CN106966692A - The pug formula and its pottery of a kind of health fictile - Google Patents

The pug formula and its pottery of a kind of health fictile Download PDF

Info

Publication number
CN106966692A
CN106966692A CN201611196006.6A CN201611196006A CN106966692A CN 106966692 A CN106966692 A CN 106966692A CN 201611196006 A CN201611196006 A CN 201611196006A CN 106966692 A CN106966692 A CN 106966692A
Authority
CN
China
Prior art keywords
health
fictile
tourmaline
warming
min speed
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201611196006.6A
Other languages
Chinese (zh)
Inventor
蔡少希
黄跃滨
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangzhou Hong Qi Environmental Protection Technology Co Ltd
Original Assignee
Guangzhou Hong Qi Environmental Protection Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangzhou Hong Qi Environmental Protection Technology Co Ltd filed Critical Guangzhou Hong Qi Environmental Protection Technology Co Ltd
Priority to CN201611196006.6A priority Critical patent/CN106966692A/en
Publication of CN106966692A publication Critical patent/CN106966692A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of pug formula of health fictile and its pottery, it is made by tourmaline, medical stone, ox bone, activated carbon powder, pure natural seabed float stone, clay, aluminium silicon-oxy tetrahedron and Himalaya mineral salt, each raw material is size-reduced, sieving, mixing, ball milling and be pressed into mud cake, then kettle shape base substrate is made to be fired, it is polished after natural cooling, you can.The present invention makes pottery pot using the tourmaline and medical stone for containing various trace elements as raw material, the energy dissolution various trace elements during use, thus to human body microelement-supplementing, and the pH of water in kettle can also be adjusted, to reach the purpose of health.

