need to only pass through
Computerized flat knitting machine weaves.During tentering is heated, the PUR of monofilament surface melts and monofilament and warp binds exists
Together, screen cloth is formed, the tissue of cloth cover is reinforced, does not result in the check crack phenomenon of cloth.And without the sizing of upper resin liquid, reduce and spin
Fabric passes through chemically treated process, makes product more environmentally-friendly, and process velocity is fast, and cost is low.
Further, the monofilament passes through twin-screw extrusion to the present invention using TPEE particles, Masterbatch and hot melt adhesive tablet
Equipment extrude wire-drawing shape, wherein, TPEE particles, Masterbatch and hot melt adhesive tablet enter twin-screw extrusion equipment before drying 4 ~
6 hours, make its moisture control below 0.5%.TPEE particles and Masterbatch, which are mixed into the first screw rod, melts extrusion, hot melt
Micelle, which injects, melts extrusion in the second screw rod, the material of two screw rods sprays wire drawing by same spinneret, and makes PUR bag
TPEE plastic cement and color masterbatch are covered, forming surface has the elastic thread of PUR.Preferably, the TPEE plastic cement and color masterbatch on the monofilament
It is 60 ~ 90% by weight content, PUR is 10 ~ 40% by weight content.TPEE plastic cement has the elasticity and engineering of rubber
The intensity of plastics；Soft segment assigns its elasticity, makes it as rubber；Hard section assigns its processing characteristics, makes it as plastics；With rubber phase
Than it has more preferable processing characteristics and longer service life；Compared with engineering material, equally there is the characteristics of intensity is high, and
More preferably, elasticity is good for pliability and dynamic mechanical；It is combined using the self character and PUR of TPEE materials, makes the spinning
Fabric has the indeformable advantage of good stretching, and screen cloth will not can be deformed for a long time, and service life is long.
Further, the housekeeping temperature of the sizing stenter is 110 ~ 160 degrees Celsius, shaping time to the present invention
For 20 ~ 60 seconds.Heating tentering will be carried out by the woven cloth of Computerized flat knitting machine, make cloth cover smooth, it is whole that the condition meets heating
During reason, PUR, which melts, makes monofilament together with warp binds, so that each contact point is bonded together, reinforces cloth
The tissue in face, does not result in the check crack phenomenon of cloth.
It is applied to make the elastic force ribbon of chair, sofa, bed according to the screen cloth that the present invention makes, elasticity is good, durable in use.
Certainly, the present invention is elaborated above in association with embodiment, only technical concept to illustrate the invention and
Feature, it is therefore, all according to the present invention its object is to allow person skilled in the art to understand present disclosure and be carried out
The equivalent change or modification that Spirit Essence is done, should all cover within the scope of the present invention.
Claims (6)
1. a kind of screen cloth preparation method, it is characterised in that：The screen cloth is woven by monofilament and yarn by Computerized flat knitting machine before this, monofilament
It is the elastic thread that surface has PUR；Then arranged using stenter of shaping, make cloth cover smooth, and in heating tentering
During, the PUR of monofilament surface melts and by monofilament together with warp binds, forms screen cloth.
2. a kind of screen cloth preparation method according to claim 1, it is characterised in that：The monofilament using TPEE particles,
Masterbatch and hot melt adhesive tablet extrude wire-drawing shape by twin-screw extrusion equipment, wherein, TPEE particles and Masterbatch are mixed into the
Melt extrusion in one screw rod, hot melt adhesive tablet, which injects, melts extrusion in the second screw rod, the material of two screw rods passes through same spinneret
Wire drawing is sprayed, and PUR is coated TPEE plastic cement and color masterbatch, forming surface has the elastic thread of PUR.
3. a kind of screen cloth preparation method according to claim 2, it is characterised in that：The TPEE particles, Masterbatch and
Hot melt adhesive tablet is dried 4 ~ 6 hours before entering twin-screw extrusion equipment, makes its moisture control below 0.5%.
4. a kind of screen cloth preparation method according to claim 2, it is characterised in that：TPEE plastic cement and color on the monofilament
Female is 60 ~ 90% by weight content, and PUR is 10 ~ 40% by weight content.
5. a kind of screen cloth preparation method according to claim 1, it is characterised in that：The housekeeping of the sizing stenter
Temperature is 110 ~ 160 degrees Celsius, and shaping time is 20 ~ 60 seconds.
6. a kind of screen cloth preparation method according to claim 1 ~ 5 any one, it is characterised in that：The screen cloth of gained is used for
Make chair, sofa, the elastic force ribbon of bed.