Description

The pug formula and its pottery of a kind of health fictile
Technical field
The present invention relates to health-promotion kettle field, the pug formula and its pottery of specifically a kind of health fictile.
Background technology
With constantly improving for people's living standard, the requirement to quality of the life and food health is also constantly being carried It is high.Existing kettle teapot is typically to be made of stainless steel, iron or aluminium, many in second-rate stainless steel to use reclaimed materials system Into easy when heating up water to discharge many harmful heavy metal ion, human body content of beary metal can be caused for a long time by drinking It is exceeded, or even cause heavy metal poisoning；Iron kettle is that iron section is melted into perfusion to form mostly, in order to which antirust can use chemistry inside iron kettle Coating, heated heat up water can also discharge multiple harmful substances.Although and aluminium kettle material is light, will not get rusty, aluminium is to human body Harm it is also larger.Although having occurred the pottery pot of various materials in the market, it also avoid above unlike material kettle and had The problem of having, but the using effect of these kettles is not fine, and the function without health.
The content of the invention
It is an object of the invention to provide a kind of pug formula of health fictile and its pottery, to solve the above-mentioned back of the body The problem of being proposed in scape technology.
To achieve the above object, the present invention provides following technical scheme：
A kind of pug formula of health fictile, is made by the material of following weight fraction：By following weight fraction Material be made：Tourmaline 10~16%, medical stone 10~14%, ox bone 8~12%, activated carbon powder 4~6%, pure day Right seabed float stone 4~6%, clay 40~50%, aluminium silicon-oxy tetrahedron 3~9%, Himalaya mineral salt 5~11%.
It is used as further scheme of the invention：It is made by the material of following weight fraction：Tourmaline 11~15%, wheat Meal stone 11~13%, ox bone 9~11%, activated carbon powder 4~6%, pure natural seabed float stone 4~6%, clay 42~48%, aluminium Silicon-oxy tetrahedron 4~8%, Himalaya mineral salt 6~10%.
It is used as further scheme of the invention：It is made by the material of following weight fraction：Tourmaline 13%, wheat meal Stone 12%, ox bone 10%, activated carbon powder 5%, pure natural seabed float stone 5%, clay 44%, aluminium silicon-oxy tetrahedron 5% likes horse traction Refined mineral salt 6%.
A kind of pottery of the pug formula of described health fictile, comprises the following steps：
(1) raw material tourmaline, medical stone, ox bone, activated carbon powder, pure natural seabed float stone, clay, aluminium silica four sides are prepared Body and Himalaya mineral salt, are crushed respectively, cross 240~300 mesh sieves, standby；
(2) it is uniformly mixed according to a ratio, dispensing is added to the water 4~6h of placement, natural cooling stirs, ball milling 50~ 60h, material：Ball：Water=1：(2.2~2.6)：(0.8~1.2), crosses 300~400 mesh sieves, is then pressed into mud cake stand-by；
(3) kettle shape base substrate is made in obtained mud cake；
(4) 600 DEG C are being warming up to 5~10 DEG C/min speed, then 980 are warming up to 15~20 DEG C/min speed~ 1020 DEG C and turn weak reductive firing atmosphere, are then warming up to 1160~1200 DEG C with 4~6 DEG C/min speed and turn middle reductive firings Atmosphere, then be warming up to 1240~1260 DEG C with 3~5 DEG C/min speed and turn weight reducing atmosphere, with 3~5 DEG C/min speed Constant temperature 12h at 1280~1300 DEG C, 1300 DEG C is warming up to, is finally stopped working, natural cooling；
(5) it is polished wait after the kettle shape base substrate natural cooling baked, you can.
Tourmaline, is a kind of special pole of structure containing more than the 10 kinds of trace element favourable to human body such as magnesium, aluminium, iron, boron Property crystalline solid.Itself can long-term negative ion release, trace element, purify water, can be with the chlorine in outlet running water, so as to change Become the acidity of water, remove harmful element, discharge the trace element beneficial to human body.
Medical stone, inorganic silicon-aluminum hydrochlorate, such as whole macroelements wanted containing needed by human body, potassium, sodium, calcium, magnesium, copper, molybdenum Deng 58 kinds of elements.With adsorptivity, dissolubility, modulability, bioactivity and mineralising, can adsorb the metal that dissociates in water from Son, the medical stone after being soaked through water, leachable 40 multiple element, wherein being trace element in nearly 20；In addition, also containing micro dilute Earth elements.Containing 15% or so aluminum oxide in medical stone, as neutral oxide, chance alkali, which reacts, in aqueous reduces pH Value, meets acid and reacts raising pH value, so that the function with bidirectional modulation pH.
Aluminium silicon-oxy tetrahedron, is alumino-silicate compound, whole alumina (silica) tetrahedron is carried negative electricity, to keep electricity Neutrality, easily adsorbs the cation such as K to positively charged+、Na+、Ca2+、Mg2+Plasma compensation balance.Exist in its character a lot Uniform passage and cavity, alumina (silica) tetrahedron internal surface area is up to 500~1000m2, can effectively adsorb, mistake Molecule of different sizes in many foreign gases and mixed gas and harmful substance are filtered, is preferable filtering or absorption new material.
Himalaya mineral salt, is mined salt from the deep ore deposits of 600 meters of the Himalaya, is that reserve is most in the world Big and purity highest crystal salt mineral reserve, composition contains 84 kinds of the mineral matters such as iodine, potassium, calcium, magnesium, iron, is more than the ten of common rock salt Times.All it is the element beneficial to the person, not comtaminated, 100% is pure natural, non-coloring, the rock salt of no processing, possesses release to people The beneficial anion of body；Radiation and human body identical natural frequency；Provide by the spectrum three produced by translucent crystal structure Plant natural functions.
Compared with prior art, the beneficial effects of the invention are as follows：
The present invention makes pottery pot using the tourmaline and medical stone for containing various trace elements as raw material, in the mistake used Energy dissolution various trace elements in journey, thus to human body microelement-supplementing, and the pH of water in kettle can also be adjusted, it is foster to reach Raw purpose.
Embodiment
Below in conjunction with the embodiment of the present invention, the technical scheme in the embodiment of the present invention is clearly and completely described, Obviously, described embodiment is only a part of embodiment of the invention, rather than whole embodiments.Based in the present invention Embodiment, the every other embodiment that those of ordinary skill in the art are obtained under the premise of creative work is not made, all Belong to the scope of protection of the invention.
Embodiment 1
The pug formula of health fictile, is made by the material of following weight fraction：Tourmaline 10%, medical stone 14%, ox bone 8%, activated carbon powder 6%, pure natural seabed float stone 4%, clay 50%, aluminium silicon-oxy tetrahedron 3%, Himalaya Mineral salt 5%.
In above-described embodiment, the pottery of the pug formula of health fictile, step is as follows：
(1) raw material tourmaline, medical stone, ox bone, activated carbon powder, pure natural seabed float stone, clay, aluminium silica four sides are prepared Body and Himalaya mineral salt, are crushed respectively, cross 240 mesh sieves, standby；
(2) it is uniformly mixed according to a ratio, dispensing is added to the water placement 4h, natural cooling stirs, ball milling 60h, material： Ball：Water=1：2.2：1.2,300 mesh sieves are crossed, mud cake are then pressed into stand-by；
(3) kettle shape base substrate is made in obtained mud cake；
(4) 600 DEG C are being warming up to 5 DEG C/min speed, then with 15 DEG C/min speed be warming up to 980 DEG C and turn it is weak also Former firing atmosphere, is then warming up to 1160 DEG C with 4 DEG C/min speed and turns middle reductive firing atmosphere, then with 3 DEG C/min speed It is warming up to 1240 DEG C and turns weight reducing atmosphere, constant temperature 12h at 1280 DEG C, 1300 DEG C is warming up to 3 DEG C/min speed, finally put out Fire, natural cooling；
(5) it is polished wait after the kettle shape base substrate natural cooling baked, you can.
Embodiment 2
The pug formula of health fictile, is made by the material of following weight fraction：Tourmaline 13%, medical stone 12%, ox bone 10%, activated carbon powder 5%, pure natural seabed float stone 5%, clay 44%, aluminium silicon-oxy tetrahedron 5%, Himalaya Mineral salt 6%.
In above-described embodiment, the pottery of the pug formula of health fictile, step is as follows：
(1) raw material tourmaline, medical stone, ox bone, activated carbon powder, pure natural seabed float stone, clay, aluminium silica four sides are prepared Body and Himalaya mineral salt, are crushed respectively, cross 270 mesh sieves, standby；
(2) it is uniformly mixed according to a ratio, dispensing is added to the water placement 5h, natural cooling stirs, ball milling 55h, material： Ball：Water=1：2.4：1,350 mesh sieves are crossed, mud cake are then pressed into stand-by；
(3) kettle shape base substrate is made in obtained mud cake；
(4) 600 DEG C are being warming up to 7.5 DEG C/min speed, then are being warming up to 1000 DEG C with 18 DEG C/min speed and turn Weak reductive firing atmosphere, is then warming up to 1180 DEG C with 5 DEG C/min speed and turns middle reductive firing atmosphere, then with 4 DEG C/min's Speed is warming up to 1250 DEG C and turns weight reducing atmosphere, is warming up to constant temperature 12h at 1290 DEG C, 1300 DEG C with 4 DEG C/min speed, most After stop working, natural cooling；
(5) it is polished wait after the kettle shape base substrate natural cooling baked, you can.
Embodiment 3
The pug formula of health fictile, is made by the material of following weight fraction：Tourmaline 16%, medical stone 10%, ox bone 12%, activated carbon powder 4%, pure natural seabed float stone 6%, clay 40%, aluminium silicon-oxy tetrahedron 5%, Himalaya Mineral salt 7%.
In above-described embodiment, the pottery of the pug formula of health fictile, step is as follows：
(1) raw material tourmaline, medical stone, ox bone, activated carbon powder, pure natural seabed float stone, clay, aluminium silica four sides are prepared Body and Himalaya mineral salt, are crushed respectively, cross 300 mesh sieves, standby；
(2) it is uniformly mixed according to a ratio, dispensing is added to the water placement 6h, natural cooling stirs, ball milling 60h, material： Ball：Water=1：2.6：0.8,400 mesh sieves are crossed, mud cake are then pressed into stand-by；
(3) kettle shape base substrate is made in obtained mud cake；
(4) 600 DEG C are being warming up to 10 DEG C/min speed, then are being warming up to 1020 DEG C with 20 DEG C/min speed and turn weak Reductive firing atmosphere, is then warming up to 1200 DEG C with 6 DEG C/min speed and turns middle reductive firing atmosphere, then with 5 DEG C/min speed Rate is warming up to 1260 DEG C and turns weight reducing atmosphere, is warming up to constant temperature 12h at 1300 DEG C, 1300 DEG C with 5 DEG C/min speed, finally It is flame-out, natural cooling；
(5) it is polished wait after the kettle shape base substrate natural cooling baked, you can.
It is obvious to a person skilled in the art that the invention is not restricted to the details of above-mentioned one exemplary embodiment, Er Qie In the case of without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, no matter From the point of view of which point, embodiment all should be regarded as exemplary, and be nonrestrictive, the scope of the present invention is by appended power Profit is required rather than described above is limited, it is intended that all in the implication and scope of the equivalency of claim by falling Change is included in the present invention.

Claims (4)

1. a kind of pug formula of health fictile, it is characterised in that be made by the material of following weight fraction：Tourmaline 10~16%, medical stone 10~14%, ox bone 8~12%, activated carbon powder 4~6%, pure natural seabed float stone 4~6%, clay 40~50%, aluminium silicon-oxy tetrahedron 3~9%, Himalaya mineral salt 5~11%.
2. the pug formula of health fictile according to claim 1, it is characterised in that by the material of following weight fraction It is made：Tourmaline 11~15%, medical stone 11~13%, ox bone 9~11%, activated carbon powder 4~6%, pure natural seabed Float stone 4~6%, clay 42~48%, aluminium silicon-oxy tetrahedron 4~8%, Himalaya mineral salt 6~10%.
3. the pug formula of health fictile according to claim 1, it is characterised in that by the material of following weight fraction It is made：Tourmaline 13%, medical stone 12%, ox bone 10%, activated carbon powder 5%, pure natural seabed float stone 5%, clay 44%, aluminium silicon-oxy tetrahedron 5%, Himalaya mineral salt 6%.
4. a kind of pottery of the pug formula of health fictile as described in claims 1 to 3 is any, it is characterised in that Comprise the following steps：
(1) prepare raw material tourmaline, medical stone, ox bone, activated carbon powder, pure natural seabed float stone, clay, aluminium silicon-oxy tetrahedron with And Himalaya mineral salt, crush respectively, cross 240~300 mesh sieves, it is standby；
(2) it is uniformly mixed according to a ratio, dispensing is added to the water 4~6h of placement, natural cooling stirs, 50~60h of ball milling, Material：Ball：Water=1：(2.2~2.6)：(0.8~1.2), crosses 300~400 mesh sieves, is then pressed into mud cake stand-by；
(3) kettle shape base substrate is made in obtained mud cake；
(4) 600 DEG C are being warming up to 5~10 DEG C/min speed, then 980~1020 is warming up to 15~20 DEG C/min speed DEG C and turn weak reductive firing atmosphere, then with 4~6 DEG C/min speed be warming up to 1160~1200 DEG C turn in reductive firing gas Atmosphere, then be warming up to 1240~1260 DEG C with 3~5 DEG C/min speed and turn weight reducing atmosphere, with 3~5 DEG C/min speed liter Temperature is finally stopped working to constant temperature 12h at 1280~1300 DEG C, 1300 DEG C, natural cooling；
(5) it is polished wait after the kettle shape base substrate natural cooling baked, you can.
CN201611196006.6A 2016-12-22 2016-12-22 The pug formula and its pottery of a kind of health fictile Pending CN106966692A (en)